Tailoring Microstructure and Morphology via Sequential Fluorination to Enhance the Photovoltaic Performance of Low-Cost Polymer Donors for Organic Solar Cells.

For utilizing organic solar cells (OSCs) for commercial applications, reducing the overall cost of the photo absorbent materials is also very crucial. Herein, such a challenge is addressed by synergistically controlling the amount of fluorine (F)-substituents (n = 2, 4) on a low-cost wide-bandgap molecular design involving alternate fluorinated-thienyl benzodithiophene donor and 2,5-difluoro benzene (2FBn) or 2,3,5,6 tetrafluorobenzene (4FBn) to form two new polymer donors PBDT-2FBn and PBDT-4FBn, respectively. As expected, sequential fluorination causes a lowering of the frontier energy levels and planarization of polymer backbone via F···S and C-H···F noncovalent molecular locks, which results in more pronounced molecular packing and enhanced crystallinity from PBDT-2FBn to PBDT-4FBn. By mixing with IT-4F acceptor, PBDT-2FBn:IT-4F-based blend demonstrates favorable molecular orientation with shorter π-π stacking distance, higher carrier mobilities and desirable nanoscale morphology, hence delivering a higher power conversion efficiency (PCE) of 9.3% than PBDT-2FBn:IT-4F counterpart (8.6%). Furthermore, pairing PBDT-2FBn with BTP-BO-4Cl acceptor further improved absorption range and promoted privileged morphology for efficient exciton dissociation and charge transport, resulting in further improvement of PCE to 10.2% with remarkably low energy loss of 0.46 eV. Consequently, this study provides valuable guidelines for designing efficient and low-cost polymer donors for OSC applications.

Understanding the Critical Role of Sequential Fluorination of Phenylene Units on the Properties of Dicarboxylate Bithiophene-Based Wide-Bandgap Polymer Donors for Non-Fullerene Organic Solar Cells.

Design and development of wide bandgap (WBG) polymer donors with low-lying highest occupied molecular orbitals (HOMOs) are increasingly gaining attention in non-fullerene organic photovoltaics since such donors can synergistically enhance power conversion efficiency (PCE) by simultaneously minimizing photon energy loss (Eloss ) and enhancing the spectral response. In this contribution, three new WBG polymer donors, P1, P2, and P3, are prepared by adding phenylene cores with a different number of fluorine (F) substituents (n = 0, 2, and 4, respectively) to dicarboxylate bithiophene-based acceptor units. As predicted, fluorination effectively aides in the lowering of HOMO energy levels, tailoring of the coplanarity and molecular ordering in the polymers. Thus, fluorinated P2 and P3 polymers show higher coplanarity and more intense interchain aggregation than P1, leading to higher charge carrier mobilities and superior phase-separated morphology in the optimized blend films with IT-4F. As a result, both P2:IT-4F and P3:IT-4F realize the best PCEs of 6.89% and 7.03% (vs 0.16% for P1:IT-4F) with lower Eloss values of 0.65 and 0.55 eV, respectively. These results signify the importance of using phenylene units with sequential fluorination in polymer backbone for modifying the optoelectronic properties and realizing low Eloss values by synergistically lowering the HOMO energy levels.

Single-Component Organic Solar Cells Based on Intramolecular Charge Transfer Photoabsorption.

Conjugated donor-acceptor molecules with intramolecular charge transfer absorption are employed for single-component organic solar cells. Among the five types of donor-acceptor molecules, the strong push-pull structure of DTDCPB resulted in solar cells with high JSC, an internal quantum efficiency exceeding 20%, and high VOC exceeding 1 V with little photon energy loss around 0.7 eV. The exciton binding energy (EBE), which is a key factor in enhancing the photocurrent in the single-component device, was determined by quantum chemical calculation. The relationship between the photoexcited state and the device performance suggests that the strong internal charge transfer is effective for reducing the EBE. Furthermore, molecular packing in the film is shown to influence photogeneration in the film bulk.