RESUMO
Pickering emulsion polymerization, stabilized by inorganic nanoparticles such as iron oxide nanoparticles (IONPs), can be used to fabricate scaffolds with the desired porosity and pore size. These nanoparticles create stable emulsions that can be processed under harsh polymerization conditions. IONPs, apart from serving as an emulsifier, impart beneficial bioactivities such as antibacterial and pro-angiogenic activity. Here, we coated IONPs with three different weights of oleic acid (5.0 g, 7.5 g, and 10.0 g) to synthesize oleic acid-IONPs (OA-IONPs) that possess the desired hydrophobicity (contact angle > 100°). Next, glycidyl methacrylate and trimethylolpropane triacrylate were polymerized using the Pickering emulsion polymerization technique stabilized by the OA-IONPs. The physicochemical properties of the resulting porous scaffolds were thoroughly characterized using scanning electron microscopy (SEM), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FT-IR), vibrating sample magnetometry (VSM), and a universal testing machine (UTM). The SEM images confirmed the formation of a porous scaffold. The IONPs content, measured using inductively coupled plasma mass spectrometry (ICP-MS), was in the range of 22-26 µg/mg of the scaffold. The mechanical strengths of the scaffolds were in the range of cancellous bone. The degradation profile of the scaffolds varied between 29% and 41% degradation over 30 days. In vitro cytotoxicity studies conducted using the fibroblast (L929) and osteosarcoma (MG-63) cell lines proved that these scaffolds were non-toxic. SEM images showed that the MG-63 cells adhered firmly to the scaffolds and exhibited a well-spread morphology. The antibacterial activity was confirmed by percentage inhibition studies, SEM analysis of bacterial membrane distortion, and reactive oxygen species (ROS) generation in the bacteria. Chick chorioallantoic membrane assay showed that the total vessel length and branch points were significantly increased in the presence of the scaffolds. These results confirm the pro-angiogenic potential of the fabricated scaffolds. The physicochemical, mechanical, and biological properties of the material suggest that the developed scaffolds would be suitable for bone tissue engineering applications.
Assuntos
Ácido Oleico , Engenharia Tecidual , Engenharia Tecidual/métodos , Espectroscopia de Infravermelho com Transformada de Fourier , Emulsões , Alicerces Teciduais/química , Antibacterianos/farmacologia , Acrilatos , Nanopartículas Magnéticas de Óxido de Ferro , PorosidadeRESUMO
Transdermal patch for local drug delivery has attained huge attention as an attractive alternative to existing drug delivery techniques as it is painless and user-friendly. However, most adhesive hydrogels either do not have adequate adhesion with the skin or cause discomfort while being removed from the skin surface due to excessive adhesion. To address this challenge, we developed an adhesive hydrogel based on laponite-confined dopamine polymerization as a transdermal patch. Laponite RDS nanoclay was used to control the hydrogel's viscous behavior and dopamine polymerization. The laponite polymerized polydopamine (l-PDA) was incorporated into poly(vinyl alcohol) (PVA) to make the PVA-l-PDA hydrogel. The laponite-confined polymerization improved the hydrogels' water contact angle and adhesion strength. The adhesion strength of the PVA-l-PDA hydrogel was adequate to adhere to the evaluated goat skin, glass, and polypropylene surfaces. Notably, the PVA-l-PDA hydrogel was easy to peel off from the skin. Further, we evaluated the drug release profile in goat skin using lidocaine as a model drug. We observed the controlled release of lidocaine from the PVA-l-PDA hydrogel compared to the PVA-PDA hydrogel. In addition, the nanoclay-confined adhesive hydrogel did not show any cytotoxic effect in fibroblasts. Altogether, PVA-l-PDA hydrogels offer appropriate adhesive strength, toughness, and biocompatibility. Thus, the PVA-l-PDA hydrogel has the potential to be an efficient transdermal patch.
Assuntos
Adesivos , Hidrogéis , Dopamina , Polimerização , Adesivo TransdérmicoRESUMO
Curcumin is a highly potent nutraceutical associated with various health benefits. However, its hydrophobic nature affects its bioavailability and bioactivity, and limits nutraceutical applications. Drug-in-cyclodextrin-in-liposome has the ability to mask the hydrophobic nature of drug and achieve better encapsulation. Also, encapsulating iron oxide nanoparticles (IONPs) within liposomes endow additional beneficial functionalities of IONPs. In the present study, curcumin-ß-cyclodextrin inclusion complex (IC) and IONPs were co-encapsulated within liposomes (curcumin-in-ß-cyclodextrin-in-nanomagnetoliposomes) to achieve the synergistic antioxidant potential of curcumin and IONPs. IC of curcumin-ß-cyclodextrin was prepared by a simple rapid method and successful inclusion was confirmed by Fourier transform infrared spectroscopy (FTIR) and nuclear magnetic resonance (NMR). Mean diameter of IONPs was found to be 180nm and X-ray diffraction pattern confirmed the formation of hematite nanoparticles. Band gap energy calculated using absorption spectra was 2.25eV, which falls in close proximity with the theoretically calculated values of hematite. Mean diameter of curcumin-in-ß-cyclodextrin-in-nanomagnetoliposomes was 67nm and encapsulation efficiency of curcumin was found to be 71%. Further, the co-encapsulated particles possessed significantly low IC50 value (64.7791µg/ml, p<0.01) compared to conventional curcumin liposome and IONPs, indicating its synergistically enhanced radical scavenging property.