The impact of different surface treatments on repair bond strength of conventionally, subtractive-, and additive-manufactured denture bases.

OBJECTIVE: This study aimed to examine the shear bond strength (SBS) of repair material to conventionally, subtractive-, and additive-manufactured denture bases after different surface treatments. MATERIALS AND METHODS: Disk-shaped test specimens (N = 300) were prepared from denture base materials produced by one conventional (Procryla), one subtractive (Yamahachi), and one additive (Curo Denture) method. The test specimens were randomly divided into five groups (n = 10) and exposed to a variety of surface treatments-Group A: no surface treatment; Group B: grinding with silicon carbide paper; Group C: sandblasting; Group D: erbium: yttrium-aluminum-garnet laser; and Group E: plasma. Repair was performed with autopolymerizing acrylic resin (Meliodent). Surface roughness analyses were performed with a profilometer. Scanning electron microscopy was used to examine one specimen from each subgroup. SBS was evaluated on a universal testing machine. Failure types were observed under a stereomicroscope. RESULTS: Surface roughness values were significantly higher in all test materials in Group D than in the other groups (p < 0.001). For conventional resin, the SBS values were higher in Group C than in Groups A, D, and E (p < 0.001). For CAD/CAM material, Groups B and C had significantly greater SBS increases compared with Group E (p < 0.001). For 3D material, Group D showed higher SBS than all groups except Group C (p < 0.001). CONCLUSIONS: For SBS, sandblasting was most effective in the conventional group, whereas laser treatment was the most effective in the additive-manufactured group. For the subtractive group, surface treatments other than plasma exhibited similar SBS. CLINICAL SIGNIFICANCE: In repairing fractured prostheses, any degree of roughening suitable for the material content may provide an SBS benefit.

The effect of various surface treatments on the repair bond strength of denture bases produced by digital and conventional methods.

There is limited information on the repairability of prostheses produced with digital technology. This study aims to evaluate various surface treatments on flexural bond strength of repaired dentured base resins produced by digital and conventional methods. A total of 360 samples were prepared from one heat-polymerized, one CAD/CAM milled and one 3D printed denture base materials. All of the test samples were subjected to thermocycling (5-55 °C, 5000 cycles) before and after repair with auto-polymerizing acrylic resin. The test samples were divided into five subgroups according to the surface treatment: grinding with silicon carbide (SC), sandblasting with Al2O3 (SB), Er:YAG laser (L), plasma (P) and negative control (NC) group (no treatment). In addition, the positive control (PC) group consisted of intact samples for the flexural strength test. Surface roughness measurements were performed with a profilometer. After repairing the test samples, a universal test device determined the flexural strength values. Both the surface topography and the fractured surfaces of samples were examined by SEM analysis. The elemental composition of the tested samples was analyzed by EDS. Kruskal-Wallis and Mann-Whitney U tests were performed for statistical analysis of data. SB and L surface treatments statistically significantly increased the surface roughness values of all three materials compared to NC subgroups (p < 0.001). The flexural strength values of the PC groups in all three test materials were significantly higher than those of the other groups (p < 0.001). The repair flexural strength values were statistically different between the SC-SB, L-SB, and NC-SB subgroups for the CAD/CAM groups, and the L-SC and L-NC subgroups for the 3D groups (p < 0.001). The surface treatments applied to the CAD/CAM and heat-polymerized groups did not result in a statistically significant difference in the repair flexural strength values compared to the NC groups (p > 0.05). Laser surface treatment has been the most powerful repair method for 3D printing technique. Surface treatments led to similar repair flexural strengths to untreated groups for CAD/CAM milled and heat-polymerized test samples.

Cold plasma application to fresh green leafy vegetables: Impact on microbiology and product quality.

Fresh green leafy vegetables (FGLVs) are consumed either garden-fresh or by going through very few simple processing steps. For this reason, foodborne diseases that come with the consumption of fresh products in many countries have prioritized the development of new and reliable technologies to reduce food-related epidemics. Cold plasma (CP) is considered one of the sustainable and green processing approaches that inactivate target microorganisms without causing a significant temperature increase during processing. This review presents an overview of recent developments regarding the commercialization potential of CP-treated FGLVs, focusing on specific areas such as microbial inactivation and the influence of CP on product quality. The effect of CP differs according to the power of the plasma, frequency, gas flow rate, application time, ionizing gases composition, the distance between the electrodes and pressure, as well as the characteristics of the product. As well as microbial decontamination, CP offers significant potential for increasing the shelf life of perishable and short-shelf-life products. In addition, organizations actively involved in CP research and development and patent applications (2016-2022) have also been analyzed.

Effect of nonthermal argon plasma treatment on the surface properties and phase transformation of zirconia.

PURPOSE: This study aims to evaluate the effect of applying different parameters of nonthermal argon plasma (NTAP) on the surface roughness and phase transformation of yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) ceramics. METHODS: A total of 60 zirconia samples were prepared and randomly divided into six groups according to their surface treatments (n = 10). Group 1: control group; Group 2: argon plasma with a flow rate of 5 lt/min for 4 min; Group 3: 8 lt/min for 4 min; Group 4: 8 lt/min for 2 min; Group 5: 5 l/min for 2 min; Group 6: air abrasion with Al2O3 particle. The surface roughness was measured with a profilometer, and surface topography was observed using scanning electron microscopy (SEM). X-ray diffraction (XRD) analysis was performed to investigate the phase transformation. RESULTS: The air abrasion group showed the highest surface roughness. The lowest relative monoclinic phase amount (Xm) was observed in the control group (0.4%), and the highest Xm value was observed in group 6 (7.8%). CONCLUSION: While the air abrasion group showed the highest average surface roughness, it also caused the highest phase transformation. With a flow rate of 8 lt/min for 2 min NTAP treatment increased the surface roughness without causing significant phase transformation.

The effect of nonthermal argon plasma surface treatment on the fracture resistance of monolithic zirconia restorations containing tetragonal and cubic grains.

PURPOSE: The aim of this study was to investigate the effect of nonthermal argon plasma (NP) surface treatment on the fracture resistance of monolithic zirconia restorations with different microstructures. METHODS: Twenty restorations were prepared from each of two tetragonal and two cubic zirconia materials (80 restorations in total). The restorations were then divided into two subgroups (n = 10) for each material according to the surface treatment applied: air abrasion or NP. The surface topography of the treated groups was examined using a scanning electron microscope. All restorations were fixed to metal dies with resin cement, subjected to thermal cycling, and then underwent fracture resistance testing with a universal testing device. Two-way ANOVA and Bonferroni tests were used for statistical analysis of the data (α = 0.05). RESULTS: The type of surface treatment and the type of zirconia material were shown to significantly affect the fracture resistance of the restorations. The air-abraded groups showed significantly higher fracture resistance (N) than the NP groups (P < 0.001). CONCLUSION: The results of this study suggest that air abrasion surface treatment has a more favorable effect on the fracture resistance of tetragonal and cubic zirconia restorations than NP surface treatment.

Cold plasma technology: bactericidal effects on Geobacillus stearothermophilus and Bacillus cereus microorganisms.

INTRODUCTION: Cold plasma, also known as Low Temperature Atmospheric Pressure Plasma (LTAPP) is a novel technology consisting of neutral and charged particles, including free radicals, which can be used to destroy or inactivate microorganisms. Research has been conducted regarding the effect of cold plasma on gram-positive bacteria; however, there is limited research regarding its ability to inactivate the spore-formers Geobacillus stearothermophilus and Bacillus cereus. PURPOSE: The purpose of this study was to determine if cold plasma inactivates G. stearothermophilus and B. cereus vegetative cells and spores. METHODS: Nine hundred eighty-one samples were included in this study (762 experimental and 219 controls). Experimental samples were exposed indirectly or directly to cold plasma, before plating and incubating for 16 hours. Control samples were not exposed to cold plasma. The percentage-kill and cell number reductions were calculated from Colony Forming Units (CFU). Data were statistically analyzed at the .05 level using one-way ANOVA, Kruskal Wallis and Tukey's tests. RESULTS: There was a statistically significant difference in the inactivation of G. stearothermophilus vegetative cells receiving indirect and direct exposure (p=0.0001 and p=0.0013, respectively), as well as for B. cereus vegetative cells and spores (p=0.0001 for direct and indirect). There was no statistically significant difference in the inactivation of G. stearothermophilus spores receiving indirect exposure (p=0.7208) or direct exposure (p=0.0835). CONCLUSION: Results demonstrate that cold plasma exposure effectively kills G. stearothermophilus vegetative cells and B. cereus vegetative cells and spores; however, G. stearothermophilus spores were not significantly inactivated.