RESUMO
Polypropylene fiber reinforcement is an effective method to enhance the durability of concrete structures. With the increasing public interest in the widespread use of polypropylene fiber reinforced concrete (PFRC), the necessity of evaluating the mechanism of polypropylene fiber (PF) on the permeability of concrete has become prominent. This paper describes the influence of PF on the concrete permeability exposed to freeze-thaw cycles under compressive and tensile stress. The permeability of PFRC under compressive and tensile loads is accurately measured by a specialized permeability setup. The permeability of PFRC under compressive and tensile loads, the volume change of PFRC under compressive load, and the relationship between compressive stress levels at minimum permeability and minimum volume points of PFRC are discussed. The results indicate that the addition of PF adversely affects the permeability of concrete without freeze-thaw damage and cracks. However, it decreases the permeability of concrete specimens exposed to freeze-thaw cycles and cracking. Under compressive load, the permeability of PFRC initially decreases slowly and follows by a significant increase as the compressive stress level increases. This phenomenon correlates with the volume change of the specimen. The compressive stress level of the minimum permeability point and compressive stress level of the minimum volume point of PFRC exhibit a linear correlation, with a fitted proportional function parameter γ ≈ 0.98872. Under tensile load, the permeability of PFRC increases gradually with radial deformation and follows by a significant increase. The strain-permeability curves of PFRC under loading are studied and consist of two stages. In stage I, the permeability of PFRC gradually decreases with the increase of strain under compressive load, while the permeability increases with the increase of strain under tensile load. In stage II, under compressive load, the permeability of PFRC increases with the increase of freeze-thaw cycles, whereas under tensile load, the permeability gradually decreases with the increase of freeze-thaw cycles. The reduction of PF on the permeability of PFRC under tensile load is greater than that under compressive load. In future research, the relationship between strain and permeability of PFRC can be integrated with its constitutive relationship between stress and strain to provide a reference for the application of PF in the waterproofing of concrete structures.
RESUMO
Carbon fibre-reinforced polymer (CFRP) plates can efficiently repair or enhance the mechanical properties of the square hollow section. However, the loading end of such a CFRP-strengthened member is prone to local bearing failure under compressive load. Given this limitation, an innovative CFRP-plate-strengthened square hollow section composite member (CFRP-SHSCM) was raised, and the thick-walled section was welded on both ends of the thin-walled steel column. The mechanical properties of CFRP-SHSCMs were investigated through parameter finite element (FE) analysis, focusing on the influence of the amount of CFRP layers (nc), the slenderness ratio (λ), the initial geometric imperfections (v0), the CFRP layouts (2S and 4S) and the length of the exposed steel column (Le). The load-displacement curves, the bearing force, and typical failure modes were also acquired. Results indicated that with increasing nc and v0, and decreasing λ, the conventional CFRP-SHSCMs were prone to local bearing failure with poor ductility, leading to the insufficient use of the CFRP plate, in contrast, the improved CFRP-SHSCMs primarily underwent overall buckling failure and exhibited better bearing force and ductility. Finally, the modified Perry-Robertson formula was put forward to predict the ultimate load of the CFRP-SHSCMs. The coefficients of variation between the FE simulation and the theoretical results were 0.00436 and 0.0292, respectively.