Critical Current Density and Vortex Dynamics in Pristine and Irradiated KCa2Fe4As4F2.

We report the critical current density (Jc) and vortex pinning properties in single crystals of a novel iron-based superconductor (IBS) KCa2Fe4As4F2 with large Jc in the pristine state, before and after introduction of artificial defects by swift-particle irradiation. The effects of 2.6 GeV U and 3 MeV proton irradiations in KCa2Fe4As4F2 single crystals on transition temperature Tc and Jc, including its dose dependence, are systematically studied. Jc~8 MA/cm2 under a self-field at 2 K in the pristine crystal is strongly enhanced up to 19.4 and 17.5 MA/cm2 by irradiation of 2.6 GeV U-ions and 3 MeV protons, respectively. Suppression of Tc and dose dependence of Jc in KCa2Fe4As4F2 is different from that in a representative IBS of (Ba,K)Fe2As2, which can be explained by considering the presence of embedded defects in pristine KCa2Fe4As4F2. The vortex dynamics in the pristine and proton irradiated KCa2Fe4As4F2 single crystals are also investigated from the analyses of the field dependence of Jc and the normalized magnetic relaxation rate. In addition to the contribution of embedded defects, weak collective pinning is considered for comprehensive analyses. Vortex dynamics in KCa2Fe4As4F2 is similar to those in (Ba,K)Fe2As2 to some extent, and different from that in anisotropic Li0.8Fe0.2OHFeSe. Large anisotropy, due to the presence of insulating blocking layers in KCa2Fe4As4F2, which leads to much lower irreversibility field (Hirr) compared with 122-type IBSs, strongly affect the vortex dynamics.

Dynamics and mechanism of oxygen annealing in Fe1+yTe0.6Se0.4 single crystal.

Iron chalcogenide Fe(Te,Se) attracted much attention due to its simple structure, which is favorable for probing the superconducting mechanism. Its less toxic nature compared with iron arsenides is also advantageous for applications of iron-based superconductors. By intercalating spacer layers, superconducting transition temperature has been raised over 40 K. On the other hand, the presence of excess Fe is almost unavoidable in Fe(Te,Se) single crystals, which hinders the appearance of bulk superconductivity and causes strong controversies over its fundamental properties. Here we report a Systematical study of O2-annealing dynamics in Fe(1+y)Te(1-x)Sex by controlling the amount of O2, annealing temperature, and time. Bulk superconductivity can be gradually induced by increasing the amount of O2 and annealing time at suitable temperatures. The optimally annealed crystals can be easily obtained by annealing with ~1.5% molar ratio of oxygen at 400 °C for more than 1 hour. Superconductivity was witnessed to evolve mainly from the edge of the crystal to the central part. After the optimal annealing, the complete removal of excess Fe was demonstrated via STM measurements. Some fundamental properties were recharacterized and compared with those of as-grown crystals to discuss the influence of excess Fe.