Effect of Polybutylene Succinate Additive in Polylactic Acid Blend Fibers via a Melt-Blown Process.
Molecules
; 28(20)2023 Oct 22.
Article
em En
| MEDLINE
| ID: mdl-37894694
ABSTRACT
This work aimed to study the influence of the polybutylene succinate (PBS) content on the physical, thermal, mechanical, and chemical properties of the obtained polylactic acid (PLA)/PBS composite fibers. PLA/PBS blend fibers were prepared by a simple melt-blown process capable of yielding nanofibers. Morphological analysis revealed that the fiber size was irregular and discontinuous in length. Including PBS affected the fiber size distribution, and the fibers had a smoother surface with increased amounts of added PBS. Differential scanning calorimetry analysis (DSC) revealed that the crystallization temperature of the PLA sheet (105.8 °C) was decreased with increasing PBS addition levels down to 91.7 °C at 10 wt.% PBS. This suggests that the addition of PBS may affect PLA crystallization, which is consistent with the X-ray diffraction analysis that revealed that the crystallinity of PLA (19.2%) was increased with increasing PBS addition up to 28.1% at 10 wt% PBS. Moreover, adding PBS increased the tensile properties while the % elongation at break was significantly decreased.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Revista:
Molecules
Assunto da revista:
BIOLOGIA
Ano de publicação:
2023
Tipo de documento:
Article
País de afiliação:
Tailândia