High Polymer Molecular Weight Yields Solar Cells with Simultaneously Improved Performance and Thermal Stability.

Simple synthetic routes, high active layer thickness tolerance as well as stable organic solar cells are relentlessly pursued as key enabling traits for the upscaling of organic photovoltaics. Here, the potential to address these issues by tuning donor polymer molecular weight is investigated. Specifically, the focus is on PTQ10, a polymer with low synthetic complexity, with number average molecular weights of 2.4, 6.2, 16.8, 52.9, and 54.4 kDa, in combination with three different non-fullerene acceptors, namely Y6, Y12, and IDIC. Molecular weight, indeed, unlocks a threefold increase in power conversion efficiency for these blends. Importantly, efficiencies above 10% for blade coated devices with thicknesses between 200 and 350 nm for blends incorporating high molecular weight donor are shown. Spectroscopic, GIWAXS and charge carrier mobility data suggest that the strong photocurrent improvement with molecular weight is related to both, improved electronic transport and polymer contribution to exciton generation. Moreover, it is demonstrated that solar cells based on high molecular weight PTQ10 are more thermally stable due to a higher glass transition temperature, thus also improving device stability.

Doping Approaches for Organic Semiconductors.

Electronic doping in organic materials has remained an elusive concept for several decades. It drew considerable attention in the early days in the quest for organic materials with high electrical conductivity, paving the way for the pioneering work on pristine organic semiconductors (OSCs) and their eventual use in a plethora of applications. Despite this early trend, however, recent strides in the field of organic electronics have been made hand in hand with the development and use of dopants to the point that are now ubiquitous. Here, we give an overview of all important advances in the area of doping of organic semiconductors and their applications. We first review the relevant literature with particular focus on the physical processes involved, discussing established mechanisms but also newly proposed theories. We then continue with a comprehensive summary of the most widely studied dopants to date, placing particular emphasis on the chemical strategies toward the synthesis of molecules with improved functionality. The processing routes toward doped organic films and the important doping-processing-nanostructure relationships, are also discussed. We conclude the review by highlighting how doping can enhance the operating characteristics of various organic devices.

Heteroleptic Ruthenium(II) Complexes with 2,2'-Bipyridines Having Carbonitriles as Anchoring Groups for ZnO Surfaces: Syntheses, Physicochemical Properties, and Applications in Organic Solar Cells.

Heteroleptic ruthenium (II) complexes were used for sensitizing ZnO surfaces in organic solar cells (OSCs) as mediators with photoactive layers. The complexes [Ru(4,4'-X2-bpy)(Mebpy-CN)2]2+ (with X = -CH3, -OCH3 and -N(CH3)2; bpy = 2,2'-bipyridine; Mebpy-CN = 4-methyl-2,2'-bipyridine-4'-carbonitrile) were synthesized and studied by analytical and spectroscopical techniques. Spectroscopic, photophysical, and electrochemical properties were tuned by changing the electron-donating ability of the -X substituents at the 4,4'-positions of the bpy ring and rationalized by quantum mechanical calculations. These complexes were attached through nitrile groups to ZnO as interfacial layer in an OSC device with a PBDB-T:ITIC photoactive layer. This modified inorganic electron transport layer generates enhancement in photoconversion of the solar cells, reaching up to a 23% increase with respect to the unsensitized OSCs. The introduction of these dyes suppresses some degradative reactions of the nonfullerene acceptor due to the photocatalytic activity of zinc oxide, which was maintained stable for about 11 months. Improving OSC efficiencies and stabilities can thus be achieved by a judicious combination of new inorganic and organic materials.

Hydroxypropyl Cellulose Adhesives for Transfer Printing of Carbon Nanotubes and Metallic Nanostructures.

Transfer printing is one of the key nanofabrication techniques for the large-scale manufacturing of complex device architectures. It provides a cost-effective and high-throughput route for the integration of independently processed materials into spatially tailored architectures. Furthermore, this method enables the fabrication of flexible and curvilinear devices, paving the way for the fabrication of a new generation of technologies for optics, electronics, and biomedicine. In this work, hydroxypropyl cellulose (HPC) membranes are used as water soluble adhesives for transfer printing processes with improved performance and versatility compared to conventional silicone alternatives. The high-water solubility and excellent mechanical properties of HPC facilitate transfer printing with high yield for both metal and carbon nanotubes (CNTs) inks. In the case of metal inks, crack-free stripping of silver films and the simple fabrication of Moiré Plasmonic architectures of different geometries are demonstrated. Furthermore, HPC membranes are used to transfer print carbon nanotube films with different thicknesses and up to 77% transparency in the visible and near infrared region with potential applications as transparent conductive substrates. Finally, the use of prepatterned HPC membranes enables nanoscale patterning of CNT with feature resolution down to 1 µm.

Will organic thermoelectrics get hot?

The generally low energy density from most heat sources-the Sun, Earth as well as most human activities-implies that solid-state thermoelectric devices are the most versatile heat harvesters since, unlike steam engines, they can be used on a small scale and at small temperature differences. In this opinion piece, we first discuss the materials requirements for the widespread use of thermoelectrics. We argue that carbon-based materials, such as conducting polymers and carbon nanotubes, are particularly suited for large area and low-temperature operation applications, as they are abundant, low-toxicity and easy to process. We combine experimentally observed macro-trends and basic thermoelectric relations to evaluate the major performance limitations of this technology thus far and propose a number of avenues to take the thermoelectric efficiency of organic materials beyond the state of the art. First, we emphasize how charge carrier mobility, rather than charge density, is currently limiting performance, and discuss how to improve mobility by exploiting anisotropy, high persistence length materials and composites with long and well-dispersed carbon nanotubes. We also show that reducing thermal conductivity could double efficiency while reducing doping requirements. Finally, we discuss several ways in which composites could further boost performance, introducing the concept of interface engineering to produce phonon stack-electron tunnel composites. This article is part of a discussion meeting issue 'Energy materials for a low carbon future'.

Non-reciprocal diffraction in magnetoplasmonic gratings.

Phase-matching conditions-used to bridge the wave vector mismatch between light and surface plasmon polaritons (SPPs)-have been exploited recently to enable nonreciprocal optical propagation and enhanced magneto-optic responses in magnetoplasmonic systems. Here we show that using diffraction in conjunction with plasmon excitations leads to a photonic system with a more versatile and flexible response. As a testbed, we analyzed diffracted magneto-optical effects in magnetoplasmonic gratings, where broken time-reversal symmetry induces frequency shifts in the energy and angular spectra of plasmon resonance. These result in exceptionally large responses in the diffracted magneto-optical effect. The concepts presented here can be used to develop non-reciprocal optical devices that exploit diffraction, in order to achieve tailored electromagnetic responses.

Exploring the origin of high optical absorption in conjugated polymers.

The specific optical absorption of an organic semiconductor is critical to the performance of organic optoelectronic devices. For example, higher light-harvesting efficiency can lead to higher photocurrent in solar cells that are limited by sub-optimal electrical transport. Here, we compare over 40 conjugated polymers, and find that many different chemical structures share an apparent maximum in their extinction coefficients. However, a diketopyrrolopyrrole-thienothiophene copolymer shows remarkably high optical absorption at relatively low photon energies. By investigating its backbone structure and conformation with measurements and quantum chemical calculations, we find that the high optical absorption can be explained by the high persistence length of the polymer. Accordingly, we demonstrate high absorption in other polymers with high theoretical persistence length. Visible light harvesting may be enhanced in other conjugated polymers through judicious design of the structure.

Giant Optical Polarization Rotation Induced by Spin-Orbit Coupling in Polarons.

We have uncovered a giant gyrotropic magneto-optical response for doped ferromagnetic manganite La_{2/3}Ca_{1/3}MnO_{3} around the near room-temperature paramagnetic-to-ferromagnetic transition. At odds with current wisdom, where this response is usually assumed to be fundamentally fixed by the electronic band structure, we point to the presence of small polarons as the driving force for this unexpected phenomenon. We explain the observed properties by the intricate interplay of mobility, Jahn-Teller effect, and spin-orbit coupling of small polarons. As magnetic polarons are ubiquitously inherent to many strongly correlated systems, our results provide an original, general pathway towards the generation of magnetic-responsive gigantic gyrotropic responses that may open novel avenues for magnetoelectric coupling beyond the conventional modulation of magnetization.

Dynamic disorder, phonon lifetimes, and the assignment of modes to the vibrational spectra of methylammonium lead halide perovskites.

We present Raman and terahertz absorbance spectra of methylammonium lead halide single crystals (MAPbX3, X = I, Br, Cl) at temperatures between 80 and 370 K. These results show good agreement with density-functional-theory phonon calculations. Comparison of experimental spectra and calculated vibrational modes enables confident assignment of most of the vibrational features between 50 and 3500 cm-1. Reorientation of the methylammonium cations, unlocked in their cavities at the orthorhombic-to-tetragonal phase transition, plays a key role in shaping the vibrational spectra of the different compounds. Calculations show that these dynamic effects split Raman peaks and create more structure than predicted from the independent harmonic modes. This explains the presence of extra peaks in the experimental spectra that have been a source of confusion in earlier studies. We discuss singular features, in particular the torsional vibration of the C-N axis, which is the only molecular mode that is strongly influenced by the size of the lattice. From analysis of the spectral linewidths, we find that MAPbI3 shows exceptionally short phonon lifetimes, which can be linked to low lattice thermal conductivity. We show that optical rather than acoustic phonon scattering is likely to prevail at room temperature in these materials.

Poly(3-hexylthiophene) nanowires in porous alumina: internal structure under confinement.

We study the structure of poly(3-hexylthiophene) (P3HT) subjected to nanoscale confinement in two dimensions (2D) as imposed by the rigid walls of nanopore anodic aluminum oxide (AAO) templates. P3HT nanowires with aspect ratios (length-to-diameter) above 1000 and diameters ranging between 15 nm and 350 nm are produced in the pores of the AAO templates via two processing routes. These are, namely, drying a solution or cooling from the melt. Our study focuses on the effects of nanoconfinement on the semicrystalline nature of the nanowires, the orientation of crystals, and the evolution of the structures that P3HT might develop under confinement, which we investigate by combining imaging (SEM), spectroscopic (FTIR, photoluminescence) and structural characterization (WAXS, DSC) techniques. Solution-processed P3HT nanowires are essentially amorphous and porous, whereas melt-processed nanowires are semicrystalline, and present a more compact morphology and smoother surfaces. In the latter case, the orientation of crystals was found to strongly depend on the pore diameter. In large diameter nanowires (250 nm and 120 nm), crystals are oriented laying the π-π stacking direction parallel to the nanowire axis. In contrast, in small diameter nanowires, the π-π stacking direction is mainly perpendicular to the nanowires, as crystals are likely to nucleate at pore walls. The structural evolution of P3HT upon heating into weakly (250 nm in diameter) and strongly (15 nm in diameter) confining pores has been studied. A complex set of structures is observed, i.e., crystals, a solid layered mesophase, a nematic/smectic mesophase, and the isotropic melt. Interestingly, a rare crystal polymorph (form II) is also observed under strong confinement conditions together with the usual lamellar crystal form I. Furthermore, we show that nanoconfinement stabilizes form II: such crystals are still present at 210 °C while in the bulk they get converted to form I crystals at around 50 °C.

Upscaling Thermoelectrics: Micron-Thick, Half-a-Meter-Long Carbon Nanotube Films with Monolithic Integration of p- and n-Legs.

In order for organic thermoelectrics to successfully establish their own niche as energy-harvesting materials, they must reach several crucial milestones, including high performance, long-term stability, and scalability. Performance and stability are currently being actively studied, whereas demonstrations of large-scale compatibility are far more limited and for carbon nanotubes (CNTs) are still missing. The scalability challenge includes material-related economic considerations as well as the availability of fast deposition methods that produce large-scale films that simultaneously satisfy the thickness constraints required for thermoelectric modules. Here we report on true solutions of CNTs that form gels upon air exposure, which can then be dried into micron-thick films. The CNT ink can be extruded using a slot-shaped nozzle into a continuous film (more than half a meter in the present paper) and patterned into alternating n- and p-type components, which are then folded to obtain the finished thermoelectric module. Starting from a given n-type film, differentiation between the n and p components is achieved by a simple postprocessing step that involves a partial oxidation reaction and neutralization of the dopant. The presented method allows the thermoelectric legs to seamlessly interconnect along the continuous film, thus avoiding the need for metal electrodes, and, most importantly, it is compatible with large-scale printing processes. The resulting thermoelectric legs retain 80% of their power factor after 100 days in air and about 30% after 300 days. Using the proposed methodology, we fabricate two thermoelectric modules of 4 and 10 legs that can produce maximum power outputs of 1 and 2.4 µW, respectively, at a temperature difference ΔT of 46 K.

Impact of Oligoether Side-Chain Length on the Thermoelectric Properties of a Polar Polythiophene.

Conjugated polymers with oligoether side chains make up a promising class of thermoelectric materials. In this work, the impact of the side-chain length on the thermoelectric and mechanical properties of polythiophenes is investigated. Polymers with tri-, tetra-, or hexaethylene glycol side chains are compared, and the shortest length is found to result in thin films with the highest degree of order upon doping with the p-dopant 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ). As a result, a stiff material with an electrical conductivity of up to 830 ± 15 S cm-1 is obtained, resulting in a thermoelectric power factor of about 21 µW m-1 K-2 in the case of as-cast films. Aging at ambient conditions results in an initial decrease in thermoelectric properties but then yields a highly stable performance for at least 3 months, with values of about 200 S cm-1 and 5 µW m-1 K-2. Evidently, identification of the optimal side-chain length is an important criterion for the design of conjugated polymers for organic thermoelectrics.

Effect of structure and interlayer diffusion in organic position sensitive photodetectors based on complementary wedge donor/acceptor layers.

We have developed organic photodetectors based on two complementary wedge layers made of CuPc and C60 and observed a strong spatial dependence of the spectral response on the position of the incident light spot. Photocurrent measurements are correlated with atomic force microscopy (AFM), micro-Raman and ellipsometry maps in order to provide insights into the local donor/acceptor concentration, layer thickness and nature of the donor-acceptor interface along the direction of the thickness gradient. Deviations in spatial dependence between experimental photocurrent values and those predicted with a model assuming a sharp and well defined organic-organic interface are discussed in terms of inter-diffusion layers.

Spectrum on demand light source (SOLS) for advanced photovoltaic characterization.

We report a multi-purpose spectrum-on-demand light source (SOLS), conceived primarily but not exclusively for the multiple and advanced characterization of photovoltaic (PV) materials and devices. The apparatus is a spectral shaper illumination device, providing a tunable and spectrally shaped light beam produced by modulating the intensity and/or wavelength range of a primary light source. SOLS stands out from the state of the art because it produces almost any spectrum on demand and delivers two types of output: a spectrally shaped and spatially homogeneous beam over its cross section for areal illumination or a spatially and spectrally split beam into its wavelength components, a unique capability suited to characterize lateral-tandem (Rainbow) solar cells. The tuneability from broadband to narrowband illumination enables two characterization devices into one, namely, a solar simulator for the determination of the power conversion efficiency and an external quantum efficiency measuring system. We expect the SOLS setup to accelerate material screening, enabling the discovery and optimization of novel multi-component materials and devices, in particular for emergent PV technologies like organic, metal halide perovskites, or multi-junction geometries, as well as novel PV applications such as indoors, building integrated, or agrivoltaics, among others.

RAINBOW Organic Solar Cells: Implementing Spectral Splitting in Lateral Multi-Junction Architectures.

While multi-junction geometries have the potential to boost the efficiency of organic solar cells, the experimental gains yet obtained are still very modest. This work proposes an alternative spectral splitting device concept in which various individual semiconducting junctions with cascading bandgaps are laid side by side, thus the name RAINBOW. Each lateral sub-cell receives a fraction of the spectrum that closely matches the main absorption band of the given semiconductor. Here, simulations are used to identify the important material and device properties of each RAINBOW sub-cell. Using the resulting design rules, three systems are selected, with narrow, medium, and wide effective bandgaps, and their potential as sub-cells in this geometry is experimentally investigated. With the aid of a custom-built setup that generates spectrally spread sunlight on demand, the simulations are experimentally validated, showing that this geometry can lead to a reduction in thermalization losses and an improvement in light harvesting, which results in a relative improvement in efficiency of 46.6% with respect to the best sub-cell. Finally, a working proof-of-concept monolithic device consisting of two sub-cells deposited from solution on the same substrate is fabricated, thus demonstrating the feasibility and the potential of the RAINBOW solar cell concept.

Conductive Bacterial Nanocellulose-Polypyrrole Patches Promote Cardiomyocyte Differentiation.

The low endogenous regenerative capacity of the heart, added to the prevalence of cardiovascular diseases, triggered the advent of cardiac tissue engineering in the last decades. The myocardial niche plays a critical role in directing the function and fate of cardiomyocytes; therefore, engineering a biomimetic scaffold holds excellent promise. We produced an electroconductive cardiac patch of bacterial nanocellulose (BC) with polypyrrole nanoparticles (Ppy NPs) to mimic the natural myocardial microenvironment. BC offers a 3D interconnected fiber structure with high flexibility, which is ideal for hosting Ppy nanoparticles. BC-Ppy composites were produced by decorating the network of BC fibers (65 ± 12 nm) with conductive Ppy nanoparticles (83 ± 8 nm). Ppy NPs effectively augment the conductivity, surface roughness, and thickness of BC composites despite reducing scaffolds' transparency. BC-Ppy composites were flexible (up to 10 mM Ppy), maintained their intricate 3D extracellular matrix-like mesh structure in all Ppy concentrations tested, and displayed electrical conductivities in the range of native cardiac tissue. Furthermore, these materials exhibit tensile strength, surface roughness, and wettability values appropriate for their final use as cardiac patches. In vitro experiments with cardiac fibroblasts and H9c2 cells confirmed the exceptional biocompatibility of BC-Ppy composites. BC-Ppy scaffolds improved cell viability and attachment, promoting a desirable cardiomyoblast morphology. Biochemical analyses revealed that H9c2 cells showed different cardiomyocyte phenotypes and distinct levels of maturity depending on the amount of Ppy in the substrate used. Specifically, the employment of BC-Ppy composites drives partial H9c2 differentiation toward a cardiomyocyte-like phenotype. The scaffolds increase the expression of functional cardiac markers in H9c2 cells, indicative of a higher differentiation efficiency, which is not observed with plain BC. Our results highlight the remarkable potential use of BC-Ppy scaffolds as a cardiac patch in tissue regenerative therapies.

Unraveling the Influence of the Preexisting Molecular Order on the Crystallization of Semiconducting Semicrystalline Poly(9,9-di-n-octylfluorenyl-2,7-diyl (PFO).

Understanding the complex crystallization process of semiconducting polymers is key for the advance of organic electronic technologies as the optoelectronic properties of these materials are intimately connected to their solid-state microstructure. These polymers often have semirigid backbones and flexible side chains, which results in a strong tendency to organize/order in the liquid state. Therefore, crystallization of these materials frequently occurs from liquid states that exhibit-at least partial-molecular order. However, the impact of the preexisting molecular order on the crystallization process of semiconducting polymers- indeed, of any polymer-remained hitherto unknown. This study uses fast scanning calorimetry (FSC) to probe the crystallization kinetics of poly(9,9-di-n-octylfluorenyl-2,7-diyl (PFO) from both an isotropic disordered melt state (ISO state) and a liquid-crystalline ordered state (NEM state). Our results demonstrate that the preexisting molecular order has a profound impact on the crystallization of PFO. More specifically, it favors the formation of effective crystal nucleation centers, speeding up the crystallization kinetics at the early stages of phase transformation. However, samples crystallized from the NEM state require longer times to reach full crystallization (during the secondary crystallization stage) compared to those crystallized from the ISO state, likely suggesting that the preexisting molecular order slows down the advance in the latest stages of the crystallization, that is, those governed by molecular diffusion. The fitting of the data with the Avrami model reveals different crystallization mechanisms, which ultimately result in a distinct semicrystalline morphology and photoluminescence properties. Therefore, this work highlights the importance of understanding the interrelationships between processing, structure, and properties of polymer semiconductors and opens the door for performing fundamental investigations via newly developed FSC methodologies of such materials that otherwise are not possible with conventional techniques.

Matching electron transport layers with a non-halogenated and low synthetic complexity polymer:fullerene blend for efficient outdoor and indoor organic photovoltaics.

The desired attributes of organic photovoltaics (OPV) as a low cost and sustainable energy harvesting technology demand the use of non-halogenated solvent processing for the photoactive layer (PAL) materials, preferably of low synthetic complexity (SC) and without compromising the power conversion efficiency (PCE). Despite their record PCEs, most donor-acceptor conjugated copolymers in combination with non-fullerene acceptors are still far from upscaling due to their high cost and SC. Here we present a non-halogenated and low SC ink formulation for the PAL of organic solar cells, comprising PTQ10 and PC61BM as donor and acceptor materials, respectively, showing a record PCE of 7.5% in blade coated devices under 1 sun, and 19.9% under indoor LED conditions. We further study the compatibility of the PAL with 5 different electron transport layers (ETLs) in inverted architecture. We identify that commercial ZnO-based formulations together with a methanol-based polyethyleneimine-Zn (PEI-Zn) chelated ETL ink are the most suitable interlayers for outdoor conditions, providing fill factors as high as 74% and excellent thickness tolerance (up to 150 nm for the ETL, and >200 nm for the PAL). In indoor environments, SnO2 shows superior performance as it does not require UV photoactivation. Semi-transparent devices manufactured entirely in air via lamination show indoor PCEs exceeding 10% while retaining more than 80% of the initial performance after 400 and 350 hours of thermal and light stress, respectively. As a result, PTQ10:PC61BM combined with either PEI-Zn or SnO2 is currently positioned as a promising system for industrialisation of low cost, multipurpose OPV modules.

High-Throughput Screening of Blade-Coated Polymer:Polymer Solar Cells: Solvent Determines Achievable Performance.

Optimization of a new system for organic solar cells is a multiparametric analysis problem that requires substantial efforts in terms of time and resources. The strong microstructure-dependent performance of polymer:polymer cells makes them particularly difficult to optimize, or to translate previous knowledge from spin coating into more scalable techniques. In this work, the photovoltaic performance of blade-coated devices was studied based on the promising polymer:polymer system PBDB-T and PF5-Y5 as donor and acceptor, respectively. Using the recently developed high-throughput methodology, the system was optimized for multiple variables, including solvent system, active layer composition, ratio, and thickness, among others, by fabricating more than 500 devices with less than 24 mg of each component. As a result, the power conversion efficiency of the blade-coated devices varied from 0.08 to 6.43 % in the best device. The performed statistical analysis of the large experimental data obtained showed that solvent selection had the major impact on the final device performance due to its influence on the active layer microstructure. As a conclusion, the use of the plot of the device efficiency in the Hansen space was proposed as a powerful tool to guide solvent selection in organic photovoltaics.

Correction: Blade coated P3HT:non-fullerene acceptor solar cells: a high-throughput parameter study with a focus on up-scalability.

[This corrects the article DOI: 10.1039/C9TA07361B.].