RESUMO
In this study, the effect of graphene oxide nanosheets (GONs) embedded in a thin-film composite (TFC) polyamide (PA) membrane on the acid resistance of the membrane was investigated by comparison with the effect of oxidized single-walled carbon nanotubes (o-SWNTs). Both GONs and o-SWNTs increased the hydrophilicity of the membranes and caused the formation of ridges and clustered bumps on the surfaces, resulting in slightly improved water permeability. However, the o-SWNTs-embedded membrane did not show a difference in acid resistance depending on the concentration of embedded material, but the acid resistance of the GONs-embedded membrane increased with increasing concentration. The acid resistance of the GONs-embedded membranes appears to be mainly due to the barrier effect caused by the nanosheet shape of the GONs along with a sacrificial role of the PA layer protruded by the addition of GONs and the decrease of acid reaction sites by the hydrogen bonding between GONs and PA. When the TFC PA membrane was prepared with a high amount (300 ppm) of the GONs without considering aggregation of GONs, membrane selectivity exceeding 95% was maintained 4.7 times longer than the control TFC membrane. This study shows that the acid resistance can be enhanced by the use of GONs, which give a barrier effect to the membrane.
RESUMO
Membrane fouling remains a critical factor limiting the widespread use of membrane processes in water and wastewater treatment. To mitigate membrane fouling, we introduced a patterned morphology on the membrane surface using a lithographic method. A modified immersion precipitation method was developed to relieve the formation of dense layer at the solvent-nonsolvent interface, that is, the opposite side of the patterned surface. Diverse patterned membranes, such as pyramid-, prism-, and embossing-patterned membranes, were prepared and compared with a flat membrane in terms of morphology, permeability, and biofouling. Patterned membrane fidelity was largely dependent on the polymer concentration in cast solution. The patterned surface augmented the water flux in proportion to the roughness factor of the patterned membrane. However, the type of pattern did not affect substantially the mean pore size on the patterned surface. Deposition of microbial cells on the patterned membrane was significantly reduced compared to that on the flat membrane in the membrane bioreactor (MBR) for wastewater treatment. This was attributed to hydraulic resistance of the apex of the patterned surface, which induced local turbulence.