Effect of Tooth Brushing Cycles and Dentifrice Fluoride Concentration on a Glazed CAD/CAM Ceramic.

PURPOSE: To evaluate the effect of tooth brushing and dentifrice fluoride (F-) concentration on changes in color and translucency (ΔE00 and ΔT00, respectively), surface gloss (GS), surface roughness (Sa), and microstructure of a glazed CAD/CAM ceramic. MATERIALS AND METHODS: Ceramic blocks (e.max/CAD) were sectioned into rectangular plates (14 x 12 x 1 mm), and one surface of each sample was glazed. Samples were divided into three groups according to the F- concentration in the dentifrice (0, 1,100, and 5,000 µg/g) and were then subjected to 60,000 tooth brushing cycles. Luminosity and color were measured using a spectrophotometer at baseline and after every 20,000 cycles to obtain their ΔE00 and ΔT00 values. Another set of samples was prepared to measure the GS with a gloss meter and the Sa with a confocal laser microscope. The GS and Sa results were subjected to analysis of variance, Tukey test, and Dunnett test (α = .05). RESULTS: After 60,000 tooth brushing cycles, all of the variables were clinically acceptable, and there were no significant differences in the ΔE00, ΔT00, GS, or Sa among the fluoridated dentifrices. The GS values decreased significantly as the number of tooth brushing cycles increased. CONCLUSION: The ΔE00, ΔT00, GS, and Sa values were all clinically acceptable after the glazed e.max/CAD ceramic had been subjected to 60,000 tooth brushing cycles with dentifrices containing up to 5,000 µg/g of F-.

Effect of build orientation in gloss, roughness and color of 3D-printed resins for provisional indirect restorations.

OBJECTIVES: The purpose of this study was to evaluate the effect of build orientation of 3D-printed provisional resins (3DRs) on gloss (Gs), surface roughness (Sa), maximum profile valley depth (Rv), and color difference (∆E00). METHODS: PMMA CAD/CAM blocks (Vita Temp/Vita) were sectioned and served as a Control. Four 3DRs (Cosmos-SLA/Yller, Cosmos-DLP/Yller, PriZma-Bioprov/Makertech, Nanolab/Wilcos) were obtained as discs (15-mm diameter, 2.5-mm thickness) in three orientations (0°, 45°, and 90°) using different 3D printers (Form 2/Formlabs, P30/Straumann, Hunter/Flashforge, W3D/Wilcos, respectively). Samples were then cleaned with isopropyl alcohol prior to post-curing in specific post-curing units. Half of the samples' surface was covered with an adhesive tape and submitted to 10,000 toothbrushing (TB) cycles. The Gs and Sa at the brushed and not brushed surfaces were evaluated with a glossmeter (Novo-curve) and a laser confocal microscope (OLS5000) (n = 10), which also obtained the Rv and 3D representative images of the interface between not brushed and brushed surfaces. Electron microscopy images of the surface of some samples was also performed (n = 3). On another set of samples (n = 5), the coordinates of luminosity and color were obtained with a spectrophotometer (Easyshade V) at baseline and after 16.7 h and 200 h of UVB aging, to calculate the ∆E00 using CIEDE:2000 formula. Additionally, 3DRs photoinitiators were identified using a minispectrometer (USB2000 +) (n = 5). Data of Gs and Sa were submitted to three-way-, Rv to two-way-, and ∆E00 to mixed-ANOVA tests, followed by Tukey's test (α = 0.05). For all variables, results from experimental groups were compared to control using Dunnett's test (α = 0.05). Student's t-test was used to compare the control at different TB cycles (Gs, Sa) or aging periods (∆E00) (α = 0.05). RESULTS: Build orientation of 3DRs did not influence any of the variables studied. The 10,000 TB cycles resulted in a decrease in Gs and increase in Sa for all resins tested. The control showed higher Gs after 10,000 TB cycles than Cosmos-SLA and Nanolab resins. Compared to all 3DRs, Control presented lower ∆E00 after 200 h of UVB aging. All 3DRs presented higher ∆E00 than the clinically acceptable after 200 h of UVB aging. Lucirin® TPO was identified in all 3DRs, although PriZma might also present other photoinitiators and Nanolab might present Irgacure 369. SIGNIFICANCE: Alterations in build orientation are very useful and frequently performed in the day-today of 3D-printing, thus its effect in the optical properties and in the topography of 3D-printed restorations is very relevant. For the evaluated 3D-printed provisional resins, build orientation did not influence any of the variables studied (Gs, Sa, Rv, and ∆E00), even after toothbrushing cycles and UVB aging.

Doppler echocardiography in a healthy, non-sedated Southern Sea Lion (Otaria flavescens) - a preliminary approach about the feasibility and clinical utility.

Echocardiography is commonly used in veterinary clinical practice for many species but is not as easily applied in non-sedated marine mammals. Additionally, Doppler echocardiography provides further information on hemodynamics, estimation of cardiac output, characterization of flow patterns, and diastolic function. However, its applications in marine mammals have not been as widely explored either. The present report aimed to characterize the left ventricle structure and function of the Southern Sea Lion (Otaria flavescens) through a Doppler echocardiography study. Data were obtained from a healthy animal trained for different veterinary examination routines. This communication constitutes the first report of Doppler echocardiography with stroke volume, and cardiac output measurement in pinnipeds, and the first report of measurement of myocardial performance index in aquatic mammals. This data brought initial information about in vivo structure and function of the heart of the Southern Sea Lion that can be safely and effectively evaluated with the use of transthoracic Doppler echocardiography. Our data have both clinical and research implications for future studies evaluating diseases of the cardiopulmonary system in pinnipeds, and cardiovascular physiology investigation in diving mammals.

Effect of build orientation in accuracy, flexural modulus, flexural strength, and microhardness of 3D-Printed resins for provisional restorations.

PURPOSE: This study evaluated the effects of 3D-printing build orientation on accuracy, flexural modulus (FM), flexural strength (FS), and microhardness of selected, commercial 3D-printed provisional resins (3DRs). MATERIAL AND METHODS: PMMA CAD/CAM provisional material (Vita Temp/Vita) served as Control. Four 3DRs (Cosmos-SLA/Yller, Cosmos-DLP/Yller, PriZma-Bioprov/Makertech, Nanolab/Wilcos) were used in three printing orientations (0°, 45°, and 90°). Printed samples were cleaned with isopropyl alcohol prior to post-curing in specific post-curing units. For each group, 20 bar-shaped samples (25 × 2x2 mm) and ten disc-shaped samples (15-mm diameter, 2.5-mm thick) were obtained. The dimensions of bar samples were measured and the mean percent errors were compared to the reference (digital) values to obtain "accuracy" (n = 20). Samples were then aged in distilled water at 37 °C and half were submitted to a three-point bend test in a universal testing machine after 24 h and the other half after 1 year (n = 10). Disc samples were polished prior to microhardness evaluation (n = 10). Microstructure and elemental composition of filler particles in the 3DRs were analyzed using scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS) (n = 3). Accuracy and microhardness were submitted to two way-, and FM and FS to three way-ANOVA, followed by Tukey's tests. Results of experimental groups were compared to a milled PMMA Control using Dunnett's tests, and Student's t-tests compared FM and FS to Control at different aging periods (α = 0.05). RESULTS: Except for Cosmos-DLP, the 90° orientation demonstrated the best overall accuracy in all dimensions evaluated. The overall accuracy of Cosmos-SLA was not significantly different from Control and higher than other 3DRs. The FM of all 3DRs was lower than Control, regardless of orientation and aging period. After 1 year of aging, FS of 45°-Cosmos-SLA and all orientations of PriZma were not different from Control, while 90°-Cosmos-SLA was higher. Build orientation had no influence on microhardness of the 3DRs: Nanolab was the only resin harder than Control. Very few nanometric spherical filler particles were found in Cosmos-SLA, Cosmos-DLP, and PriZma, while Nanolab presented higher number of particles having irregular shapes and sizes. CONCLUSIONS: In general, although build orientation did not influence microhardness results, the 90° -orientation resulted in the best overall accuracy for most 3DRs. After 1-year water storage, Cosmos-SLA printed vertically showed the highest FS, while the PMMA Control obtained the highest FM for both aging periods.

First description of the Burmeister porpoise (Phocoena spinipinnis) electrocardiogram.

The aim of this study was to make the first characterization of the electrocardiogram (ECG) of the Burmeister porpoise (Phocoena sipinipinnis). A total of three ECGs were made in one, wild juvenile female (body weight = 32.5 kg, Lt = 1.45 m), temporarily held in captivity for rehabilitation at Mar del Plata Aquarium (Argentina). For ECG recordings, the animal was removed from its pool on a stretcher under constant veterinary supervision. A traditional six-lead system in the frontal plane was used, with the typical four "extremities" electrodes positioned bilaterally. ECGs were readable and all waves were detectable. The QRS complexes were characterized by Q wave absence in all leads. The ECG characteristically displayed distinctly defined STs, with a T wave clearly differentiated from the QRS complex. An STs elevation was detected in leads II and III. The mean electrical axis was -79°, meaning a cranial left axis orientation. The animal showed normal sinus rhythm and heart rate (HR) showed a continuous oscillation between tachycardia and bradycardia. Mean HR from all recordings was 147.02 ± 24.95 bpm (range = 71-176, n = 178). Evidence of the occurrence of respiratory sinus arrhythmia was detected through HR variations and RR interval differences, which suggested an adequate cardiovascular system compensation to handling conditions. This study has reported ECG amplitude and duration measurements of a potentially healthy specimen, which represents the starting point for the determination of normal ECG values for this species. Also, it has confirmed that ECG is a valuable noninvasive tool for rapid cardiac health assessment in small cetaceans.

Color alterations, flexural strength, and microhardness of 3D printed resins for fixed provisional restoration using different post-curing times.

OBJECTIVES: To evaluate the effect of post-curing times on the color change, flexural strength (FS), modulus (FM) and microhardness at different depths of four 3D printed resins. MATERIALS AND METHODS: A characterization of the light emitted by 3D-resin post-curing unit (Wash and Cure 2.0, Anycubic) was performed. The tested 3D printed resins were Cosmos Temp3D (COS), SmartPrint BioTemp (SM) Resilab3D Temp (RES) and Prizma3D BioProv (PRI) were evaluated under five different post-curing conditions (no post-curing or 5-, 10-, 15, and 20 min of post-curing). For color change analysis, 10 mm diameter x 1 mm thick discs (n = 7) were printed, and the luminosity, color and translucency were measured before post-curing as control, and repeatedly after 5 min cycles of post-curing until a total of 20 min was reached for ΔE00 [CIED2000 (1:1:1)] calculation. For FS and FM, 25 × 2×2 mm (n = 10, for each post-curing time) 3D printed bars were subjected to a 3-point being test. Knoop microhardness (KHN) was measured transversally on 5 × 5×5 mm blocks (n = 10, for each post-curing time). Color results were analyzed by one-way repeated measures ANOVA (factor: color change). FS and FM were analyzed by two-way ANOVA (factors: Material*Post-Curing Time). KHN was analyzed individually for each material by two-way ANOVA (factors: Depth*Post-Curing Time). RESULTS: The post-curing time significantly influenced the ΔE00, FS, FM and KHN of all the evaluated materials. COS and SMA presented ΔE00 values above the acceptability threshold after 5 and 10 min of post-curing, respectively. The FS of RES reached a plateau after 5 min of post-curing, and for PRI and SMA, the FS stabilized after 10 min of post-curing. The post-curing process improved the KHN of the tested materials, and longer exposure periods were associated to higher KHN values at all the evaluated depths. SIGNIFICANCE: A fine adjustment of the post-curing time is crucial to produce adequate mechanical properties in 3D-printed restorative resins, while minimizing the color alterations on the restorations. For the evaluated resins, 5-10 min of post-curing will result in adequate mechanical properties, without affecting the acceptability in the color of the material. However, the results are material-dependent, and evaluation of each specific resin is advised.

Comparison of the operative time and presence of voids of incremental and bulk-filling techniques on Class II composite restorations.

OBJECTIVES: To compare the operative time and presence of air voids on Class II restorations fabricated by dental practitioners with 1 to 5 years of experience using incremental and bulk-filling techniques. METHOD AND MATERIALS: Four techniques were evaluated: incremental, bulk-filling, bulk-filling with heated composite, and snowplow technique. Standardized mandibular first molars with a MOD (mesial, occlusal, and distal) cavity were used. Voluntary operators made two restorations using each technique and the time required for each restoration was recorded. The restorations were scanned by micro-computed tomography to calculate the volume of the restoration occupied by air voids. The "operative time" and "volume of air voids" were analyzed individually by two-way ANOVA and Tukey HSD post hoc (α = .05) for the factors operator and insertion technique. A correlation between "operative time" and "volume of air voids" was evaluated using Pearson coefficient (α = .05). RESULTS: The incremental technique required significantly longer time, yet no differences were observed between the bulk-filling techniques. There were no significant differences between techniques regarding the volume of air voids. A significant, but weak, and inverse linear correlation (P = .0059; r = -.29; r2 = 8.41%) was found between the operative time and volume of air voids. CONCLUSION: There were no significant differences in the volume of air voids among the evaluated techniques, although bulk-filling techniques required a shorter operative time. Hence, implementing bulk-filling techniques by dental schools and restorative dental practitioners with different levels of expertise may reduce chair time and produce a volume of air voids similar to the incremental technique.

Tomografia computadorizada das cavidades naso-sinusais: Algumas ocorrências interessantes / Comouterized tomography of the nasal & paranasal cavities: some intersting ocurrences

No estudo das cavidades naso-sinusais por tomografia computadorizada, o especialista pode encontrar ocorrências interessantes por sua raridade ou por seu valor especial como ilustração de uma determinada patologia ou peculiaridade anatômica. Em ambos os casos, o especialista sente a compulsão de exibilas aos colegas, principalmente àqueles que se iniciam no assunto, quer radiologistas, quer otorrinos. Na presente comunicação são apresentadas nove de tais ocorrências, das quais cinco por terem sido consideradas raras (mucocele gigante da concha nasal média, pneumatização da concha nasal inferior, encefalomeningocele basal transetmoidal (intranasal) congênita, pneumatização do septo nasal pelo seio frontal, peumatização extensa do assoalho da órbita