Mechanical Properties of Fully Recycled Aggregate Concrete Reinforced with Steel Fiber and Polypropylene Fiber.

The study and utilization of fully recycled aggregate concrete (FRAC), in which coarse and fine aggregates are completely replaced by recycled aggregates, are of great significance in improving the recycling rate of construction waste, reducing the carbon emission of construction materials, and alleviating the ecological degradation problems currently faced. In this paper, investigations were carried out to study the effects of steel fiber (0.5%, 1.0%, and 1.5%) and polypropylene fiber (0.9 kg/m3, 1.2 kg/m3 and 1.5 kg/m3) on the properties of FRAC, including compressive strength, splitting tensile strength, the splitting tensile load-displacement curve, the tensile toughness index, flexural strength, the load-deflection curve, and the flexural toughness index. The results show that the compressive strength, splitting tensile strength, and flexural strength of fiber-reinforced FRAC were remarkably enhanced compared with those of ordinary FRAC, and the maximum increase was 56.9%, 113.3%, and 217.0%, respectively. Overall, the enhancement effect of hybrid steel-polypropylene fiber is more significant than single-mixed fiber. Moreover, the enhancement of the crack resistance, tensile toughness, and flexural toughness obtained by adding steel fiber to the FRAC is more significant than that obtained by adding polypropylene fiber. Furthermore, adding polypropylene fiber alone and mixing it with steel fiber showed different FRAC splitting tensile and flexural properties.

Enhancing the Mechanical and Durability Properties of Fully Recycled Aggregate Concrete Using Carbonated Recycled Fine Aggregates.

The global construction industry is increasingly utilizing concrete prepared from recycled aggregate as a substitute for natural aggregate. However, the subpar performance of recycled fine aggregate (RFA) has resulted in its underutilization, particularly in the structural concrete exposed to challenging environments, including those involving chlorine salts and freeze-thaw climates. This study aimed to enhance the performance of RFA as a substitute for river sand in concrete as well as fulfill the present demand for fine aggregates in the construction sector by utilizing accelerated carbonation treatment to create fully recycled aggregate concrete (FRAC) composed of 100% recycled coarse and fine aggregates. The impacts of incorporating carbonated recycled fine aggregate (C-RFA) at various replacement rates (0%, 25%, 50%, 75%, and 100%) on the mechanical and durability properties of FRAC were investigated. The results showed that the physical properties of C-RFA, including apparent density, water absorption, and crushing value, were enhanced compared to that of RFA. The compressive strength of C-RFC100 was 19.8% higher than that of C-RFC0, while the water absorption decreased by 14.6%. In a comparison of C-RFC0 and C-RFC100, the chloride permeability coefficients showed a 50% decrease, and the frost resistance increased by 27.6%. According to the findings, the mechanical and durability properties, the interfacial transition zones (ITZs), and micro-cracks of the C-RFC were considerably enhanced with an increased C-RFA content.