RESUMO
This work focuses on the development of an electrocatalytic material by annealing a composite of a transition metal coordination material, iron hexacyanoferrate (Prussian blue) immobilized on carboxylic-acid-functionalized reduced graphene oxide. Pyrolysis at 500 °C under a nitrogen atmosphere formed nanoporous core-shell structures with efficient activity, which mostly included iron carbide species capable of participating in the oxygen reduction reaction in alkaline media. The physicochemical properties of the iron-based catalyst were elucidated using transmission electron microscopy, X-ray diffraction, Mössbauer spectroscopy, and various electrochemical techniques, such as cyclic voltammetry and rotating ring-disk electrode (RRDE) voltammetry. To improve the electroreduction of oxygen over the studied catalytic material, an external magnetic field was utilized, which positively shifted the potential by ca. 20 mV. The formation of undesirable intermediate peroxide species was decreased compared with the ORR measurements without an external magnetic field.
RESUMO
The present paper focuses on the fabrication of coatings based on vinyltrimethoxysilane and the influence of various corrosion media on the coatings produced. Coatings were deposited on two substrate materials, namely, titanium Grade 2 and titanium alloy Ti13Nb13Zr, by immersion in a solution containing vinyltrimethoxysilane, anhydrous ethyl alcohol, acetic acid and distilled water. The obtained coatings were characterized in terms of surface morphology, adhesion to the substrate and corrosion resistance. As corrosion solutions, four different simulated physiological fluids, which differed in the contents of individual ions, and a 1 mol dm-3 NaBr solution were used. The chloride ions contained in the simulated physiological fluids did not lead to pitting corrosion of titanium Grade 2 and titanium alloy Ti13Nb13Zr. This investigation shows that titanium undergoes pitting corrosion in a bromide ion medium. It is demonstrated that the investigated coatings slow down corrosion processes in all corrosion media examined.
RESUMO
The paper reports the results of the examination of the protective properties of silane coatings based on vinyltrimethoxysilane (VTMS) and ethanol (EtOH), doped with the following electrolytes: acetic acid (AcOH), lithium perchlorate LiClO4, sulphuric acid (VI) H2SO4 and ammonia NH3. The coatings were deposited on stainless steel X20Cr13 by the sol-gel dip-coating method. The obtained VTMS/EtOH/Electrolyte coatings were characterized in terms of corrosion resistance, surface morphology and adhesion to the steel substrate. Corrosion tests were conducted in sulphate media acidified up to pH = 2 with and without chloride ions Cl-, respectively. The effectiveness of corrosion protection was determined using potentiometric curves. It has been demonstrated that the coatings under study slow down the processes of corrosion of the steel substrate, thus effectively protecting it against corrosion.
RESUMO
We develop a concept of fabrication of the multilayer network films on electrodes by exploring the ability of a Keggin-type polyoxometallate, phosphododecamolybdate (PMo(12)O(40)(3-)), to form stable anionic monolayers (templates) on carbon and metals including platinum. By repeated alternate treatments in the solution of PMo(12)O(40)(3-) (or in the colloidal suspension of polyoxometallate-protected Pt-nanoparticles) and in the solution of monomer (e.g. anilinium) cations, the amount of the material can be increased systematically (layer-by-layer) to form stable three-dimensional assemblies on electrode (e.g. glassy carbon) surfaces. In the resulting hybrid (organic-inorganic) films, the layers of negatively charged polyoxometallate, or polyoxometallate-protected (stabilized) Pt-nanoparticles, are linked or electrostatically attracted by ultra-thin layers of such positively charged conducting polymers as polyaniline (PANI), polypyrrole (PPy) or poly(3,4-ethylenedioxythiophene), PEDOT. Consequently, the attractive physicochemical properties of polymers and reactivity of polyoxometallate or noble metal particles are combined. The films are functionalized and show electrocatalytic properties towards reduction of nitrite, bromate, hydrogen peroxide or oxygen. They are of importance to the chemical and biochemical sensing as well as to the biochemical and medical applications.