Improving Buried Interface Contact by Bidentate Anchoring for Inverted Perovskite Solar Cells.

Nickel oxide (NiOx) is a promising hole transport layer (HTL) to fabricate efficient and large-scale inverted perovskite solar cells (PSCs) due to its low cost and superior chemical stability. However, inverted PSCs based on NiOx are still lagging behind that of other HTL because of the poor quality of buried interface contact. Herein, a bidentate ligand, 4,6-bis (diphenylphosphino) phenoxazine (2DPP), is used to regulate the NiOx surface and perovskite buried interface. The diphosphine Lewis base in the 2DPP molecule can coordinate both with NiOx and lead ions at NiOx/perovskite interface, leading to high-quality perovskite films with minimized defects. It is found that the inverted PSCs with 2DPP-modified buried interface exhibit double advantages of being both fast charge extraction and reduced nonradiative recombination, which is a combination of multiple factors including favorable energetic alignment, improved interface contact and strong binding between NiOx/2DPP and perovskite. The optimal PSC based on 2DPP modification yields a champion power conversion efficiency (PCE) of 21.9%. The unencapsulated PSC maintains above 75% of its initial PCE in the air with a relative humidity (RH) of 30-40% for 1000 h.

Controllable Fabrication of Vertical Graphene with Tunable Growth Nature by Remote Plasma-Enhanced Chemical Vapor Deposition.

As an important member of the graphene family, vertical graphene (VG) has broad applications like field emission, energy storage, and sensors owing to its fascinating physical and chemical properties. Among various fabrication methods for VG, plasma enhanced chemical vapor deposition (PECVD) is most employed because of the fast growth rate at relatively low temperature for the high-quality VG. However, to date, relations between growth manner of VG and growth parameters such as growth temperature, dosage of gaseous carbon source, and electric power to generate plasma are still less known, which in turn hinder the massive production of VG for further applications. In this study, the growth behavior of VG was studied as functions of temperature, plasma power, and gas composition (or chamber pressure). It was found that the growth behavior of VG is sensitive to the growth conditions mentioned above. Although conditions with high growth temperature, large flow rate of mixed gas of methane and carrier gases, and high plasma power may be helpful for the fast growth of VG, brunching of VG is simultaneously enhanced, which in turn decreases the vertical growth nature of VG. High-quality VG can be achieved by optimizing the growth parameters. It was revealed that the vertical growth nature of VG is governed by the electric field at the interfacial layer between VG and the substrate, for which its strength is influenced by the density of plasma. These findings are important for the general understanding of the VG growth and provided a feasible way for the controllable fabrication of VG using the remote PECVD method which is usually believed to be unsuitable for the fabrication of VG.

Graphene-enhanced intermolecular interaction at interface between copper- and cobalt-phthalocyanines.

Interfacial electronic structures of copper-phthalocyanine (CuPc), cobalt-phthalocyanine (CoPc), and graphene were investigated experimentally by using photoelectron spectroscopy. While the CuPc/graphene interface shows flat band structure and negligible interfacial dipole indicating quite weak molecule-substrate interaction, the CuPc/CoPc/graphene interface shows a large interfacial dipole and obvious energy level bending. Controlled experiments ruled out possible influences from the change in film structure of CuPc and pure π-π interaction between CoPc and CuPc. Analysis based on X-ray photoelectron spectroscopy and density functional theory reveals that the decrease in the work function for the CuPc/CoPc/graphene system is induced by the intermolecular interaction between CuPc and CoPc which is enhanced owning to the peculiar electronic properties at the CoPc-graphene interface.

The effects of oxygen on controlling the number of carbon layers in the chemical vapor deposition of graphene on a nickel substrate.

While oxygen is typically considered undesirable during the chemical vapor deposition (CVD) of graphene on metal substrates, we demonstrate that suitable amounts of oxygen in the CVD system can in fact improve the uniformity and thickness control of the graphene film. The role of oxygen on the CVD of graphene on a nickel substrate using a propylene precursor was investigated with various surface analytical techniques. It was found that the number of carbon layers in the deposited graphene sample decreases as the concentration of oxygen increases. In particular, single-layer graphene can be easily obtained with an oxygen/propylene ratio of 1/9. In the presence of oxygen, a thin layer of nickel oxide will form on the substrate. The oxide layer decreases the concentration of carbon atoms dissolved in the nickel substrate and results in graphene samples with a decreasing number of carbon layers.