Green polymer chemistry: investigating the mechanism of radical ring-opening redox polymerization (R3P) of 3,6-dioxa-1,8-octanedithiol (DODT).

The mechanism of the new Radical Ring-opening Redox Polymerization (R3P) of 3,6-dioxa-1,8-octanedithiol (DODT) by triethylamine (TEA) and dilute H2O2 was investigated. Scouting studies showed that the formation of high molecular weight polymers required a 1:2 molar ratio of DODT to TEA and of DODT to H2O2. Further investigation into the chemical composition of the organic and aqueous phases by 1H-NMR spectroscopy and mass spectrometry demonstrated that DODT is ionized by two TEA molecules (one for each thiol group) and thus transferred into the aqueous phase. The organic phase was found to have cyclic disulfide dimers, trimers and tetramers. Dissolving DODT and TEA in water before the addition of H2O2 yielded a polymer with Mn = 55,000 g/mol, in comparison with Mn = 92,000 g/mol when aqueous H2O2 was added to a DODT/TEA mixture. After polymer removal, MALDI-ToF MS analysis of the residual reaction mixtures showed only cyclic oligomers remaining. Below the LCST for TEA in water, 18.7 °C, the system yielded a stable emulsion, and only cyclic oligomers were found. Below DODT/TEA and H2O2 1:2 molar ratio mostly linear oligomers were formed, with <20% cyclic oligomers. The findings support the proposed mechanism of R3P.

Gelatin and galactomannan-based scaffolds: Characterization and potential for tissue engineering applications.

In this work, we produced gelatin films containing different concentrations of galactomannan by casting solutions. The films were crosslinked by immersion in 30mM solution of 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide hydrochloride (EDC). The crosslinking of gelatin-containing films was confirmed by the reduction of free amine band intensity (3400-3200cm(-1)) in the GEL IR, as well as by the evaluation of its behavior when immersed in phosphate-buffer solution. The crosslinking of galactomannan film was confirmed by the formation of new ether bonds, as observed by increasing intensity of the band at 1148cm(-1), and the reduction of OH band intensity (3600-3200cm(-1)). The presence of galactomannan and the crosslinking mediated by EDC were responsible to improve elasticity in the gelatin-based films. The samples did not show cytotoxicity during 24h or 48h. In addition, rat mesenchymal stem cells adhered to the films regardless of galactomannan concentration. The results indicated that the gelatin/galactomannan films are potential biomaterials for use as scaffolds for tissue engineering.