Effect of deproteinization and tubular occlusion on microtensile bond strength and marginal microleakage of resin composite restorations
J. appl. oral sci
; 17(5): 462-466, Sept.-Oct. 2009. ilus, tab
Article
em En
| LILACS
| ID: lil-531398
Biblioteca responsável:
BR1.1
ABSTRACT
Dentin adhesion procedure presents limitations, especially regarding to lifetime stability of formed hybrid layer. Alternative procedures have been studied in order to improve adhesion to dentin. OBJECTIVE:
The aim of this study was to evaluate in vitro the influence of deproteinization or dentin tubular occlusion, as well as the combination of both techniques, on microtensile bond strength (µTBS) and marginal microleakage of composite resin restorations. MATERIAL ANDMETHODS:
Extracted erupted human third molars were randomly divided into 4 groups. Dentin surfaces were treated with one of the following procedures (A) 35 percent phosphoric acid gel (PA) + adhesive system (AS); (B) PA + 10 percent NaOCl + AS; (C) PA + oxalate + AS and (D) PA + oxalate + 10 percent NaOCl + AS. Bond strength data were analyzed statistically by two-way ANOVA and Tukey's test. The microleakage scores were analyzed using Kruskal-Wallis and Mann-Whitney non-parametric tests. Significance level was set at 0.05 for all analyses.RESULTS:
µTBS data presented statistically lower values for groups D and B, ranking data as A>C>B>D. The use of oxalic acid resulted in microleakage reduction along the tooth/restoration interface, being significant when used alone. On the other hand, the use of 10 percent NaOCl alone or in combination with oxalic acid, resulted in increased microleakage.CONCLUSIONS:
Dentin deproteinization with 10 percent NaOCl or in combination with oxalate significantly compromised both the adhesive bond strength and the microleakage at interface. Tubular occlusion prior to adhesive system application seems to be a useful technique to reduce marginal microleakage.Palavras-chave
Texto completo:
1
Base de dados:
LILACS
Assunto principal:
Colagem Dentária
/
Adaptação Marginal Dentária
/
Resinas Compostas
/
Infiltração Dentária
/
Materiais Dentários
/
Dentina
Tipo de estudo:
Clinical_trials
Limite:
Humans
Idioma:
En
Revista:
J. appl. oral sci
Assunto da revista:
ODONTOLOGIA
Ano de publicação:
2009
Tipo de documento:
Article
País de afiliação:
Brasil