Characterisation of native and decellularised porcine tendon under tension and compression: A closer look at glycosaminoglycan contribution to tendon mechanics.

Decellularised porcine superflexor tendon (pSFT) has been characterised as a suitable scaffold for anterior cruciate ligament replacement, with dimensions similar to hamstring tendon autograft. However, decellularisation of tissues may reduce or damage extracellular matrix components, leading to undesirable biomechanical changes at a whole tissue scale. Although the role of collagen in tendons is well established, the mechanical contribution of glycosaminoglycans (GAGs) is less evident and could be altered by the decellularisation process. In this study, the contribution of GAGs to the tensile and compressive mechanical properties of pSFT was determined and whether decellularisation affected these properties by reducing GAG content or functionality. PSFTs were either enzymatically treated using chondroitinase ABC to remove GAGs or decellularised using previously established methods. Native, GAG-depleted and decellularised pSFT groups were then subjected to quantitative assays and biomechanical characterisation. In tension, specimens underwent stress relaxation and strength testing. In compression, specimens underwent confined compression testing. The GAG-depleted group was found to have circa 86% reduction of GAG content compared to native and decellularised groups. There was no significant difference in GAG content between native (3.75 ± 0.58 µg/mg) and decellularised (3.40 ± 0.37 µg/mg) groups. Stress relaxation testing discovered the time-independent and time-dependent relaxation moduli of the decellularised group were reduced ≥50% compared to native and GAG-depleted groups. However, viscoelastic behaviour of native and GAG-depleted groups resulted similar. Strength testing discovered no differences between native and GAG-depleted group's properties, albeit a reduction ∼20% for decellularised specimens' linear modulus and tensile strength compared to native tissue. In compression testing, the aggregate modulus was found to be circa 74% lower in the GAG-depleted group than the native and decellularised groups, while the zero-strain permeability was significantly higher in the GAG-depleted group (0.86 ± 0.65 mm4/N) than the decellularised group (0.03 ± 0.04 mm4/N). The results indicate that GAGs may significantly contribute to the mechanical properties of pSFT in compression, but not in tension. Furthermore, the content and function of GAGs in pSFTs are unaffected by decellularisation and the mechanical properties of the tissue remain comparable to native tissue.

Decellularised human bone allograft from different anatomical sites as a basis for functionally stratified repair material for bone defects.

Tissue engineered bone solutions aim to overcome the limitations of autologous and allogeneic grafts. Decellularised tissues are produced by washing cellular components from human or animal tissue to produce an immunologically safe and biocompatible scaffold, capable of integration following implantation. A decellularisation procedure utilising low concentration sodium dodecyl sulphate (0.1% w/v) was applied to trabecular bone from human femoral heads (FH) and tibial plateaus (TP). Biological (histology, DNA quantification), biomechanical (compression testing) and structural (µCT) comparisons were made between decellularised and unprocessed cellular tissue. Total DNA levels of decellularised FH and TP bone were below 50 ng mg-1 dry tissue weight and nuclear material was removed. No differences were found between cellular and decellularised bone, from each anatomical region, for all the biomechanical and structural parameters investigated. Differences were found between cellular FH and TP and between decellularised FH and TP. Decellularised FH had a higher ultimate compressive stress, Young's modulus and 0.2% proof stress than decellularised TP (p = 0.001, 0.002, 0.001, Mann Whitney U test, MWU). The mineral density of cellular and decellularised TP bone was significantly greater than cellular and decellularised FH bone respectively (cellular: p = 0.001, decellularised: p < 0.001, MWU). The bone volume fraction and trabecular thickness of cellular and decellularised FH bone were significantly greater than cellular and decellularised TP bone respectively (cellular: p = 0.001, 0.005; decellularised: p < 0.001, <0.001, MWU). Characterisation of decellularised trabecular bone from different anatomical regions offers the possibility of product stratification, allowing selection of biomechanical properties to match particular anatomical regions undergoing bone graft procedures.

Stratifying the mechanical performance of a decellularized xenogeneic tendon graft for anterior cruciate ligament reconstruction as a function of graft diameter: An animal study.

OBJECTIVES: This study investigated the biomechanical performance of decellularized porcine superflexor tendon (pSFT) grafts of varying diameters when utilized in conjunction with contemporary ACL graft fixation systems. This aimed to produce a range of 'off-the-shelf' products with predictable mechanical performance, depending on the individual requirements of the patient. METHODS: Decellularized pSFTs were prepared to create double-bundle grafts of 7 mm, 8 mm, and 9 mm diameter. Femoral and tibial fixation systems were simulated utilizing Arthrex suspension devices and interference screws in bovine bone, respectively. Dynamic stiffness and creep were measured, followed by ramp to failure from which linear stiffness and load at failure were measured. The mechanisms of failure were also recorded. RESULTS: Dynamic stiffness was found to increase with greater graft diameter, with significant differences between all groups. Conversely, dynamic creep reduced with increasing graft diameter with significant differences between the 7 mm and 9 mm groups and the 8 mm and 9 mm groups. Significant differences were also found between the 7 mm, 8 mm, and 9 mm groups for linear stiffness, but no significant differences were found between groups for load at failure. The distribution of failure mechanisms was found to change with graft diameter. CONCLUSION: This study showed that decellularized pSFTs demonstrate comparable biomechanical properties to other ACL graft options and are a potentially viable option for ACL reconstruction. Although grafts can be stratified by their diameter to provide varying biomechanical properties, it may be more appropriate to alter the fixation technique to stratify for a greater diversity of biomechanical requirements.Cite this article: Bone Joint Res 2019;8:518-525.

The effects of irradiation dose and storage time following treatment on the viscoelastic properties of decellularised porcine super flexor tendon.

Decellularised porcine super flexor tendon (pSFT) offers a promising solution to the replacement of damaged anterior cruciate ligament. It is desirable to package and terminally sterilise the acellular grafts to eliminate any possible harmful pathogens. However, irradiation techniques can damage the collagen structure and consequently reduce the mechanical properties. The aims of this study were to investigate the effects of irradiation sterilisation of varying dosages on the viscoelastic properties of the decellularised pSFT. Decellularised pSFT tendons were subjected to irradiation sterilisation using either 30kGygamma, 55kGygamma, 34kGy E-beam, 15kGygamma, 15kGy E-beam and (15+15) kGy E-beam (fractionated dose). Specimens then underwent stress relaxation testing at 0 and 12months post sterilisation to determine whether any effect on the viscoelastic properties was progressive. Significant differences were found which demonstrated that all irradiation treatments had an effect on the time-independent and time-dependent viscoelastic properties of irradiated tendons compared to peracetic acid only treated controls. No significant differences were found between the irradiated groups and no significant differences were found between groups at 0 and 12months. These results indicate the decellularised pSFT graft has a stable shelf-life.

The effects of irradiation on the biological and biomechanical properties of an acellular porcine superflexor tendon graft for cruciate ligament repair.

Acellular xenogeneic tissues have the potential to provide 'off-the-shelf' grafts for anterior cruciate ligament (ACL) repair. To ensure that such grafts are sterile following packaging, it is desirable to use terminal sterilization methods. Here, the effects of gamma and electron beam irradiation on the biological and biomechanical properties of a previously developed acellular porcine superflexor tendon (pSFT) were investigated. Irradiation following treatment with peracetic acid was compared to peracetic acid treatment alone and the stability of grafts following long-term storage assessed. Irradiation did not affect total collagen content or biocompatibility (determined using a contact cytotoxicity assay) of the grafts, but slightly increased the amount of denatured collagen in and decreased the thermal denaturation temperature of the tissue in a dose dependant fashion. Biomechanical properties of the grafts were altered by irradiation (reduced ultimate tensile strength and Young's modulus, increased failure strain), but remained superior to reported properties of the native human ACL. Long term storage at 4°C had no negative effects on the grafts. Of all the conditions tested, a dose of minimum 25 kGy of gamma irradiation had least effect on the grafts, suggesting that this dose produces a biocompatible pSFT graft with adequate mechanical properties for ACL repair. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2477-2486, 2017.

Results of a smoking cessation clinic in community pharmacy practice.

OBJECTIVES: To describe and assess the effectiveness of a smoking cessation clinic. DESIGN: Single group, unblinded study. SETTING: Seven chain (mass-merchandise) community pharmacies in Virginia. PARTICIPANTS: Forty-eight patients who were smokers when admitted to the study. INTERVENTIONS: Fifteen community chain pharmacists were trained using a smoking cessation training manual developed at the Virginia Commonwealth University School of Pharmacy. From April 1, 1997, through December 31, 1999, interested patients met individually with a study pharmacist during scheduled clinic times in semiprivate counseling areas. A patient chart was maintained at the site and updated after each visit. The first 30 patients completed a questionnaire after the third visit to the smoking cessation clinic to assess satisfaction with pharmacists and the overall program. MAIN OUTCOME MEASURE: Rate of long-term smoking cessation. RESULTS: Of the 48 patients, 12 (25.0%) abstained from smoking cigarettes for 12 months or more beyond their predetermined quit dates. Abstinence rates for 1, 3, and 6 months were 43.8%, 31.3%, and 25.0%, respectively. Women were nearly five times more successful in attaining long-term abstinence than were men (33.3% versus 6.7%; P= .047). No significant differences were observed in cessation rates related to age, number of cigarettes smoked per day, level of nicotine dependence, number of previous quit attempts, or method of cessation. Increased appetite and weight gain were the most frequently reported withdrawal symptoms (16.7% of patients). Patients expressed satisfaction with the pharmacists and the smoking cessation program. CONCLUSION: Compared with other types of previously reported interventions, a community pharmacist-managed smoking cessation clinic achieved greater long-term smoking cessation rates.