Oxidation of Ceramic Materials Based on HfB2-SiC under the Influence of Supersonic CO2 Jets and Additional Laser Heating.

The features of oxidation of ultra-high-temperature ceramic material HfB2-30 vol.%SiC modified with 1 vol.% graphene as a result of supersonic flow of dissociated CO2 (generated with the use of high-frequency induction plasmatron), as well as under the influence of combined heating by high-speed CO2 jets and ytterbium laser radiation, were studied for the first time. It was found that the addition of laser radiation leads to local heating of the central region from ~1750 to ~2000-2200 °C; the observed temperature difference between the central region and the periphery of ~300-550 °C did not lead to cracking and destruction of the sample. Oxidized surfaces and cross sections of HfB2-SiC-CG ceramics with and without laser heating were investigated using X-ray phase analysis, Raman spectroscopy and scanning electron microscopy with local elemental analysis. During oxidation by supersonic flow of dissociated CO2, a multilayer near-surface region similar to that formed under the influence of high-speed dissociated air flows was formed. An increase in surface temperature with the addition of laser heating from 1750-1790 to 2000-2200 °C (short term, within 2 min) led to a two to threefold increase in the thickness of the degraded near-surface area of ceramics from 165 to 380 microns. The experimental results indicate promising applications of ceramic materials based on HfB2-SiC as part of high-speed flying vehicles in planetary atmospheres predominantly composed of CO2 (e.g., Venus and Mars).

Investigation of the Effect of Supersonic Flow of Dissociated Nitrogen on ZrB2-HfB2-SiC Ceramics Doped with 10 vol.% Carbon Nanotubes.

The method of fabricating dense ultra-high temperature ceramic materials ZrB2−HfB2−SiC−CCNT was developed using a combination of sol-gel synthesis and reaction hot pressing approaches at 1800 °C. It was found that the introduction of multilayer nanotubes (10 vol.%) led to an increase in the consolidation efficiency of ceramics (at temperatures > 1600 °C). The obtained ZrB2−HfB2−SiC and ZrB2−HfB2−SiC−CCNT materials were characterized by a complex of physical and chemical analysis methods. A study of the effects on the modified sample ZrB2−HfB2−SiC−CCNT composition speed flow of partially dissociated nitrogen, using a high-frequency plasmatron, showed that, despite the relatively low temperature established on the surface (≤1585 °C), there was a significant change in the chemical composition and surface microstructure: in the near-surface layer, zirconium−hafnium carbonitride, amorphous boron nitride, and carbon were present. The latter caused changes in crucial characteristics such as the emission coefficient and surface catalyticity.