Self-assembled monolayers (SAMs) based on Br-2PACz ([2-(3,6-dibromo-9H-carbazol-9-yl)ethyl]phosphonic acid) 2PACz ([2-(9H-Carbazol-9-yl)ethyl]phosphonic acid) and MeO-2PACz ([2-(3,6-dimethoxy-9H-carbazol-9-yl)ethyl]phosphonic acid) molecules were investigated as hole-extracting interlayers in organic photovoltaics (OPVs). The highest occupied molecular orbital (HOMO) energies of these SAMs were measured at -6.01 and -5.30â eV for Br-2PACz and MeO-2PACz, respectively, and found to induce significant changes in the work function (WF) of indium-tin-oxide (ITO) electrodes upon chemical functionalization. OPV cells based on PM6 (poly[(2,6-(4,8-bis(5-(2-ethylhexyl-3-fluoro)thiophen-2-yl)-benzo[1,2-b:4,5-b']dithiophene))-alt-(5,5-(1',3'-di-2-thienyl-5',7'-bis(2-ethylhexyl)benzo[1',2'-c:4',5'-c']dithiophene-4,8-dione)]) : BTP-eC9 : PC71 BM ([6,6]-phenyl-C71-butyric acid methyl ester) using ITO/Br-2PACz anodes exhibited a maximum power conversion efficiency (PCE) of 18.4 %, outperforming devices with ITO/MeO-2PACz (14.5 %) and ITO/poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT : PSS) (17.5 %). The higher PCE was found to originate from the much higher WF of ITO/Br-2PACz (-5.81â eV) compared to ITO/MeO-2PACz (4.58â eV) and ITO/PEDOT : PSS (4.9â eV), resulting in lower interface resistance, improved hole transport/extraction, lower trap-assisted recombination, and longer carrier lifetimes. Importantly, the ITO/Br-2PACz electrode was chemically stable, and after removal of the SAM it could be recycled and reused to construct fresh OPVs with equally impressive performance.
RESUMO
Total hip joint replacement offers dramatic improvement in the quality of life but deep infection is the most feared complication of this procedure. The infection threatens the function of the joint, the preservation of the limb, and occasionally even the life of the patient. For the surgeon it is a disastrous anticlimax, which follows a procedure that may have given the patient freedom from pain and increased mobility.