RESUMO
We have developed an innovative thin-film nanocomposite membrane that contains cellulose acetate (CA) with small amounts of TiO2-decorated graphene oxide (GO) (ranging from 0.5 wt.% to 2 wt.%) sandwiched between two polytetrafluoroethylene (PTFE)-like thin films. The PTFE-like films succeeded in maintaining the bulk porosity of the support while increasing the thermal and chemical robustness of the membrane and boosting the catalytic activity of TiO2 nanoparticles. The membranes exhibited a specific chemical composition and bonding, with predominant carbon-oxygen bonds from CA and GO in the bulk, and carbon-fluorine bonds on their PTFE-like coated sides. We have also tested the membranes' photocatalytic activities on azithromycin-containing wastewaters, demonstrating excellent efficiency with more than 80% degradation for 2 wt.% TiO2-decorated GO in the CA-GO-TiO2/PTFE-like membranes. The degradation of the azithromycin formulation occurs in two steps, with reaction rates being correlated to the amount of GO-TiO2 in the membranes.
RESUMO
The aim of this study involved the synthesis and characterization of polyurethane (PUR) foams obtained from poly(ethylene terephthalate) (PET) depolymerization products and two types of filling agents, namely fly ash and glass waste. The depolymerized PET-based products were obtained by zinc acetate-catalyzed glycolysis process in diethylene glycol (DEG) as a co-reactant. The resulting glycolysis products were contacted with methylene diphenyl diisocyanate, castor oil, and reinforcing agents. The resulting PUR specimens were characterized by Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), EDX mapping, mechanical tests, and thermal analysis. The analysis confirmed that the best mechanical performances were registered by the specimens with the lowest concentration of filling agent, while the highest thermal resistance was achieved by the PUR foams with the highest concentration of reinforcing agent.
RESUMO
The paper addresses environmental protection by valorizing an important agri-food waste category, namely fruit and vegetables with focusing on the main characteristics regarding consumption, waste quantities, and ways for valorizing these materials. Thus, vast research was undertaken in order to emphasize the main commodities and their potential application as adsorbents for organic and inorganic pollutants. The main methods or treatment techniques applied for the valorization of eco-materials as adsorbents were presented and the principal efficiency results were indicated. The advantages and disadvantages of using these eco-materials as adsorbents in wastewater treatment were revealed and future recommendations were established. According to the international statistics, the most purchased and consumed five commodities were studied regarding waste generations as potential conversion into eco-materials with an adsorbent role for water pollutants. Thus, the performances for adsorbents based on fruit wastes (such as citrus, banana, apples, grapes, mango) and vegetable wastes (such as potatoes, tomatoes, cabbage, carrots, cauliflower, and/or broccoli) were studied and highlighted in this research.
RESUMO
The influence of waste glass and red mud addition as alternative source of aluminosilicate precursors on the microstructural, mechanical, and leaching properties of bottom ash-based geopolymer was studied in this work through mineralogical, morphological, and spectroscopic analysis, as well as by conducting compressive strength and leaching tests. The bottom ash-based geopolymer composites were synthesized by adding a constant amount of waste glass (10% by weight) and increasing amounts of red mud (up to 30% by weight). The results derived from FTIR, 29Si and 27Al MAS NMR, and SEM-EDX revealed that adding up to 10% (by weight) red mud to the synthesis mixes leads to an increase in the degree of geopolymerization of the activated mixes. The compressive strength followed the same trend. An increase of more than 10% (by weight) red mud added to the synthesis mixes results in a significant decrease of compressive strength of the geopolymer composites. A low leachability of geopolymer composites in regard with their contaminants was revealed especially for those with good compressive strength.
RESUMO
A novel hydrogel composite based on gellan gum and graphene oxide (GG/GO) was synthesized, characterized and tested for sorption capacity in this work. The microstructural, thermogravimetric and spectroscopic analysis confirmed the formation of the GG/GO composite. Comparative batch sorption experiments revealed a sorption capacity of the GG/GO composite for Zn (II) ions of approximately 2.3 higher than that of pure GG. The GG/GO composite exhibits a maximum sorption capacity of 272.57 mg/g at a pH of Zn (II) initial solution of 6. Generally, the sorption capacity of the sorbents is approximately 1.5 higher in slightly acidic conditions (pH 6) comparative with that for strong acidic conditions (pH 3). The sorption isotherms revealed that the sorption followed a monolayer/homogenous behavior. The sorption kinetic data were well fitted by the pseudo-second-order kinetic model, and were consistent with those derived from sorption isotherms. The intraparticle diffusion was considered to be the rate-determining step. Two main sorption mechanisms for Zn (II) were identified namely, ion exchange at low pH values, and both ion exchange and chemisorption in weekly acidic conditions.