Thin and flexible solid-state electrolyte (SSE) films with high ionic conductivity and low interfacial resistance are urgently required for lithium metal batteries (LMBs). However, it's still challenging to reduce the film thickness to <20 µm, especially for those with high ceramic contents. Herein, a facile slurry casting method is developed to prepare the ultra-thin (14 µm) Li3Zr2Si2PO12 (LZSP) films with ceramic content up to 91% using a composite polymer binder, polyvinylidene fluoride (PVDF), and polyethylene oxide (PEO). It shows that PEO not only enhanced the film flexibility but also makes it be easily peeled off to form a freestanding membrane, PLN. To promote the interfacial ion transport, PEO/lithium bis(trifluoromethylsulfonyl)imide (LiTFSI) is introduced to the film surface, and the resultant tri-layer film, PPLN, shows a satisfying room temperature ionic conductivity of 0.116 mS cm-1, high Li+ transference number of 0.79, and good compatibility with metal lithium. As a result, LMBs using LiFePO4 cathode and PPLN electrolyte exhibit excellent safety as well as electrochemical performances in the wide temperature range between room temperature (RT) and 100 °C.
RESUMO
Controllable synthesis of electrode materials with desirable morphology and size is of significant importance and challenging for high-performance supercapacitors. Herein, we propose an efficient hydrothermal approach to controllable synthesis of hierarchical porous three-dimensional (3D) ZnCo2O4 composite films directly on Ni foam substrates. The composite films consisted of two-dimensional (2D) nanosheets array anchored with one-dimensional (1D) nanowires. The morphologies of ZnCo2O4 arrays can be easily controlled by adjusting the concentration of NH4F. The effect of NH4F in the formation of these 3D hierarchical porous ZnCo2O4 nanosheets@nanowires films is systematically investigated based on the NH4F-independent experiments. This unique 3D hierarchical structure can help enlarge the electroactive surface area, accelerate the ion and electron transfer, and accommodate structural strain. The as-prepared hierarchical porous ZnCo2O4 nanosheets@nanowires films exhibited inspiring electrochemical performance with high specific capacitance of 1289.6 and 743.2 F g-1 at the current density of 1 and 30 A g-1, respectively, and a remarkable long cycle stability with 86.8% capacity retention after 10 000 cycles at the current density of 1 A g-1. Furthermore, the assembled asymmetric supercapacitor using the as-prepared ZnCo2O4 nanosheets@nanowires films as the positive electrode and active carbon as negative electrode delivered a high energy density of 39.7 W h kg-1 at a power density of 400 W kg-1. Our results show that these unique hierarchical porous 3D ZnCo2O4 nanosheets@nanowires films are promising candidates as high-performance electrodes for energy storage applications.