RESUMO
Borosilicate glasses are widely used for radioactive waste disposal due to their ability to incorporate a variety of contaminants and radionuclides while exhibiting high durability in various disposal scenarios. This research evaluated the dissolution of borosilicate glass using both single-pass-flow-through (ASTM C1662-18) and product consistency test (ASTM C1285-21) methods with different solutions, including a cementitious-contacted water (called grout-contacted, GC, from this point) and solutions with varying levels of dissolved cementitious species such as Si, Ca, Al. The results indicated that the presence of Ca plays a crucial role in suppressing glass corrosion, as evidenced by the slower normalized dissolution rates, which were one order of magnitude lower for boron and two orders of magnitude lower for rhenium, observed in both Ca-amended and GC solutions compared to the pH 12 buffer solution. This effect is attributed to the formation of a dense, low-porosity, and strongly bonded calcium silicate hydrate (CSH) layer on the glass surface, which implies that a glass corrosion process is influenced by ion exchange involving alkali ions Na+, K+, Ca2+, and hydrogen-containing species. A small number of glass particles treated in the GC solution showed minor corrosion pits in the form of shallow craters with an average diameter of approximately 500 µm. This observation is correlated with a significant reduction, 2000 to 3000 times lower, in the cumulative volume of glass pores, indicating that smaller pore voids were "sealed" in the presence of Ca2+ ions, likely attributed to the formation of CSH precipitation or other corrosion products such as calcium carbonate saturated from the grout solution. These findings suggest that the presence of dissolved Ca in the GC solution can slow down the dissolution of borosilicate glass, contrary to the expected trend of higher dissolution rates resulting from exposure to high alkaline and thus higher pH solutions.
RESUMO
In this study, we report the synthesis of a new cubic neodymium-rhenium metallic alloy NdRe2 through the utilization of high pressure and laser heating in a diamond anvil cell. NdRe2 crystallizes in the Fd3¯m space group with a lattice parameter equal to 7.486 (2) Å and Z = 8 at 24 (1) GPa and 2,200 (100) K. It was studied using high-pressure single-crystal X-ray diffraction. The compound crystallizes in the cubic MgCu2 structure type. Its successful synthesis further proves that high-pressure high-temperature conditions can be used to obtain alloys holding a Laves phase structure. Ab initio calculations were done to predict the mechanical properties of the material. We also discuss the usage of extreme conditions to synthesize and study materials present in the nuclear waste.
RESUMO
The novel structure of lanthanum hydroxyborate La2B2O5(OH)2 was synthesized by the reaction of partially hydrolyzed lanthanum and boron oxide in a diamond anvil cell under high-pressure/high-temperature (HPHT) conditions of 30 GPa and â¼2,400 K. The single-crystal X-ray structure determination of the lanthanum hydroxyborate revealed: P3¯c1, a = 6.555(2) Å, c = 17.485(8) Å, Z = 6, R1 = 0.056. The three-dimensional structure consists of discrete planar BO3 groups and three crystallographically different La ions: one is surrounded by 9, one by 10, and one by 12 oxygen anions. The band gap was estimated using ab initio calculations to be 4.64 eV at ambient pressure and 5.26 eV at 30 GPa. The current work describes the novel HPHT lanthanum hydroxyborate with potential application as a deep-ultraviolet birefringent material.
RESUMO
Human Immunodeficiency Virus Type 1 (HIV-1) remains one of the leading causes of death worldwide. Present combination antiretroviral therapy has substantially improved HIV-1 related pathology. However, delivery of therapeutic agents to the HIV reservoir organ like Central nervous system (CNS) remains a major challenge primarily due to the ineffective transmigration of drugs through Blood Brain Barrier (BBB). The recent advent of nanomedicine-based drug delivery has stimulated the development of innovative systems for drug delivery. In this regard, particular focus has been given to nanodiamond due to its natural biocompatibility and non-toxic nature-making it a more efficient drug carrier than other carbon-based materials. Considering its potential and importance, we have characterized unmodified and surface-modified (-COOH and -NH2) nanodiamond for its capacity to load the anti-HIV-1 drug efavirenz and cytotoxicity, in vitro. Overall, our study has established that unmodified nanodiamond conjugated drug formulation has significantly higher drug loading capacity than surface-modified nanodiamond with minimum toxicity. Further, this nanodrug formulation was characterized by its drug dissolution profile, transmigration through the BBB, and its therapeutic efficacy. The present biological characterizations provide a foundation for further study of in-vivo pharmacokinetics and pharmacodynamics of nanodiamond-based anti-HIV drugs.
Assuntos
Fármacos Anti-HIV/farmacologia , Fármacos Anti-HIV/farmacocinética , Benzoxazinas/farmacologia , Benzoxazinas/farmacocinética , Portadores de Fármacos/metabolismo , Nanodiamantes , Alcinos , Astrócitos/efeitos dos fármacos , Astrócitos/metabolismo , Sobrevivência Celular/efeitos dos fármacos , Células Cultivadas , Ciclopropanos , Portadores de Fármacos/toxicidade , Células Endoteliais/efeitos dos fármacos , Células Endoteliais/metabolismo , Humanos , Macrófagos/efeitos dos fármacos , Macrófagos/virologia , Neurônios/efeitos dos fármacos , Neurônios/fisiologiaRESUMO
Pseudo-negative compressibility in layered materials is a phenomenon typically limited to in situ high-pressure experiments in some clay minerals and carbon-based materials. We show that the MXene Ti3C2T x expands along its crystallographic c direction when compressed in the presence of H2O. This expansive effect occurs when a mixture of powders and excess water is quasi-hydrostatically compressed in a diamond anvil cell; it also occurs to a much larger extent when powders are pressed uniaxially into discs and, notably, persists after pressure is released. We attribute the expansion to the insertion of H2O molecules and have identified shear-induced slipping of the nanosheets comprising multilayered MXene particles as a possible cause of this behavior in the latter case. This both has implications for the processing of MXenes and contributes to the field of materials with pseudo-negative compressibility by adding a new member for further investigation.
RESUMO
Modern ab initio calculations predict ionic and superionic states in highly compressed water and ammonia. The prediction apparently contradicts state-of-the-art experimentally established phase diagrams overwhelmingly dominated by molecular phases. Here we present experimental evidence that the threshold pressure of ~120 GPa induces in molecular ammonia the process of autoionization to yet experimentally unknown ionic compound--ammonium amide. Our supplementary theoretical simulations provide valuable insight into the mechanism of autoionization showing no hydrogen bond symmetrization along the transformation path, a remarkably small energy barrier between competing phases and the impact of structural rearrangement contribution on the overall conversion rate. This discovery is bridging theory and experiment thus opening new possibilities for studying molecular interactions in hydrogen-bonded systems. Experimental knowledge on this novel ionic phase of ammonia also provides strong motivation for reconsideration of the theory of molecular ice layers formation and dynamics in giant gas planets.
RESUMO
We have studied the structural stability of NaBH(4) under pressures up to 17 GPa and temperatures up to 673 K in a diamond anvil cell and formed an extended high P-T phase diagram using combined synchrotron x-ray diffraction and Raman spectroscopy. Even though few reports on phase diagram of NaBH(4) are found in current literature, up to our knowledge this is the first experimental work using diamond anvil cell in a wide pressure/temperature range. Bulk modulus, its temperature dependence, and thermal expansion coefficient for the ambient cubic phase of NaBH(4) are found to be 18.76(1) GPa, -0.0131 GPa K(-1), and 12.5x10(-5)+23.2x10(-8) T/K, respectively. We have also carried out Raman spectroscopic studies at room temperature up to 30 GPa to reinvestigate the phase transitions observed for NaBH(4). A comparative symmetry analysis also has been carried out for different phases of NaBH(4).
Assuntos
Boroidretos/química , Pressão , Temperatura , Análise Espectral Raman , Difração de Raios XRESUMO
Ammonia borane, NH(3)BH(3), has attracted significant interest as a promising candidate material for hydrogen storage. The effect of pressure on the bonding in NH(3)BH(3) was investigated using Raman spectroscopy to over 20 GPa in a diamond anvil cell, and two new transitions were observed at approximately 5 and 12 GPa. Vibrational frequencies for the modes of the NH(3) proton donor group exhibited negative pressure dependence, which is consistent with the behavior of conventional hydrogen bonds, while the vibrational frequencies of the BH(3) proton acceptor group showed positive pressure dependence. The observed behavior of these stretching modes supports the presence of dihydrogen bonding at high pressure. In addition, the BH(3) and NH(3) bending modes showed an increase in spectral complexity with increasing pressure together with a discontinuity in d nu/d P which suggests rotational disorder in this molecule. These results may provide guidance for understanding and developing improved hydrogen storage materials.