Pressure-Induced Anion Order-Disorder Transition in Layered Perovskite Sr2LiHOCl2.

While cation order-disorder transitions have been extensively investigated because of their decisive impact on chemical and physical properties, only few anion order-disorder transitions are known. Here, we show that Sr2CuO2Cl2-type layered perovskite Sr2LiHOCl2 exhibits a pressure-induced H-/O2- order-disorder transition. When synthesized at ambient and low pressures (≤2 GPa), Sr2LiHOCl2 is isostructural to orthorhombic Eu2LiHOCl2 (Cmcm) with a H-/O2- order at the equatorial sites. However, applying a higher pressure (5 GPa) during synthesis causes the equatorial anions to be disordered, leading to a tetragonal symmetry (I4/mmm) with a loss of the superstructure. The structural analysis revealed that, in the ambient pressure phase, HLi2Sr4 and OLi2Sr4 octahedra have distinct sizes to stabilize otherwise underbonded oxide ions, which is less important at the higher pressure. Anion-disordered Sr2LiHOBr2 and Ba2LiHOCl2 were also obtained at 5 GPa. Given the abundant layer-type anion order in perovskite-based oxyhydrides (e.g., La2LiHO3), the inclusion of additional anions (e.g., chloride) expands the frontiers of anion ordering patterns and their distribution control with the benefit of improving ionic conduction in solids.

Lone-Pair-Induced Intra- and Interlayer Polarizations in Sillén-Aurivillius Layered Perovskite Bi4NbO8Br.

Sillén-Aurivillius layered perovskite oxyhalides Bi4MO8X (M = Nb, Ta; X = Cl, Br) are of great interest because of their potential as lead-free ferroelectrics in addition to their function as visible-light-responsive photocatalysts. In this work, we revisited the crystal structure of Bi4NbO8Br (space group: P21cn), revealing that the intralayer polarization is not based on the reported NbO6 octahedral tilting but is derived from the stereochemically active Bi3+ lone pair electrons (LPEs) and the octahedral off-centering of Nb5+ cations. The revised structure (space group: Ic) has additional interlayer polarizations (calculated: 0.6 µC/cm2), in agreement with recent experiments on Bi4NbO8Br. The occurrence of polarization due to stereochemically active LPEs and Nb-site off-centering is similar to Aurivillius-type ferroelectrics (e.g., Bi2WO6), with comparable spontaneous polarizations in the in-plane direction (calculated: 43.5 µC/cm2). This, together with the out-of-plane polarization, indicates that Sillén-Aurivillius compounds have great potential as ferroelectric materials.

Layered Perovskite Oxyiodide with Narrow Band Gap and Long Lifetime Carriers for Water Splitting Photocatalysis.

The development of semiconductors with narrow band gap and high stability is crucial for achieving solar to chemical energy conversion. Compounds with iodine, which has a high polarizability, have attracted attention because of their narrow band gap and long carrier lifetime, as typified by halide perovskite solar cells; however, they have been regarded as unsuitable for harsh photocatalytic water splitting because iodine is prone to self-oxidation. Here, we demonstrate that Ba2Bi3Nb2O11I, a layered Sillén-Aurivillius oxyiodide, not only has access to a wider range of visible light than its chloride and bromide counterparts, but also functions as a stable photocatalyst, efficiently oxidizing water. Density functional theory calculations reveal that the oxygen 2p orbitals in the perovskite block, rather than the fluorite Bi2O2 block as previously pointed out, anomalously push up the valence band maximum, which can be explained by a modified Madelung potential analysis that takes into account the high polarizability of iodine. In addition, the highly polarizable iodide contributes to longer carrier lifetime of Ba2Bi3Nb2O11I, allowing for a significantly higher quantum efficiency than its chloride and bromide counterparts. Visible-light-driven Z-scheme water splitting was achieved for the first time in an iodine-based system using Ba2Bi3Nb2O11I as an oxygen-evolution photocatalyst. The present study provides a novel approach for incorporating polarizable "soft" anions into building blocks of layered materials to manipulate the band structure and improve the carrier dynamics for visible-light responsive functions.

Dehydration of Electrochemically Protonated Oxide: SrCoO2 with Square Spin Tubes.

Controlling oxygen deficiencies is essential for the development of novel chemical and physical properties such as high-Tc superconductivity and low-dimensional magnetic phenomena. Among reduction methods, topochemical reactions using metal hydrides (e.g., CaH2) are known as the most powerful method to obtain highly reduced oxides including Nd0.8Sr0.2NiO2 superconductor, though there are some limitations such as competition with oxyhydrides. Here we demonstrate that electrochemical protonation combined with thermal dehydration can yield highly reduced oxides: SrCoO2.5 thin films are converted to SrCoO2 by dehydration of HSrCoO2.5 at 350 °C. SrCoO2 forms square (or four-legged) spin tubes composed of tetrahedra, in contrast to the conventional infinite-layer structure. Detailed analyses suggest the importance of the destabilization of the SrCoO2.5 precursor by electrochemical protonation that can greatly alter reaction energy landscape and its gradual dehydration (H1-xSrCoO2.5-x/2) for the SrCoO2 formation. Given the applicability of electrochemical protonation to a variety of transition metal oxides, this simple process widens possibilities to explore novel functional oxides.

Bi4AO6Cl2 (A = Ba, Sr, Ca) with Double and Triple Fluorite Layers for Visible-Light Water Splitting.

Layered oxyhalides containing double or triple fluorite layers are promising visible-light-responsive water-splitting photocatalysts with unique band structures. Herein, we report on the synthesis, structure, and photocatalytic property of Bi4BaO6Cl2 (I4/mmm) with alternating double (Bi2O2) and triple (Bi2BaO4) fluorite layers, which was extracted from the crystallographic database on the basis of Madelung potential calculations. Rietveld refinements from powder X-ray and neutron diffraction data revealed the presence of cationic disorder between Bi2O2 and Bi2BaO4 layers, leading to electrostatic stabilization. DFT calculations suggested that photogenerated electrons and holes flow through the double and triple layers, respectively, which may suppress electron-hole recombination. We expanded this double-triple system to include Bi4CaO6Cl2 and Bi4SrO6Cl2 with orthorhombic distortions and different degrees of cationic disorder, which allow band gap tuning. All the double-triple compounds Bi4AO6Cl2 showed stable water-splitting photocatalysis in the presence of a sacrificial reagent.

Valence Band Engineering of Layered Bismuth Oxyhalides toward Stable Visible-Light Water Splitting: Madelung Site Potential Analysis.

A layered oxychloride Bi4NbO8Cl is a visible-light responsive catalyst for water splitting, with its remarkable stability ascribed to the highly dispersive O-2p orbitals in the valence band, the origin of which, however, remains unclear. Here, we systematically investigate four series of layered bismuth oxyhalides, BiOX (X = Cl, Br, I), Bi4NbO8X (X = Cl, Br), Bi2GdO4X (X = Cl, Br), and SrBiO2X (X = Cl, Br, I), and found that Madelung site potentials of anions capture essential features of the valence band structures of these materials. The oxide anion in fluorite-like blocks (e.g., [Bi2O2] slab in Bi4NbO8Cl) is responsible for the upward shift of the valence band, and the degree of electrostatic destabilization changes depending on building layers and their stacking sequence. This study suggests that the Madelung analysis enables a prediction and design of the valence band structures of bismuth and other layered oxyhalides and is applicable even to a compound where DFT calculation is difficult to perform.

Kinetic analysis of silicon-lithium alloying reaction in silicon single crystal using soft X-ray absorption spectroscopy.

Silicon has been considered to be one of the most promising anode active materials for next-generation lithium-ion batteries due to its large theoretical capacity (4200 mA h g-1, Li22Si5). However, silicon anodes suffer from degradation due to large volume expansion and contraction. To control the ideal particle morphology, an experimental method is required to analyze anisotropic diffusion and surface reaction phenomena. This study investigates the anisotropy of the silicon-lithium alloying reaction using electrochemical measurements and Si K-edge X-ray absorption spectroscopy on silicon single crystals. During the electrochemical reduction process in lithium-ion battery systems, the continuous formation of solid electrolyte interphase (SEI) films prevents the achievement of steady-state conditions. Instead, the physical contact between silicon single crystals and lithium metals can prevent the effect of SEI formation. The apparent diffusion coefficient and the surface reaction coefficient are determined from the progress of the alloying reaction analyzed by X-ray absorption spectroscopy. While the apparent diffusion coefficients show no clear anisotropy, the apparent surface reaction coefficient of Si (100) is more significant than that of Si (111). This finding indicates that the surface reaction of silicon governs the anisotropy of practical lithium alloying reaction for silicon anodes.

Simultaneous measurement of specific heat and thermal conductivity in pulsed magnetic fields.

We report an experimental setup for simultaneously measuring specific heat and thermal conductivity in feedback-controlled pulsed magnetic fields of 50 ms duration at cryogenic temperatures. A stabilized magnetic field pulse obtained by the feedback control, which dramatically improves the thermal stability of the setup and sample, is used in combination with the flash method to obtain absolute values of thermal properties up to 37.2 T in the 22-16 K temperature range. We describe the experimental setup and demonstrate the performance of the present method with measurements on single-crystal samples of the geometrically frustrated quantum spin-dimer system SrCu2(BO3)2. Our proof-of-principle results show excellent agreement with data taken using a standard steady-state method, confirming the validity and convenience of the present approach.

Manipulation of charge carrier flow in Bi4NbO8Cl nanoplate photocatalyst with metal loading.

Separation of photoexcited charge carriers in semiconductors is important for efficient solar energy conversion and yet the control strategies and underlying mechanisms are not fully established. Although layered compounds have been widely studied as photocatalysts, spatial separation between oxidation and reduction reaction sites is a challenging issue due to the parallel flow of photoexcited carriers along the layers. Here we demonstrate orthogonal carrier flow in layered Bi4NbO8Cl by depositing a Rh cocatalyst at the edges of nanoplates, resulting in spatial charge separation and significant enhancement of the photocatalytic activity. Combined experimental and theoretical studies revealed that lighter photogenerated electrons, due to a greater in-plane dispersion of the conduction band (vs. valence band), can travel along the plane and are readily trapped by the cocatalyst, whereas the remaining holes hop perpendicular to the plane because of the anisotropic crystal geometry. Our results propose manipulating carrier flow via cocatalyst deposition to achieve desirable carrier dynamics for photocatalytic reactions in layered compounds.