RESUMO
When exposed to air, silver artifacts undergo an unpleasant darkening and shiny loss, commonly known as tarnishing. At the present, the development of protective coatings by using eco-friendly and biocompatible materials, able to ensure high transparency and to hinder the degradation of silver objects, remains a huge challenge. In this study, chitosan was used for the first time to realize sustainable coatings for silver protection. Both pure and benzotriazole-containing chitosan coatings were prepared and applied on sterling silver disks. A commercial product based on acrylic resin was used as a reference. The aesthetic features and protective properties of these coatings were evaluated by performing two different types of aging treatments. In particular, the assessment of the protective efficacy was carried out by reproducing both highly aggressive polluted environments and real-like museums' storage conditions. In the first case, chitosan-based coatings with benzotriazole performed better, whereas in storage conditions all the chitosan films showed comparable efficacy. Compositional, morphological and structural analyses were used to evaluate the protective properties of the coatings and to detect any physical or chemical modifications after the aging treatments. Our findings reveal that the two different testing methods provide complementary information. Moreover, chitosan coatings can achieve protective efficacy comparable with that of the commercial product but using non-toxic solvents and a renewable biopolymer. Chitosan coatings, designed for cultural heritage conservation, are thus promising for the protection of common sterling silver objects.
Assuntos
Quitosana , Prata , Biopolímeros , Quitosana/química , Prata/químicaRESUMO
The protection of metals from atmospheric corrosion is a task of primary importance for many applications and many different products have been used, sometimes being toxic and harmful for health and the environment. In order to overcome drawbacks due to toxicity of the corrosion inhibitors and harmful organic solvents and to ensure long-lasting protection, new organic compounds have been proposed and their corrosion inhibition properties have been investigated. In this work, we describe the use of a new environment-friendly anticorrosive coating that takes advantage of the synergism between an eco-friendly bio-polymer matrix and an amino acid. The corrosion inhibition of a largely used Copper-based (Cu-based) alloy against the chloride-induced indoor atmospheric attack was studied using chitosan (CH) as a biopolymer and l-Cysteine (Cy) as an amino acid. To evaluate the protective efficacy of the coatings, tailored accelerated corrosion tests were carried out on bare and coated Cu-based alloys, further, the nature of the protective film formed on the Cu-based alloy surface was analyzed by Fourier-transformed infrared spectroscopy (FTIR) while the surface modifications due to the corrosion treatments were investigated by optical microscopy (OM). The evaluation tests reveal that the Chitosan/l-Cysteine (CH/Cy) coatings exhibit good anti-corrosion properties against chloride attack whose efficiency increases with a minimum amount of Cy of 0.25 mg/mL.
Assuntos
Ligas/química , Quitosana/química , Cloretos/química , Cobre/química , Cisteína/química , Materiais Revestidos Biocompatíveis/química , Corrosão , Magnésio/química , Teste de Materiais/métodos , Propriedades de Superfície , Zinco/químicaRESUMO
Mesoporous silica nanoparticles (MSNPs) are currently used in different fields like catalysis, nanomedicine, and conservation science, taking advantage of their high surface area. Here, we synthesized and functionalized mesoporous dendritic fibrous nanoparticles to realize a smart delivery system of protective agents for metals. Different MSNPs were obtained via the microemulsion method followed by a hydrothermal or refluxing treatment at different w/o ratios, times, and temperatures. Dendritic spherical silica nanoparticles with specific features such as an appropriate size (450 nm), a very large surface area (600 m2 g-1), and a high yield synthesis (86%) were selected for surface modification. The fiber surface of the selected MSNPs was functionalized with 3-aminopropyl triethoxysilane (3-APTES). 3-APTES works as a pH-driven "nanogate", suppressing the immediate leakage of the total guest molecule load and modulating the release as a function of pH conditions. Surface-modified MSNPs were tested as a reservoir of the most diffused corrosion inhibitors: Mercaptobenzothiazole (MBT) and 1H-Benzotriazole (BTA); their release properties were studied in solutions with pH = 4 and 7. Functionalized and non-functionalized MSNPs showed a good loading efficiency of guest molecules (34-64%) and a pH-dependent release of the corrosion inhibitors on a timescale of several hours.
RESUMO
The aim of this study is to propose a non-invasive multi-spectroscopic approach for the characterization of oil painting artworks that use a copper plates as substrate in place of a canvas. Indeed, in the last decade, many studies have been conducted on artworks made of single materials (e.g., paintings, stones, metals). However, the characterization and conservation of composite artifacts has never be fully investigated even though many masterpieces were created using this particular technique. In this work, several spectroscopic techniques such as Infrared Spectroscopy (FTIR), Energy-Dispersive X-Ray Fluorescence spectroscopy (EDXRF), and high spatial resolution Field Emission Scanning Electron Microscopy coupled with Energy Dispersive X-ray Spectroscopy (EDS), and Optical Microscopy (OM) were performed. The obtained results allowed to fully characterize the micro-chemical and microstructural features of the painted surfaces and of the metal plate. Particularly effective was the use of MA-XRF, resulting in the chemical map of the painted surfaces. Furthermore, traces of the mechanical preparation of the plate were found under the painted layers. Finally, the interface area between the paint film and the metallic support was characterized at a micro scale. This was particularly important in order to identify the degradation products formed by the interaction between the fatty acids of the binder and copper-based substrates.
RESUMO
The aim of this study was to develop smart materials with stimuli-responsive properties for the long-term protection of steel. The idea was to obtain a tailored and controlled release of protective agents in response to the environment stimuli. First, the protective efficacy of three inhibitors containing a carboxylic moiety, such as p-aminobenzoic (pAB), succinic (SA), and caffeic (CA) acids, was investigated in alkaline chloride solutions. The results revealed that pAB is the most effective protective agent, significantly better than SA and CA. It is surprising that the steel surface in the pAB solution remains unchanged even after 5 months of corrosion treatment, whereas the formation of degradation products in the SA and CA solutions was observed after only 6 days. Based on these findings, pAB was selected and used for the functionalization of silica nanoparticles and layered double hydroxides (LDHs) that can act as delivery vehicles and as an inhibitor reservoir. Specifically, pAB was chemisorbed on silica amino groups via an amide bond, and this makes possible a gradual inhibitor release induced by an alkaline environment. The intercalation of pAB in its anionic form into the LDHs structure is responsible for a completely different behavior since the release is induced by chloride ions and occurs by an anionic exchange reaction. Thus, these materials play a dual role by acting as an inhibitor reservoir and by capturing chlorides. These findings reveal that it is possible to create a reservoir of corrosion inhibitors gradually released on demand based on the chemical environment. The stimuli-responsive properties and the complementary protective action of inhibitor-loaded silica and LDHs make them attractive for the long-term protection of steel and open the way for innovative solutions in the preservation of concrete cultural heritage.