NIR Emitting Nanoprobes Based on Cyclic RGD Motif Conjugated PbS Quantum Dots for Integrin-Targeted Optical Bioimaging.

Here, silica-coated PbS quantum dots (QDs) with photoluminescence emission properties in the near-infrared (NIR) region are proposed as potential effective single particle optical nanoprobes for future in vivo imaging of tumors. The dispersibility in aqueous medium of hydrophobic PbS QDs was accomplished by growing a silica shell on their surface by exploiting a base assisted water-in-oil microemulsion method. The silica-coated PbS QDs were then conjugated with a specifically designed cyclic arginine-glycine-aspartic acid (cRGD) peptide that is able to specifically recognize αvß3 integrins, which are overexpressed in angiogenic tumor-induced vasculatures and on some solid tumors, to achieve tumor-specific targeting. The cRGD peptide PbS silica-coated QDs were systematically characterized, at each step of their preparation, by means of complementary optical and structural techniques, demonstrating appropriate colloidal stability and the maintenance of their optical futures in aqueous solutions. The cellular uptake of cRGD peptide functionalized luminescent nanostructures in human melanoma cells, where overexpression of αvß3 was observed, was assessed by means of confocal microscopy analysis and cytometric study. The selectivity of the cRGD peptide PbS silica-coated QDs for the αvß3 integrin was established, consequently highlighting the significant potential of the developed NIR emitting nanostructures as optically traceable nanoprobes for future αvß3 integrin receptor in vivo targeting in the NIR region.

Lipid-based systems loaded with PbS nanocrystals: near infrared emitting trackable nanovectors.

Hydrophobic PbS nanocrystals (NCs) emitting in the near infrared spectral region were encapsulated in the core of micelles and in the bilayer of liposomes, respectively, to form polyethylene glycol (PEG)-grafted phospholipids. The phospholipid-based functionalization process of PbS NCs required the replacement of the pristine capping ligand at the NC surface with thiol molecules. The procedures carried out for two systems, micelles and liposomes, using PEG-modified phospholipids were carefully monitored by optical, morphological and structural investigations. The hydrodynamic diameter and the colloidal stability of both micelles and liposomes loaded with PbS NCs were evaluated using Dynamic Light Scattering (DLS) and ζ-potential experiments, and both were satisfactorily stable in physiological media. The cytotoxicity of the resulting PbS NC-loaded nanovectors was assessed by the in vitro investigation on Saos-2 cells, indicating that the toxicity of the PbS NC loaded liposomes was lower than that of the micelles with the same NC cargo, which is reasonable due to the different overall composition of the two prepared nanocarriers. Finally, the cellular uptake in the Saos-2 cells of both the NC containing systems was evaluated by means of confocal microscopy studies by exploiting a visible fluorescent phospholipid and demonstrating the ability of both luminescent nanovectors to be internalized. The obtained results show the great potential of the prepared emitting nanoprobes for imaging applications in the second biological window.

Highly selective luminescent nanostructures for mitochondrial imaging and targeting.

Here a luminescent hybrid nanostructure based on functionalized quantum dots (QDs) is used as a fluorescent imaging agent able to target selectively mitochondria thanks to the molecular recognition of the translocator protein (TSPO). The selective targeting of such an 18 kDa protein mainly located in the outer mitochondrial membrane and overexpressed in several pathological states including neurodegenerative diseases and cancers may provide valuable information for the early diagnosis and therapy of human disorders. In particular, the rational design of amino functionalized luminescent silica coated QD nanoparticles (QD@SiO2 NPs) provides a versatile nanoplatform to anchor a potent and selective TSPO ligand, characterized by a 2-phenyl-imidazo[1,2-a]pyridine acetamide structure along with a derivatizable carboxylic end group, useful to conjugate the TSPO ligand and achieve TSPO-QD@SiO2 NPs by means of a covalent amide bond. The colloidal stability and optical properties of the proposed nanomaterials are comprehensively investigated and their potential as mitochondrial imaging agents is fully assessed. Sub-cellular fractionation, together with confocal laser scanning fluorescence microscopy and co-localization analysis of targeted TSPO-QD@SiO2 NPs in C6 glioma cells overexpressing the TSPO, proves the great potential of these multifunctional nanosystems as in vitro selective mitochondrial imaging agents.

Assembly of a photosynthetic reaction center with ABA tri-block polymersomes: highlights on protein localization.

The reconstitution of the integral membrane protein photosynthetic reaction center (RC) in polymersomes, i.e. artificial closed vesicles, was achieved by the micelle-to-vesicle transition technique, a very mild protocol based on size exclusion chromatography often used to drive the incorporation of proteins contemporarily to liposome formation. An optimized protocol was used to successfully reconstitute the protein in a fully active state in polymersomes formed by the tri-block copolymers PMOXA22-PDMS61-PMOXA22. The RC is very sensitive to its solubilizing environment and was used to probe the positioning of the protein in the vesicles. According to charge-recombination experiments and to the enzymatic activity assay, the RC is found to accommodate in the PMOXA22 region of the polymersome, facing the water bulk solution, rather than in the PDMS61 transmembrane-like region. Furthermore, polymersomes were found to preserve protein integrity efficiently as the biomimetic lipid bilayers but show a much longer temporal stability than lipid based vesicles.

Discrimination of geographical origin of lentils (Lens culinaris Medik.) using isotope ratio mass spectrometry combined with chemometrics.

The aim of this study was to predict the geographic origin of lentils by using isotope ratio mass spectrometry (IRMS) in combination with chemometrics. Lentil samples from two origins, i.e. Italy and Canada, were analysed obtaining the stable isotope ratios of δ(13)C, δ(15)N, δ(2)H, δ(18)O, and δ(34)S. A comparison between median values (U-test) highlighted statistically significant differences (p<0.05) for all isotopic parameters between the lentils produced in these two different geographic areas, except for δ(15)N. Applying principal component analysis, grouping of samples was observed on the basis of origin but with overlapping zones; consequently, two supervised discriminant techniques, i.e. partial least squares discriminant analysis and k-nearest neighbours algorithm were used. Both models showed good performances with external prediction abilities of about 93% demonstrating the suitability of the methods developed. Subsequently, isotopic determinations were also performed on the protein and starch fractions and the relevant results are reported.

Electronic nose and isotope ratio mass spectrometry in combination with chemometrics for the characterization of the geographical origin of Italian sweet cherries.

Sweet cherries from two Italian regions, Apulia and Emilia Romagna, were analysed using electronic nose (EN) and isotope ratio mass spectrometry (IRMS), with the aim of distinguishing them according to their geographic origin. The data were elaborated by statistical techniques, examining the EN and IRMS datasets both separately and in combination. Preliminary exploratory overviews were performed and then linear discriminant analyses (LDA) were used for classification. Regarding EN, different approaches for variable selection were tested, and the most suitable strategies were highlighted. The LDA classification results were expressed in terms of recognition and prediction abilities and it was found that both EN and IRMS performed well, with IRMS showing better cross-validated prediction ability (91.0%); the EN-IRMS combination gave slightly better results (92.3%). In order to validate the final results, the models were tested using an external set of samples with excellent results.

Biotin-decorated silica coated PbS nanocrystals emitting in the second biological near infrared window for bioimaging.

Nanoparticles (NPs) emitting in the second biological near infrared (NIR) window of the electromagnetic spectrum have been successfully synthesized by growing a silica shell on the hydrophobic surface of OLEA/TOP PbS nanocrystals (NCs), by means of a reverse microemulsion approach, and subsequently decorated with biotin molecules. The fabrication of very uniform and monodisperse NPs, formed of SiO2 shell coated single core PbS NCs, has been demonstrated by means of a set of complementary optical and structural techniques (Vis-NIR absorption and photoluminescence spectroscopy, transmission electron microscopy) that have highlighted how experimental parameters, such as PbS NC and silica precursor concentration, are crucial to direct the morphology and optical properties of silica coated PbS NPs. Subsequently, the silica surface of the core-shell NPs has been grafted with amino groups, in order to achieve covalent binding of biotin to NIR emitting silica coated NPs. Finally the successful reaction with a green-fluorescent labelled streptavidin has verified the molecular recognition response of the biotin molecules decorating the PbS@SiO2 NP surface. Dynamic light scattering (DLS) and ζ-potential techniques have been used to monitor the hydrodynamic diameter and colloidal stability of both PbS@SiO2 and biotin decorated NPs, showing their high colloidal stability in physiological media, as needed for biomedical applications. Remarkably the obtained biotinylated PbS@SiO2 NPs have been found to retain emission properties in the 'second optical window' of the NIR region of the electromagnetic spectrum, thus representing attractive receptor-targeted NIR fluorescent probes for in vivo tumour imaging.

Non-targeted 1H NMR fingerprinting and multivariate statistical analyses for the characterisation of the geographical origin of Italian sweet cherries.

In this study, non-targeted (1)H NMR fingerprinting was used in combination with multivariate statistical techniques for the classification of Italian sweet cherries based on their different geographical origins (Emilia Romagna and Puglia). As classification techniques, Soft Independent Modelling of Class Analogy (SIMCA), Partial Least Squares Discriminant Analysis (PLS-DA), and Linear Discriminant Analysis (LDA) were carried out and the results were compared. For LDA, before performing a refined selection of the number/combination of variables, two different strategies for a preliminary reduction of the variable number were tested. The best average recognition and CV prediction abilities (both 100.0%) were obtained for all the LDA models, although PLS-DA also showed remarkable performances (94.6%). All the statistical models were validated by observing the prediction abilities with respect to an external set of cherry samples. The best result (94.9%) was obtained with LDA by performing a best subset selection procedure on a set of 30 principal components previously selected by a stepwise decorrelation. The metabolites that mostly contributed to the classification performances of such LDA model, were found to be malate, glucose, fructose, glutamine and succinate.

Hybrid charge transfer complexes based on archaeal glycolipids wrapping single walled carbon nanotubes.

SWNTs have been functionalized with an archaeal glycolipid which wraps around the nano-objects in a single layer or bilayer, as a function of the nanotube diameter. Hydrogen bonds between the lipid glucose rings and the aromatic SWNT walls are involved in the formation of hybrid complexes resulting in electron transfer from the glycolipid to the nanotubes.

Photodegradation of nalidixic acid assisted by TiO(2) nanorods/Ag nanoparticles based catalyst.

Two different nanosized TiO2-based catalysts supported onto glass with tailored photocatalytic properties upon irradiation by UV light were successfully employed for the degradation of nalidixid acid, a widely diffused antibacterial agent of environmental relevance known to be non-biodegradable. Anatase rod-like TiO2 nanocrystals (TiO2NRs) and a semiconductor oxide-noble metal nanocomposite TiO2 NRs/Ag nanoparticles (NPs), synthesized by colloidal chemistry routes, were cast onto glass slide and employed as photocatalysts. A commercially available catalyst (TiO2 P25), also immobilized onto a glass slide, was used as a reference material. It was found that both TiO2 NRs/Ag NPs composite and TiO2 NRs demonstrated a photocatalytic efficiency significantly higher than the reference TiO2 P25. Specifically, TiO2 NRs/Ag NPs showed a photoactivity in nalidixic acid degradation 14 times higher than TiO2 P25 and 4 times higher than bare TiO2 NRs in the first 60min of reaction. Several by-products were identified by HPLC-MS along the nalidixic acid degradation, thus getting useful insight on the degradation pathway. All the identified by-products resulted completely removed after 6h of reaction.

Functionalized luminescent nanocrystals on patterned surfaces obtained by radio frequency glow discharges.

In this work a genuine combination of a bottom-up approach, which is based on synthesis and functionalization of emitting nanocrystals (NCs), with a top-down strategy, which relies on a flexible and versatile cold plasma process, is shown. Luminescent semiconducting colloidal NCs consisting of a CdSe core coated with a ZnS shell (CdSe@ZnS) are directly assembled onto micro-patterned substrates previously functionalized by means of glow discharges performed through physical masks. The NC assembly is driven by electrostatic interactions that led to their successful organization into spatially resolved domains. Two distinct protocols are tested, the former using a plasma deposition process combined with an electrostatic layer-by-layer procedure, the latter based on a two-step plasma deposition/treatment process. The procedures are thoroughly monitored with fluorescence microscopy, atomic force microscopy, x-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, transmission electron microscopy and scanning electron microscopy. The two-step plasma protocol is demonstrated to be more efficient in directing a uniform and specific assembly of luminescent NCs with respect to the hybrid procedure. The presented 'mix and match' approach offers great potential for integrating NCs, with their unique size-dependent properties, into microstructures, providing a universal platform for the fabrication of sensors, biochips, displays and switches.

Polyelectrolyte multilayers as a platform for luminescent nanocrystal patterned assemblies.

The fabrication of uniform and patterned nanocrystal (NC) assemblies has been investigated by exploiting the possibility of carefully tailoring colloidal NC surface chemistry and the ability of polyelectrolyte (PE) to functionalize substrates through an electrostatic layer-by-layer (LbL) strategy. Appropriate deposition conditions, substrate functionalization, and post-preparative treatments were selected to tailor the substrate surface chemistry to effectively direct the homogeneous electrostatic-induced assembly of NCs. Water-dispersible luminescent NCs, namely, (CdSe)ZnS and CdS, were differently functionalized by (1) ligand-exchange reaction, (2) growth of a hydrophilic silica shell, and (3) formation of a hydrophilic inclusion complex, thus providing functional NCs stable in a defined pH range. The electrostatically charged functional NCs represent a comprehensive selection of examples of surface-functionalized NCs, which enables the systematic investigation of experimental parameters in NC assembly processes carried out by combining LbL procedures with microcontact printing and also exploiting NC emission, relevant for potential applications, as a prompt and effective probe for evaluating assembly quality. Thus, an ample showcase of combinations has been investigated, and the spectroscopic and morphological features of the resulting NC-based structures have been discussed.

Nanocomposites based on highly luminescent nanocrystals and semiconducting conjugated polymer for inkjet printing.

In this work nanocomposites based on organic-capped semiconductor nanocrystals formed of a core of CdSe coated with a shell of ZnS (CdSe@ZnS), with different sizes, and a semiconducting conjugated polymer, namely poly[(9,9-dihexylfluoren-2,7-diyl)-alt- (2,5-dimethyl-1,4-phenylene)] (PF-DMB) have been investigated. The nanocomposites are prepared by mixing the pre-synthesized components in organic solvents, thereby assisting the dispersion of the organic-coated nano-objects in the polymer host. UV-vis steady state and time-resolved spectroscopy along with (photo)electrochemical techniques have been performed to characterize the obtained materials. The study shows that the embedded nanocrystals increase the PF-DMB stability against oxidation and, at the same time, extend the light harvesting capability to the visible spectral region, thus resulting in detectable photocurrent signals. The nanocomposites have been dispensed by means of a piezo-actuated inkjet system. Such inks present viscosity and surface tension properties well suited for stable and reliable drop-on-demand printing using an inkjet printer. The fabrication of arrays of single-color pixels made of the nanocomposites and micrometers in size has been performed. Confocal and atomic force microscopy have confirmed that inkjet-printed microstructures present the intrinsic emission properties of both the embedded nanocrystals and PF-DMB, resulting in a combined luminescence. Finally, the morphology of the printed pixels is influenced by the embedded nanofillers.

Instrumental and multivariate statistical analyses for the characterisation of the geographical origin of Apulian virgin olive oils.

In this paper, virgin olive oils (VOOs) coming from three different geographic origins of Apulia, were analysed for free acidity, peroxide value, spectrophotometric indexes, chlorophyll content, sterol, fatty acid, and triacylglycerol compositions. In order to predict the geographical origin of VOOs, different multivariate approaches were applied. By performing principal component analysis (PCA) a modest natural grouping of the VOOs was observed on the basis of their origin, and consequently three supervised techniques, i.e., general discriminant analysis (GDA), partial least squares-discriminant analysis (PLS-DA) and soft independent modelling of class analogy (SIMCA) were used and the results were compared. In particular, the best prediction ability was produced by applying GDA (average prediction ability of 82.5%), even if interesting results were obtained also by applying the other two classification techniques, i.e., 77.2% and 75.5% for PLS-DA and SIMCA, respectively.

Emerging methods for fabricating functional structures by patterning and assembling engineered nanocrystals.

Inorganic nanocrystals and nanoparticles have aroused increasing attention in the last years due to their original optoelectronic, thermodynamic, mechanical and catalytic properties, which are extremely attractive for fundamental understanding as well as for their huge potential in applications. The ability to strongly exploit the original potential of such nano-objects and access their properties relies on the ability to bridge the gap between the nanoscopic and mesoscopic scale. Indeed, to integrate nanoparticles in structures, materials and finally devices, their incorporation in processable systems, and their organization in morphologically controlled assembly and/or ordered arrays is crucial. The fabrication of 2/3 D patterned micro- and nanostructure is a promising strategy for integrating the nanoparticles in macroscopic entities in order to properly exploit their unprecedented functionality for biomedical, electronic, catalytic materials and devices. In this paper, different and complementary strategies able to engineer inorganic colloidal nanocrystals due to their organization in original functional materials and structures will be described.

Soluble proteome investigation of cobalt effect on the carotenoidless mutant of Rhodobacter sphaeroides.

AIMS: To investigate the surviving capability of Rhodobacter sphaeroides under phototrophic conditions in the presence of high cobalt concentration and its influence on the photosynthetic apparatus biosynthesis. METHODS AND RESULTS: Cells from R. sphaeroides strain R26.1 were grown anaerobically in a medium containing 5.0 mmol l(-1) cobalt ions and in a control medium. Metal toxicity was investigated comparing the soluble proteome of Co(2+)-exposed cells and cells grown in control medium by two-dimensional gel electrophoretic analysis. Significant changes in the expression level were detected for 43 proteins, the majority (35) being up-regulated. The enzyme porphobilinogen deaminase (PBGD) was found down-regulated and its activity was investigated. CONCLUSIONS: The up-regulated enzymes mainly belong to the general category of proteins and DNA degradation enzymes, suggesting that part of the catabolic reaction products can rescue bacterial growth in photosynthetically impaired cells. Furthermore, the down-regulation of PBGD strongly indicates that this key enzyme of the tetrapyrrole and bacteriochlorophyll synthesis is directly involved in the metabolic response. SIGNIFICANCE AND IMPACT OF THE STUDY: Data and experiments show that the cobalt detrimental effect on the photosynthetic growth of R. sphaeroides is associated with an impaired expression and functioning of PBGD.

Effect of aggregation state, temperature and phospholipids on photobleaching of photosynthetic pigments in spinach Photosystem II core complexes.

Photosystem II (PSII) complex activity is known to decrease under strong white light illumination, and this photoinhibition phenomenon is connected to the photobleaching of the PSII photosynthetic pigments. In this work the pigment photobleaching has been studied on PSII core complexes, by observing the effects of different factors such as the aggregation state (PSII monomers and dimers were used), temperature (20 degrees C and 10 degrees C temperatures were tested) and the presence of the exogenous phospholipids (cardiolipin and phosphatidylglycerol). In particular, PSII resistance against white light stress was studied by means of UV/VIS Absorption and Fluorescence Emission measurements. It was found that PSII dimers resulted more resistant against photobleaching and that lower temperature reduces the pigment photodestruction. Moreover, the presence of phosphatidylglycerol or cardiolipin enhanced the PSII resistance to the photobleaching phenomenon, mainly at lower temperatures.

Modification of spontaneous emission of (CdSe)ZnS nanocrystals embedded in nanoimprinted photonic crystals.

Highly luminescent (CdSe)ZnS nanocrystals, with band edge emission in the red region of the visible spectrum, were successfully synthesized and incorporated in a resist, namely mr-NIL 6000. The nanocomposite material was imprinted by using conventional nanoimprint lithography (NIL) process. We report on the fabrication and characterization of nanoimprinted photonic crystals in this new functional material. Experiments showed good imprint properties of the NC/polymer based material and that the surface nanostructuration improves the light extraction efficiency by over 2 compared to a nanoimprinted unpatterned surface.

Hybrid nanocomposites based on luminescent colloidal nanocrystals in poly(methyl methacrylate): spectroscopical and morphological studies.

We report on preparation process and optical characterization of a nanocomposite material obtained dispersing colloidal semiconductor nanocrystals (NCs), namely CdS and CdSe@ZnS core-shell system in poly(methyl methacrylate) (PMMA). Such method allows a large flexibility on nanocrystal materials and on the choice of the polymer characteristics. Nanocomposite thin films were extensively investigated by means optical and morphological techniques. The effects on NC composition, concentration, size, and surface chemistry on the spectroscopical and structural behaviour of the nanocomposite properties were studied. The NC size dependent optical properties of the nanocomposites are mainly accounted by the NC composition and size, while the morphology of the films is explained on the base of the NC surface characteristics and their concentration in the nanocomposites.