RESUMO
In this work, core and core-shell microparticles formed by Ni-Mn-Co oxides with controlled composition were fabricated by an oxalate-assisted co-precipitation route, and their properties were analysed by diverse microscopy and spectroscopy techniques. The microparticles exhibit dimensions within the 2-6 µm range and mainly consist of NiO and NiMn2O4, the latter being promoted as the temperature of the treatment increases, especially in the shell region of the microparticles. Aspects such as the shell dimensions, the vibrational modes of the spinel compounds primarily observed in the shell region, the oxidation states of the cations at the surface of the microparticles, and the achievement of a Ni-rich 811 core and a Mn-rich 631 shell were thoroughly evaluated and discussed in this work.
RESUMO
Zn2GeO4 is considered a very promising alternative to current luminescent semiconductors. Previous results suggest that its emitted wavelength may depend on different variables, such as particle size and morphology, among others. In this work, we have prepared pure and highly homogeneous Zn2GeO4 nanorods under hydrothermal synthesis conditions with a willemite-like structure. Their luminescent properties have been explored and their band gap is estimated, which are distinct from those of previously reported Zn2GeO4 bulk particles. Therefore, our results identify particle morphology as a crucial factor for maximizing and fine-tuning the luminescence of Zn2GeO4 nano-phosphors.
RESUMO
This study focuses on the fabrication of polymer nanocomposite films using polyvinyl alcohol (PVA)/graphene quantum dots (GQDs). We investigate the relationship between the structural, thermal, and nanoscale morphological properties of these films and their photoluminescent response. Although according to X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), and differential thermal analysis (DTA), the incorporation of GQDs does not significantly affect the percentage crystallinity of the PVA matrix, for a range of added GQD concentrations, atomic force microscopy (AFM) showed the formation of islands with apparent crystalline morphology on the surface of the PVA/GQD films. This observation suggests that GQDs presumably act as nucleating agents for island growth. The incorporation of GQDs also led to the formation of characteristic surface pores with increased stiffness and frictional contrast, as indicated by ultrasonic force microscopy (UFM) and frictional force microscopy (FFM) data. The photoluminescence (PL) spectra of the films were found to depend both on the amount of GQDs incorporated and on the film morphology. For GQD loads >1.2%wt, a GQD-related band was observed at ~1650 cm-1 in FT-IR, along with an increase in the PL band at lower energy. For a load of ~2%wt GQDs, the surface morphology was characterized by extended cluster aggregates with lower stiffness and friction than the surrounding matrix, and the PL signal decreased.