RESUMO
PURPOSE: Low-cost resin 3D printers have been used to produce affordable interim single crowns in public and private dental practices. The purpose of this study was to assess the impact of different computer-aided design (CAD) software programs on 3D trueness, microscopic marginal and internal gaps, time to design, and interproximal contacts of low-cost 3D-printed single crowns. MATERIALS AND METHODS: This in vitro study was performed on a total of 90 standardized resin-prepared teeth adapted to a dental manikin. For comparison among CAD software programs, 45 tooth preparations received 3D-printed crowns designed with one of three CAD software programs by an experienced technician and identified as groups TRIOS (n = 15), EXOCAD (n = 15), and ZZ (Zirkonzahn; n = 15). To assess interoperator reproducibility, 15 additional crowns were designed by a dental clinician (group ZZ-DENT) and 15 by a dental prosthetic technician (group ZZ-PROS), both with basic 1-week CAD/CAM training. Finally, as a control group, 15 crowns were milled using a high-end five-axis milling device (group ZZ-CONTROL). Statistically significant differences for 3D trueness, microscopic gaps, time to design, and interproximal contacts among groups were assessed with the Kruskal-Wallis test. RESULTS: No statistically significant differences in 3D trueness or marginal or internal gaps were found, either among different software programs or CAD operators (P > .05). However, Group TRIOS took significantly longer to design than EXOCAD and ZZ groups (P = .001). Less-experienced operators were significantly outperformed in time and interproximal contacts (P = .001) by the CAD technician using the same software program. Finally, control milled crowns (ZZ-CONTROL) significantly outperformed the respective 3D-printed copies (ZZ) in all assessed variables (P < .001). CONCLUSIONS: Different CAD software programs may affect the time required to design, but they do not significantly affect clinical outcomes of low-cost 3D-printed resin crowns if designed by an experienced CAD technician.
Assuntos
Adaptação Marginal Dentária , Planejamento de Prótese Dentária , Reprodutibilidade dos Testes , Coroas , Desenho Assistido por Computador , Software , Impressão Tridimensional , Porcelana DentáriaRESUMO
PURPOSE: To compare the accuracy of dentists with different levels of expertise in computer-aided design (CAD) and prosthodontics to digitally design single crowns. MATERIAL AND METHODS: This in vitro study was conducted on 12 prepared teeth in 2 reference dental study models. The models were scanned using an intraoral scanner. Four dentists with different levels of clinical and CAD expertise (PROS: clinicians experienced in prosthodontics [n = 2]; CAD: experts in CAD [n = 2]) performed digital waxing on all prepared teeth using the same CAD software program. The resulting digital crown designs were compared to STL files of the original teeth to assess 3D deviations. The total cervical, distal, mesial, and occlusal surface deviations of the crowns from both groups were compared using paired t and Wilcoxon signed-rank tests (α = .05). RESULTS: The total median 3D deviation was 0.10 mm (range: 0.03 to 0.61 mm) for the PROS group and 0.14 mm (range: 0.07 to 0.58 mm) for the CAD group. The PROS group presented significantly smaller total 3D (P = .021) and cervical margin (P = .001) deviations. There were no significant differences between groups on the distal, mesial, or occlusal surfaces (P > .05). The CAD group performed digital waxing significantly faster (P = .001). CONCLUSION: Within the limitations of this study, the present findings suggest that clinical experience has a higher impact on the accuracy of digital wax patterns of single crowns than CAD experience.
Assuntos
Cerâmica , Planejamento de Prótese Dentária , Planejamento de Prótese Dentária/métodos , Coroas , Desenho Assistido por Computador , SoftwareRESUMO
AIM: There is controversy in the literature regarding clinical outcomes of CAD/CAM laminate veneers. The aim of the present study was to assess the impact of different levels of CAD expertise and different software programs on the reliability and reproducibility of digital wax patterns of laminate veneers and single crowns. MATERIALS AND METHODS: The present preliminary in vitro study was performed on 10 prepared maxillary central incisors available in dental study models. Of the total, five central incisors were prepared with shoulder finish lines for single crowns, whereas the other five underwent incisal shoulder preparation for laminate veneers. The models were scanned using an intraoral scanner. Four dentists (group DENT) and four CAD dental technicians (group CAD) with expertise in different software programs performed digital diagnostic waxing on all prepared teeth. The resulting digital wax patterns (n = 80) were exported as standard tessellation language (STL) files and superimposed on gold standard digital wax patterns (obtained from the original shape of the teeth before preparations). 3D mesh deviations at the cervical margins as well as distal, mesial, and incisal/palatal surfaces between each STL and the gold standard digital wax patterns were calculated in millimeters using a CAD software program. The mean time required by each operator to perform digital waxing was also recorded. Paired comparisons between groups DENT and CAD as well as between nondental and dental software programs were performed for the crowns and laminate veneers using the Wilcoxon signed-rank and paired t tests (α = 0.05). RESULTS: For group DENT, median deviations for single crowns were 0.15 mm (range: 0.08 to 1.05 mm) and for laminate veneers they were 0.15 mm (range: 0.08 to 0.76 mm). For group CAD, median deviations for single crowns were 0.16 mm (range: 0.09 to 0.73 mm) and for laminate veneers they were 0.10 mm (range: 0.06 to 0.53 mm). The Wilcoxon signed-rank test revealed a statistically significant difference between groups DENT and CAD (P = 0.041) and between the software programs (P = 0.029) for laminate veneers, but not for single crowns (P > 0.05). Furthermore, mean times required for group CAD and for dental software programs were significantly shorter than those for group DENT (P = 0.001) and for nondental software programs (P = 0.001), respectively. CONCLUSION: Within the limitations of the present study, the findings suggest that CAD expertise and the software program significantly affect digital wax patterns for laminate veneers, but not for single crowns. (Int J Comput Dent 2022;25(4):361-0; doi: 10.3290/j.ijcd.b3555819).
Assuntos
Planejamento de Prótese Dentária , Facetas Dentárias , Humanos , Reprodutibilidade dos Testes , Planejamento de Prótese Dentária/métodos , Porcelana Dentária , Desenho Assistido por Computador , CoroasRESUMO
STATEMENT OF PROBLEM: The digital waxing of single crowns can be affected by the quality of intraoral scans and use of computer-aided design (CAD) software programs. However, clinical outcomes of the resulting crowns are also affected by computer-aided manufacturing (CAM) methodologies. Studies on the effect of different levels of expertise on digital waxing are lacking. PURPOSE: The purpose of this in vitro study was to assess the impact of different levels of expertise on the reliability and reproducibility of margin outlining during digital waxing. MATERIAL AND METHODS: Thirty analogs of implant stock abutments (Ø4.8×4 mm) were embedded into resin blocks. To simulate different clinical situations, abutments were divided into 3 groups: 10 abutments (group GOS) received artificial gingiva and were scanned with an open system intraoral scanner, while 10 abutments with (group GIS) and 10 abutments without artificial gingiva (group IS) were scanned with an intraoral scanner within an integrated CAD-CAM system. All resulting standard tessellation language (STL) files were used by 2 different observers (an experienced CAD professional and a clinician with basic CAD knowledge) to digitally design a left mandibular central incisor in the same software program. All resulting digital crown designs were exported to STL files to assess crown margin accuracy at the coupling interface by superimposition with the control STL file of the scan body designed for the same abutment by the manufacturer. For this purpose, a CAD software program was used to automatically calculate median, minimum, and maximum deviations of margins in millimeters. Statistically significant pairwise differences among groups and between observers were assessed with the Wilcoxon signed-rank test (α=.05). RESULTS: For the CAD professional, median deviations between designed crown STL files and the control STL of the scan body were 0.08 mm (range: 0.04 to 0.15) for group GOS; 0.10 mm (range: 0.06 to 0.18) for group GIS; and 0.05 mm (range: 0.03 to 0.08) for group IS. For the clinician, median deviations were 0.08 mm (range: 0.04 to 0.12) for group GOS; 0.11 mm (range: 0.07 to 0.17) for group GIS; and 0.05 mm (range: 0.04 to 0.11) for group IS. There were no significant differences between observers (P>.05). However, statistically significant differences were found between group IS and the other 2 groups (P=.001) but not between groups GOS and GIS (P>.05). CONCLUSIONS: The present findings suggest that a digital wax pattern made with a dental CAD software program is not affected by varying levels of expertise but might be affected by subgingival margins.
Assuntos
Desenho Assistido por Computador , Coroas , Planejamento de Prótese Dentária , Gengiva , Reprodutibilidade dos TestesRESUMO
The aim of this report is to present a digital workflow technique to design a customized abutment for provisionalization of an immediate-placed implant based on the natural emergence profile of the tooth to be extracted. The workflow involves the combination of intraoral and CBCT scans, from which three-dimensional (3D) reconstructions of soft tissue and alveolar bone, as well as of the tooth to be extracted are obtained and exported as STL files. The files are imported to a computer-aided design (CAD) software, in which a virtual wax-up and custom abutment design are performed considering the natural emergence profile of the patient's tooth prior to extraction. Since the customized abutment is digitally designed, it can also be used as a scan body, to be directly scanned intraorally after soft tissue healing around an interim implant restoration. The custom abutment digitally designed can be then produced by milling zirconia with an optimally chosen color, in accordance with the aesthetic needs of the patient.
RESUMO
OBJECTIVES: To evaluate the effect of atmospheric pressure plasma (PLA), sandblasting (SAN), silanization (SIL) and hydrophobic bonding resin (HBR) on the micro-shear bond strength (MSBS) of fresh nanofilled (NF) or microhybrid (MH) composites to water-aged nanofilled composite. MATERIALS AND METHODS: NF plates were fabricated and stored in distilled water for 4 months. The aged plates were assigned to the groups (n = 6): 1- untreated; 2- SAN + SIL + HBR; 3- HBR; 4- PLA + HBR; 5- SAN + HBR; 6- SAN + PLA + HBR; and 7- PLA. Two fresh composite cylinders were constructed on each plate with NF or MH composites and tested after 24 h or 1 year of water-storage, using the MSBS testing. Data were analyzed by three-way ANOVA and Tukey test (α = 0.05). RESULTS: NF yielded better outcomes than MH at 24 h, which was not observed at 1 year. HBR showed the highest MSBS results, while untreated and PLA groups yielded the lowest one. MSBS reduced for all groups after 1 year. CONCLUSIONS: Only HBR can obtain good MSBS results, while PLA alone was not beneficial. After 1 year, a reduction in repair MSBS was observed and the type of composite did not influence the results. CLINICAL RELEVANCE: The repair technique can be simplified with the use of only an adhesive and macromechanical retentions in the old composite, regardless the type of fresh composite.
Assuntos
Colagem Dentária , Gases em Plasma , Argônio , Resinas Compostas , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , Propriedades de SuperfícieRESUMO
PURPOSE: The aim of this study was to evaluate the influence of indirect restorative material type and thickness on the transmission of different wavelengths from a broad-banded dental curing light. METHODS: Four dental indirect restorative materials for computer-aided design and computer-aided manufacturing (CAD/CAM) were evaluated: [RC] resin/ceramic hybrid material (Lava Ultimate), [FC] feldspathic ceramic (VitaBlocs), and two zirconia-based ceramics ([ZK] Katana; and [ZL] Lava). Total loss of irradiance (TL) was measured for blue (WB, 425-490nm) and violet (WV, 350-425nm) wavelengths. Specimens of 15×15mm with varying thicknesses (0.5, 1.0, 1.5, and 2.0mm) were fabricated (n=5). A plasma-arc dental light-curing unit was used (Arc Light-II). To assess TL as a function of wavelength, a software (Spectra Suite v5.1) connected to a spectroradiometer (USB2000) and an integrating sphere (CTSM-LSM-60-SF) was used. Data was subjected to statistical analysis (two-way ANOVA and post-hoc Tukey test, α=0.05). RESULTS: A 0.5mm interposition resulted in TL from 50.5 to 67.2%, depending on material. Increased thickness resulted in higher TL for all materials. FC showed less TL compared to ZK. In general, WV showed higher TL than did WB, and WV/WB proportion decreased with increasing thickness. CONCLUSIONS: Indirect materials significantly reduced TL, and this effect is greater with increasing thickness. WV showed lower penetration compared to WB.
Assuntos
Materiais Dentários , Cura Luminosa de Adesivos Dentários , Luz , Teste de Materiais , Cerâmica , Resinas Compostas , Desenho Assistido por Computador , Polimerização , Cimentos de Resina , ZircônioRESUMO
To evaluate the bond strength of composite resin containing or not biomaterial (S-PRG) to sound/eroded dentine. Methods: Occlusal dentin of 30 human molars (n=15) had half of its surface kept uneroded, while on the other half an erosive lesion was produced by cycling in citric acid (pH 2.3) and supersaturated solution (pH 7.0). On both eroded (ED) and non-eroded (SD) substrates, two restorative systems (containing or not S-PRG) were tested. Composite resin cylinders were built and, after storage in water (24h), were submitted to bond strength test. The analysis of the fracture pattern was performed under an optical microscope (40x). The obtained values of bond strength (MPa) were submitted to ANOVA (two factors) and Tukey multiple comparisons tests (p<0.05). Results: According to the results, there was difference between substrates (<0.001) and restorative materials (p=0.002) evaluated. For the microtensile bond strength, the values obtained were: SDNB (47.6±12.2 MPa), SDWB (34.1±15.8 MPa), EDNB (31.1±8.3 MPa) and EDWB (15.5±13.6 MPa), revealing a statistically significant difference in the evaluated substrates and restorative materials. Conclusion: Bond strength of eroded substrate is inferior to the sound substrate and the restorative system containing S-PRG biomaterial influences negatively the results of bonding to sound/eroded dentin (AU)
Assuntos
Humanos , Masculino , Feminino , Resinas Compostas , Dentina , Erosão DentáriaRESUMO
PURPOSE: To investigate the bonding efficacy of a multimode adhesive to plasma-treated and -untreated (control) dentin using a mini-interfacial fracture toughness (mini-iFT) test. MATERIALS AND METHODS: Twenty human molars were used in a split-tooth design (n = 10). The adhesive Scotchbond Universal (SBU; 3M ESPE) was applied in etch-and-rinse (E&R) and self-etch (SE) modes. Mid-coronal dentin was exposed and covered with a standardized smear layer ground to 320 grit. One half of each dentin surface received 15 s of non-thermal atmospheric plasma (NTAP), while the other half was covered with a metallic barrier and kept untreated. Following the E&R mode, dentin was plasma treated immediately after phosphoric acid etching. SBU and a resin-based composite were applied to dentin following the manufacturer's instructions. Six mini-iFT specimens were prepared per tooth (1.5 x 2.0 x 16 to 18 mm), and a single notch was prepared at the adhesive-dentin interface using a 150-µm diamond blade under water cooling. Half of the mini-iFT specimens were immediately loaded until failure in a 4-point bending test, while the other half were first stored in distilled water for 6 months. After testing, the exact dimensions of the notch were measured with a measuring optical microscope, from which ΚIc was determined. RESULTS: Three-way ANOVA revealed higher mini-iFT for SBU applied in E&R than SE mode for both storage times, irrespective of NTAP treatment. CONCLUSION: Overall, mini-iFT did not decrease for any of the experimental groups upon 6-month aging, while plasma treatment did not show a direct beneficial effect on mini-iFT of SBU applied in either E&R or SE mode.
Assuntos
Colagem Dentária , Adesivos Dentinários , Resinas Compostas , Cimentos Dentários , Dentina , Humanos , Teste de Materiais , Cimentos de Resina , Propriedades de Superfície , Resistência à TraçãoRESUMO
Resumo Objetivo: Este trabalho avaliou o efeito de quatro agentes clareadores na permeabilidade dental. Material e Métodos: Dentes bovinos foram divididos em quatro grupos (n = 10). A permeabilidade inicial dos dentes foi determinada previamente ao clareamento, utilizando equipamento de permeabilidade. Em seguida, foram aplicados os géis clareadores e a permeabilidade novamente mensurada. Os resultados foram expressos em porcentagem de aumento da permeabilidade e os dados submetidos à análise estatística (ANOVA e teste Tukey). Resultados: O Whiteness HP Maxx resultou em maior aumento de permeabilidade (145,7±76,3), quando comparado com Whiteness HP Blue (57,5±36,1) e Pola Office Plus (72,7±19,5). Esses produtos não apresentaram diferença estatística com relação ao Opalescence Boost PF (101,4±46,3). Conclusão: Todos os agentes clareadores testados aumentaram a permeabilidade. A intensidade desse aumento foi dependente do produto utilizado.
Objective: This study evaluated the effect of four bleaching agents on the dental permeability. Material and Methods: Bovine teeth were divided into four groups (n=10), and the initial dental permeability was measured before the bleaching treatments, using a dental hydraulic permeability device. Afterwards, teeth were bleached with whitening products, and the final permeability was recorded. The results were expressed in percentage of increasing permeability (%) and data were submitted to ANOVA and Tukey's test. Results: Whiteness HP Maxx produced higher dental permeability (145.7±76.3) than Whiteness HP Blue (57.5±36.1) and Pola Office Plus (72.7±19.5), which did not differ from Opalescence Boost PF (101.4±46.3). Conclusion: All bleaching agents increased the dental permeability. The increasing intensity was product-dependent.
RESUMO
PURPOSE: To investigate the influence of atmospheric pressure plasma (APP) treatment on the microtensile dentin bond strength of two etch-and-rinse adhesive systems, after one week and one year of water storage, and additionally to observe the micromorphology of resin/dentin interfaces under scanning electronic microscopy (SEM). MATERIALS AND METHODS: The occlusal enamel was removed from third human molars to expose a flat dentin surface. The teeth were then randomly divided into six groups (n = 7), according to two adhesives (Optibond FL and XP-Bond) and three APP treatments (untreated dentin [control], APP application before or after acid etching). After performing the composite resin buildup on bonded dentin, the teeth were sectioned perpendicularly to the bonded interface to obtain beam-shaped specimens (cross-sectional area of ~0.9 mm2). The specimens were tested in tension until failure after one week and one year of water storage (1.0 mm/min rate). Bond strength data were analyzed by three-way ANOVA and Tukey's post-hoc test (α = 0.05%). Bonded beam specimens from each tooth were also prepared for interfacial SEM investigation. RESULTS: At one week, APP treatment applied after acid etching increased the dentin bond strength for XP Bond, while no effect was observed for Optibond FL. After one year, the bond strength of XP Bond decreased in groups where APP was applied after etching. The evaluation time did not influence the bond strength for Optibond FL. CONCLUSION: One-year evaluation did not show any sign of degradation of interfacial structures in any group. Application of APP to etched dentin combined with a two-step etch-and-rinse adhesive significantly increased bond strength at one week, but the effect was not stable after one year and was adhesive dependent.
Assuntos
Condicionamento Ácido do Dente/métodos , Colagem Dentária , Dentina/ultraestrutura , Gases em Plasma/química , Cimentos de Resina/química , Argônio/química , Resinas Compostas/química , Materiais Dentários/química , Adesivos Dentinários/química , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Distribuição Aleatória , Estresse Mecânico , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Água/químicaRESUMO
PURPOSE: This study evaluated (1) the dentin bond strength of fluoridated restorative systems following aging and (2) the enamel/dentin microhardness around restorations after a pH-cycling regimen. MATERIALS AND METHODS: Sixty-four human third molars and four restorative systems were used. A resin-modified glass ionomer (GC Fuji II LC) was used as a fluoride-containing material in the positive control group, while Adper Easy Bond adhesive and Filtek Z350 XT composite resin, which are not fluoridated, were used together in the negative control group. Beautifil II composite resin and FL-Bond II adhesive, both fluoride-containing materials, were compared to Bond Force and Estelite Sigma Quick restorative system, which only contain fluoride in the adhesive. For dentin bond strengths, specimens of each material were fabricated for two test groups (n=8): group 1: tested after 24 h; group 2: tested after 1 year of storage in artificial saliva. Both groups were tested using a microtensile method. For the cross-sectional microhardness test, standardized Class V cavities were prepared and filled with the different restorative systems. After experiencing repeated thermocycling and being subjected to pH-cycling, the teeth were sectioned. The microhardness was measured in enamel and dentin at 50 µm from the cavity wall and at six depths in relation to the surface subjected to pH cycling. RESULTS: None of the restorative systems showed decreased bond strength after storage for one year in artificial saliva. No significant differences in microhardness were observed among the restorative materials on enamel and dentin. CONCLUSION: All the restorative systems evaluated presented stable bond strength after one year of storage. The pH cycling caused a reduction in the superficial enamel microhardness close to the cavity wall. In dentin, the demineralization affected the superficial and sub-surface areas.
Assuntos
Cariostáticos/química , Colagem Dentária , Materiais Dentários/química , Restauração Dentária Permanente , Dentina/ultraestrutura , Fluoretos/química , Desmineralização do Dente/patologia , Bis-Fenol A-Glicidil Metacrilato/química , Cariostáticos/farmacologia , Resinas Compostas/química , Esmalte Dentário/efeitos dos fármacos , Dentina/efeitos dos fármacos , Adesivos Dentinários/química , Fluoretos/farmacologia , Cimentos de Ionômeros de Vidro/química , Dureza , Humanos , Concentração de Íons de Hidrogênio , Teste de Materiais , Cimentos de Resina/química , Resinas Sintéticas/química , Saliva Artificial/química , Estresse Mecânico , Resistência à Tração , Fatores de TempoRESUMO
This study evaluated the effects of indirect restorative materials, curing conditions and time on the degree of conversion (DC) of a dual-cured resin cement using infrared spectroscopy. The resin cement (RelyX Unicem 2, 3M ESPE) was applied to the diamond surface of a horizontal attenuated-total-reflectance unit and activated using one of following conditions: self-cure, direct light exposure, light exposure through indirect restorative materials (resin nano-ceramic: Lava Ultimate, 3M ESPE or feldspathic ceramic: Vita Blocks Mark II, Vita Zahnfabrik). Four thicknesses (0.5, 1.0, 1.5 or 2.0 mm) of each indirect material were analyzed, and the light-activation was performed using a blue LED light. Data (n=5) were analyzed by three-way ANOVA, Tukey's post hoc and Dunnett's tests (α=5%). No significant differences in DC were observed between indirect materials of similar thickness. All groups exhibited higher DC after 10 min than after 5 min. At both times points, the self-cure group exhibited significantly lower DC than all the light exposure groups. Only when the overlying indirect restoration had a thickness of 2 mm did DC decrease significantly. The presence of a thick, indirect restoration can decrease the DC of resin cement. DC after 10 min was higher than after 5 min. The self-cure mode yielded lower DC than the light-activating one.
Assuntos
Luz , Cimentos de Resina/química , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
This study evaluated the effects of indirect restorative materials, curing conditions and time on the degree of conversion (DC) of a dual-cured resin cement using infrared spectroscopy. The resin cement (RelyX Unicem 2, 3M ESPE) was applied to the diamond surface of a horizontal attenuated-total-reflectance unit and activated using one of following conditions: self-cure, direct light exposure, light exposure through indirect restorative materials (resin nano-ceramic: Lava Ultimate, 3M ESPE or feldspathic ceramic: Vita Blocks Mark II, Vita Zahnfabrik). Four thicknesses (0.5, 1.0, 1.5 or 2.0 mm) of each indirect material were analyzed, and the light-activation was performed using a blue LED light. Data (n=5) were analyzed by three-way ANOVA, Tukey's post hoc and Dunnett's tests (α=5%). No significant differences in DC were observed between indirect materials of similar thickness. All groups exhibited higher DC after 10 min than after 5 min. At both times points, the self-cure group exhibited significantly lower DC than all the light exposure groups. Only when the overlying indirect restoration had a thickness of 2 mm did DC decrease significantly. The presence of a thick, indirect restoration can decrease the DC of resin cement. DC after 10 min was higher than after 5 min. The self-cure mode yielded lower DC than the light-activating one.
.Este estudo avaliou os efeitos do tipo de material restaurador indireto, da condição de ativação e do tempo no grau de conversão de um cimento resinoso de dupla ativação, utilizando espectroscopia de luz infravermelha. O cemento resinoso (RelyX Unicem 2, 3M ESPE) foi aplicado à superfície do diamante da unidade de reflectância atenuada e ativado segundo as seguintes condições: ativação química, exposição direta da luz e aplicação da luz através de dois materiais protéticos: resina nano-cerâmica (Lava Ultimate, 3M ESPE) ou cerâmica feldspática (Vita Blocks Mark II, Vita Zahnfabrik). Quatro espessuras de cada um desses materiais (0,5; 1,0; 1,5 e 2,0 mm) foram analisadas e a ativação realizada com luz LED. Os dados (n=5) foram analisados pela ANOVA três fatores, testes de Tukey e Dunnett (5%). Nenhuma diferença do grau de conversão foi observada entre os materiais. Todos os grupos mostraram maior grau de conversão após 10 min que após 5 min. Em ambos os tempos, o grupo ativado quimicamente teve menor grau de conversão que todos os grupos fotoativados. O grau de conversão foi reduzido somente quando foi utilizada a peça protética de 2 mm. Espessas peças protéticas podem reduzir o grau de conversão do cemento resinoso. A grau de conversão após 10 min é maior que após 5 min da cimentação. A ativação química produz menor grau de conversão que a fotoativação.
.Assuntos
Luz , Cimentos de Resina/química , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
PURPOSE: To determine the influence of atmospheric pressure plasma (APP) treatment on the microtensile dentin bond strength of two self-etching adhesive systems after one year of water storage as well as observe the contact angle changes of dentin treated with plasma and the micromorphology of resin/dentin interfaces using SEM. MATERIALS AND METHODS: For contact angle measurements, 6 human molars were sectioned to remove the occlusal enamel surface, embedded in PMMA resin, and ground to expose a flat dentin surface. Teeth were divided into two groups: 1) argon APP treatment for 30 s, and 2) blown air (control). For the microtensile test, 28 human third molars were used and prepared similarly to contact angle measurements. Teeth were randomly divided into 4 groups (n = 7) according to two self-etching adhesives and APP treatment (with/without). After making the composite resin buildup, teeth were sectioned perpendicular to the bonded interface to obtain beam specimens. The specimens were tested after 24 h and one year of water storage until failure. Bond strength data were analyzed by three-way ANOVA and Tukey's post-hoc test (α = 0.05%). Three beam specimens per group that were not used in the bond strength test were prepared for interfacial SEM analysis. RESULTS: APP application decreased the contact angle, but increased the bond strength only for one adhesive tested. SEM evaluation found signs of degradation within interfacial structures following 1-year aging in water. APP increased the dentin surface energy, but the effects of APP and 1-year water storage on dentin bond strength were product dependent. CONCLUSION: APP increased the dentin surface energy. It also increased the bond strength for Scotchbond Universal, but storage for one year negated the positive effect of APP treatment.
Assuntos
Colagem Dentária , Adesivos Dentinários/química , Dentina/ultraestrutura , Gases em Plasma/química , Adesividade , Argônio/química , Resinas Compostas/química , Materiais Dentários/química , Análise do Estresse Dentário/instrumentação , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Distribuição Aleatória , Cimentos de Resina/química , Estresse Mecânico , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Água/química , MolhabilidadeRESUMO
OBJECTIVE: This study evaluated the effects of carbamide peroxide and hydrogen peroxide on the biaxial flexural strength and flexural modulus of bovine dentin. MATERIALS AND METHODS: Thirty coronal dentin disks (0.5 mm thick × 6.0 mm diameter) were prepared from bovine teeth. The disks were randomly divided into three groups (n=10): A control group (unbleached), a group bleached with 10% carbamide peroxide (8 h at 37°C), and a group bleached with 38% hydrogen peroxide (three 10 min applications at 37°C). The specimens were tested in a biaxial flexural apparatus held in a universal testing machine at 1.27 mm/min until failure occurred, and the biaxial mechanical properties were calculated. For each test parameter, the data were statistically analyzed by Fisher's PLSD test (predetermined α = 0.05). RESULTS: The group bleached with 38% hydrogen peroxide demonstrated significantly lower flexural strength than the unbleached control group. Hydrogen peroxide treatment resulted in a significantly lower flexural modulus compared with the control group and with carbamide peroxide bleaching. CONCLUSION: Exposure of dentin to hydrogen peroxide significantly reduced both the flexural strength and the flexural modulus compared with the no-treatment control, whereas exposure to carbamide peroxide did not significantly affect either parameter.
RESUMO
PURPOSE: To evaluate the effect of different in vitro aging methods on color change (CC) of an experimental dental resin-based composite using CIELAB (ΔEab ) and CIEDE2000 (ΔE00 ) color-difference formulas. MATERIALS AND METHODS: The CC was evaluated with a spectrophotometer (CM700d, Konica Minolta, Tokyo, Japan) according to the CIE chromatic space. Disk-shaped specimens (Φ = 5 × 1 mm thick) (N = 10) were submitted to different in vitro aging methods: 30 days of water aging (WA); 120 hours of ultraviolet light aging (UVA); or 300 hours of an accelerated artificial aging (AAA) method with cycles of 4 hours of UV-B light exposure and 4 hours of moisture condensation to induce CC. The temperature was standardized at 37°C for all aging methods. CC was evaluated with ΔEab and ΔE00 formulas. Differences in individual Lab coordinates were also calculated. Data for the individual color parameters were submitted to one-way analysis of variance and Tukey's test for multiple comparisons (α = 0.05). RESULTS: All in vitro aging methods tested induced CC, in the following order: WA: ΔEab = 0.83 (0.1); ΔE00 = 1.15 (0.1) < AAA: ΔEab = 5.64 (0.2); ΔE00 = 5.01 (0.1) < UVA: ΔEab = 6.74 (0.2); ΔE00 = 6.03 (0.4). No changes in L* or a* coordinates were ≥1; the methods with UV aging showed a yellowing effect due a large positive change in b*. CONCLUSIONS: All in vitro aging methods tested induced a CC, but to different extents. Changes in color followed similar trends, but with different absolute values when calculated with the CIELAB and the CIEDE2000 formulas. CLINICAL SIGNIFICANCE: Establishing the efficacy of different artificial aging methods and differences between color change using CIELAB and CIEDE2000 formulas are important to standardize color stability evaluations and facilitate the comparison of outcomes from different studies in the literature.
Assuntos
Cor , Resinas Compostas , Materiais Dentários , Técnicas In Vitro , Raios UltravioletaRESUMO
This paper presents the state of the art of self-etch adhesive systems. Four topics are shown in this review and included: the historic of this category of bonding agents, bonding mechanism, characteristics/properties and the formation of acid-base resistant zone at enamel/dentin-adhesive interfaces. Also, advantages regarding etch-and-rinse systems and classifications of self-etch adhesive systems according to the number of steps and acidity are addressed. Finally, issues like the potential durability and clinical importance are discussed. Self-etch adhesive systems are promising materials because they are easy to use, bond chemically to tooth structure and maintain the dentin hydroxyapatite, which is important for the durability of the bonding.
Assuntos
Colagem Dentária/métodos , Adesivos Dentinários/química , Condicionamento Ácido do Dente , Humanos , Teste de Materiais , Resistência ao Cisalhamento , Estresse Mecânico , Propriedades de Superfície , Temperatura , Fatores de TempoRESUMO
This paper presents the state of the art of self-etch adhesive systems. Four topics are shown in this review and included: the historic of this category of bonding agents, bonding mechanism, characteristics/properties and the formation of acid-base resistant zone at enamel/dentin-adhesive interfaces. Also, advantages regarding etch-and-rinse systems and classifications of self-etch adhesive systems according to the number of steps and acidity are addressed. Finally, issues like the potential durability and clinical importance are discussed. Self-etch adhesive systems are promising materials because they are easy to use, bond chemically to tooth structure and maintain the dentin hydroxyapatite, which is important for the durability of the bonding.
Este artigo apresenta o estado da arte de sistemas adesivos autocondicionantes. Quatro temas são apresentados nesta revisão: o histórico desta categoria de agentes de união, o mecanismo de adesão, as características/propriedades, e a formação da zona ácido-base resistente nas interfaces esmalte/dentina-adesivo. Além disso, as vantagens relativas aos sistemas de condicionamento total ( etch-and-rinse ) e as classificações dos sistemas adesivos autocondicionantes de acordo com o número de passos e acidez são abordados. Por fim, são discutidas questões como a durabilidade potencial e a importância clínica. Sistemas adesivos autocondicionantes são materiais promissores porque são fáceis de usar, unem-se quimicamente à estrutura do dente e preservam a hidroxiapatita dentinária, o que é importante para a durabilidade da ligação.
Assuntos
Humanos , Colagem Dentária/métodos , Adesivos Dentinários/química , Condicionamento Ácido do Dente , Teste de Materiais , Resistência ao Cisalhamento , Estresse Mecânico , Propriedades de Superfície , Temperatura , Fatores de TempoRESUMO
This study evaluated the effects of humidity conditions and evaluation times on the dentin bond strength (DBS) of two self-adhesive resin cements (RC). The RC used were: RelyX Unicem (3M ESPE) and Clearfil SA Cement (Kuraray Med.). One hundred and twenty coronal portions of bovine incisors (n = 10) were used. Buccal surfaces were abraded in order to expose a flat dentinal surface (180-grit SiC) and to standardize the smear layer formation (600-grit SiC). The humidity conditions tested were: dry (air-dried for 10 s), slightly moist (water application with disposable applicator on dried dentin and water excess removed with absorbent paper), and moist (same application without water removal). The RC were used according to the manufacturers' recommendations and were applied to prepolymerized resin discs (2 mm thick; Sinfony, 3M ESPE), which were subsequently bonded to the dentin surfaces. After 24 h, half of the teeth were prepared for the microtensile bond strength test, while the other half were stored in water for 6 months and tested in tension (0.5 mm/min) until failure. A 3-way analysis of variance and the Tukey test were performed (preset alpha of 0.05). No RC showed any reduction of DBS after 6 months, and no significant difference was observed between them. The moist dentin increased the bond strength of Clearfil SA Cement for both periods of time. Humidity conditions can change the DBS; however, the study's results were product-dependent.