Aqueous Sol-Gel Synthesis of Different Iron Ferrites: From 3D to 2D.

In this study, an aqueous sol-gel synthesis method and subsequent dip-coating technique were applied for the preparation of yttrium iron garnet (YIG), yttrium iron perovskite (YIP), and terbium iron perovskite (TIP) bulk and thin films. The monophasic highly crystalline different iron ferrite powders have been synthesized using this simple aqueous sol-gel process displaying the suitability of the method. In the next step, the same sol-gel solution was used for the fabrication of coatings on monocrystalline silicon (100) using a dip-coating procedure. This resulted, likely due to substrate surface influence, in all coatings having mixed phases of both garnet and perovskite. Thermogravimetric (TG) analysis of the precursor gels was carried out. All the samples were investigated by X-ray powder diffraction (XRD) analysis. The coatings were also investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM) and Mössbauer spectroscopy. Magnetic measurements were also carried out.

Lanthanum and Manganese Co-Doping Effects on Structural, Morphological, and Magnetic Properties of Sol-Gel Derived BiFeO3.

In this work, lanthanum and manganese co-substitution effects on different properties of bismuth ferrite solid solutions Bi1-xLaxFe0.85Mn0.15O3 (x from 0 to 1) prepared by a sol-gel synthetic approach have been investigated. It was observed that the structural, morphological, and magnetic properties of obtained specimens are influenced by the amount of introduced La3+ ions. Surprisingly, only the compound with a composition of BiFe0.85Mn0.15O3 was not monophasic, and the presence of neighboring phases was determined from X-ray diffraction analysis and Mössbauer measurements. Structural transitions from orthorhombic to cubic and back to orthorhombic were also observed depending on the La3+ amount. Antiferromagnetic behaviour was observed for all of the samples, with the highest magnetisation values for Bi0.5La0.5Fe0.85Mn0.15O3. Additionally, structural attributes and morphological features were evaluated by Raman spectroscopy and scanning electron microscopy (SEM), respectively.

Study of gadolinium substitution effects in hexagonal yttrium manganite YMnO3.

In the present work, gadolinium substitution effects on the properties of yttrium manganite YxGd1-xMn0.97Fe0.03O3 (x from 0 to 1 with a step of 0.2) synthesized by an aqueous sol-gel method have been investigated. Partial substitution of Mn3+ by 57Fe3+ in the manganite was also performed in order to investigate deeper the structural properties of synthesized compounds applying Mössbauer spectroscopy. It was demonstrated that substitution of Y3+ by Gd3+ ions leads to the changes of structural, magnetic and morphological properties of investigated system. The crystal structure gradually transformed from hexagonal to orthorhombic with an increase of Gd3+ content in the crystal lattice. The mixed phase was obtained when x = 0.6, whereas other compounds were determined to be monophasic. Magnetization measurements revealed paramagnetic behavior of all specimens, however magnetization values were found to be dependent on chemical composition of the samples. Solid solutions with orthorhombic structure revealed higher magnetization values compared to those of hexagonal samples. The highest magnetization was observed for pure GdMn0.97Fe0.03O3. Structural properties were investigated by powder X-ray diffraction, Mössbauer, FTIR and Raman spectroscopies. Morphological features of the synthesized specimens were studied by scanning electron microscopy (SEM).

Sonication accelerated formation of Mg-Al-phosphate layered double hydroxide via sol-gel prepared mixed metal oxides.

Single-phase magnesium-aluminium layered double hydroxide (LDH) intercalated with dihydrogen phosphate was successfully produced by hydration of nanopowder of the respective mixed metal oxide (MMO) obtained using sol-gel based method followed by a two-step anion exchange hydroxide-to-chloride and chloride-to-phosphate. The MMO with the metal cation ratio of Mg/Al = 2:1 was prepared using the aqueous sol-gel method. Processes of the parent Mg2Al-OH LDH formation and the successive anion-exchanges, ОН- → Cl- and Cl- → H2PO4-, were considerably accelerated via the application of high-power (1.5 kW) ultrasound. The crystalline phases formed at all stages of the Mg2Al-H2PO4 LDH production were characterized using X-ray diffraction, scanning electron microscopy, scanning transmission electron microscopy, inductive coupled plasma optical emission spectroscopy, Fourier transform infrared spectroscopy, and thermogravimetric analysis. Based on the data of chemical analysis and the XRD data, the type of the intercalated phosphate anion was determined and the arrangement of this anion in the interlayer was modelled.