Mesoporous Composite Bioactive Compound Delivery System for Wound-Healing Processes.

Currently, the treatment of wounds is still a challenge for healthcare professionals due to high complication incidences and social impacts, and the development of biocompatible and efficient medicines remains a goal. In this regard, mesoporous materials loaded with bioactive compounds from natural extracts have a high potential for wound treatment due to their nontoxicity, high loading capacity and slow drug release. MCM-41-type mesoporous material was synthesized by using sodium trisilicate as a silica source at room temperature and normal pressure. The synthesized mesoporous silica was characterized by using Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), N2 absorption-desorption (BET), Dynamic Light Scattering (DLS) and Fourier transform infrared spectroscopy (FT-IR), revealing a high surface area (BET, 1244 m2/g); pore diameter of approx. 2 nm; and a homogenous, ordered and hexagonal geometry (TEM images). Qualitative monitoring of the desorption degree of the Salvia officinalis (SO) extract, rich in ursolic acid and oleanolic acid, and Calendula officinalis (CO) extract, rich in polyphenols and flavones, was performed via the continuous recording of the UV-VIS spectra at predetermined intervals. The active ingredients in the new composite MCM-41/sage and marigold (MCM-41/SO&CO) were quantified by using HPLC-DAD and LC-MS-MS techniques. The evaluation of the biological composites' activity on the wound site was performed on two cell lines, HS27 and HaCaT, naturally involved in tissue-regeneration processes. The experimental results revealed the ability to stimulate collagen biosynthesis, the enzymatic activity of the main metalloproteinases (MMP-2 and MMP-9) involved in tissue remodeling processes and the migration rate in the wound site, thus providing insights into the re-epithelializing properties of mesoporous composites.

New Chalcogenide Glass-Ceramics Based on Ge-Zn-Se for IR Applications.

The consumer market requests infrared (IR) optical components, made of relatively abundant and environmentally friendly materials, to be integrated or attached to smartphones. For this purpose, three new chalcogenides samples, namely Ge23.3Zn30.0Se46.7 (d_GZSe-1), Ge26.7Zn20.0Se53.3 (d_GZSe-2) and Ba4.0Ge12.0Zn17.0Se59.0I8.0 (d_GZSe-3) were obtained by mechanical alloying and processed by spark plasma sintering into dense bulk disks. Obtaining a completely amorphous and homogeneous material proved to be difficult. d_GZSe-2 and d_GZSe-3 are glass-ceramics with the amount of the amorphous phase being 19.7 and 51.4 wt. %, while d_GZSe-1 is fully polycrystalline. Doping with barium and iodine preserves the amorphous phase formed by milling and lowers the sintering temperature from 350 °C to 200 °C. The main crystalline phase in all of the prepared samples is cubic ZnSe or cubic Zn0.5Ge0.25Se, while in d_GZSe-3 the amorphous phase contains GeSe4 clusters. The color of the first two sintered samples is black (the band gap values are 0.42 and 0.79 eV), while d_GZSe-3 is red (Eg is 1.37 eV) and is transparent in IR domain. These results are promising for future research in IR materials and thin films.

Microwave and Terahertz Properties of Spark-Plasma-Sintered Zr0.8Sn0.2TiO4 Ceramics.

Zr0.8Sn0.2TiO3 (ZST) powders synthesized by solid-state reaction were subject to processing by spark plasma sintering (SPS). A single-phase ceramic with a high relative density of 95.7% and 99.6% was obtained for sintering temperatures of 1150 °C and 1200 °C, respectively, and for a dwell time of 3 min. In order to reduce the oxygen vacancies, as-sintered discs were annealed in air at 1000 °C. The dielectric loss of the annealed samples, expressed by the Q × f product, measured in the microwave (MW) domain, varied between 35 THz and 50 THz. The intrinsic losses (Q × f ~ 60 THz) were derived by using terahertz time-domain spectroscopy (THz-TDS).

Measurements of Surface Impedance in MgB2 in DC Magnetic Fields: Insights in Flux-Flow Resistivity.

We present the multifrequency measurements of the surface resistance of spark-plasma-sintered MgB2 performed through a dielectric loaded resonator operating at 16.5 and 26.7 GHz. By normally applying magnetic fields ≤1.2 T to the sample surface, we drove it in the mixed state. By means of data-rooted analysis, we found that the sample vortex dynamics could be fully described within a single-component approach. Pinning phenomena were present and characterized by a depinning frequency smaller than the measurement ones. The multiband nature of the superconductor emerged in the flux-flow resistivity, whose field dependence could be interpreted well within theoretical models. By exploiting them, the upper critical field was extracted in the low-temperature range, which exhibited a consistent temperature trend with the values obtained at the onset of the resistive transition near Tc, and was well in line with literature data on other polycrystalline samples.

Sintered and 3D-Printed Bulks of MgB2-Based Materials with Antimicrobial Properties.

Pristine high-density bulk disks of MgB2 with added hexagonal BN (10 wt.%) were prepared using spark plasma sintering. The BN-added samples are machinable by chipping them into desired geometries. Complex shapes of different sizes can also be obtained by the 3D printing of polylactic acid filaments embedded with MgB2 powder particles (10 wt.%). Our present work aims to assess antimicrobial activity quantified as viable cells (CFU/mL) vs. time of sintered and 3D-printed materials. In vitro antimicrobial tests were performed against the bacterial strains Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, Staphylococcus aureus ATCC 25923, Enterococcus faecium DSM 13590, and Enterococcus faecalis ATCC 29212; and the yeast strain Candida parapsilosis ATCC 22019. The antimicrobial effects were found to depend on the tested samples and microbes, with E. faecium being the most resistant and E. coli the most susceptible.

Antimicrobial Activity of MgB2 Powders Produced via Reactive Liquid Infiltration Method.

We report for the first time on the antimicrobial activity of MgB2 powders produced via the Reactive Liquid Infiltration (RLI) process. Samples with MgB2 wt.% ranging from 2% to 99% were obtained and characterized, observing different levels of grain aggregation and of impurity phases. Their antimicrobial activity was tested against Staphylococcus aureus ATCC BAA 1026, Enterococcus faecalis ATCC 29212, Escherichia coli ATCC 25922, Pseudomonas aeruginosa ATCC 27853, and Candida albicans ATCC 10231. A general correlation is observed between the antibacterial activity and the MgB2 wt.%, but the sample microstructure also appears to be very important. RLI-MgB2 powders show better performances compared to commercial powders against microbial strains in the planktonic form, and their activity against biofilms is also very similar.

Epitaxial Non c-Axis Twin-Free Bi2Sr2CaCu2O8+δ Thin Films for Future THz Devices.

Thin films of (117) Bi2Sr2Ca2CuO8+δ (Bi-2212) were grown by Molecular Organic Chemical Vapor Deposition (MOCVD) on (110) SrTiO3 and (110) LaAlO3 substrates. Substrates were vicinal with off angles up to 20°. Films are 3D epitaxial and X-ray diffraction φ-ψ scans demonstrate that, while the films grown on a flat substrate are composed of twinned grains, the films on vicinal substrate are twin-free. A higher quality is obtained if growth is performed at two temperatures: Growth starts at 550⁻600 °C and continues at 700⁻750 °C. The twin-free film grown by the two-temperature method shows a zero-resistance critical temperature of 37 and 32 K when the measuring current is applied in-plane parallel and perpendicular to [001] direction of the substrate. Twin-free non c-axis thin films are promising for fabrication of novel planar THz devices.

Influence of In-Gap States on the Formation of Two-Dimensional Election Gas at ABO3/SrTiO3 Interfaces.

We explored in-gap states (IGSs) in perovskite oxide heterojunction films. We report that IGSs in these films play a crucial role in determining the formation and properties of interfacial two-dimensional electron gas (2DEG). We report that electron trapping by IGSs opposes charge transfer from the film to the interface. The IGS in films yielded insulating interfaces with polar discontinuity and explained low interface carrier density of conducting interfaces. An ion trapping model was proposed to explain the physics of the IGSs and some experimental findings, such as the unexpected formation of 2DEG at the initially insulating LaCrO3/SrTiO3 interface and the influence of substitution layers on 2DEG.

Finite element analysis on a medical implant.

Several studies have shown a tight connection between several ocular pathologies and an increased risk of hip fractures due to falling, especially among elderly patients. The total replacement of the hip joint is a major surgical intervention that aims to restore the function of the affected hip by various factors, such as arthritis, injures, and others. A corkscrew-like femoral stem was designed in order to preserve the bone stock and to prevent the occurrence of iatrogenic fractures during the hammering of the implant. In this paper, the finite element analysis for the proposed design was applied, considering different loads and three types of materials. A finite element analysis is a powerful tool to simulate, optimize, design, and select suitable materials for new medical implants. The results showed that the best scenario was for Ti6Al4V alloy, although Ti and 316L stainless steel had a reasonable high safety factor.

Computer assisted design and finite element analysis of contact lenses.

Contact lenses are an attractive alternative for vision corrections. Their improvement can be achieved by optimizing the geometry, use of new materials, and application of high precision processing technologies. The optimized design can be obtained by computer-aided design, considering the principles of geometrical optics. Inventor Professional and other similar advanced 3D CAD software allows complex approaches, selection of suitable materials with better mechanical/ optical properties. This is useful for the preparation of the virtual design for 3D printing or CNC fabrication. A finite element analysis is also of interest for testing the best design/ material choice. In this paper, the finite element analysis for a tri-curve contact lens was applied. The selected materials were PMMA and polycarbonate. The applied compressive loads were in the range from 10 to 100MPa. Our results showed that the best scenario was for the polycarbonate, but PMMA also had a high safety factor. The maximum compression load with a reasonable safety factor (of 7-9 depending on materials) was 12MPa.

Evaluation of pristine and Eu 2O3-added MgB 2 ceramics for medical applications: hardness, corrosion resistance, cytotoxicity and antibacterial activity.

Nano- or micropowders of Eu2O3 were added to MgB2, resulting in a composition of (MgB2)0.975(EuO1.5)0.025. Pristine and doped samples were prepared using spark plasma sintering and tested for (i) Vickers hardness, (ii) pH evolution in phosphate-buffered saline solution, (iii) corrosion resistance (Tafel polarization curves), (iv) cytotoxicity (in vitro tests), and (v) antibacterial activity. Eu2O3 addition influenced the investigated properties. Solutions of MgB2-based samples show a relatively high saturation pH of 8.5. This value is lower than that of solutions incubated with Mg or other Mg-based biodegradable alloys reported in the literature. MgB2-based samples have lower electro-corrosion rates than Mg. Their Vickers hardness is 6.8-10.2GPa, and these values are higher than those of biodegradable Mg-based alloys. MgB2 has low in vitro biocompatibility, good antibacterial activity against Escherichia coli, and mild activity against Staphylococcus aureus. Our results suggest that MgB2-based materials deserve attention in biomedical applications, such as implants or sterile medical instruments.

High hardness BaCb-(BxOy/BN) composites with 3D mesh-like fine grain-boundary structure by reactive spark plasma sintering.

Boron carbide B4C powders were subject to reactive spark plasma sintering (also known as field assisted sintering, pulsed current sintering or plasma assisted sintering) under nitrogen atmosphere. For an optimum hexagonal BN (h-BN) content estimated from X-ray diffraction measurements at approximately 0.4 wt%, the as-prepared BaCb-(BxOy/BN) ceramic shows values of Berkovich and Vickers hardness of 56.7 +/- 3.1 GPa and 39.3 +/- 7.6 GPa, respectively. These values are higher than for the vacuum SPS processed B4C pristine sample and the h-BN -mechanically-added samples. XRD and electronic microscopy data suggest that in the samples produced by reactive SPS in N2 atmosphere, and containing an estimated amount of 0.3-1.5% h-BN, the crystallite size of the boron carbide grains is decreasing with the increasing amount of N2, while for the newly formed lamellar h-BN the crystallite size is almost constant (approximately 30-50 nm). BN is located at the grain boundaries between the boron carbide grains and it is wrapped and intercalated by a thin layer of boron oxide. BxOy/BN forms a fine and continuous 3D mesh-like structure that is a possible reason for good mechanical properties.

'Beautiful' unconventional synthesis and processing technologies of superconductors and some other materials.

Superconducting materials have contributed significantly to the development of modern materials science and engineering. Specific technological solutions for their synthesis and processing helped in understanding the principles and approaches to the design, fabrication and application of many other materials. In this review, we explore the bidirectional relationship between the general and particular synthesis concepts. The analysis is mostly based on our studies where some unconventional technologies were applied to different superconductors and some other materials. These technologies include spray-frozen freeze-drying, fast pyrolysis, field-assisted sintering (or spark plasma sintering), nanoblasting, processing in high magnetic fields, methods of control of supersaturation and migration during film growth, and mechanical treatments of composite wires. The analysis provides future research directions and some key elements to define the concept of 'beautiful' technology in materials science. It also reconfirms the key position and importance of superconductors in the development of new materials and unconventional synthesis approaches.

Nanoblast synthesis and consolidation of (La0.8Sr0.2)(Ga0.9Mg0.1)O(3-delta) under Spark plasma sintering conditions.

Four-cation nanograined strontium and magnesium doped lanthanum gallate (La0.8Sr0.2) (Ga0.9Mg0.1)O(3-delta) (LSGM) and its composite with 2 wt% of ceria (LSGM-Ce) were prepared. Morphologically homogeneous nanoreactors, i.e., complex intermediate metastable aggregates of desired composition were assembled by spray atomization technique, and subsequently loaded with nanoparticles of highly energetic C3H6N6O6. Rapid nanoblast calcination technique was applied and the final composition was synthesized within the preliminary localized volumes of each single nanoreactor on the first step of spark plasma treatment. Subsequent SPS consolidations of nanostructured extremely active LSGM and LSGM-Ce powders were achieved by rapid treatment under pressures of 90-110 MPa. This technique provided the heredity of the final structure of nanosize multimetal oxide, allowed the prevention of the uncontrolled agglomeration during multicomponent aggregates assembling, subsequent nanoblast calcination, and final ultra-rapid low-temperature SPS consolidation of nanostructured ceramics. LaSrGaMgCeO(3-delta) nanocrystalline powder consisting of approximately 11 nm crystallites was consolidated to LSGM-Ce nanoceramic with average grain size of approximately 14 nm by low-temperature SPS at 1250 degrees C. Our preliminary results indicate that nanostructured samples of (La0.8Sr0.2)(Ga0.9Mg0.1)O(3-delta) with 2 wt% of ceria composed of approximataley 14 nm grains can exhibit giant magnetoresistive effect in contrast to the usual paramagnetic properties measured on the samples with larger grain size.