RESUMO
The decomposition of methanol-d4 (CD3OD) on Rh nanoclusters grown by the deposition of Rh vapors onto an ordered thin film of Al2O3/NiAl(100) was studied, with various surface-probe techniques and largely under near-ambient-pressure (NAP) conditions. The results showed a superior reactivity of small Rh clusters (diameter < 1.5 nm) exposed to CD3OD at 5 × 10-3-0.1 mbar at 400 K; the gaseous production of CO and D2 from decomposed methanol-d4 per Rh surface site on the small Rh clusters with diameters of â¼1.1 nm was nearly 8 times that on large ones with diameters of â¼3.5 nm. The promotion of reactivity with decreased cluster size under NAP conditions was evidently greater than that under ultrahigh vacuum conditions. Moreover, the concentration of atomic carbon (C*; where * denotes adsorbate)-a key catalyst poisoner-yielded from the dissociation of CO* from dehydrogenated methanol-d4 was significantly smaller on small clusters (diameter < 1.5 nm). The NAP size effect on methanol-d4 decomposition involved the surface hydroxyl (OH*) from the little co-adsorbed water (H2O*) that was dissociated at a probability dependent on the cluster size. H2O* was more likely dissociated into OH* on small Rh clusters, by virtue of their more reactive d-band structure, and the OH* then effectively promoted the O-D cleavage of methanol-d4, as the rate-determining step, and thus the reaction probability; on the other hand, the OH* limited CO* dissociation on small Rh clusters via both adsorbate and lateral effects. These results suggest that the superior properties of small Rh clusters in both reactivity and anti-poisoning would persist and be highly applicable under "real-world" catalysis conditions.
RESUMO
We have studied the decomposition of methanol-d4 on thin film Al2O3/NiAl(100) under near-ambient-pressure conditions, with varied surface-probe techniques and calculations based on density-functional theory. Methanol-d4 neither adsorbed nor reacted on Al2O3/NiAl(100) at 400 K under ultrahigh vacuum conditions, whereas they dehydrogenated, largely to methoxy-d3 (CD3O*, * denoting adsorbates) and formaldehyde-d2 (CD2O*), on the surface when the methanol-d4 partial pressure was increased to 10-3 mbar and above. The dehydrogenation was facilitated by hydroxyl (OH* or OD*) from the dissociation of little co-adsorbed water; a small fraction of CD2O* interacted further with OH* (OD*) to form, via intermediate CD2OOH* (CD2OOD*), formic acid (DCOOH* or DCOOD*). A few surface carbonates were also yielded, likely on the defect sites of Al2O3/NiAl(100). The results suggest that alumina not only supports metal clusters but also participates in reactions under realistic catalytic conditions. One may consider accordingly the multiple functions of alumina while designing ideal catalysts.
RESUMO
Progress toward single-molecule electronics relies on a thorough understanding of the understanding of local physio-chemical processes and development of synthetic routines for controlled heterocoupling. We demonstrate a structurally unexpected ring closure process for a homo-coupled 4,4'-bipicenyl, realized in on-surface synthesis. An initial covalent C-C coupling of 4-bromopicene locks at lower temperatures the position and geometrically shields part of 4,4'-bipicenyl. Employing this effect of shielding might offer a path toward controlled stepwise hetero-coupling. At higher temperatures, a thermally activated three-dimensional rotation upon hydrogen dissociation, a dehydrogenative roto-cyclization, lifts the surface dimensionality restriction, and leads to the formation of a perylene. Thereby, the shielded molecular part becomes accessible again.