Effect of gallium on growth of Streptococcus mutans NCTC 10449 and dental tissues.

Gallium-doped phosphate-based glasses (Ga-PBG) were assessed for their impact on Streptococcus mutans and dental mineralisation, firstly by disc diffusion assays followed by biofilms grown on nitrocellulose filter membrane (NFM) and constant-depth film fermentor (CDFF). Short-time exposure (10 min) effects of Ga-PBG on S. mutans biofilm were compared with that of 0.2% chlorhexidine. The effects of Ga-PBG on bovine enamel (which was investigated under pH-cycling condition) and dentine were analysed using transverse microradiography (TMR), profilometry and inductively coupled plasma optical-emission spectrometry (ICP-OES). The disc diffusion assays showed inhibition zones of 24.5 ± 0.5 mm for Ga-PBG compared with controls (C-PBG). Ga-PBG showed statistically significant growth inhibition of S. mutans biofilms on NFM (p = 0.001) and CDFF (p < 0.046) compared with hydroxyapatite (HA) and C-PBG. The CDFF assay revealed a maximum of 2.11 log colony-forming unit (CFU) reduction at 48 h, but short-time exposure effects were comparable with that of 0.2% chlorhexidine only on older biofilms (maximum of 0.59 vs. 0.69 log CFU reduction at 120 h). TMR analyses of the enamel revealed non-significant mineral loss (p = 0.37) only in the case of Ga-PBG samples compared with controls including sodium fluoride. ICP-OES analyses indicated transient gallium adsorption into dentine by calcium displacement. The results confirmed that gallium inhibited S. mutans growth and appears to have the potential to protect the enamel surface under conditions representative of the oral environment. Further work is needed to establish whether it has an application in daily oral hygiene procedures to prevent or reduce caries.

Forensic analysis of wooden safety matches -- a case study.

In this case, an individual was suspected of attempting to burn materials potentially relating to a murder case. A number of spent and unspent matches were seized at the scene by police for forensic examination. Coincidentally, a police raid at the suspect's house revealed a number of matchboxes, all of the same brand, containing matches that had a visual similarity to those recovered at the scene. Stable Isotope Profiling (SIP) was used to assess whether matches could either be distinguished or shown to be indistinguishable by 13C and 2H isotopic composition. These results were then compared to those from the X-ray diffraction (XRD) analysis of match heads and microscopy of the wood. SIP showed the scene matches and seized matches to be different, which was confirmed by XRD and microscopy analyses.

Stable isotope analysis of safety matches using isotope ratio mass spectrometry--a forensic case study.

Isotope ratio mass spectrometry (IRMS) was used to assess what contribution the technique could make towards the comparative analysis of matchstick samples within the 'normal' framework of a forensic investigation. A method was developed to allow the comparison of samples submitted as a result of an investigation, with the added advantage of rapid sample turn-around expected within this field. To the best of our knowledge this is the first time that wooden safety matches have been analysed using IRMS. In this particular case, bulk stable isotope analysis carrried out on a 'like-for-like' basis could demonstrate conclusively that matches seized from a suspect were different from those collected at the scene of crime. The maximum delta13C variability observed within one box was 2.5 per thousand, which, in conjunction with the error of measurement, was regarded to yield too wide an error margin as to permit differentiation of matchsticks based on 13C isotopic composition alone given that the 'natural' 13C abundance in wood ranges from -20 to -30 per thousand. However, from the delta2H values obtained for crime scene matches and seized matches of -114.5 per thousand and -65 per thousand, respectively, it was concluded that the matches seized were distinctly different from those collected at the crime scene.