An atomic-scale evaluation of the fracture toughness of silica glass.

Using an atomistic technique consistent with continuum balance laws and drawing on classical fracture mechanics theory, we estimate the resistance to fracture propagation of amorphous silica. We discuss correspondence and deviations from classical linear elastic fracture mechanics theory including size dependence, rigid/floppy modes of deformation, and the effects of surface energy and stress.

Interaction of NaOH solutions with silica surfaces.

HYPOTHESIS: Sodium adsorption on silica surfaces depends on the solution counter-ion. Here, we use NaOH solutions to investigate basic environments. SIMULATIONS: Sodium adsorption on hydroxylated silica surfaces from NaOH solutions were investigated through molecular dynamics with a dissociative force field, allowing for the development of secondary molecular species. FINDINGS: Across the NaOH concentrations (0.01 M - 1.0 M), ∼50% of the Na+ ions were concentrated in the surface region, developing silica surface charges between - 0.01 C/m2 (0.01 M NaOH) and - 0.76 C/m2 (1.0 M NaOH) due to surface site deprotonation. Five inner-sphere adsorption complexes were identified, including monodentate, bidentate, and tridentate configurations and two additional structures, with Na+ ions coordinated by bridging oxygen and hydroxyl groups or water molecules. Coordination of Na+ ions by bridging oxygen atoms indicates partial or complete incorporation of Na+ ions into the silica surface. Residence time analysis identified that Na+ ions coordinated by bridging oxygen atoms stayed adsorbed onto the surface four times longer than the mono/bi/tridentate species, indicating formation of relatively stable and persistent Na+ ion adsorption structures. Such inner-sphere complexes form only at NaOH concentrations of > 0.5 M. Na+ adsorption and lifetimes have implications for the stability of silica surfaces.

Surface Structure and Stability of Partially Hydroxylated Silica Surfaces.

Surface energies of silicates influence crack propagation during brittle fracture and decrease with surface relaxation caused by annealing and hydroxylation. Molecular-level simulations are particularly suited for the investigation of surface processes. In this work, classical MD simulations of silica surfaces are performed with two force fields (ClayFF and ReaxFF) to investigate the effect of force field reactivity on surface structure and energy as a function of surface hydroxylation. An unhydroxylated fracture surface energy of 5.1 J/m2 is calculated with the ClayFF force field, and 2.0 J/m2 is calculated for the ReaxFF force field. The ClayFF surface energies are consistent with the experimental results from double cantilever beam fracture tests (4.5 J/m2), whereas ReaxFF underestimated these surface energies. Surface relaxation via annealing and hydroxylation was performed by creating a low-energy equilibrium surface. Annealing condensed neighboring siloxane bonds increased the surface connectivity, and decreased the surface energies by 0.2 J/m2 for ClayFF and 0.8 J/m2 for ReaxFF. Posthydroxylation surface energies decreased further to 4.6 J/m2 with the ClayFF force field and to 0.2 J/m2 with the ReaxFF force field. Experimental equilibrium surface energies are ∼0.35 J/m2, consistent with the ReaxFF force field. Although neither force field was capable of replicating both the fracture and equilibrium surface energies reported from experiment, each was consistent with one of these conditions. Therefore, future computational investigations that rely on accurate surface energy values should consider the surface state of the system and select the appropriate force field.