Prodelphinidins enhance dentin matrix properties and promote adhesion to methacrylate resin.

OBJECTIVE: Investigate the bioactivity and stability of Rhodiola rosea (RR) fractions as a natural source of prodelphinidin gallate (PDg) on dentin collagen via analysis of the viscoelastic and resin-dentin adhesive properties of the dentin matrix. METHODS: The biomimicry and stability of RR subfractions (F1, F2, F3 and F4) with collagen were determined by dynamic mechanical analysis (DMA). DMA used a strain sweep method to assess the dentin matrix viscoelastic properties [storage (E'), loss (E"), and complex (E*) moduli and tan δ] after treatment, 7-, 30- and 90-days of storage in simulated body fluids (SBF). Resin-dentin interface properties were assessed after 1 and 90-days in SBF by microtensile bond strength test and confocal laser scanning microscopy. Data were analyzed using two and one-way ANOVA and post-hoc tests (α = 0.05). RESULTS: RR fractions increased dentin matrix complex (96 - 69 MPa) and storage (95 - 68 MPa) moduli, compared to the control (∼9 MPa) in the ranking order: F2 ≥ F3 = F1 = F4 > control (p < 0.001). Treatment did not affect tan δ values. After 30- and 90-days, RR-treated dentin E*, E' and tan δ decreased (p < 0.001). F2 fraction yielded the highest microtensile bond strength (43.9 MPa), compared to F1, F4 (35.9 - 31.7 MPa), and control (29 MPa). RR-treated interfaces mediated stable surface modifications and enhanced collagen-methacrylate resin interactions at the bioadhesive interface. SIGNIFICANCE: Prodelphinidin gallates from RR are potent and reasonably stable biomimetic agents to dentin. Higher potency of F2 fraction with the dentin matrix and the adhesive interface is associated with a degree of polymerization of 2-3 and gallo(yl) motifs.

Chemical Transformation of B- to A-type Proanthocyanidins and 3D Structural Implications.

In nature, proanthocyanidins (PACs) with A-type linkages are relatively rare, likely due to biosynthetic constraints in the formation of additional ether bonds to be introduced into the more common B-type precursors. However, A-type linkages confer greater structural rigidity on PACs than do B-type linkages. Prior investigations into the structure-activity relationships (SAR) describing how plant-derived PACs with B- and complex AB-type linkages affect their capacity for dentin biomodification indicate that a higher ratio of double linkages leads to a greater interaction with dentin type I collagen. Thus, A-type PACs emerge as particularly intriguing candidates for interventional functional biomaterials. This study employed a free-radical-mediated oxidation using DPPH to transform trimeric and tetrameric B-type PACs, 2 and 4, respectively, into their exclusively A-type linked analogues, 3 and 5, respectively. The structures and absolute configurations of the semisynthetic products, including the new all-A-type tetramer 5, were determined by comprehensive spectroscopic analysis. Additionally, molecular modeling investigated the conformational characteristics of all trimers and tetramers, 1-5. Our findings suggest that the specific interflavan linkages significantly impact the flexibility and low-energy conformations of the connected monomeric units, which conversely can affect the bioactive conformations relevant for dentin biomodification.

Modulatory role of terminal monomeric flavan-3-ol units in the viscoelasticity of dentin.

Flavan-3-ol monomers are the building blocks of proanthocyanidins (PACs), natural compounds from plants shown to mediate specific biologic activities on dentin. While the stereochemistry of the terminal flavan-3-ols, catechin (C) versus epicatechin (EC), impacts the biomechanical properties of the dentin matrix treated with oligomeric PACs, structure-activity relationships driving this bioactivity remain elusive. To gain insights into the modulatory role of the terminal monomers, two highly congruent trimeric PACs from Pinus massoniana only differing in the stereochemistry of the terminal unit (Trimer-C vs. Trimer-EC) were prepared to evaluate their chemical characteristics as well as their effects on the viscoelasticity and biostability of biomodified dentin matrices via infrared spectroscopy and multi-scale dynamic mechanical analyses. The subtle alteration of C versus EC as terminal monomers lead to distinct immediate PAC-trimer biomodulation of the dentin matrix. Nano- and micro-dynamic mechanical analyses revealed that Trimer-EC increased the complex moduli (0.51 GPa) of dentin matrix more strongly than Trimer-C (0.26 GPa) at the nanoscale length (p < 0.001), whereas the reverse was found at the microscale length (p < .001). The damping capacity (tan δ) of dentin matrix decreased by 70% after PAC treatment at the nano-length scale, while increased values were found at the micro-length scale (~0.24) compared to the control (0.18 ; p < .001). An increase in amide band intensities and a decrease of complex moduli was observed after storage in simulated body fluid for both Trimer-C and Trimer-EC modified dentin. The stereochemical configuration of the terminal monomeric units, C and EC, did not impact the chemo-mechanical stability of dentin matrix.

Unprecedented Benzoquinone Motifs Reveal Post-Oligomerizational Modification of Proanthocyanidins.

Proanthocyanidins (PACs) are complex flavan-3-ol polymers with stunning chemical complexity due to oxygenation patterns, oxidative phenolic ring linkages, and intricate stereochemistry of their heterocycles and inter-flavan linkages. Being promising candidates for dental restorative biomaterials, trace analysis of dentin bioactive cinnamon PACs now yielded novel trimeric (1 and 2) and tetrameric (3) PACs with unprecedented o- and p-benzoquinone motifs (benzoquinonoid PACs). Challenges in structural characterization, especially their absolute configuration, prompted the development of a new synthetic-analytical approach involving comprehensive spectroscopy, including NMR with quantum mechanics-driven 1H iterative functionalized spin analysis (HifSA) plus experimental and computational electronic circular dichroism (ECD). Vital stereochemical information was garnered from synthesizing 4-(2,5-benzoquinone)flavan-3-ols and a truncated analogue of trimer 2 as ECD models. Discovery of the first natural benzoquinonoid PACs provides new evidence to the experimentally elusive PAC biosynthesis as their formation requires two oxidative post-oligomerizational modifications (POMs) that are distinct and occur downstream from both quinone-methide-driven oligomerization and A-type linkage formation. While Nature is known to achieve structural diversity of many major compound classes by POMs, this is the first indication of PACs also following this common theme.

Immediate and Sustained Root Caries Prevention of Fluoride Varnish Combined with Toothpastes.

The aim of this study was to determine the immediate and sustained effect of a fluoride varnish and its combinations with toothpastes in preventing root caries development using a salivary microcosm in vitro model. Human root dentin specimens (n = 150) were randomly divided into 5 experimental protocols (n = 30): (1) Fluoride Varnish (V); (2) V followed by Paste One (V + PO); (3) V followed by Paste Plus (V + PP); (4) V followed by PO and PP (V + PO + PP); and (5) No treatment (control). One varnish layer was applied on the specimens (except for the control group) and kept for 18 h. Then, the varnish was removed and toothpaste treatments were initiated according to experimental groups. For the short-term incubation model (n = 15), the specimens were also immediately subjected to 7-day cariogenic challenge. For that, human saliva was used as bacterial inoculum and McBain artificial saliva containing 2% sucrose as growth medium. The other half of the specimens (n = 15) were used to study the varnish's sustained effect by long-term incubation (8 weeks) before cariogenic challenge. The protocols' anti-caries properties were evaluated by dentin porosity (rhodamine intensity; RI) and mineral density, while their anti-biofilm effects were evaluated using biofilm's biomass and viability assays. For short- and long-term incubation models, all experimental regimens resulted in statistically significant decreases (p < 0.05) in the RI (up to 180 µm and 120 µm, respectively) as well as higher mineral density compared to No treatment (p < 0.001). V + PO + PP and/or V + PO resulted in statistically lower RI compared to V for some depths (p < 0.05) in both models. There were changes in RI and mineral density within groups over time. All experimental treatments exhibited anti-biofilm effects. All prevention protocols exhibited immediate and sustained anti-caries effect against root caries development. The combination of a fluoride varnish with PO resulted in superior additional anti-caries effects.

Seco B-Type Oligomers from Pinus massoniana Expand the Procyanidin Chemical Space and Exhibit Dental Bioactivity.

Investigation of a pine bark extract for bioactive proanthocyanidin oligomers resulted in the isolation of structurally related dimeric seco B-type procyanidin derivatives, 1-5. This includes scalemic mixtures of gambiriin A1 (1a) and A2 (2a) and their newly described optical antipodes, ent-gambiriin A1 (1b) and ent-gambiriin A2 (2b), respectively, as well as a racemic mixture of the newly described (ent-)gambiriin A5 (3a/3b). Furthermore, the study now fully characterizes the previously reported optically pure dimers gambiriin B1 (4) and gambirflavan D1 (5), and characterized the novel seco B-type procyanidin trimer, 6 (gambirifuran C1). Thermal conversion of catechin in aqueous solution provided further evidence for the structures of 1-6 and led to the purification of semisynthetic 1a and 2a as well as additional dimers 7-10. Elucidating the structures of the natural dimers, 1-5, from comprehensive NMR and ECD data and synthetic evidence provided crucial reference points for establishing the structure of the seco B-type procyanidin trimer, 6. Serving as assigned building blocks, data from the dimers supported the 3D structural assignment of 6 based on NMR substituent chemical shift differences (s.c.s., syn. ΔδC) and component-based empirical ECD calculations. Within the newly characterized series of PAC-related molecules, 5 exhibited high dentin biomodification potential. In addition, considering the nomenclature issues and plausible biosynthetic pathways of this group of compounds led to a consolidated nomenclature of all currently known seco B-type procyanidins. These findings, thereby, expand the chemical space of bioactive catechin oligomers, which have promise as agents for the natural enhancement of dental biomaterials. Finally, the current knowledge of the chemical space of seco B-type procyanidin derivatives was compiled to the level of absolute configuration.

B-type Proanthocyanidins with Dentin Biomodification Activity from Cocoa (Theobroma cacao).

To enable translational studies, a scalable preparative isolation scheme was developed for underivatized cocoa (Theobroma cacao) proanthocyanidins (PACs), affording six all-B-type oligomeric PACs, including a new tetramer 4. Their structures, including absolute configuration, were unambiguously established by comprehensive spectroscopic and chemical methods. Evaluation of the PACs' dentin biomodification properties employed dynamic mechanical and infrared spectroscopic analyses in dentin bioassay models. PAC treatment enhanced the biomechanical strength of dentin by 5- to 15-fold compared to untreated dentin. Among the PAC agents, the pentamer, cinnamtannin A3 (6), led to the highest complex modulus value of 131 MPa, whereas the "branched" tetramer, 4, showed the lowest, yet still significant bioactivity. This study of specifically singly linked medium-length oligomeric PACs indicates that the linkage site is paramount in determining the potency of these PACs as dentin biomodifiers.

Comparison of collagen features of distinct types of caries-affected dentin.

OBJECTIVES: To compare the biodegradability, mechanical behavior, and physicochemical features of the collagen-rich extracellular matrix (ECM) of artificial caries-affected dentin (ACAD), natural caries-affected dentin (NCAD) and sound dentin (SD). METHODS: Dentin specimens from human molars were prepared and assigned into groups according to the type of dentin: ACAD, NCAD, or SD. ACAD was produced by incubation of demineralized SD with Streptococcus mutans in a chemically defined medium (CDM) with 1% sucrose for 7 days at 37 °C under anaerobic conditions. Specimens were assessed to determine collagen birefringence, biodegradability, mechanical behavior, and chemical composition. Data were individually processed and analyzed by ANOVA and post-hoc tests (α = 0.05). RESULTS: CDM-based biofilm challenge reduced loss, storage, and complex moduli in ACAD (p < 0.001), while the damping capacity remained unaffected (p = 0.066). Higher red and lower green birefringence were found in ACAD and NCAD when compared with SD (p < 0.001). Differently to ACAD, SD and NCAD presented higher biodegradability to exogenous proteases (p = 0.02). Chemical analysis of the integrated areas of characteristic bands that assess mineral quality (carbonate/phosphate and crystallinity index), mineral to matrix (phosphate/amide I) and post-translational modifications (amide III/CH2, pentosidine/CH2, and pentosidine/amide III) (p<0.05) showed that NCAD was significantly different from SD while ACAD exhibited intermediate values. CONCLUSIONS: CDM-based biofilm challenge produced a dentin ECM with decreased mechanical properties and increased collagen maturity. The compositional and structural conformation of the ACAD suggested that CDM-based biofilm challenge showed potential to produce artificial lesions by revealing a transitional condition towards mimicking critical features of NCAD. CLINICAL SIGNIFICANCE: This study highlights the importance of developing a tissue that mimics the features of natural caries-affected dentin ECM for in vitro studies. Our findings suggested the potential of a modified biofilm challenge protocol to produce and simulate a relevant substrate, such as caries-affected dentin.

Proanthocyanidin Tetramers and Pentamers from Cinnamomum verum Bark and Their Dentin Biomodification Bioactivities.

To enable the further exploration of structure-activity relationships (SARs) of proanthocyanidins (PACs) with dentin biomodification abilities, Cinnamomum verum was selected for scaled-up purification of mixed A-/B-type, medium-size PAC oligomers. Sequential purification by centrifugal partition chromatography (CPC), Sephadex LH-20, and semiprep HPLC chromatography yielded four underivatized tetrameric (5-8) and two pentameric (9-10) PACs. Their unambiguous structural characterization involved extensive spectral and chemical degradation approaches to show that epicatechin units are connected by plant-specific combinations of doubly linked A- and singly linked B-type interflavanyl bonds. The biomechanical properties (via dynamic mechanical analysis) and physicochemical structure (via infrared spectroscopy) were assessed to evaluate the biomodification potency of PAC-treated collagen in a preclinical dentin model. This study revealed that (4→8) versus (4→6) bonds in PAC interflavan linkages have limited influence on biomechanical outcomes of dentin. By exhibiting a 25-fold increase in the complex modulus of treated dentin compared to control, aesculitannin E (5) was found to be the most potent PAC known to date for enhancing the mechanical properties of dentin in this preclinical model.

Biomimetic Growth of Metal-Organic Frameworks for the Stabilization of the Dentin Matrix and Control of Collagenolysis.

The dentin matrix is a collagenous scaffold structurally involved in anchoring resin-based materials to the tooth. Time-dependent degradation of this scaffold at the resin-dentin interface remains a core problem in adhesive dentistry, limiting the service life of dental fillings. This study explored the use of emergent materials termed metal-organic frameworks (MOFs)─formed by the self-assembly of metal ions and organic building blocks─to safeguard the collagen integrity in the functional dentin matrix. We demonstrate that collagen fibrils (from demineralized human dentin) can induce the biomimetic growth of MOF crystals as protective coatings to strengthen and stabilize the fibrils. Zeolitic imidazolate framework-8 (ZIF-8), a zinc-based microporous MOF, was used to fabricate the MOF composites via a "one-pot" reaction in water. The ZIF-modified dentin matrix presented superior mechanical strength and resistance to proteolysis, which can positively affect the longevity of collagen as an anchoring substrate. This work identifies a potential biomedical application of biomimetically synthesized MOFs in repairing dental tissues critical to restorative therapies.

Proanthocyanidin encapsulation for sustained bioactivity in dentin bioadhesion: A two-year study.

OBJECTIVES: To determine the long-term effect on the stability of dentin-resin interfaces after the addition of polylactide (PLA) capsules containing proanthocyanidin (PAC) to adhesive resin. METHODS: Sub-micron (SM) and micron (M) size capsules containing PACs were produced using a combination of emulsification and solvent evaporation techniques and characterized. Human dentin surfaces (n = 8) were etched (35% glycolic acid) and primed (15% enriched Vitis vinifera extract solution - VVe), followed by the application of an experimental adhesive containing 0 (control), 1.5 wt% of SM or M PAC-filled PLA capsules light cured for 40 s. A crown was built using commercial composite. After 24 h-immersion (37 °C) in simulated body fluid, specimens were serially sectioned into resin-dentin beams. Microtensile bond strength (TBS), micro-permeability and fracture pattern were assessed immediately and after 1 and 2 years. Data were statistically analyzed using two-way ANOVA and post-hoc test (α = 0.05). RESULTS: Polydisperse capsules were manufactured with average diameter of 0.36 µm and 1.08 µm for SM and M, respectively. The addition of capsules did not affect TBS (p = 0.889). After 2 years, TBS significantly decreased in SM (p = 0.006), whereas M showed similar initial values (p = 0.291). Overall, less micro-permeability was found in M than the control and SM group (p < 0.001). After 2 years, fractured surfaces from capsule-containing groups failed within the adhesive layer while control fractured at the bottom of the hybrid layer. SIGNIFICANCE: The addition of PAC-filled PLA microcapsules in a dental adhesive did not affect the bond strength while increased and sustained the protection against micro-permeability in the interface, likely due to release of PACs.

Galloylated proanthocyanidins in dentin matrix exhibit biocompatibility and induce differentiation in dental stem cells.

Aim: Grape seed extract contains a complex mixture of proanthocyanidins (PACs), a plant biopolymer used as a biomaterial to improve reparative and preventive dental therapies. Co-polymerization of PACs with type I collagen mechanically reinforces the dentin extracellular matrix. This study assessed the biocompatibility of PACs from grape seed extract on dental pulp stem cells (DPSCs) in a model simulating leaching through dentin to the pulp cavity. The aim was to determine the type of PACs (galloylated vs. non-galloylated) within grape seed extract that are most compatible with dental pulp tissue. Methodology: Human demineralized dentin was treated with selectively-enriched dimeric PACs prepared from grape seed extract using liquid-liquid chromatography. DPSCs were cultured within a 2D matrix and exposed to PAC-treated dentin extracellular matrix. Cell proliferation was measured using the MTS assay and expression of odontoblastic genes was analyzed by qRT-PCR. Categorization of PACs leaching from dentin was performed using HPLC-MS. Results: Enriched dimeric fractions containing galloylated PACs increased the expression of certain odontoblastic genes in DPSCs, including Runt-related transcription factor 2 (RUNX2), vascular endothelial growth factor (VEGF), bone morphogenetic protein 2 (BMP2), basic fibroblast growth factor (FGF2), dentin sialophosphoprotein (DSPP) and collagen, type I, alpha 1 (COLI). Galloylated dimeric PACs also exhibited minor effects on DPSC proliferation, resulting in a decrease compared to control after five days of treatment. The non-galloylated dimer fraction had no effect on these genes or on DPSC proliferation. Conclusions: Galloylated PACs are biocompatible with DPSCs and may exert a beneficial effect on cells within dental pulp tissue. The observed increase in odontoblastic genes induced by galloylated PACs together with a decrease in DPSC proliferation is suggestive of a shift toward cell differentiation. This data supports the use of dimeric PACs as a safe biomaterial, with galloylated dimeric PACs exhibiting potential benefits to odontoblasts supporting dentin regeneration.

The stoic tooth root: how the mineral and extracellular matrix counterbalance to keep aged dentin stable.

Aging is a physiological process with profound impact on the biology and function of biosystems, including the human dentition. While resilient, human teeth undergo wear and disease, affecting overall physical, psychological, and social human health. However, the underlying mechanisms of tooth aging remain largely unknown. Root dentin is integral to tooth function in that it anchors and dissipates mechanical load stresses of the tooth-bone system. Here, we assess the viscoelastic behavior, composition, and ultrastructure of young and old root dentin using nano-dynamic mechanical analysis, micro-Raman spectroscopy, small angle X-ray scattering, atomic force and transmission electron microscopies. We find that the root dentin overall stiffness increases with age. Unlike other mineralized tissues and even coronal dentin, however, the ability of root dentin to dissipate energy during deformation does not decay with age. Using a deconstruction method to dissect the contribution of mineral and organic matrix, we find that the damping factor of the organic matrix does deteriorate. Compositional and ultrastructural analyses revealed higher mineral-to-matrix ratio, altered enzymatic and non-enzymatic collagen cross-linking, increased collagen d-spacing and fibril diameter, and decreased abundance of proteoglycans and sulfation pattern of glycosaminoglycans . Therefore, even in the absence of remodeling, the extracellular matrix of root dentin shares traits of aging with other tissues. To explain this discrepancy, we propose that altered matrix-mineral interactions, possibly mediated by carbonate ions sequestered at the mineral interface and/or altered glycosaminoglycans counteract the deleterious effects of aging on the structural components of the extracellular matrix. STATEMENT OF SIGNIFICANCE: Globally, a quarter of the population will be over 65 years old by 2050. Because many will retain their dentition, it will become increasingly important to understand and manage how aging affects teeth. Dentin is integral to the protective, biomechanical, and regenerative features of teeth. Here, we demonstrate that older root dentin not only has altered mechanical properties, but shows characteristic shifts in mineralization, composition, and post-translational modifications of the matrix. This strongly suggests that there is a mechanistic link between mineral and matrix components to the biomechanical performance of aging dentin with implications for efforts to slow or even reverse the aging process.

Paradoxical effects of galloyl motifs in the interactions of proanthocyanidins with collagen-rich dentin.

Plant-derived proanthocyanidins (PACs) mediate physicochemical modifications to the dentin extracellular matrix (ECM). The structure-activity relationships of PACs remain largely unknown, mostly due to the varied complex composition of crude extracts, as well as the challenges of purification and mechanistic assessment. To assess the role of galloylated PACs as significant contributors to high yet unstable biomodification activity to the dentin ECM, we removed the galloyl moieties (de-galloylation) via enzymatic hydrolysis from three galloyl-rich PAC-containing extracts (Camellia sinensis, Vitis vinifera, and Hamamelis virginiana). The biomechanical and biological properties of dentin were assessed upon treatment with these extracts vs. their de-galloylated counterparts. An increase in the complex modulus of the dentin matrix was found with all extracts, however, the crude extract was significantly higher when compared to the de-galloylated version. Exhibiting the highest content of galloylated PACs among the investigated plants, Camellia sinensis crude extract also exhibited the biggest relapse in mechanical properties after one-month incubation. De-galloylation did not modify the damping capacity of dentin ECM. Moreover, PAC-mediated protection against proteolytic degradation was unaffected by de-galloylation. The de-galloylation experiments confirmed that gallic acid in galloylated rich-PAC extracts drive stronger yet significantly less sustained mechanical effects in dentin ECM.

Do Certain Flavonoid IMPS Have a Vital Function?

Flavonoids are a vast group of metabolites that are essential for vascular plant physiology and, thus, occur ubiquitously in plant-based/-derived foods. The solitary designation of thousands of known flavonoids hides the fact that their metabolomes are structurally highly diverse, consist of disparate subgroups, yet undergo a certain degree of metabolic interconversion. Unsurprisingly, flavonoids have been an important theme in nutrition research. Already in the 1930s, it was discovered that the ability of synthetic Vitamin C to treat scurvy was inferior to that of plant extracts containing Vitamin C. Subsequent experimental evidence led to the proposal of Vitamin P (permeability) as an essential phytochemical nutrient. However, attempts to isolate and characterize Vitamin P gave confusing and sometimes irreproducible results, which today can be interpreted as rooted in the unrecognized (residual) complexity of the intervention materials. Over the years, primarily flavonoids (and some coumarins) were known as having Vitamin P-like activity. More recently, in a NAPRALERT meta-analysis, essentially all of these Vitamin P candidates were identified as IMPs (Invalid/Improbable/Interfering Metabolic Panaceas). While the historic inability to define a single compound and specific mode of action led to general skepticism about the Vitamin P proposition for "bioflavonoids," the more logical conclusion is that several abundant and metabolically labile plant constituents fill this essential role in human nutrition at the interface of vitamins, cofactors, and micronutrients. Reviewing 100+ years of the multilingual Vitamin P and C literature provides the rationales for this conclusion and new perspectives for future research.

Unveiling structure-activity relationships of proanthocyanidins with dentin collagen.

OBJECTIVE: To elucidate the structure-activity relationships (SARs) of proanthocyanidins (PACs) with type I collagen using sixteen chemically defined PACs with degree of polymerization (DP) 2-6. METHODS: Under a dentin model, the biomimicry of PACs with type I collagen was investigated by dynamic mechanical analysis (DMA) and infrared spectroscopy. The dentin matrix was modified with PACs from Pinus massoniana [monomers (Mon-1 and Mon-2), dimers (Dim-1-Dim-4), trimers (Tri-1-Tri-4), tetramers (Tet-1-Tet-5), and hexamer (Hex-1)]. A strain sweep method in a 3-point bending submersion clamp was used to assess the viscoelastic properties [storage (E'), loss (E"), and complex moduli (E*) and tan δ] of the dentin matrix before and after biomodification. Biochemical analysis of the dentin matrix was assessed with FTIR spectroscopy. Data were statistically analyzed using one-way ANOVA and post-hoc tests (α = 0.05). RESULTS: DP had a significant effect on modified dentin moduli (tetramers ≈ trimers > hexamers ≈ dimers > monomers ≈ control, p < 0.001). Trimers and tetramers yielded 6- to 8-fold increase in the mechanical properties of modified dentin and induced conformational changes to the secondary structure of collagen. Modifications to the tertiary structure of collagen was shown in all PAC modified-dentin matrices. SIGNIFICANCE: Findings establish three key SARs: (i) increasing DP generally enhances biomimicry potential of PACs in modulating the mechanical and chemical properties of dentin (ii) the secondary structure of dentin collagen is affected by the position of B-type inter-flavanyl linkages (4ß â†’ 6 and 4ß â†’ 8); and (iii) the terminal monomeric flavan-3-ol unit plays a modulatory role in the viscoelasticity of dentin.

In vitro anti-erosive property of a mint containing bioactive ingredients.

PURPOSE: To evaluate the in vitro protective effect of a mint formulation containing (-)-epigallocatechin-3-gallate (EGCg-mint) on root dentin exposed to a highly erosive environment in the presence and absence of proteolytic challenge. METHODS: Root dentin specimens were subjected to an erosion-remineralization cycling model (6×/day; 5 days) that included 5-minute immersion in 1% citric acid and 60-minute immersion in remineralization solution (RS). At the remineralization half-time, the specimens were treated (n= 20) with EGCg-mint, RS (negative control) or sodium fluoride (1,000 ppm of NaF; positive control). Half of the specimens were kept overnight in RS (pH cycling) and the other half in RS with Clostridium histolyticum collagenase (pH-proteolytic cycling). Erosion depth was measured using optical profilometry and data analyzed by two-way ANOVA and Tukey tests (α= 0.05). RESULTS: Under pH-cycling, NaF resulted in statistically lower erosion depth compared to EGCg-mint (P= 0.020) and RS (P= 0.005). Under pH-proteolytic cycling, EGCg-mint and NaF significantly decreased the tissue loss (erosion depth, P< 0.001) compared to the RS. The EGCg-mint exhibited an anti-erosion property on root dentin under a proteolytic challenge. NaF presented an anti-erosion property regardless of the erosive cycling model. CLINICAL SIGNIFICANCE: The anti-erosive action of an over-the-counter mint, containing active ingredients, including epigallocatechin-3-gallate, is likely by the protective mechanisms of the dentin extracellular matrix.

Hydroxy acids for adhesion to enamel and dentin: Long-term bonding performance and effect on dentin biostability.

OBJECTIVES: To test the demineralization potential, bonding performance, and dentin biostability when using hydroxy acids for etching enamel and dentin. METHODS: Surface microhardness, roughness and depth of demineralization were investigated after etching enamel and dentin with 35 % glycolic acid (Gly), tartaric acid (Ta), gluconic acid (Glu), gluconolactone (Gln), or phosphoric acid (Pa) (n = 5/group). Dentin microtensile bond strength (µTBS) after 24 h or 1 year of bonding (n = 8 teeth/group) and enamel shear bond strength (SBS) after 24 h (n = 10 teeth/group) were obtained. In dentin, failure mode was classified as adhesive, cohesive in dentin/resin, or mixed. Dentin biostability was assessed by loss of dry weight and collagen degradation after 30-day incubation (n = 10 beams/group). Statistical analysis consisted of ANOVA with post-hoc Tukey's HSD, Tukey-Kramer test, Bonferroni correction, and Fisher's exact tests (α = 0.05). RESULTS: Gly showed better or similar results than Pa for enamel microhardness and dentin roughness, while no significant differences were observed among Ta, Glu, and Gln (p > .05). Hydroxy acids produced significantly shallower demineralization than Pa (p < .05). Gln resulted in the lowest SBS and µTBS, while Gly, Glu, Ta, and Pa showed no significant difference. There was no significant difference in µTBS between 24 h and 1 year of storage. The association between failure mode and etchant was statistically significant after 24 h only (p < .001). Hydroxy acids resulted in higher dentin biostability than Pa (p < .05). CONCLUSIONS: Gly, Glu and Ta resulted in adequate bonding performance and reduced dentin degradation and are potential alternative etchants to improve long-term stability of adhesive restorations. CLINICAL SIGNIFICANCE: This study supports the potential use of hydroxy acids as alternative etchants when bonding to enamel and dentin and demonstrates that specific acids are more suitable to be used in adhesion since they result in appropriate bond strength and less dentin degradation.

In vitro Study of the Role of Human Neutrophil Enzymes on Root Caries Progression.

The role of the host immune system in caries progression is mainly speculative, and it is believed that it entails the enzymatic degradation of the dentin organic matrix. The aim of this study was to evaluate the proteolytic effect of human neutrophil enzymes on root caries progression. For this, specimens of bovine root dentin were divided into 4 groups (n = 30): caries (C), caries + neutrophils (C + N), no caries (Control), and no caries + neutrophils (Control + N). Streptococcus mutans biofilm (105 CFU/mL) was grown on the root surface to artificially induce root carious lesions (C and C + N groups). Specimens were then exposed to neutrophils (5 × 106 cells/mL) for 48 h (C + N and Control + N groups). Caries development and neutrophil exposures were repeated a 2nd and 3rd time. Caries depth (CD) and dentin demineralization (DD) were assessed by infiltration of rhodamine B using fluorescence microscopy. Collagen fibril ultrastructure was characterized under a polarized microscope with Picrosirius red staining. There were no significant differences (p > 0.05) in CD and DD between the C and C + N groups for 1, 2, and 3 caries-neutrophil exposures. Immature collagen was significantly less present in the carious groups (C, p = 0.003; C + N, p = 0.01) than in the noncarious groups in the most superficial 200 µm. We thus concluded that human neutrophil enzymes did not influence short-term root caries progression, and immature collagen fibrils were more susceptible to degradation during S. mutans-induced root caries progression.

Surface-Directed Mineralization of Fibrous Collagen Scaffolds in Simulated Body Fluid for Tissue Engineering Applications.

The use of polymer additives that stabilize fluidic amorphous calcium phosphate is key to obtaining intrafibrillar mineralization of collagen in vitro. On the other hand, this biomimetic approach inhibits the nucleation of mineral crystals in unconfined extrafibrillar spaces, that is, extrafibrillar mineralization. The extrafibrillar mineral content is a significant feature to replicate from hard connective tissues such as bone and dentin as it contributes to the final microarchitecture and mechanical stiffness of the biomineral composite. Herein, we report a straightforward route to produce densely mineralized collagenous composites via a surface-directed process devoid of the aid of polymer additives. Simulated body fluid (1×) is employed as a biomimetic crystallizing medium, following a preloading procedure on the collagen surface to quickly generate the amorphous precursor species required to initiate matrix mineralization. This approach consistently leads to the formation of extrafibrillar bioactive minerals in bulk collagen scaffolds, which may offer an advantage in the production of osteoconductive collagen-apatite materials for tissue engineering and repair purposes.