The aerosol pyrolysis method from nitrate precursors was used to prepare the Mn-CeO2 catalyst containing Mn2O3, CeO2, and Mn-doped CeO2 nanoparticles for catalyzing carbonous soot oxidation. The prepared Mn-CeO2 catalysts have high specific surface areas, Ce3+ ratio, and oxygen vacancy defects; these are a benefit for soot oxidation. The T50 for soot oxidation on the 0.57Mn-CeO2 catalyst is as low as 355 °C, which is 329 °C lower than that for soot oxidation without a catalyst. The catalysts were characterized using XRD, SEM-EDS, HRTEM, XPS, Raman spectroscopy, H2-TPR-MS, O2-TPD-MS, soot-TPR-MS, and operando DRIFTS-MS. The functions of Mn2O3, CeO2, and Mn-doped CeO2 in the 0.57Mn-CeO2 catalyst are unveiled. Mn-doped CeO2 plays a key role and CeO2 participates in soot oxidation, while Mn2O3 is used to enhance higher ratios of Ce3+, via the reaction of Mn3+ + Ce4+ = Mn4+ + Ce3+. The mechanism of soot oxidation on Mn-CeO2 was proposed.
RESUMO
The catalytic activity of a transition metal (host) oxide can be influenced by doping with a second cation (dopant), but the key factors dominating the activity of the doped catalyst are still controversial. Herein, CeO2 doped with Ni, Mn, and Y catalysts prepared using aerosol pyrolysis were used to demonstrate the positive, negative, and additive effects on CO oxidation as a model reaction. Various characterization results indicated that Ni, Mn, and Y had been successfully doped into the CeO2 lattice. The catalytic activities of each catalyst for CO conversion were in the order of Ni-CeO2 > Mn-CeO2 > CeO2 > Y-CeO2. Operando DRIFTS-MS and various characterization methods were applied to reveal the intrinsic nature of the doping effects. The accumulation rate of the surface bidentate carbonates determined the CO oxidation. A definition to evaluate the doping effect was proposed, which is anticipated to be useful for developing a rational catalyst with a high CO oxidation activity. The CO oxidation reactivities displayed strong correlations with the surface factors obtained from operando DRIFTS-MS analysis and the structure factors from XPS and Raman analyses.