Investigations into the Antifungal, Photocatalytic, and Physicochemical Properties of Sol-Gel-Produced Tin Dioxide Nanoparticles.

Transmission electron microscopy (TEM), atomic force microscopy (AFM), X-ray diffraction (XRD), energy dispersive X-ray (EDX), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), and Fourier transform infrared (FTIR) spectroscopy were applied to evaluate the tin dioxide nanoparticles (SnO2 NPs) amalgamated by the sol-gel process. XRD was used to examine the tetragonal-shaped crystallite with an average size of 26.95 (±1) nm, whereas the average particle size estimated from the TEM micrograph is 20.59 (±2) nm. A dose-dependent antifun3al activity was performed against two fungal species, and the activity was observed to be increased with an increase in the concentration of SnO2 NPs. The photocatalytic activity of SnO2 NPs in aqueous media was tested using Rhodamine 6G (Rh-6G) under solar light illumination. The Rh-6G was degraded at a rate of 0.96 × 10-2 min for a total of 94.18 percent in 350 min.

Structural and biological investigation of biogenically synthesized titanium dioxide nanoparticles: Calcination and characterization.

The antimicrobial drug resistance is increasing with the passage of time due to wide and improper use of broad spectrum drugs and the demand of the new drug increases day by day. The present study was planned to encounter this problem by synthesizing titanium dioxide nanoparticles (TiO2 NPs) by an eco-friendly route using Cannabis sativa leaves extract. The synthesized TiO2 NPs were calcined at 100, 300, 600, and 900°C in a muffle furnace. The crystallographic parameters were studied by X-ray diffraction and the phase transition occurred above 600°C. The surface morphology of the synthesized samples was studied by transmission electron microscopy (TEM), and scanning electron microscopy (SEM) and the particle size was measured through the ImageJ software. The elemental composition and purity of all the samples were studied by performing energy dispersive X-ray (EDX). All the synthesized TiO2 NPs were tested for their antimicrobial effect against Gram-positive and Gram-negative bacteria using the agar well diffusion method. The activity was found higher against Gram-negative bacteria and compared to Gram-positive bacteria.