Degradation of cathode materials in lithium-ion batteries results in the presence of transition metal ions in the electrolyte, and these ions are known to play a major role in capacity fade and cell failure. Yet, while it is known that transition metal ions migrate from the metal oxide cathode and deposit on the graphite anode, their specific influence on anode reactions and structures, such as the solid electrolyte interphase (SEI), is still quite poorly understood due to the complexity in studying this interface in operational cells. In this work we combine operando electrochemical atomic force microscopy (EC-AFM), electrochemical quartz crystal microbalance (EQCM), and electrochemical impedance spectroscopy (EIS) measurements to probe the influence of a range of transition metal ions on the morphological, mechanical, chemical, and electrical properties of the SEI. By adding representative concentrations of Ni2+, Mn2+, and Co2+ ions into a commercially relevant battery electrolyte, the impacts of each on the formation and stability of the anode interface layer is revealed; all are shown to pose a threat to battery performance and stability. Mn2+, in particular, is shown to induce a thick, soft, and unstable SEI layer, which is known to cause severe degradation of batteries, while Co2+ and Ni2+ significantly impact interfacial conductivity. When transition metal ions are mixed, SEI degradation is amplified, suggesting a synergistic effect on the cell stability. Hence, by uncovering the roles these cathode degradation products play in operational batteries, we have provided a foundation upon which strategies to mitigate or eliminate these degradation products can be developed.
RESUMO
X-ray computed tomography (X-ray CT) is a non-destructive characterization technique that in recent years has been adopted to study the microstructure of battery electrodes. However, the often manual and laborious data analysis process hinders the extraction of useful metrics that can ultimately inform the mechanisms behind cycle life degradation. This work presents a novel approach that combines two convolutional neural networks to first locate and segment each particle in a nano-CT LiNiMnCoO2 (NMC) electrode dataset, and successively classifies each particle according to the presence of flaws or cracks within its internal structure. Metrics extracted from the computer vision segmentation are validated with respect to traditional threshold-based segmentation, confirming that flawed particles are correctly identified as single entities. Successively, slices from each particle are analyzed by a pre-trained classifier to detect the presence of flaws or cracks. The models are used to quantify microstructural evolution in uncycled and cycled NMC811 electrodes, as well as the number of flawed particles in a NMC622 electrode. As a proof-of-concept, a 3-phase segmentation is also presented, whereby each individual flaw is segmented as a separate pixel label. It is anticipated that this analysis pipeline will be widely used in the field of battery research and beyond.
Assuntos
Processamento de Imagem Assistida por Computador , Redes Neurais de Computação , Processamento de Imagem Assistida por Computador/métodos , Tomografia Computadorizada por Raios X/métodos , Computadores , EletrodosRESUMO
Semipermeable polymeric anion exchange membranes are essential for separation, filtration and energy conversion technologies including reverse electrodialysis systems that produce energy from salinity gradients, fuel cells to generate electrical power from the electrochemical reaction between hydrogen and oxygen, and water electrolyser systems that provide H2 fuel. Anion exchange membrane fuel cells and anion exchange membrane water electrolysers rely on the membrane to transport OH- ions between the cathode and anode in a process that involves cooperative interactions with H2O molecules and polymer dynamics. Understanding and controlling the interactions between the relaxation and diffusional processes pose a main scientific and critical membrane design challenge. Here quasi-elastic neutron scattering is applied over a wide range of timescales (100-103 ps) to disentangle the water, polymer relaxation and OH- diffusional dynamics in commercially available anion exchange membranes (Fumatech FAD-55) designed for selective anion transport across different technology platforms, using the concept of serial decoupling of relaxation and diffusional processes to analyse the data. Preliminary data are also reported for a laboratory-prepared anion exchange membrane especially designed for fuel cell applications.
Assuntos
Polímeros , Água , Ânions , Troca Iônica , Íons , Membranas Artificiais , Polímeros/química , Água/químicaRESUMO
Rechargeable Mg/S batteries have the potential to provide a compelling battery for a range of applications owing to their high capacity and gravimetric energy density, safety, and low-cost construction. However, the Mg/S energy storage is not widely developed and deployed due to technical challenges, which include short cycle lifespan and lack of suitable electrolyte. To study the microstructure degradation of Mg/S batteries, multiscale X-ray tomography, an inherently nondestructive method, is performed on dismantled Swagelok Mg/S cells comprising a graphene-sulfur cathode and a super-P separator. For the first time, 3D microstructure visualization and quantification reveal the dissolution (volume fraction decreases from 13.5% to 0.7%, surface area reduces from 2.91 to 1.74 µm2 µm-3 ) and agglomeration of sulfur particles, and the carbon binder densification after 10 cycles. Using tomography data, the image-based simulations are then performed. The results show that the insoluble polysulfides can inevitably block the Mg2+ transportation via shuttle effect. The representative volume should exceed 8200 µm3 to represent bulk cathode. This work elucidates that the Mg/S cell performance is significantly affected by microstructural degradation, and moreover demonstrates how multiscale and multimodal characterization can play an indispensable role in developing and optimizing the Mg/S electrode design.
RESUMO
PURPOSE: Cardiovascular disease (CVD) and cancer mortality rates in Eastern Europe are among the highest in the world. Although diet is an important risk factor, traditional eating habits in this region have not yet been explored. This analysis assessed the relationship between traditional dietary pattern and mortality from all-causes, CVD and cancer in Eastern European cohorts. METHODS: Data from the Health, Alcohol and Psychosocial factors in Eastern Europe prospective cohort were used, including participants from Russia, Poland and the Czech Republic. Based on food frequency questionnaire data, we constructed an Eastern European diet score (EEDS) from nine food groups which can be considered as traditional in this region. The relationship between categorical (low, moderate, high) and continuous (range 0-18) EEDS and mortality was estimated with Cox-regression. RESULTS: From 18,852 eligible participants, 2234 died during follow-up. In multivariable adjusted models, participants with high adherence to the traditional Eastern European diet had significantly higher risk of all-cause (HR 1.23; 95% CI 1.08-1.42) and CVD (1.34; 1.08-1.66) deaths compared to those with low adherence. The association with cancer mortality was only significant in Poland (high vs. low EEDS: 1.41; 1.00-1.98). From the specific EEDS components, high consumption of lard was significantly positively related to all three mortality outcomes, while preserved fruit and vegetable consumption showed consistent inverse associations. CONCLUSION: Our results suggest that traditional eating habits may contribute to the poor health status, particularly the high CVD mortality rates, of populations in Eastern Europe. Adequate public health nutritional interventions in this region are essential.
Assuntos
Doenças Cardiovasculares , Dieta , Doenças Cardiovasculares/epidemiologia , República Tcheca , Humanos , Mortalidade , Polônia/epidemiologia , Estudos Prospectivos , Fatores de Risco , Federação RussaRESUMO
Understanding and ultimately controlling the properties of the solid-electrolyte interphase (SEI) layer at the graphite anode/liquid electrolyte boundary are of great significance for maximizing the performance and lifetime of lithium-ion batteries (LIBs). However, comprehensive in situ monitoring of SEI formation and evolution, alongside measurement of the corresponding mechanical properties, is challenging due to the limitations of the characterization techniques commonly used. This work provides a new insight into SEI formation during the first lithiation and delithiation of graphite battery anodes using operando electrochemical atomic force microscopy (EC-AFM). Highly oriented pyrolytic graphite (HOPG) is investigated first as a model system, exhibiting unique morphological and nanomechanical behavior dependent on the various electrolytes and commercially relevant additives used. Then, to validate these findings with respect to real-world battery electrodes, operando EC-AFM of individual graphite particles like those in commercial systems are studied. Vinylene carbonate (VC) and fluoroethylene carbonate (FEC) are shown to be effective additives to enhance SEI layer stability in 1 M LiPF6/ethylene carbonate/ethyl methyl carbonate (EC/EMC) electrolytes, attributed to their role in improving its structure, density, and mechanical strength. This work therefore presents an unambiguous picture of SEI formation in a real battery environment, contributes a comprehensive insight into SEI formation of electrode materials, and provides a visible understanding of the influence of electrolyte additives on SEI formation.
RESUMO
Osteoderms are hard tissues embedded in the dermis of vertebrates and have been suggested to be formed from several different mineralized regions. However, their nano architecture and micro mechanical properties had not been fully characterized. Here, using electron microscopy, µ-CT, atomic force microscopy and finite element simulation, an in-depth characterization of osteoderms from the lizard Heloderma suspectum, is presented. Results show that osteoderms are made of three different mineralized regions: a dense apex, a fibre-enforced region comprising the majority of the osteoderm, and a bone-like region surrounding the vasculature. The dense apex is stiff, the fibre-enforced region is flexible and the mechanical properties of the bone-like region fall somewhere between the other two regions. Our finite element analyses suggest that when combined into the osteoderm structure, the distinct tissue regions are able to shield the body of the animal by bearing the external forces. These findings reveal the structure-function relationship of the Heloderma suspectum osteoderm in unprecedented detail. STATEMENT OF SIGNIFICANCE: The structures of bone and teeth have been thoroughly investigated. They provide a basis not only for understanding the mechanical properties and functions of these hard tissues, but also for the de novo design of composite materials. Osteoderms, however, are hard tissues that must possess mechanical properties distinct from teeth and bone to function as a protective armour. Here we provide a detailed analysis of the nanostructure of vertebrate osteoderms from Heloderma suspectum, and show that their mechanical properties are determined by their multiscale hierarchical tissue. We believe this study contributes to advance the current knowledge of the structure-function relationship of the hierarchical structures in the Heloderma suspectum osteoderm. This knowledge might in turn provide a source of inspiration for the design of bioinspired and biomimetic materials.
Assuntos
Osso e Ossos/ultraestrutura , Derme/ultraestrutura , Lagartos/anatomia & histologia , Animais , Osso e Ossos/química , Derme/químicaRESUMO
The spatial resolution of 3D imaging techniques is often balanced by the achievable field of view. Since pore size in shales spans more than two orders of magnitude, a compromise between representativeness and accuracy of the 3D reconstructed shale microstructure is needed. In this study, we characterise the effect of imaging resolution on the microstructural and mass transport characteristics of shales using micro and nano-computed tomography. 3D mass transport simulation using continuum and numerical physics respectively is also compared to highlight the significance of the Knudsen effect on the reconstructed solid surface. The result shows that porosity measured by micro-CT is 25% lower than nano-CT, resulting in an overestimated pore size distribution and underestimated pore connectivity. This leads to a higher simulated intrinsic permeability. An overestimated diffusive flux and underestimated permeability are obtained from the continuum mass transport simulation compared to the numerical ones when the molecular-wall collision is accounted, evidenced by the large deviation of the measured Knudsen tortuosity factor and permeability correction factor. This study is believed to provide new knowledge in understanding the importance of imaging resolution and gas flow physics on mass transport in porous media.
RESUMO
Graphene-based carbon sponges can be used in different applications in a large number of fields including microelectronics, energy harvesting and storage, antimicrobial activity and environmental remediation. The functionality and scope of their applications can be broadened considerably by the introduction of metallic nanoparticles into the carbon matrix during preparation or post-synthesis. Here, we report on the use of X-ray micro-computed tomography (CT) as a method of imaging graphene sponges after the uptake of metal (silver and iron) nanoparticles. The technique can be used to visualize the inner structure of the graphene sponge in 3D in a non-destructive fashion by providing information on the nanoparticles deposited on the sponge surfaces, both internal and external. Other deposited materials can be imaged in a similar manner providing they return a high enough contrast to the carbon microstructure, which is facilitated by the low atomic mass of carbon.
RESUMO
An elemental sulfur electrode was imaged with X-ray micro and nano computed tomography and segmented into its constituent phases. Morphological parameters including phase fractions and pore and particle size distributions were calculated directly from labelled image data, and flux based simulations were performed to determine the effective molecular diffusivity of the pore phase and electrical conductivity of the conductive carbon and binder phase, Deff and σeff, that can be used as an input for Li-S battery modelling. In addition to its crucial role in providing electrical conductivity within the sulfur electrode, the intrinsic porosity of the carbon binder domain was found to significantly influence Li-ion transport within the electrode. Neglecting this intrinsic porosity results in an overestimation of the electrical conductivity within the sulfur electrode, and an underestimation of the tortuosity of the Li-ion conducting phase by ca. 56%. The derivation of effective transport parameters directly from image data may aid in the development of more realistic models of Li-S battery systems by reducing the reliance on empirical correlations, and the uncertainties arising from assumptions made in these correlations.
RESUMO
OBJECTIVES: We previously demonstrated oxidative stress in bipolar patients and a relationship between the age of illness onset and total glutathione, a principal antioxidant. In this study, we sought to replicate these findings in a new cohort of patients. METHODS: We recruited bipolar patients from Warneford Hospital, Oxford, UK, of similar age and grouped them according to age of onset of illness. The early-onset group comprised patients with onset at <23 years, and the late group comprised patients with onset at >30 years. A third group, comprising age-matched healthy volunteers, was also included. Reduced and oxidized glutathione, cysteine, and cystine were determined in plasma, using high-performance liquid chromatography. Mitochondrial DNA copy number, measured in whole blood, was also compared between patients and healthy controls. RESULTS: Significant increases in oxidative stress were observed in the patient groups, compared with the control group; however, no differences in glutathione-related oxidative stress measures were detected between the early- and late-onset bipolar patient groups. No differences were observed in the amount of mitochondrial DNA, and there was no correlation with mood state. CONCLUSION: Using a more accurate method to quantify oxidative stress than in our previous study, we show that oxidative stress is a consistent feature of bipolar disorder. Although we did not reproduce our finding correlating age of onset of illness to oxidative stress, we have shown, once again, that oxidative stress is a consistent feature of bipolar disorder.
Assuntos
Transtorno Bipolar/sangue , Glutationa/sangue , Estresse Oxidativo/fisiologia , Adulto , Antioxidantes/metabolismo , Transtorno Bipolar/diagnóstico , Estudos de Coortes , Feminino , Humanos , Masculino , Pessoa de Meia-Idade , Mitocôndrias/metabolismoRESUMO
Lithium-based rechargeable batteries such as lithium-ion (Li-ion), lithium-sulfur (Li-S), and lithium-air (Li-air) cells typically consist of heterogenous porous electrodes. In recent years, there has been growing interest in the use of in-situ and operando micro-CT to capture their physical and chemical states in 3D. The development of in-situ electrochemical cells along with recent improvements in radiation sources have expanded the capabilities of micro-CT as a technique for longitudinal studies on operating mechanisms and degradation. In this paper, we present an overview of the capabilities of the current state of technology and demonstrate novel tomography cell designs we have developed to push the envelope of spatial and temporal resolution while maintaining good electrochemical performance. A bespoke PEEK in-situ cell was developed, which enabled imaging at a voxel resolution of ca. 230 nm and permitted the identification of sub-micron features within battery electrodes. To further improve the temporal resolution, future work will explore the use of iterative reconstruction algorithms, which require fewer angular projections for a comparable reconstruction.
RESUMO
Carbon nitride materials with graphitic to polymeric structures (gCNH) were investigated as catalyst supports for the proton exchange membrane (PEM) water electrolyzers using IrO2 nanoparticles as oxygen evolution electrocatalyst. Here, the performance of IrO2 nanoparticles formed and deposited in situ onto carbon nitride support for PEM water electrolysis was explored based on previous preliminary studies conducted in related systems. The results revealed that this preparation route catalyzed the decomposition of the carbon nitride to form a material with much lower N content. This resulted in a significant enhancement of the performance of the gCNH-IrO2 (or N-doped C-IrO2) electrocatalyst that was likely attributed to higher electrical conductivity of the N-doped carbon support.
RESUMO
A novel electrochemical cell has been designed and built to allow for in situ energy-dispersive X-ray diffraction measurements to be made during reduction of UO2 to U metal in LiCl-KCl at 500°C. The electrochemical cell contains a recessed well at the bottom of the cell into which the working electrode sits, reducing the beam path for the X-rays through the molten-salt and maximizing the signal-to-noise ratio from the sample. Lithium metal was electrodeposited onto the UO2 working electrode by exposing the working electrode to more negative potentials than the Li deposition potential of the LiCl-KCl eutectic electrolyte. The Li metal acts as a reducing agent for the chemical reduction of UO2 to U, which appears to proceed to completion. All phases were fitted using Le Bail refinement. The cell is expected to be widely applicable to many studies involving molten-salt systems.
RESUMO
Lithium sulfur (Li-S) batteries offer higher theoretical specific capacity, lower cost and enhanced safety compared to current Li-ion battery technology. However, the multiple reactions and phase changes in the sulfur conversion cathode result in highly complex phenomena that significantly impact cycling life. For the first time to the authors' knowledge, a multi-scale 3D in-situ tomography approach is used to characterize morphological parameters and track microstructural evolution of the sulfur cathode across multiple charge cycles. Here we show the uneven distribution of the sulfur phase fraction within the electrode thickness as a function of charge cycles, suggesting significant mass transport limitations within thick-film sulfur cathodes. Furthermore, we report a shift towards larger particle sizes and a decrease in volume specific surface area with cycling, suggesting sulfur agglomeration. Finally, we demonstrate the nano-scopic length-scale required for the features of the carbon binder domain to become discernible, confirming the need for future work on in-situ nano-tomography. We anticipate that X-ray tomography will be a powerful tool for optimization of electrode structures for Li-S batteries.
RESUMO
Lithium-ion battery performance is intrinsically linked to electrode microstructure. Quantitative measurement of key structural parameters of lithium-ion battery electrode microstructures will enable optimization as well as motivate systematic numerical studies for the improvement of battery performance. With the rapid development of 3-D imaging techniques, quantitative assessment of 3-D microstructures from 2-D image sections by stereological methods appears outmoded; however, in spite of the proliferation of tomographic imaging techniques, it remains significantly easier to obtain two-dimensional (2-D) data sets. In this study, stereological prediction and three-dimensional (3-D) analysis techniques for quantitative assessment of key geometric parameters for characterizing battery electrode microstructures are examined and compared. Lithium-ion battery electrodes were imaged using synchrotron-based X-ray tomographic microscopy. For each electrode sample investigated, stereological analysis was performed on reconstructed 2-D image sections generated from tomographic imaging, whereas direct 3-D analysis was performed on reconstructed image volumes. The analysis showed that geometric parameter estimation using 2-D image sections is bound to be associated with ambiguity and that volume-based 3-D characterization of nonconvex, irregular and interconnected particles can be used to more accurately quantify spatially-dependent parameters, such as tortuosity and pore-phase connectivity.
RESUMO
BACKGROUND: There is emerging evidence that glutamatergic system dysfunction might play an important role in the pathophysiology of bipolar depression. This review focuses on the use of glutamate receptor modulators for depression in bipolar disorder. OBJECTIVES: 1. To assess the effects of ketamine and other glutamate receptor modulators in alleviating the acute symptoms of depression in people with bipolar disorder.2. To review the acceptability of ketamine and other glutamate receptor modulators in people with bipolar disorder who are experiencing acute depression symptoms. SEARCH METHODS: We searched the Cochrane Depression, Anxiety and Neurosis Review Group's Specialised Register (CCDANCTR, to 9 January 2015). This register includes relevant randomised controlled trials (RCTs) from: the Cochrane Library (all years), MEDLINE (1950 to date), EMBASE (1974 to date), and PsycINFO (1967 to date). We cross-checked reference lists of relevant papers and systematic reviews. We did not apply any restrictions to date, language or publication status. SELECTION CRITERIA: Randomised controlled trials (RCTs) comparing ketamine, memantine, or other glutamate receptor modulators with other active psychotropic drugs or saline placebo in adults with bipolar depression. DATA COLLECTION AND ANALYSIS: At least two review authors independently selected studies for inclusion, assessed trial quality and extracted data. Primary outcomes for this review were response rate and adverse events. Secondary outcomes included remission rate, depression severity change scores, suicidality, cognition, quality of life, and dropout rate. We contacted study authors for additional information. MAIN RESULTS: Five studies (329 participants) were included in this review. All included studies were placebo-controlled and two-armed, and the glutamate receptor modulators - ketamine (two trials), memantine (two trials), and cytidine (one trial) - were used as add-on drugs to mood stabilisers. The treatment period ranged from a single intravenous administration (all ketamine studies), to repeated administration for memantine and cytidine (8 to 12 weeks, and 12 weeks, respectively). Three of the studies took place in the USA, one in Taiwan, and in one, the location was unclear. The majority (70.5%) of participants were from Taiwan. All participants had a primary diagnosis of bipolar disorder, according to the DSM-IV or DSM-IV-TR, and were in a current depressive phase. The severity of depression was at least moderate in all but one study.Among all glutamate receptor modulators included in this review, only ketamine appeared to be more efficacious than placebo 24 hours after the infusion for the primary outcome, response rate (odds ratio (OR) 11.61, 95% confidence interval (CI) 1.25 to 107.74; P = 0.03; I² = 0%, 2 studies, 33 participants). This evidence was rated as low quality. The statistically significant difference disappeared at three days, but the mean estimate still favoured ketamine (OR 8.24, 95% CI 0.84 to 80.61; 2 studies, 33 participants; very low quality evidence). We found no difference in response between ketamine and placebo at one week (OR 4.00, 95% CI 0.33 to 48.66; P = 0.28, 1 study; 18 participants; very low quality evidence).There was no significant difference between memantine and placebo in response rate one week after treatment (OR 1.08, 95% CI 0.06 to 19.05; P = 0.96, 1 study, 29 participants), two weeks (OR 4.88, 95% CI 0.78 to 30.29; P = 0.09, 1 study, 29 participants), four weeks (OR 5.33, 95% CI 1.02 to 27.76; P = 0.05, 1 study, 29 participants), or at three months (OR, 1.66, 95% CI 0.69 to 4.03; P = 0.26, I² = 36%, 2 studies, 261 participants). These findings were based on very low quality evidence.There was no significant difference between cytidine and placebo in response rate at three months (OR, 1.13, 95% CI 0.30 to 4.24; P = 0.86, 1 study, 35 participants; very low quality evidence).For the secondary outcome of remission, no significant differences were found between ketamine and placebo, nor between memantine and placebo. For the secondary outcome of change scores from baseline on depression scales, ketamine was more effective than placebo at 24 hours (MD -11.81, 95% CI -20.01 to -3.61; P = 0.005, 2 studies, 32 participants) but not at one or two weeks after treatment. There was no difference between memantine and placebo for this outcome.We found no significant differences in terms of adverse events between placebo and ketamine, memantine, or cytidine. There were no differences between ketamine and placebo, memantine and placebo, or cytidine and placebo in total dropouts. No data were available on dropouts due to adverse effects for ketamine or cytidine; but no difference was found between memantine and placebo. AUTHORS' CONCLUSIONS: Reliable conclusions from this review are severely limited by the small amount of data usable for analysis. The body of evidence about glutamate receptor modulators in bipolar disorder is even smaller than that which is available for unipolar depression. Overall, we found limited evidence in favour of a single intravenous dose of ketamine (as add-on therapy to mood stabilisers) over placebo in terms of response rate up to 24 hours; ketamine did not show any better efficacy in terms of remission in bipolar depression. Even though ketamine has the potential to have a rapid and transient antidepressant effect, the efficacy of a single intravenous dose may be limited. Ketamine's psychotomimetic effects could compromise study blinding; this is a particular issue for this review as no included study used an active comparator, and so we cannot rule out the potential bias introduced by inadequate blinding procedures.We did not find conclusive evidence on adverse events with ketamine. To draw more robust conclusions, further RCTs (with adequate blinding) are needed to explore different modes of administration of ketamine and to study different methods of sustaining antidepressant response, such as repeated administrations. There was not enough evidence to draw meaningful conclusions for the remaining two glutamate receptor modulators (memantine and cytidine). This review is limited not only by completeness of evidence, but also by the low to very low quality of the available evidence.
Assuntos
Antidepressivos/uso terapêutico , Transtorno Bipolar/tratamento farmacológico , Citidina/uso terapêutico , Depressão/tratamento farmacológico , Antagonistas de Aminoácidos Excitatórios/uso terapêutico , Ketamina/uso terapêutico , Memantina/uso terapêutico , Adulto , Transtorno Bipolar/psicologia , Depressão/psicologia , Humanos , Ensaios Clínicos Controlados Aleatórios como AssuntoRESUMO
The electrodeposition of metallic lithium is a major cause of failure in lithium batteries. The 3D microstructure of electrodeposited lithium 'moss' in liquid electrolytes has been characterised at sub-micron resolution for the first time. Using synchrotron X-ray phase contrast imaging we distinguish mossy metallic lithium microstructures from high surface area lithium salt formations by their contrasting X-ray attenuation.
Assuntos
Galvanoplastia , Imageamento Tridimensional , Lítio/química , Galvanoplastia/métodos , Imageamento Tridimensional/métodos , Síncrotrons , Raios XRESUMO
A new technique combining in situ X-ray diffraction using synchrotron radiation and infrared thermal imaging is reported. The technique enables the application, generation and measurement of significant thermal gradients, and furthermore allows the direct spatial correlation of thermal and crystallographic measurements. The design and implementation of a novel furnace enabling the simultaneous thermal and X-ray measurements is described. The technique is expected to have wide applicability in material science and engineering; here it has been applied to the study of solid oxide fuel cells at high temperature.
RESUMO
Graphitic carbon nitrides are investigated for developing highly durable Pt electrocatalyst supports for polymer electrolyte fuel cells (PEFCs). Three different graphitic carbon nitride materials were synthesized with the aim to address the effect of crystallinity, porosity, and composition on the catalyst support properties: polymeric carbon nitride (gCNM), poly(triazine) imide carbon nitride (PTI/Li+Cl-), and boron-doped graphitic carbon nitride (B-gCNM). Following accelerated corrosion testing, all graphitic carbon nitride materials are found to be more electrochemically stable compared to conventional carbon black (Vulcan XC-72R) with B-gCNM support showing the best stability. For the supported catalysts, Pt/PTI-Li+Cl- catalyst exhibits better durability with only 19% electrochemical surface area (ECSA) loss versus 36% for Pt/Vulcan after 2000 scans. Superior methanol oxidation activity is observed for all graphitic carbon nitride supported Pt catalysts on the basis of the catalyst ECSA.