Atomic layer deposition assisted non-destructive strategy for cleaning Ag dendrites based SERS substrates.

Ag dendrites have recently been widely reported due to their excellent surface-enhanced Raman scattering (SERS) properties. However, prepared pristine Ag dendrites are usually contaminated by organic impurities, which has a huge negative impact on their Raman detection and greatly limits their practical applications. In this paper, we reported a facile strategy to obtain clean Ag dendrites by high temperature decomposition of organic impurities. With the assistance of ultra-thin coating via atomic layer deposition (ALD), the nanostructure of Ag dendrites can be retained at high temperature. SERS activity can be recovered after etching ALD coating. Chemical composition tests indicate that the organic impurities can be effectively removed. As a result, the clean Ag dendrites can obtain more clearly discernible Raman peaks and lower limits of detection than the pristine Ag dendrites. Furthermore, it was demonstrated that this strategy is also applicable to clean other substrates, such as gold nanoparticles. Therefore, high temperature annealing with the help of ALD sacrifice coating is a promising and non-destructive strategy to clean the SERS substrates.

Atomic layer deposition assisted fabrication of large-scale metal nanogaps for surface enhanced Raman scattering.

Metal nanogaps can confine electromagnetic field into extremely small volumes, exhibiting strong surface plasmon resonance effect. Therefore, metal nanogaps show great prospects in enhancing light-matter interaction. However, it is still challenging to fabricate large-scale (centimeter scale) nanogaps with precise control of gap size at nanoscale, limiting the practical applications of metal nanogaps. In this work, we proposed a facile and economic strategy to fabricate large-scale sub-10 nm Ag nanogaps by the combination of atomic layer deposition (ALD) and mechanical rolling. The plasmonic nanogaps can be formed in the compacted Ag film by the sacrificial Al2O3deposited via ALD. The size of nanogaps are determined by the twice thickness of Al2O3with nanometric control. Raman results show that SERS activity depends closely on the nanogap size, and 4 nm Ag nanogaps exhibit the best SERS activity. By combining with other porous metal substrates, various sub-10 nm metal nanogaps can be fabricated over large scale. Therefore, this strategy will have significant implications for the preparation of nanogaps and enhanced spectroscopy.