Controlling the two-dimensional polymerization processes of two-dimensional covalent organic frameworks (2D COFs) is essential to fully realizing their distinct properties. Although most 2D COFs have been isolated as polycrystalline aggregates with only nanometer-scale crystalline domains, we have identified rapid, solvothermal conditions that provide micrometer-scale and larger single-crystal 2D polymers for a few 2D COFs. Yet it remains unclear why certain conditions produce far larger 2D polymers than others, which hinders generalizing these findings. The guiding principles for controlled two-dimensional polymerization in solution remain unclear. Here, we study the crystallization processes of both single-crystalline and polycrystalline 2D COFs using ultrasmall-angle X-ray scattering (USAXS) for the first time, through which we characterized COF formation conditions with scattering data collected every few seconds. In situ USAXS experiments revealed distinct growth mechanisms between single-crystalline and polycrystalline COFs and suggested a nonclassical particle fusion-based growth model for single-crystalline COFs that results in faceted, hexagonal particles. These findings were corroborated by in situ wide-angle X-ray scattering (WAXS) experiments and scanning electron microscopy (SEM). In contrast, polymerizations that provide polycrystalline COFs evolve as spherical aggregates that do not fuse in the same way. These insights into how micrometer-sized, crystalline 2D polymers are formed in solution point a way forward to establishing a robust connection between the 2D polymer structure and designed properties by controlling their polymerization processes.
RESUMO
2D covalent organic frameworks (2D COFs) are attractive candidates for next-generation membranes due to their robust linkages and uniform, tunable pores. Many publications have claimed to achieve selective molecular transport through COF pores, but reported performance metrics for similar networks vary dramatically, and in several cases the reported experiments are inadequate to support such conclusions. These issues require a reevaluation of the literature. Published examples of 2D COF membranes for liquid-phase separations can be broadly divided into two categories, each with common performance characteristics: polycrystalline COF films (most >1 µm thick) and weakly crystalline or amorphous films (most <500 nm thick). Neither category has demonstrated consistent relationships between the designed COF pore structure and separation performance, suggesting that these imperfect materials do not sieve molecules through uniform pores. In this perspective, rigorous practices for evaluating COF membrane structures and separation performance are described, which will facilitate their development toward molecularly precise membranes capable of performing previously unrealized chemical separations. In the absence of this more rigorous standard of proof, reports of COF-based membranes should be treated with skepticism. As methods to control 2D polymerization improve, precise 2D polymer membranes may exhibit exquisite and energy efficient performance relevant for contemporary separation challenges.
RESUMO
Two-dimensional covalent organic frameworks (2D COFs) form as layered 2D polymers whose sheets stack through high-surface-area, noncovalent interactions that can give rise to different interlayer arrangements. Manipulating the stacking of 2D COFs is crucial since it dictates the effective size and shape of the pores as well as the specific interactions between functional aromatic systems in adjacent layers, both of which will strongly influence the emergent properties of 2D COFs. However, principles for tuning layer stacking are not yet well understood, and many 2D COFs are disordered in the stacking direction. Here, we investigate effects of pendant chain length through a series of 2D imine-linked COFs functionalized with n-alkyloxy chains varying in length from one carbon (C1 COF) to 11 carbons (C11 COF). This series reveals previously unrecognized and unanticipated trends in both the stacking geometry and crystallinity. C1 COF adopts an averaged eclipsed geometry with no apparent offset between layers. In contrast, all subsequent chain lengths lead to some degree of unidirectional slip stacking. As pendant chain length is increased, trends show average layer offset increasing to a maximum of 2.07 Å in C5 COF and then decreasing as chain length is extended through C11 COF. Counterintuitively, shorter chains (C2-C4) give rise to lower yields of weakly crystalline materials, while longer chains (C6-C9) produce greater yields of highly crystalline materials, as confirmed by powder X-ray diffraction and scanning electron microscopy. Molecular dynamics simulations corroborate these observations, suggesting that long alkyl chains can interact favorably to promote the self-assembly of sheets. In situ proton NMR spectroscopy provides insights into the reaction equilibrium as well as the relationship between low COF yields and low crystallinity. These results provide fundamental insights into principles of supramolecular assembly in 2D COFs, demonstrating an opportunity for harnessing favorable side-chain interactions to produce highly crystalline materials.
RESUMO
Two-dimensional covalent organic frameworks (2D COFs) containing heterotriangulenes have been theoretically identified as semiconductors with tunable, Dirac-cone-like band structures, which are expected to afford high charge-carrier mobilities ideal for next-generation flexible electronics. However, few bulk syntheses of these materials have been reported, and existing synthetic methods provide limited control of network purity and morphology. Here, we report transimination reactions between benzophenone-imine-protected azatriangulenes (OTPA) and benzodithiophene dialdehydes (BDT), which afforded a new semiconducting COF network, OTPA-BDT. The COFs were prepared as both polycrystalline powders and thin films with controlled crystallite orientation. The azatriangulene nodes are readily oxidized to stable radical cations upon exposure to an appropriate p-type dopant, tris(4-bromophenyl)ammoniumyl hexachloroantimonate, after which the network's crystallinity and orientation are maintained. Oriented, hole-doped OTPA-BDT COF films exhibit electrical conductivities of up to 1.2 × 10-1 S cm-1, which are among the highest reported for imine-linked 2D COFs to date.
RESUMO
Two-dimensional (2D) covalent organic frameworks (COFs) are composed of structurally precise, permanently porous, layered macromolecular sheets, which are traditionally synthesized as polycrystalline solids with crystalline domain lengths smaller than 100 nm. Here, we polymerize imine-linked 2D COFs as suspensions of faceted single crystals in as little as 5 min at moderate temperature and ambient pressure. Single crystals of two imine-linked 2D COFs were prepared, consisting of a rhombic 2D COF (TAPPy-PDA) and a hexagonal 2D COF (TAPB-DMPDA). The sizes of TAPPy-PDA and TAPB-DMPDA crystals were tuned from 720 nm to 4 µm and 450 nm to 20 µm in width, respectively. High-resolution transmission electron microscopy revealed that the COF crystals consist of layered, 2D polymers comprising single-crystalline domains. Continuous rotation electron diffraction resolved the unit cell and crystal structure of both COFs, which are single-crystalline in the a-b plane but disordered in the stacking c dimension. Single crystals of both COFs were incorporated into gas chromatography separation columns and exhibited unusual selective retention of cyclohexane over benzene, with single-crystalline TAPPy-PDA significantly outperforming single-crystalline TAPB-DMPDA. Polycrystalline TAPPy-PDA exhibited no separation, while polycrystalline TAPB-DMPDA exhibited poor separation and the opposite order of elution, retaining benzene more than cyclohexane, indicating the importance of improved material quality for COFs to exhibit properties that derive from their precise, crystalline structures. This work represents the first example of synthesizing imine-linked 2D COF single crystals at ambient pressure and short reaction times and demonstrates the promise of high-quality COFs for molecular separations.
RESUMO
As the features of microprocessors are miniaturized, low-dielectric-constant (low-k) materials are necessary to limit electronic crosstalk, charge build-up, and signal propagation delay. However, all known low-k dielectrics exhibit low thermal conductivities, which complicate heat dissipation in high-power-density chips. Two-dimensional (2D) covalent organic frameworks (COFs) combine immense permanent porosities, which lead to low dielectric permittivities, and periodic layered structures, which grant relatively high thermal conductivities. However, conventional synthetic routes produce 2D COFs that are unsuitable for the evaluation of these properties and integration into devices. Here, we report the fabrication of high-quality COF thin films, which enable thermoreflectance and impedance spectroscopy measurements. These measurements reveal that 2D COFs have high thermal conductivities (1 W m-1 K-1) with ultra-low dielectric permittivities (k = 1.6). These results show that oriented, layered 2D polymers are promising next-generation dielectric layers and that these molecularly precise materials offer tunable combinations of useful properties.
RESUMO
Covalent organic framework (COF) membranes are of great promise for energy-efficient separations. Thick, polycrystalline COF films have been reported to separate dyes, salts, bacteria, and nanoparticles on the basis of size-selective transport through ordered pores. Here, we show that these materials function as adsorbents, not as size-sieving membranes. Binding isotherms of several dyes typical of the COF membrane literature to three COF powder samples illustrate that COFs are high-capacity adsorbents with affinities that span a range of 3 orders of magnitude, trends which map onto previously reported separation behavior. Computational results suggest that observed differences in adsorption can be correlated to variable entropic gains driving the adsorption process. Polycrystalline COF pellets show volume-dependent and flow-rate dependent "rejection" of dyes, consistent with an adsorption-based removal mechanism. Previous reports of thick, polycrystalline COF membranes used low flow rates and small dye volumes to probe rejection capabilities, where membrane and adsorbent behavior is not distinguishable. A mixed dye separation experiment in flow shows affinity-dependent performance. These results necessitate a careful reexamination of the COF membrane literature, as separations based on differential transport through 2D COF pores remain an important yet unrealized frontier.
RESUMO
Covalent organic frameworks (COFs) are highly modular porous crystalline polymers that are of interest for applications such as charge-storage devices, nanofiltration membranes, and optoelectronic devices. COFs are typically synthesized as microcrystalline powders, which limits their performance in these applications, and their limited solubility precludes large-scale processing into more useful morphologies and devices. We report a general, scalable method to exfoliate two-dimensional imine-linked COF powders by temporarily protonating their linkages. The resulting suspensions were cast into continuous crystalline COF films up to 10â cm in diameter, with thicknesses ranging from 50â nm to 20â µm depending on the suspension composition, concentration, and casting protocol. Furthermore, we demonstrate that the film fabrication process proceeds through a partial depolymerization/repolymerization mechanism, providing mechanically robust films that can be easily separated from their substrates.
RESUMO
Programming the synthesis and self-assembly of molecules is a compelling strategy for the bottom-up fabrication of ordered materials. To this end, shape-persistent macrocycles were designed with alternating carbazoles and triazoles to program a one-pot synthesis and to bind large anions. The macrocycles bind anions that were once considered too weak to be coordinated, such as PF6 (-) , with surprisingly high affinities (ß2 =10(11) M(-2) in 80:20 chloroform/methanol) and positive cooperativity, α=(4â K2 /K1 )=1200. We also discovered that the macrocycles assemble into ultrathin films of hierarchically ordered tubes on graphite surfaces. The remarkable surface-templated self-assembly properties, as was observed by using scanning tunneling microscopy, are attributed to the complementary pairing of alternating triazoles and carbazoles inscribed into both the co-facial and edge-sharing seams that exist between shape-persistent macrocycles. The multilayer assembly is also consistent with the high degree of molecular self-association observed in solution, with self-association constants of K=300 000 M(-1) (chloroform/methanol 80:20). Scanning tunneling microscopy data also showed that surface assemblies readily sequester iodide anions from solution, modulating their assembly. This multifunctional macrocycle provides a foundation for materials composed of hierarchically organized and nanotubular self-assemblies.