RESUMO
The present work describes the preparation of hydrogel based on cross-linked networks of poly (N-vinylpirrolidone), PVP, with polyethyleneglicol and agar with 90% water and PVP nancomposites with a synthetic nanoclay, Laponite XLG, for use as burn dressings. These systems were obtained in two ways: using gamma Co-60 and electron beam radiation. The gelation obtained dose was Dg= 1.72 kGy. The elastic modulus of hydrogel was independent of the method of irradiation. It was 0.39 MPa for the hydrogel irradiated with gamma Co-60 and 0.38 MPa for electron beam irradiation. The elastic modulus of the nanocomposite membrane was 1.25 MPa, three times higher. These results indicate that the PVP/Laponite XLG nanocomposite hydrogel membrane is the best choice for wound dressing applications due to its high water sorption capacity and its superior mechanical properties.
En el presente trabajo se describe la preparación de hidrogeles basados en redes entrecruzadas de poli (N-vinilpirrolidona), PVP con polietilenglicol, agar y un 90% de agua, y nanocomposites de PVP con una nanoarcilla sintética, la Laponita XLG para su empleo como apósito para quemaduras. Estos sistemas se obtuvieron por dos vías: radiación gamma de Co-60 y haz de electrones. La dosis de gelificación obtenida fue de Dg= 1.72 kGy. El módulo elástico de los hidrogeles resultó independiente del método de irradiación, siendo igual a 0.39 MPa para el irradiado con Co-60 y 0.38 MPa para el irradiado con haz de electrones. El módulo elástico de la membrana de nanocomposite fue 3 veces superior, 1.25 MPa. Estos resultados muestran que los hidrogeles de nanocomposites de PVP/Laponita XLG resultan superiores para su aplicación en el tratamiento de quemaduras, por su alta capacidad de sorción de agua y sus mejores propiedades mecánicas.