Influence of the Silver Content on Mechanical Properties of Ti-Cu-Ag Thin Films.

In this work, the ternary titanium, copper, and silver (Ti-Cu-Ag) system is investigated as a potential candidate for the production of mechanically robust biomedical thin films. The coatings are produced by physical vapor deposition-magnetron sputtering (MS-PVD). The composite thin films are deposited on a silicon (100) substrate. The ratio between Ti and Cu was approximately kept one, with the variation of the Ag content between 10 and 35 at.%, while the power on the targets is changed during each deposition to get the desired Ag content. Thin film characterization is performed by X-ray diffraction (XRD), nanoindentation (modulus and hardness), to quantitatively evaluate the scratch adhesion, and atomic force microscopy to determine the surface topography. The residual stresses are measured by focused ion beam and digital image correlation method (FIB-DIC). The produced Ti-Cu-Ag thin films appear to be smooth, uniformly thick, and exhibit amorphous structure for the Ag contents lower than 25 at.%, with a transition to partially crystalline structure for higher Ag concentrations. The Ti-Cu control film shows higher values of 124.5 GPa and 7.85 GPa for modulus and hardness, respectively. There is a clear trend of continuous decrease in the modulus and hardness with the increase of Ag content, as lowest value of 105.5 GPa and 6 GPa for 35 at.% Ag containing thin films. In particular, a transition from the compressive (-36.5 MPa) to tensile residual stresses between 229 MPa and 288 MPa are observed with an increasing Ag content. The obtained results suggest that the Ag concentration should not exceed 25 at.%, in order to avoid an excessive reduction of the modulus and hardness with maintaining (at the same time) the potential for an increase of the antibacterial properties. In summary, Ti-Cu-Ag thin films shows characteristic mechanical properties that can be used to improve the properties of biomedical implants such as Ti-alloys and stainless steel.

Biomimetic hard and tough nanoceramic Ti-Al-N film with self-assembled six-level hierarchy.

Nature uses self-assembly of a fairly limited selection of components to build hard and tough protective tissues like nacre and enamel. The resulting hierarchical micro/nanostructures provide decisive toughening mechanisms while preserving strength. However, to mimic microstructural and mechanical characteristics of natural materials in application-relevant synthetic nanostructures has proven to be difficult. Here, we demonstrate a biomimetic synthesis strategy, based on chemical vapour deposition technology, employed to fabricate a protective high-temperature resistant nanostructured ceramic TiAlN thin film with six levels of hierarchy. By using just two variants of gaseous precursors and through bottom-up self-assembly, an irregularly arranged hard and tough multilayer stack was formed, consisting of hard sublayers with herringbone micrograins, separated by tough interlayers with spherical nanograins, respectively composed of lamellar nanostructures of alternating coherent/incoherent, hard/tough, single-/poly-crystalline platelets. Micro- and nanomechanical testing, performed in situ in scanning and transmission electron microscopes, manifests intrinsic toughening mechanisms mediated by five types of interfaces resulting in intergranular, transgranular and cleavage fracture modes with zigzag-like crack patterns at multiple length-scales. The hierarchical 2.7 µm thick film self-assembled during ∼15 minutes of deposition time shows hardness, fracture stress and toughness of ∼31 GPa, ∼7.9 GPa and ∼4.7 MPa m0.5, respectively, as well as phase/microstructural thermal stability up to ∼950/900 °C. The film's microstructural and mechanical characteristics represent a milestone in the production of protective and wear-resistant thin films.

Antibacterial Silicon Oxide Thin Films Doped with Zinc and Copper Grown by Atmospheric Pressure Plasma Chemical Vapor Deposition.

Zn-doped and Cu-doped SiOx films were synthesized by atmospheric pressure plasma chemical vapor deposition to study their antibacterial efficiency against Gram-negative Escherichia coli and their cytotoxic effect on the growth of mouse cells. Zn-rich and Cu-rich particles with diameters up to several microns were found to be homogeneously distributed within the SiOx films. For both doping elements, bacteria are killed within the first three hours after exposure to the film surface. In contrast, mouse cells grow well on the surfaces of both film types, with a slight inhibition present only after the first day of exposure. The obtained results indicate that the films show a high potential for use as effective antibacterial surfaces for medical applications.

In-situ Observation of Cross-Sectional Microstructural Changes and Stress Distributions in Fracturing TiN Thin Film during Nanoindentation.

Load-displacement curves measured during indentation experiments on thin films depend on non-homogeneous intrinsic film microstructure and residual stress gradients as well as on their changes during indenter penetration into the material. To date, microstructural changes and local stress concentrations resulting in plastic deformation and fracture were quantified exclusively using numerical models which suffer from poor knowledge of size dependent material properties and the unknown intrinsic gradients. Here, we report the first in-situ characterization of microstructural changes and multi-axial stress distributions in a wedge-indented 9 µm thick nanocrystalline TiN film volume performed using synchrotron cross-sectional X-ray nanodiffraction. During the indentation, needle-like TiN crystallites are tilted up to 15 degrees away from the indenter axis in the imprint area and strongly anisotropic diffraction peak broadening indicates strain variation within the X-ray nanoprobe caused by gradients of giant compressive stresses. The morphology of the multiaxial stress distributions with local concentrations up to -16.5 GPa correlate well with the observed fracture modes. The crack growth is influenced decisively by the film microstructure, especially by the micro- and nano-scopic interfaces. This novel experimental approach offers the capability to interpret indentation response and indenter imprint morphology of small graded nanostructured features.

X-ray analysis of residual stress gradients in TiN coatings by a Laplace space approach and cross-sectional nanodiffraction: a critical comparison.

Novel scanning synchrotron cross-sectional nanobeam and conventional laboratory as well as synchrotron Laplace X-ray diffraction methods are used to characterize residual stresses in exemplary 11.5 µm-thick TiN coatings. Both real and Laplace space approaches reveal a homogeneous tensile stress state and a very pronounced compressive stress gradient in as-deposited and blasted coatings, respectively. The unique capabilities of the cross-sectional approach operating with a beam size of 100 nm in diameter allow the analysis of stress variation with sub-micrometre resolution at arbitrary depths and the correlation of the stress evolution with the local coating microstructure. Finally, advantages and disadvantages of both approaches are extensively discussed.