RESUMO
Purpose: The purpose of this study was to synthesize and structurally characterize four ant nest membranes in four different concentrations and determine the best concentration that could potentially be used as an alternative material for the production of new collagen barrier membranes. Materials and Methods: Membranes were created by mixing ant nest extracts at various concentrations of 0.5%, 1%, 1.5%, and 2%, as well as collagen, chitosan, and Polyvinyl Alcohol (PVA) using a film casting. A Universal Testing Machine (UTM) was used to evaluate mechanical properties including elastic modulus, tensile strength, maximum elongation, elongation at break, and maximum force. Water absorption was performed, FTIR was used for functional group identification, and morphology was examined using SEM. Additionally, EDS was used to identify the composition and distribution of elements in membranes. Statistical analysis was conducted using ANOVA (analysis of variance) and post hoc testing with a significance level of p <0.01 for quantitative data. Results: The results showed that the mechanical properties produced the following mean (standard deviation): elastic modulus 0.87 Mpa (0.11), tensile strength 16.32 N/mm2 (2.46), maximum elongation 4.96% (1.72), elongation at break 5.23% (1.87), and maximum force 22.50 N (5.06). The average water absorption capacity of all four membranes had a p-value <0.01. FTIR spectrum showed various peaks corresponding to functional groups, while SEM results indicated a homogeneous mixture. EDS analysis confirmed that the addition of ant plant extract at 0.5%, 1%, and 1.5% resulted in the presence of elements C, O, and Ca. Meanwhile, membranes prepared with 2% concentration had a different composition, namely C, O, Ca, and Na. Conclusion: Increasing the concentration of ant nest affects the values of the membrane's mechanical properties parameters, including the elastic modulus (0.87 Mpa), tensile strength (16.32 N/mm2), maximum elongation (4.96%), elongation at break (5.23%), and maximum force (22.50 N). The average membrane absorption of water (p value <0.01) was also affected. SEM images showed homogeneous mixing, and membrane EDS results consisted of C, O, and Ca composition. However, there was no effect on FTIR functional groups. The anthill membrane with a 1% concentration has the potential to serve as an alternative membrane in guided tissue regeneration.
RESUMO
Aim: This study aims to evaluate the clinical assessment results of periimplant soft tissue with morse taper (internal abutment connection). Methods: The study was conducted using a rapid review by searching the articles from PubMed NCBI and Cochrane by using keywords. All articles were selected by the year, duplication, title, abstract, full-text, and finally, all selected articles were processed for final review. Following clinical parameters were included; Periimplant Probing Pocket Depth (PPD), Plaque Score (PS), modified Plaque Index (mPI), Mucosal Thickness (MTh), Gingival Height (GH), periimplant mucosal zenith, Pink Esthetic Score (PES), Bleeding On Probing (BOP), Sulcus Bleeding Index (SBI), and modified Gingival Index (mGI). Results: 9 selected articles were obtained from the initial literature searching count of 70 articles. The overall samples included 326 morse taper implants. Based on the evaluation, 3 out of 4 articles reported pocket depth < 4 mm, no bleeding was reported in 2 out of 4 articles. 4 out of 4 articles reported low plaque accumulation, low soft tissue recession was reported in 3 out of 3 articles, and 4 out of 4 articles reported acceptable PES values. Conclusion: The evaluations indicate that the morse taper (internal abutment connection) has favorable assessment results based on various clinical parameters