Physicochemical properties of three bioceramic cements.

This study aimed to compare the physicochemical properties of MTA Angelus (MTA-A), MTA Repair HP (MTA-HP), and Biodentine (BD). Setting times (n = 7) were determined in accordance with ASTM C266-15. Solubility (n = 11), pH (n = 10), and calcium ion release (n = 10) were evaluated up to 28 days in accordance with ANSI/ADA specification no. 57. Radiopacity was assessed by ANSI/ADA (n = 10) and the tissue simulator method (n = 10). In both methods, the specimens were radiographed using an aluminum stepwedge and the digital radiographs were analyzed in Adobe Photoshop, determining the mean grayscale pixel values of the materials, of the 3-mm aluminum stepwedge, and of the dentin, the latter of which was analyzed on the tissue simulator. The data obtained from each test were statistically analyzed and compared (p < 0.05). MTA-A presented longer final setting time compared with the other materials. There were no significant differences in the mass values of materials during the experiment. All materials presented an alkaline pH. BD promoted greater calcium ion release in most of the experimental periods. All materials presented appropriate radiopacity. BD showed lower radiopacity than MTA-A in the tissue simulator method. All groups presented higher radiopacity in the tissue simulator when compared with the ANSI/ADA method. MTA-A, MTA-HP, and BD showed appropriate physicochemical properties and radiopacity, and were considered suitable to be used in clinical practice.

Physicochemical properties of three bioceramic cements

Abstract: This study aimed to compare the physicochemical properties of MTA Angelus (MTA-A), MTA Repair HP (MTA-HP), and Biodentine (BD). Setting times (n = 7) were determined in accordance with ASTM C266-15. Solubility (n = 11), pH (n = 10), and calcium ion release (n = 10) were evaluated up to 28 days in accordance with ANSI/ADA specification no. 57. Radiopacity was assessed by ANSI/ADA (n = 10) and the tissue simulator method (n = 10). In both methods, the specimens were radiographed using an aluminum stepwedge and the digital radiographs were analyzed in Adobe Photoshop, determining the mean grayscale pixel values of the materials, of the 3-mm aluminum stepwedge, and of the dentin, the latter of which was analyzed on the tissue simulator. The data obtained from each test were statistically analyzed and compared (p < 0.05). MTA-A presented longer final setting time compared with the other materials. There were no significant differences in the mass values of materials during the experiment. All materials presented an alkaline pH. BD promoted greater calcium ion release in most of the experimental periods. All materials presented appropriate radiopacity. BD showed lower radiopacity than MTA-A in the tissue simulator method. All groups presented higher radiopacity in the tissue simulator when compared with the ANSI/ADA method. MTA-A, MTA-HP, and BD showed appropriate physicochemical properties and radiopacity, and were considered suitable to be used in clinical practice.