rGO/ZIF-8 Aerogel for Effective Removal of Malachite Green from Wastewater.

In this study, dopamine-modified graphene aerogel (DGA) is synthesized through a one-step hydrothermal method using graphene oxide as the precursor and dopamine as the reducing agent. Subsequently, in situ immersion synthesis is conducted to obtain ZIF-8 loaded on a dopamine-modified graphene aerogel skeleton (ZDGA), featuring a regular honeycomb interconnected mesoporosity and a high specific surface area of 532.8 m2/g. The synthesized ZDGA exhibited exceptional adsorption performance for the cationic dye malachite green. At room temperature, ZDGA achieved an impressive equilibrium adsorption capacity of 6578.34 mg/g. The adsorption process followed pseudo-secondary kinetics and adhered to the Langmuir model, indicating chemically dominated adsorption on a monomolecular layer. Intraparticle diffusion was the primary rate determinant, with π-π stacking, electrostatic adsorption, hydrogen bonding, and Lewis acid-base interactions serving as the key driving forces. It has an ideal specific surface area and good cycling performance, which highlights its potential application in dye wastewater treatment.

Fatigue Behavior of the FGH96 Superalloy under High-Temperature Cyclic Loading.

Strain-controlled low-cycle fatigue (LCF) tests and stress-controlled creep-fatigue interaction (CFI) tests on the FGH96 superalloy were carried out at 550 °C to obtain the cyclic softening/hardening characteristics at different strain amplitudes and ratcheting strain characteristics under different hold time. The failure mechanism of the FGH96 superalloy under different loading conditions was analyzed through fracture observations. The results show that the FGH96 superalloy exhibits different cyclic softening/hardening characteristics at different strain amplitudes, and the introduction of the hold time at peak stress exacerbates the ratcheting strain of the FGH96 superalloy under asymmetric stress cycles. Fracture observations show that the magnitude of the strain amplitude, high-temperature oxidation, and the introduction of the hold time will affect the mechanical properties of the FGH96 superalloy and change its fracture mode.