The effect of repeated porcelain firings on the marginal fit of millable and conventional casting alloys.

The durability of dental restorations is highly determined by an accurate marginal fit, which is in turn affected by the high temperature of porcelain firing. Information is inadequate about the marginal adaptation of metal-ceramic restorations fabricated by soft metal milling technologies after repeated firings. This study aimed to compare the effect of repeated ceramic firings on the marginal fit of copings fabricated from cobalt-chromium through soft metal milling and a conventional nickel-chromium casting alloy. A single standard brass die was designed, machined, and scanned, based on which, 20 frameworks were designed and fabricated through either soft metal milling or conventional casting (n = 10 per group) and porcelain veneered. The vertical marginal fit of the metal copings was measured after 3, 5, and 7 firing cycles by using a digital microscope on 16 points around the finish line of the metal die at ×80 magnification. The data were analyzed through repeated measures ANOVA and independent t-test (α = 0.05). The marginal fit of neither metal group was significantly affected by the number of firing cycles (P = 0.747). However, the marginal discrepancy was statistically lower in the soft metal milling group than that in the casting group (P<0.001). Repeated porcelain firings did not significantly affect the marginal fit of either alloy and remained within the clinically acceptable range after firings. However, the milled alloy had superior marginal fit regardless of the number of firing cycles.

In vitro and in vivo antileishmanial effects of Nectaroscordum koelzi extract against Leishmania major.

Due to the increasing resistance to common medicinal compounds, the use of medicinal plants has received special attention. Therefore, the current survey was designed to study the antileishmanial effects of Nectaroscordum koelzi Trautv. methanolic extract against Leishmania major. In this study, after preparing the methanolic extract of N. koelzi, its effect on the amastigotes of L. major and triggering the nitric oxide (NO) were measured. Then, the in vivo effect of the methanol extract on cutaneous leishmaniasis in mice was evaluated. The best anti-amastigote effect was for the methanol extract of N. koelzi along with meglumine antimony with 50% inhibitory concentrations value of 17.4 µg/ml (p < 0.001). The 50% cytotoxic concentrations values of methanol extract, meglumine antimoniate, and methanol extract + meglumine antimoniate were 596.3, 784.6, and 296.4 µg/ml, respectively. Macrophages treated with the methanolic extract markedly (p < 0.001) induced the release of nitric oxide. After 28 days of treatment, lesions were completely (p < 0.001) healed in mice treated with the methanolic extract (100 mg/kg) + meglumine antimoniate (25 mg/kg). N. koelzi methanolic extract mainly in combination with meglumine antimoniate showed favorable antileishmanial effects on L. major, concluding that the methanolic extract of N. koelzi can be used for the production of new leishmanicidal agents agaist cutaneous leishmaniasis. Although we revealed that NO trigerring and inhibition of infection in host cells are the antileishmanial mechanism action of N. koelzi methanolic extract, more studies must be performed to clear the mechanisms and its safety.