Penetration of sodium hypochlorite into root canal dentine: effect of surfactants, gel form and passive ultrasonic irrigation.

AIM: To assess the penetration of sodium hypochlorite (NaOCl) gel or NaOCl solutions with surfactants, and the effect of passive ultrasonic irrigation (PUI) on penetration into dentinal tubules. METHODOLOGY: Bovine incisor root canals were instrumented, the roots sectioned and the dentine blocks obtained were stained with crystal violet. Dentine blocks (n = 10 per group) were exposed to 3% NaOCl gel or 3% NaOCl solution for 10 and 20 min. Other dentine blocks (n = 10 per group) were exposed to Chlor-Extra (6% NaOCl + surfactant), 6% NaOCl, 2.5% NaOCl with 0.2% cetrimide and 2.5% NaOCl for 10 and 20 min. The penetration depth of irrigants into dentinal tubules was measured in micrometres by viewing the bleached crystal violet under a stereomicroscope. Additionally, bovine incisor root canals, instrumented and stained with crystal violet, were distributed into two groups (n = 10) and irrigated with 2.5% NaOCl with PUI or conventional syringe irrigation (CSI). The penetration depth of irrigants into dentinal tubules was assessed 3 and 7 mm from the apex. Statistical analysis was performed by ANOVA and Tukey tests (α = 0.05). RESULTS: There was significantly greater penetration of 3% NaOCl solution into dentinal tubules compared with the gel form (P < 0.05). There was no difference (P > 0.05) between 6% NaOCl and Chlor-Extra, and between 2.5% NaOCl and 2.5% NaOCl + cetrimide. PUI significantly increased the penetration depth of NaOCl into dentinal tubules when compared with CSI (P < 0.05). CONCLUSIONS: In extracted bovine incisors, NaOCl gel penetrated less into dentinal tubules than NaOCl solution. The addition of surfactants did not increase the penetration depth. The use of PUI significantly increased NaOCl penetration into dentinal tubules.

Effectiveness of several solutions to prevent the formation of precipitate due to the interaction between sodium hypochlorite and chlorhexidine and its effect on bond strength of an epoxy-based sealer.

AIM: To evaluate the effectiveness of isopropyl alcohol, saline or distilled water to prevent the precipitate formed between sodium hypochlorite (NaOCl) and chlorhexidine (CHX) and its effect on the bond strength of an epoxy-based sealer in radicular dentine. METHODOLOGY: The root canals of 50 extracted human canines (n = 10) were instrumented. In G1, root canals were irrigated with 17% EDTA and 2.5% NaOCl; G2, as G1, except that 2% CHX was used as the final irrigant. In the other groups, intermediate flushes with isopropyl alcohol (G3), saline (G4) or distilled water (G5) were used between NaOCl and CHX. The specimens were submitted to SEM analysis to evaluate the presence of debris and smear layer, in the apical and cervical segments. In sequence, fifty extracted human canines were distributed into five groups (n = 10), similar to the SEM study. After root filling, the roots were sectioned transversally to obtain dentine slices, in the cervical, middle and apical thirds. The root filling was submitted to a push-out bond strength test using an electromechanical testing machine. Statistical analysis was performed using Kruskal-Wallis and Dunn's tests (α = 5%). RESULTS: All groups had similar amounts of residue precipitated on the canal walls (P > 0.05). The push-out bond strength values were similar for all groups, independently of the root third evaluated (P > 0.05). CONCLUSIONS: Isopropyl alcohol, saline and distilled water failed to prevent the precipitation of residues on canal walls following the use of NaOCl and CHX. The residues did not interfere with the push-out bond strength of the root filling.