Evaluating the osteogenic properties of polyhydroxybutyrate-zein/multiwalled carbon nanotubes (MWCNTs) electrospun composite scaffold for bone tissue engineering applications.

In this investigation, the electrospun nanocomposite scaffolds were developed utilizing poly-3-hydroxybutyrate (PHB), zein, and multiwalled carbon nanotubes (MWCNTs) at varying concentrations of MWCNTs including 0.5 and 1 wt%. Based on the SEM evaluations, the scaffold containing 1 wt% MWCNTs (PZ-1C) exhibited the lowest fiber diameter (384 ± 99 nm) alongside a suitable porosity percentage. The presence of zein and MWCNT in the chemical structure of the scaffold was evaluated by FTIR. Furthermore, TEM images revealed the alignment of MWCNTs with the fibers. Adding 1 % MWCNTs to the PHB-zein scaffold significantly enhanced tensile strength by about 69 % and reduced elongation by about 31 %. Hydrophilicity, surface roughness, crystallinity, and biomineralization were increased by incorporating 1 wt% MWCNTs, while weight loss after in vitro degradation was decreased. The MG-63 cells exhibited enhanced attachment, viability, ALP secretion, calcium deposition, and gene expression (COLI, RUNX2, and OCN) when cultivated on the scaffold containing MWCNTs compared to the scaffolds lacking MWCNTs. Moreover, the study found that MWCNTs significantly reduced platelet adhesion and hemolysis rates below 4 %, indicating their favorable anti-hemolysis properties. Regarding the aforementioned results, the PZ-1C electrospun composite scaffold is a promising scaffold with osteogenic properties for bone tissue engineering applications.

Evaluation of the effects of decellularized extracellular matrix nanoparticles incorporation on the polyhydroxybutyrate/nano chitosan electrospun scaffold for cartilage tissue engineering.

Recent research focuses on fabricating scaffolds imitating the extracellular matrix (ECM) in texture, composition, and functionality. Moreover, specific nano-bio-particles can enhance cell differentiation. Decellularized ECM nanoparticles possess all of the mentioned properties. In this research, cartilage ECM, extracted from the cow's femur condyle, was decellularized, and ECM nanoparticles were synthesized. Finally, nanocomposite electrospun fibers containing polyhydroxybutyrate (PHB), chitosan (Cs) nanoparticles, and ECM nanoparticles were fabricated and characterized. TEM and DLS results revealed ECM nanoparticle sizes of 17.51 and 21.6 nm, respectively. Optimal performance was observed in the scaffold with 0.75 wt% ECM nanoparticles (PHB-Cs/0.75E). By adding 0.75 wt% ECM, the ultimate tensile strength and elongation at break increased by about 29 % and 21 %, respectively, while the water contact angle and crystallinity decreased by about 36° and 2 %, respectively. Uneven and rougher surfaces of the PHB-Cs/0.75E were determined by FESEM and AFM images, respectively. TEM images verified the uniform dispersion of nanoparticles within the fibers. After 70 days of degradation in PBS, the PHB-Cs/0.75E and PHB-Cs scaffolds demonstrated insignificant weight loss differences. Eventually, enhanced viability, attachment, and proliferation of the human costal chondrocytes on the PHB-Cs/0.75E scaffold, concluded from MTT, SEM, and DAPI staining, confirmed its potential for cartilage tissue engineering.

Evaluation of the effects of zein incorporation on physical, mechanical, and biological properties of polyhydroxybutyrate electrospun scaffold for bone tissue engineering applications.

Materials and fabrication methods significantly influence the scaffold's final features in tissue engineering. This study aimed to blend zein with polyhydroxybutyrate (PHB) at 5, 10, and 15 wt%, fabricate scaffolds using electrospinning, and then characterize them. SEM and mechanical analyses identified the scaffold with 10 wt% zein (PHB-10Z) as the optimal sample. Incorporating 10 wt% zein reduced fiber diameter from 894 ± 122 to 531 ± 42 nm while increasing ultimate tensile strength and elongation at break by approximately 53 % and 70 %, respectively. FTIR proved zein's presence in the scaffolds and possible hydrogen bonding with PHB. TGA confirmed the miscibility of polymers. DSC and XRD analyses indicated lower crystallinity for the PHB-10Z than for PHB. AFM evaluation indicated a rougher surface for the PHB-10Z in comparison to PHB. The PHB-10Z demonstrated a more hydrophobic surface and less weight loss after 100 days of degradation in PBS than PHB. The free radical scavenging assay exhibited antioxidant activity for the zein-containing scaffold. Eventually, enhanced cell attachment, viability, and differentiation in the PHB-10Z scaffold drawn from SEM, MTT, ALP activity, and Alizarin red staining of MG-63 cells confirmed that PHB-zein electrospun scaffold is a potent candidate for bone tissue engineering applications.