RESUMO
Phototransistor using 2D semiconductor as the channel material has shown promising potential for high sensitivity photo detection. The high photoresponsivity is often attributed to the photogating effect, where photo excited holes are trapped at the gate dielectric interface that provides additional gate electric field to enhance channel charge carrier density. Gate dielectric material and its deposition processing conditions can have great effect on the interface states. Here, we use HfO2gate dielectric with proper thermal annealing to demonstrate a high photoresponsivity MoS2phototransistor. When HfO2is annealed in H2atmosphere, the photoresponsivity is enhanced by an order of magnitude as compared with that of a phototransistor using HfO2without annealing or annealed in Ar atmosphere. The enhancement is attributed to the hole trapping states introduced at HfO2interface through H2annealing process, which greatly enhances photogating effect. The phototransistor exhibits a very large photoresponsivity of 1.1 × 107A W-1and photogain of 3.3 × 107under low light illumination intensity. This study provides a processing technique to fabricate highly sensitive phototransistor for low optical power detection.
RESUMO
High activity catalysts for hydrogen evolution reaction (HER) play a key role in converting renewable electricity to storable hydrogen fuel. Great effort has been devoted to the search for noble metal free catalysts to make electrolysis viable for practical applications. Here, a non-precious metal oxide/metal catalyst with high intrinsic activity comparable to Pt/C was reported. The electrocatalyst consisting of NiO, Ni(OH)2 , Cr2 O3 , and Ni metal exhibits a low overpotential of 27, 103, and 153â mV at current densities of 10, 100, and 200â mA cm-2 , respectively, in a 1.0â m NaOH electrolyte. The activity is much higher than that of NiOx /Ni or Cr2 O3 alone, showing the synergistic effect of NiOx /Ni and Cr2 O3 on catalyzing HER. Density functional theory calculations shows that NiO and Cr2 O3 on Ni surface lower the disassociation energy barrier for breaking H-OH bond, while Ni(OH)2 and Cr2 O3 create preferred sites on Ni surface with near-zero H* adsorption free energy to promote H* to gaseous H2 evolution. These synergistic effects of multiple-oxides/metal composition enhance the disassociation of H-OH and the evolution of H* to gaseous H2 , thus achieving high activity and demonstrating a promising composition design for noble metal free catalyst.