Modified Buckwheat Husk as a Filler for Urea-Formaldehyde Resin in Plywood Production.

The aim of the presented research was to determine the suitability of both non-modified and modified buckwheat husk (BH) as a filler for urea-formaldehyde adhesive in plywood production. The effect of two modification methods, acetylation and silanization, was investigated. Infrared spectroscopy outcomes confirmed that both acetylation and silanization of the filler had occurred. Based on the results, it was found that the introduction of BH had a significant effect on both the adhesive properties and the characteristics of the manufactured plywood. The application of non-modified husks led to a reduction in viscosity and an extension of the gelation time, and the produced plywood boards were characterized by reduced bonding quality and increased delamination. Modification of the husk surface by acetylation and silanization with 3-aminopropyltriethoxysilane contributed to the noticeable improvement in the resin properties. On the other hand, the improvement in plywood properties, consisting of the increase in bonding quality and reduced delamination, was observed only in the case of the silanized husk. Furthermore, the use of non-modified and acetylated husk did not significantly influence the formaldehyde emission. The reduction in the investigated emission of formaldehyde was observed only in the case of variants containing 15 and 20% of silanized buckwheat husk.

Optimization of Isocyanate Content in PF/pMDI Adhesive for the Production of High-Performing Particleboards.

Due to the fact that impregnation with fire retardant usually reduces the strength of the produced particleboards, this research was carried out to investigate whether it is possible to use phenol-formaldehyde (PF) resin modified using various amounts (0%, 5%, 10%, 15%, and 20%) of polymeric 4,4'-methylene diphenyl diisocyanate (pMDI) for this purpose. The need to optimize the addition of pMDI is particularly important due to health and environmental aspects and high price. Furthermore, the curing process of hybrid resins is still not fully explained, especially in the case of small loadings. Manufactured particleboards differed in the share of impregnated particles (50% and 100%). The mixture of potassium carbonate and urea was used as the impregnating solution. Based on the outcomes of hybrid resins properties, it was found that the addition of pMDI leads to the increase in solid content, pH, and viscosity of the mixtures, to the improvement in resin reactivity determined using differential scanning calorimetry and to the decrease in thermal stability in the cured state evaluated using thermogravimetric analysis. Moreover, particleboard property results have shown that using impregnated particles (both 50% and 100%) decreased the strength of manufactured boards bonded using neat PF resin. However, the introduction of pMDI allowed us to compensate for the negative impact of fire-retardant-treated wood and it was found that the optimal loading of pMDI for the board containing 50% of impregnated particles is 5% and for board made entirely of treated wood it is 10%.

Properties of Particle Boards Containing Polymer Waste.

Nowadays, a significant increase in interest in renewable energy sources can be observed. Wind farms have been one of the solutions representing this trend for many years. One of the important elements of windmills is the blades. The data indicate that what to do with the blades after their use is a global problem, and so it is important to find a way to recycle them. Hence, this work aimed to use these blades in the production of wood-based materials. Two fractions of a fragmented blade were used for the tests: a small one and large one. Boards characterized by densities of 650 kg/m3 and 700 kg/m3 were produced, in which the assumed substitution of the wood material with a polymer was 20% or 40%. Mechanical properties such as bending strength (MOR), modulus of elasticity (MOE), and internal bond strength (IB) were investigated. The 2S65 variant achieved the highest static bending strength and a modulus of elasticity of 2625 N/mm2. The second best result was noted for the 4S65 variant, which was significantly different from the 2S65 variant. In the case of the variants with a density of 700 kg/m3, no significant differences were found and their results were significantly lower. Moreover, research on thickness swelling (TS) after 24 h of immersion and water absorption (WA) were also conducted. The obtained results indicate that the manufactured boards are characterized by good physical and mechanical properties.

Wood-Based Materials in Building.

Wood is a widely used building material [...].

Morphological Features of PUR-Wood Particle Composite Foams.

The aim of this study was to apply waste wood particles (WP) with different sizes from primary wood processing as a filler for open-cell PUR foams. For this purpose, various wood particle sizes were added as a filler for polyurethane foams (PUR). The effects of the addition of of 0.05−<0.125 mm, 0.125−<0.315 mm, 0.315−1.25 mm, and >1.25−2.0 of WP to the polyurethane matrix on the density, the kinetics of PUR foaming, the cell structure, and the morphology were investigated. Scanning electron microscope (SEM) and X-ray computer tomography were used. Based on the results, it was found that the addition of WP in the amount of 10% leads to an increase in density with an increase in particle size. The research shows that the morphology of the PUR-WP foam is influenced by its particle size. The difference in the number and size of cells in PUR-WP composites depends on the wood particle size. The addition of dust causes the formation of cells of much smaller sizes; confirmed by SEM images. Moreover, computer tomography clearly demonstrates that the WP are well-dispersed within the foams' structures.

Properties of Rigid Polyurethane Foam Filled with Sawdust from Primary Wood Processing.

In this study, the possibility of using sawdust, a by-product of primary wood processing, as a filler (WF) for rigid polyurethane (PUR) foams was investigated. The effects of the addition of 5, 10, 15 and 20% of WF particles to the polyurethane matrix on the foaming process, cell structure and selected physical-mechanical properties such as density, thermal conductivity, dimensional stability, water absorption, brittleness, compressive and bending strengths were evaluated. Based on the results, it was found that the addition of WF in the amount of up to 10% does not significantly affect the kinetics of the foam foaming process, allowing the reduction of their thermal conductivity, significantly reducing brittleness and maintaining high dimensional stability. On the other hand, such an amount of WF causes a slight decrease in the compressive strength of the foam, a decrease in its bending strength and an increase in water absorption. However, it is important that in spite of the observed decrease in the values of these parameters, the obtained results are satisfactory and consistent with the parameters of insulation materials based on rigid PUR foam, currently available on the market.

The Effect of Periodic Loading of Glued Laminated Beams on Their Static Bending Strength.

Engineered wood products (EWP) such as glulam beams are gaining more and more popularity due to several advantages resulting from the wood itself, as well as the constant search for structural materials of natural origin. However, building materials face some requirements regarding their strength. Thus, the study aimed to assess the static bending strength of structural beams produced with the use of pine wood, after the periodic loading of approximately 80 kN for a year. The manufactured beams differed in the type of facing layers, i.e., pine timber with a high modulus of elasticity and plywood. The produced beams, regardless of their structure, are characterized by a similar static bending strength. Moreover, it has been shown that the loading of beams in the range of about 45% of their immediate capacity does not significantly affect their static bending strength and linear modulus of elasticity.

Waste Wood Particles from Primary Wood Processing as a Filler of Insulation PUR Foams.

A significant part of the work carried out so far in the field of production of biocomposite polyurethane foams (PUR) with the use of various types of lignocellulosic fillers mainly concerns rigid PUR foams with a closed-cell structure. In this work, the possibility of using waste wood particles (WP) from primary wood processing as a filler for PUR foams with open-cell structure was investigated. For this purpose, a wood particle fraction of 0.315-1.25 mm was added to the foam in concentrations of 0, 5, 10, 15 and 20%. The foaming course of the modified PUR foams (PUR-WP) was characterized on the basis of the duration of the process' successive stages at the maximum foaming temperature. In order to explain the observed phenomena, a cellular structure was characterized using microscopic analysis such as SEM and light microscope. Computed tomography was also applied to determine the distribution of wood particles in PUR-WP materials. It was observed that the addition of WP to the open-cell PUR foam influences the kinetics of the foaming process of the PUR-WP composition and their morphology, density, compressive strength and thermal properties. The performed tests showed that the addition of WP at an the amount of 10% leads to the increase in the PUR foam's compressive strength by 30% (parallel to foam's growth direction) and reduce the thermal conductivity coefficient by 10%.

Characterisation of Wood Particles Used in the Particleboard Production as a Function of Their Moisture Content.

The properties of particleboards and the course of their manufacturing process depend on the characteristics of wood particles, their degree of fineness, geometry, and moisture content. This research work aims to investigate the physical properties of wood particles used in the particleboard production in dependence on their moisture content. Two types of particles currently used in the production of three-layer particleboards, i.e., microparticles (MP) for the outer layers of particleboards and particles for the core layers (PCL), were used in the study. The particles with a moisture content of 0.55%, 3.5%, 7%, 10%, 15%, and 20% were tested for their poured bulk density (ρp), tapped bulk density (ρt), compression ratio (k), angle of repose (αR), and slippery angle of repose (αs). It was found that irrespective of the fineness of the particles, an increase in their moisture content caused an increase in the angle of repose and slippery angle of repose and an increase in poured and tapped bulk density, while for PCL, the biggest changes in bulk density occurred in the range up to 15% of moisture content, and for MP in the range above 7% of moisture content, respectively. An increase in the moisture content of PCL in the range studied results in a significant increase in the compression ratio from 47.1% to 66.7%. The compression ratio of MP increases only up to 15% of their moisture content-a change of value from 47.1% to 58.7%.

Effects of Chip Type on the Properties of Chip-Sawdust Boards Glued with Polymeric Diphenyl Methane Diisocyanate.

This study investigates the effects of chip type and sawdust percentage on physical and mechanical properties of chip-sawdust boards. The used wood chips varied in linear dimensions and original source. The origin determined the wood quality, which translated into the chips' linear dimensions. The used materials were chips from sawmill waste processing, aggregate processing of sawmill wood, and chips intended for medium-density boards. The experiment demonstrated that the best boards in terms of mechanical properties were obtained from 4-mm-thick chips with 30% sawdust content and a density of 850 kg/m3. These boards meet the requirements of the EN 312 (2010) standard for P5 boards.

Effects of a Chipboard Structure on Its Physical and Mechanical Properties.

The paper evaluated the possibility of manufacturing wood-based boards from the material left over from sawmill processing of wood. The boards were made from chips created during cant preparation for cutting and sawdust generated during further sawnwood preparation. They were made as one- and three-ply boards with face layers containing industrial microchips. Mechanical properties determined for one-ply boards in a bend test were used as guidelines for manufacturing three-ply boards. The outcomes were much better when the core layer comprised a mix of chips and sawdust than the chips alone. The study also showed that for the assumed technological parameters it is possible to produce three-ply boards with properties meeting the criteria for P2 furniture boards.