Effect of dentin on the shear bond strength of different adhesive systems / Efeito do substrato dentinário na resistência de união ao cisalhamento de diferentes sistemas adesivos

Objective: This study assessed the shear bond strength of total-etch and self-etch adhesive systems to sound and caries-affected human dentin. Methods: The total-etch adhesive systems investigated were Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) and Single Bond (3M ESPE, St. Paul, MN, USA), and the self-etch adhesive systems were Clearfill SE Bond (Kuraray, Osaka, Japan) and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Eighty human teeth were used, 40 sound and 40 caries-affected (n=10). They were cut with a diamond disc to expose the dentinal surface and the adhesion area was standardized to 4 millimeters. Caries detector was used on the caries-affected4 teeth and the affected tissue was removed. The bond shear strength of different adhesives was tested on sound dentin (control group) and caries-affected dentin (experimental group). Z-100 composite resin cylinders were fabricated using a two-piece mold, and the specimens were stored in distilled water at 37°C for 24 hours, and submitted to the shear strength bond test using a crosshead speed of 0.5 mm/min. Results: The data were treated by analysis of variance and Tukey test and the significance level was set at 5%. Caries-affected dentin had a significant negative impact on the shear bond strength of total-etch adhesive systems. Conclusion: Shear bond strength depends on dentin status and type of adhesive system used.

Objetivo: Avaliar a resistência de união ao cisalhamento de sistemas adesivos de condicionamento ácido total e autocondicionantes em dentina humana hígida e afetada por cárie. Métodos: Os sistemas adesivos com etapa prévia de condicionamento ácido da estrutura dental utilizados foram: Scotchbond Multi Purpose Plus (3M ESPE, St. Paul, MN, USA) e Single Bond (3M ESPE, St. Paul, MN, USA), e os sistemas adesivos autocondicionantes: Clearfill SE Bond (Kuraray, Osaka, Japan) e Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA). Foram utilizados 80 dentes humanos, sendo 40 hígidos e 40 cariados (n=10), cortados com disco de diamante, expondo a superfície de dentina, e a área de adesão padronizada, em 4 mm de diâmetro. Para os dentes cariados, após corte inicial, estes eram corados com solução evidenciadora de cárie, e o tecido corado removido. Nos Grupos controle, os sistemas adesivos eram aplicados em dentina hígida, e nos Grupos experimentais, aplicados em dentina afetada por cárie. Confeccionaram--se cilindros de resina composta Z-100, com auxílio de matriz bipartida, os corpos-de-prova obtidos, armazenados em água destilada a 37°C por 24 horas, e submetidos ao ensaio de cisalhamento, a uma velocidade de 0,5 mm/min.Resultados: Foram submetidos à Análise de Variância, e ao teste de Tukey, ao nível de 5% de significância. Observou-se influência do fator substrato para os valores de resistência de união, diminuídos significantemente quando sistemas adesivos de condicionamento ácido total eram aplicados em dentina afetada por cárie. Conclusão: O presente estudo indicou que a resistência de união ao cisalhamento é dependente do tipo de dentina e do tipo de sistema adesivo utilizado.

Efeito de fontes de luz na microdureza de resinas compostas / Effect of light sources on the microhardness of composite resins

Objetivo: Avaliar a microdureza superficial de resinas compostas polimerizadas por diferentes fontes de luz. Métodos: Foram selecionadas três resinas compostas microhíbridas (Vit-l-escenceTM, Amelogen® Plus, Opallis) e uma nanoparticulada (FiltekTM Z350, 3M ESPE Dental Products, St. Paul, USA). Foram submetidas à polimerização utilizando-se um aparelho halógeno (Ultralux, Dabi Atlante, Ribeirão Preto, Brasil) com duas ponteiras, uma de vidro semi-orientada e outra de acrílico pintada e também um dispositivo à base de LED (UltraLume 2, Ultradent®, South Jordan, USA). Os corpos-de-prova obtidos a partir de uma matriz circular de alumínio, após receberem a resina composta, foram fotopolimerizados por 40 segundos e em seguida armazenados a seco por 24 horas. Decorrido esse período, procedeu-se ao ensaio de microdureza superficial Vickers, realizando-se quatro aferições na superfície de topo (dureza 1) e na superfície de base (dureza 2). Utilizou-se a análise de variância que foi complementada pelo teste de Newman-Keuls de comparações múltiplas de médias, ao nível de significância de 5%.Resultados: No topo, as menores médias de dureza foram obtidas com a resina Opallis submetida ao UltraLume 2 (Ultradent®, South Jordan, USA). As médias maiores referem-se ao compósito Vit-l-escenceTM (Ultradent®, South Jordan, USA) polimerizado com o Led UltraLume 2 (Ultradent®, South Jordan, USA) e luz halógena Ultralux PCP (Dabi Atlante, Ribeirão Preto, Brasil), seguidas da resina FiltekTM Z350 (3M ESPE Dental Products, St. Paul, USA) submetida ao UltraLume 2 (Ultradent®, South Jordan, USA). Quanto à base, a menor média de dureza também foi da resina composta Opallis (FGM, Santa Catarina, Brasil), sob ação do LED UltraLume 2 (Ultradent®, South Jordan, USA) e a maior da Vit-l-escenceTM (Ultradent®, South Jordan, USA), seguida pela Amelogen® Plus (Ultradent®, South Jordan, USA) quando polimerizada pelo Ultralux (Dabi Atlante, Ribeirão Preto, Brasil) com a ponta semi-orientada.Conclusão: O aparelho LED permitiu polimerização e consequentes valores de microdureza equivalentes ao dos aparelhos halógenos convencionais, para três dos quatro compósitos avaliados.

Objective: This study assessed the surface microhardness of compound resins cured by different light sources. Methods: Three micro hybrid (Vit-l-escenceTM, Amelogen® Plus, Opallis) and one nanoparticle (FiltekTM Z350, 3M ESPE Dental Products, St. Paul, USA) compound resins were selected. The resins were polymerized by a halogen light unit (Ultralux, Dabi Atlante, Ribeirão Preto, Brasil) with two tips, one semi-guided made of glass and another of painted acrylic and a LED-based source (UltraLume 2, Ultradent®, South Jordan, USA). Specimens constructed from a circular aluminum matrix were photopolymerized for 40 second after they received the compound resin and stored dry for 24 hours. After this period, a Vickers surface microhardness assay was performed, measuring the top (hardness 1) and base (hardness 2) surfaces four times each. Variance analyses were complemented by Newman-Keuls method, with significance set at 5%. Results: The Opallis (FGM, Santa Catarina, Brasil) resin subjected to UltraLume 2 (Ultradent®, South Jordan, USA) obtained the lowest mean hardness values for the top surface. The Vit-l-escenceTM (Ultradent®, South Jordan, USA) compound cured by Led UltraLume 2 (Ultradent®, South Jordan, USA) and by Ultralux PCP (Dabi Atlante, Ribeirão Preto, Brasil) halogen light obtained the highest mean hardness, followed by the FiltekTM Z350(3M ESPE Dental Products, St. Paul, USA) resin subjected to UltraLume 2 (Ultradent® South Jordan, USA). The Opallis (FGM, Santa Catarina, Brasil) resin cured by LED UltraLume 2 (Ultradent®, South Jordan, USA) also obtained the lowest mean hardness for the base surface and the Vit-l-escenceTM (Ultradent®, South Jordan, USA) resin obtained the highest value, followed by Amelogen® Plus, when cured by Ultralux (Dabi Atlante, Ribeirão Preto, Brasil) using the semi-guided tip. Conclusion: The polymerization and, consequently, the microhardness achieved by the LED unit was equivalent to those achieved by conventional halogen units for three of the four composites tested.

Influência de variações das normas estéticas na atratividade do sorriso / Influence of aesthetic norm variations on the attractiveness of a smile

Objetivo: Avaliar a influência de variações nas normas estéticas na percepção da atratividade do sorriso segundo dentistas e leigos. Métodos: Alterações digitais foram realizadas nos sorrisos de fotografias de dois indivíduos de sexos distintos. Foram criados 11 sorrisos para cada sexo: um sorriso ideal controle, sorriso ideal segundo normas consideradas e 10 sorrisos contendo variações individuais de cada uma das normas descritas a seguir: a) desvio de linha média 2mm e 3mm; b) linha do sorriso - linha do sorriso reta e linha do sorriso reversa; c) angulação incisivos laterais - 10º para mesial e 10º para distal; d) diastema: 0.5mm e 1mm e 5mm) proporção dental - proporção de Alber e proporção de Platão. As fotografias foram avaliadas por dois especialistas em Dentística e dois leigos, utilizando a escala visual analógica. Resultados: Foi observado que o sorriso ideal controle, em ambos os sexos e de acordo com ambos os grupos avaliadores, foi julgado favoravelmente; e que os sorrisos contendo variações estéticas receberam diferentes avaliações, algumas variações foram menos aceitas que outras. Nas avaliações realizadas foram encontradas concordâncias e discordâncias entre os avaliadores. Conclusão: Observou-se que a ausência de desvios favorece a percepção estética dos sorrisos, mas algumas variações estéticas são perceptivelmente aceitas em relação a outras e que para o sucesso dos tratamentos estéticos está condicionada a participação conjunta de dentistas e pacientes na fase do planejamento.

Objective: The work presented here aims to evaluate how aesthetic norm variations influence the perception of attractiveness of a smile according to dentists and laymen. Methods: The smiles in photographs of a man and a woman were digitally changed. Eleven smiles were created for each one: an ideal, control smile - an ideal smile according to accepted norms - and 10 smiles containing individual variations of each of the following norms: a) 2mm and 3mm deviations from the middle line; b) the contour of the smile - contour of a straight smile and contour of a reverse smile; c) the angle of the lateral incisors - a mesial angle of 10º and a distal angle of 10º; d) 0.5mm and 1mm diastema; and e) dental proportion - Alber´s Proportion and Plato´s Proportion. The photographs were evaluated by two specialists in cosmetic dentistry and two laymen using the visual analogue scale. Results: The ideal smile for both genders was well accepted by both the specialists and the laymen. The opinions on the smiles with aesthetic variations varied, some were more positive than others, some were in agreement and some were in disagreement. Conclusion: The absence of deviations favors the perceived beauty of a smile, but some aesthetic variations seem to be better accepted than others. The success of aesthetic treatments depends on the active participation of dentists and patients in the planning stage

Reabilitação estética de sorriso através de fechamento de diastemas associada ao controle de higiene bucal do paciente: relato de caso / Smile aesthetic rehabilitation by free spaces treatment associated to patient oral hygiene control: case report

A busca pela estética, por parte dos pacientes, aumentou muito nos últimos anos e cada vez mais os indivíduos procuram os consultórios odontológicos procurando soluções satisfatórias para a reabilitação estética de seus sorrisos. Várias são as técnicas e os materiais que podem ser utilizados para este fim, mas qualquer um destes que venha a ser escolhido pelos profissionais terá seu desempenho clínico e longevidade dependente dos cuidados do paciente no uso dessas restaurações, bem como da higiene bucal do mesmo no período pós-tratamento. Esse trabalho tem como objetivo mostrar o tratamento de diastemas em dentes anteriores com restaurações diretas de resina composta, discutindo normas estéticas para a confecção das mesmas e a adequação do meio bucal do paciente para o recebimento dessas restaurações, bem como o controle da higiene por parte do mesmo para a longevidade do trabalho profissional

Análise da eficácia de diferentes materiais utilizados como barreira cervical em clareamento endógeno / Analysis of the efficiency of different materials used as cervical barrier in endogenous bleaching

Objetivo: Avaliar a eficiência de três materiais usados na confecção do tampão cervical no procedimento clareador. Métodos: Foram utilizados 36 caninos humanos recém-extraídos e divididos em quatro grupos experimentais, de nove réplicas cada grupo. O grupo I foi o grupo controle, no qual não se realizou nenhum vedamento da região cervical; o grupo II corresponde ao tampão cervical feito pelo cimento de ionômero de vidro quimicamente ativado (Vidrion R); no grupo III utilizou-se o cimento de ionômero de vidro modificado por resina (Vitremer, 3M, Sumaré, Brasil) como tampão cervical; e no grupo IV foi utilizado o cimento restaurador temporário Coltosol. Uma pasta de perborato de sódio com peróxido de hidrogênio a 30% foi colocada na câmara pulpar por sete dias, seguido da colocação do corante para posterior avaliação da microinfiltração. Resultados: Os resultados obtidos entre os grupos experimentais foram estatisticamente significativos. Conclusão: O Coltosol foi o material mais efetivo contra a infiltração em direção apical. O Vitremer (3M, Sumaré, Brasil) ocupou a posição intermediária entre os grupos, e o Vidrion comportou-se melhor somente que o grupo controle, portanto, com precárias propriedades seladoras.

Objective: Evaluate the efficiency of three materials used for making the cervical buffer on the bleaching procedure. Methods: Thirty-six, recently extracted human canines were used, and divided into four experimental groups of nine replicas in each group. Group I was the control group, in which no sealing was done in the cervical region; Group II corresponded to the cervical buffer made by chemically activated glass ionomer cement (Vidrion R); in Group III resin-modified glass ionomer cement (Vitremer, 3M, Sumaré, Brazil) was used as the cervical buffer; and in Group IV Coltosol temporary restorative cement was used. A paste of sodium perborate and 30% hydrogen peroxide was placed in the pulp chamber for seven days, followed by placement of a dye to evaluate microleakage afterwards. Results: The results obtained among the experimental groups were statistically significant. Conclusion: That Coltosol was the most effective material against leakage in the apical direction. Vitremer (3M, Sumaré, Brazil) occupied the intermediate position among the groups, and Vidrion behave better than the control group only, therefore, with precarious sealing properties.

The influence of time interval between bleaching and enamel bonding.

OBJECTIVES: The purpose of this study was to investigate the penetration of a conventional adhesive material into enamel bleached with 16% carbamide peroxide and 38% hydrogen peroxide using optical light microscopy. METHODS: Extracted human teeth were randomly divided into eight experimental groups with six specimens each, according to the bleaching material and time interval after bleaching and before the bonding procedure. Groups were designated as follows: control group, restorations in unbleached teeth; restorations performed immediately after bleaching; restorations performed 7 days after bleaching; restorations performed 14 days after bleaching; and restorations performed 30 days after bleaching. The length of resin tags was measured with an Axiophot photomicroscope at 400x magnification for the calculation of the proportion of tags of study groups compared to the respective control groups. Analysis of variance was applied for comparison between groups; data were transformed into arcsine (p < 0.05). RESULTS: The specimens of experimental groups, in which restorations were performed 7, 14, and 30 days after bleaching, showed better penetration of adhesive material into enamel than specimens restored immediately after bleaching. There was no statistically significant difference between the bleaching materials employed or in the interaction between bleaching agent and time interval. CONCLUSIONS: This suggests that a time interval of at least 7 days should be allowed between enamel bleaching and placement of adhesive bonding agents for accomplishment of composite resin restorations. CLINICAL SIGNIFICANCE: Establishment of adequate time after bleaching is fundamental to allow the normal penetration of a one-bottle conventional adhesive onto the enamel surface.

Análise da rugosidade superficial de materiais restauradores estéticos: efeito de agentes clareadores e tempo / Analysis of roughness surface of aesthetic restoring materials: effect of bleaching agents and time

Este estudo in vitro avaliou o efeito de agentes clareadores na rugosidade superficial (Ra) de materiais restauradores estésticos, com o passar do tempo. Foram utilizadas duas resinas compostas, Z100 (MI) e Silux-Plus (M2), um compômero, Dyract (M3) e um inômero de vidro modificado por resina. Vitremer (M4), que foram expostos a dois agentes clareadores: Opalescence (CI), peróxido de carbamida 10% e Hi-Lite (C2), peróxido de hidrogênio 35% e como meio de imersão foi utilizada saliva artificial(Co). Foram confccionados 120 corpos de prova, sendo a Ra avaliada após 1 hora de confecção; e antes da imersão em saliva artificial (T0), após 1 dia (T1), 7 (T2), 15 (T3) e 30 (T4) dias de exposição aos agentes clareadores. No grupo controle, os corpos-de-prova ficaram somente imersos em saliva artificial. Após análise estatística de variância ANOVA (a=5%), teste de Tukey, e método da decomposição da soma de quadrados, foi possível concluir que: 1 - a Ra dos materiais restauradores estéticos, de forma geral, alterou-se após exposição aos diferentes agentes clareadores e ao longo do tempo; 2 - em função do material restaurador, M2 apresentou a maior média de Ra, seguido em ordem decrescente por M4, M3 e M1; 3 - C1 e C2 exerceram ação sobre a superfície dos materiais restauradores aumentando a Ra para todos os materiais avaliados, principalmente em M2 e M4; 4 - em função do fator tempo, observou-se influência estatísticamente significativa sobre a Ra, pois quanto maior o tempo de exposição ao agente clareador, maiores os valores médios de Ra

Efeito dos agentes clareadores sobre as estruturas dentais / Effects of dental bleaching on dental structures

A vaidade, muito mais do que o desejo de melhor mastigar, tem sido o motivodominante do desenvolvimento da Odontologia. Um dos problemas estéticos mais comuns é aalteração da cor dental. Com o intuito de satisfazer pacientes que desejam dentes brancos, oscirurgiões-dentistas têm oferecido um amplo espectro de tratamentos, que vão desde a coberturatotal dos dentes com resinas compostas ou porcelana até tratamentos mais conservadores como oclareamento dental, amplamente difundido pela mídia. Porém, muitos são os questionamentos oudúvidas relacionados ao efeito dos agentes clareadores. Sendo assim, este estudo tem por objetivoverificar, na literatura, os possíveis efeitos causados pelos agentes clareadores nas estruturas dentais(esmalte, dentina, cemento e polpa).

Vanity, much more than the desire of a more efficient mastication, has been the majortarget in Dentistry development. One of the most common esthetical problems is the alteration ofdental shade. In order to satisfy patients who wish for white teeth, dentists have provided a widevariation of treatments, ranging from total cover of the teeth with composite resins or porcelainto more conservative therapies such as dental bleaching, widely spread by the media. Even so,many are the questionaments or doubts related to the effect of the dental bleaching agents. Thus,the objective of this study is to verify, in dental literature, the possible effects caused by dentalbleaching agents on dental structures (enamel, dentin, cement and pulp).

Análise comparativa da translucidez do esmalte e de diferentes resinas compostas microparticuladas / Comparative analysis of enamel translucity and different microparticulated composite resins

Em função da atual exigência estética por parte dos pacientes e profissionais, novos materiais e técnicas têm sido desenvolvidos para que o resultado final das restaurações seja cada vez mais semelhante ao dente natural. Dentro deste contexto, a translucidez é uma das características mais difíceis de serem reproduzidas pelos materiais restauradores estéticos diretos. Por ser uma propriedade característica do esmalte encontram-se hoje no mercado resinas compostas específicas para a substituição desta estrutura. Assim, este trabalho tem como objetivo estudar comparativamente os diferentes níveis de translucidez das resinas compostas A110 e Durafill (A1, A2 e A3) e Vitalescence (TM, TY, TI, TS, TA, TG), com a translucidez de corpos-de-prova de esmalte. Pôde-se observar que todas as cores da resina composta Vitalescence apresentaram valores de translucidez muito acima dos valores encontrados para o esmalte e para as demais resinas, enquanto que as resinas compostas A110 e Durafill apresentaram valores estatisticamente semelhantes entre si e ao esmalte, com exceção para a cor A1 da resina Durafill, que se apresentou ligeiramente menos translúcida

Prótese adesiva biológica temporária - um recurso imediato: relato de um caso clínico / Temporary biological adhesive prosthesis - an immediate resource: a clinical case report

Os autores propöem a apresentaçäo de uma caso clínico, através da recuperaçäo imediata e temporária da estética, em decorrência da perda do elemento dental 11, fazendo-se uso de método simples, de baixo custo e de fácil manipulaçäo

Tratamento restaurador da fratura coronária em dente anterior pela técnica de colagem de fragmento / Restorative treatment of crown fracture on anterior teeth using direct bonding technique

A desarmonia estética em dentes anteriores pode ser causada por alteraçäo de cor, forma e tamanho do elemento dental, bem como pela presença de traumas provenientes de acidentes. No caso de fratura dental coronária, podem ser utilizadas como tratamento restaurador tanto a colagem do fragmento dental (autógeno e heterógeno) quanto restauraçöes diretas e indiretas. A colagem de fragmento autógeno é um procedimento viável para o restabelecimento funcional, morfológico e principalmente estético, tornando-se assim um tratamento restaurador de sucesso. Os autores descrevem um caso clínico desse tipo de colagem por meio de um guia espacial com a finalidade de auxiliar a adaptaçäo do fragmento ao remanescente dental. Concluem que esta técnica de colagem de fragmento é indicada por sua simplicidade e resultado estético satisfatório

Análise in vitro da adaptaçäo cervical em cavidades de classe II, restauradas com resina compactável: efeito de técnicas restauradoras / In vitro analysis of the cervical adaptation in class II, restorated with compactable resin: effect of restorative techniques

O propósito deste estudo foi analisar in vitro, através de MEV, a amplitude de fendas marginais cervicais em restauraçöes de classe II, restauradas com resina composta compactável P60 (3M), variando-se diferentes técnicas restauradoras. Foram realizadas 54 cavidades tipo slot nas superfícies M e D de 27 dentes pré-molares hígidos, com todas as margens cervicais localizadas em esmalte. Os preparos foram executados com o auxílio de máquina de padronizaçäo. As cavidades foram restauradas através de incrementos. O adesivo utilizado para todos os grupos foi o Single Bond (3M). Os dentes foram divididos em três grupos, a saber: Grupo T1 - restaurado com resina P60, seguindo as recomendaçöes do fabricante; Grupo T2 - resina P60 associada à ponta fotocondensadora transparente (TDV); Grupo T3 - utilizaçäo de resina fluida Flow-It (Jeneric/Pentron) + resina P60 + ponta fotocondensadora transparente. Após a restauraçäo, os dentes foram armazenados em saliva artificial por sete dias, submetidos à ciclagem térmica (500 ciclos, 5ºC - 55ºC), e entäo seccionados no sentido mésio-distal. Após análise e obtençäo das fotomicrografias em MEV, referentes à regiäo em estudo, a amplitude da fenda cervical foi mensurada. Os resultados foram submetidos à análise estatística de Kruskall-Wallis, e podemos concluir que: 1 - nenhuma das técnicas restauradoras impediu o desenvolvimento de fendas na parede cervical; 2 - o grupo T2, que utilizou a ponta fotocondensadora transparente, apresentou os melhores resultados, estatisticamente significantes, na reduçäo da fenda marginal cervical, quando comparado aos grupos T1 e T3; 3 - o grupo que se utilizou da associaçäo da resina fluida (grupo T3) apresentou os maiores índices de amplitude de fenda marginal

Estudo da microinfiltraçäo marginal em restauraçöes de amálgama aderido: efeito do verniz cavitário, cimento de ionômero de vidro e sistemas adesivos / Study of marginal microleakage in adhesive amalgam restoration: effects of cavity varnish, glass ionomer cement and adhesive system

Este trabalho teve como objetivo avaliar comparativamente in vitro a microinfiltraçäo marginal, nas margens oclusal e cervical de restauraçöes de Classe V, restauradas com amálgama quando da utilizaçäo do verniz cavitário, cimento de ionômero de vidro e sistema adesivo dentinário. Concluímos que: 1) nenhum material intermediário foi capaz de controlar a infiltraçäo marginal; 2) os materiais adesivos apresentaram melhor comportamento no controle da microinfiltraçäo marginal; 3) na parede oclusal os materiais intermediários apresentaram comportamento estatisticamente diferente onde G4>G3>G1>G2; 4) na parede cervical os materiais intermediários apresentaram comportamento estatisticamente diferente onde G4>G3>G2>G1

Associaçäo de pinos intrarradiculares pré-fabricados e cerômeros na restauraçäo de dentes tratados endodonticamente / Association of pre-fabricated intra-root posts and ceromers in the endodontically treated teeth restoration

O uso de pinos pré-fabricados em dentes tratados endodonticamente tem sido uma excelente alternativa, pois estes têm como principais vantagens o seu emprego relativamente simples e execuçäo com menor tempo de trabalho clínico, podendo ser realizado em única sessäo. O objetivo da restauraçäo de dentes tratados endodonticamente é reproduzir características naturais, devolvendo ao dente a estética e a funçäo mastigatória. Os autores descrevem a técnica de utilizaçäo do pino intrarradicular Unimetric© (Maillefer) e realizaçäo de uma coroa total com o sistema Artglass© (Kulzer)

Estudo da resistência de uniäo ao cisalhamento de diferentes sistemas adesivos à dentina / Shear bond strength of different dentin bonding systems

Foi avaliada, in vitro, a influência do condicionamento dentinário na resistência de uniäo ao cisalhamento de cinco sistemas adesivos, quando aplicados em dentina condicionada, ou näo, com substâncias ácidas. Foram utilizados neste estudo, o ácido fosfórico a 10 por cento e 37 por cento, o ácido maleico a 10 por cento e os sistemas adesivos Prisma Universal Bond 3 (PUB3), Scotchbond MultiUso (SBMU), Multi-Bond Alpha (MBA), All Bond 2 (AB2) e Pró-Bond (PB). Os testes estatísticos, aplicados aos valores de resistência de uniäo observados, permitiram concluir que os tratamentos dentinários com ácido fosfórico a 10 por cento e 37 por cento, assim como com o ácido maleico a 10 por cento, determinaram um melhor desempenho dos sistemas adesivos em comparaçäo com o obtido em tecido dentinário que näo foi submetido ao condicionamento ácido

Colagem de dente anterior fraturado: relato de caso clínico / Dental bonding of fractured anterior tooth: a clinical case report

Com o advento da técnica do condicionamento ácido do esmalte com Buonocore em 1955, e posterior surgimento das resinas compostas e sistemas adesivos, os dentes anteriores fraturados passaram a ser restaurados de uma forma mais conservadora, uma vez que menor quantidade de tecido dental sadio é desgastado durante o preparo, mais simples, rápida e estética

Reforço de dente anterior utilizando pinos estéticos cerâmicos associado com núcleo de resina composta / Reinforcement of the upper central incisor using ceramics post associated to composite resin core

Após tratamento endodôntico, é aconselhável o tratamento pré-protético da estrutura dental debilitada remanescente, para evitar possíveis fraturas. Os sistemas de postes intra-radiculares estabilizam a estrutura dental debilitada pelo tratamento endodôntico. Combinados com a confecção de núcleos coronários, aumentam a retenção para posterior fixação da restauração protética. Os sistemas de pinos metálicos intra-radiculares e de núcleos coronários metálicos podem ser criticados por razões de estética e biocompatibilidade. Os produtos resultantes da corrosão das ligas metálicas podem promover pigmentações em tecidos duros e moles e podem causar irritações gengivais. Estes inconvenientes prejudicam o efeito estético de qualquer tipo de restauração. As estéticas gengival e dental assumem grande importância principalmente em restaurações estéticas enteriores com sistemas de cerâmica sem metal (por ex. IPS Empress, In Ceram) e com os novos cerômeros translúcidos (por ex. Targis/Vectris, Artglass, Solidex, etc.) Para estes casos, o poste intra-radicular de Dióxido de zircônio (cerâmica) constitui a solução ideal

Recuperação estética através de colagem heterógena corono-radicular, faceta e recontorno / Esthetic resolution through heterogeneous bonding root-coronal, laminate and recontourn

Os autores descrevem uma nova opção de técnica restauradora para dentes anteriores, tratados endodonticamente, através da colagem Heterógena de fragmento dental corono-radicular, associado a procediemtos como o clareamento dental, facetamento e o recontorno estético

Avaliaçäo da infiltraçäo marginal do cimento de ionômero de vidro em cavidades de classe V: efeito de tratamento de secagem da dentina / Marginal leakage evaluation of glass ionomer cement in class V cavities: effect of the treatment of dentinal drying

Foi analisada a infiltraçäo marginal, a nível cervical e oclusal, de cavidades de Classe V executadas em pré-molares humanos e restauradas com Cimento de Ionômero de Vidro quimicamente ativado e fotoativado. As cavidades, antes de serem restauradas, foram submetidas a dois diferentes tratamentos de secagem dentinária. Para verificaçäo da infiltraçäo marginal, as amostras foram submetidas à ciclagem térmica, em uma soluçäo evidenciadora de Rodamina B a 0,2 por cento, realizando um total de 200 ciclos. A avaliaçäo da infiltraçäo marginal foi determinada através de escores e os dados obtidos submetidos à análise estatística näo-paramétrica de Wilcoxon. De acordo com os resultados, os dois materiais avaliados apresentaram estatisticamente o mesmo comportamento, independentemente do tratamento de secagem efetuado, concluindo que a diferença de tratamento de secagem dentinária näo influenciou na determinaçäo da infiltraçäo marginal