Solvation role of dimethyl sulfoxide on the interaction with dentin bonding systems after 30 months.

OBJECTIVES: To determine whether DMSO could serve as an effective pretreatment to improve the mechanical properties and minimize the degradation of the adhesive interface, through the degree of conversion (DC) and bond strength to dentin of different categories of dentin bonding systems (DBSs) after 30 months. METHODS: DMSO (0, 0.5, 1, 2, 5, 10 vol%) were incorporated into four categories of DBSs: Adper Scotchbond Multipurpose (MP), Adper Single Bond 2 (SB), Clearfil SE Bond (CSE) and Adper Scotchbond Universal (SU). DC was evaluated by Fourier transform infrared spectroscopy (FTIR). For microtensile bond strength test (µTBS), 1 % DMSO were applied on dentin as pretreatment before DBSs. For SU, both strategies were tested. Specimens for µTBS were tested after 24 h, 6 and 30 months. DC and µTBS data were subjected to two-way ANOVA and Tukey test (α < 0.05). RESULTS: Incorporating 5 %/10 % DMSO increased the DC of CSE. Controversially, when combined with SU, 2 % and 10 % DMSO jeopardized the DC. Regarding µTBS, 1 % DMSO pre-treatment increased the bond strength for MP, SB, SU-ER and SU-SE. After 30 months, MP, SU-ER and SU-SE showed a decrease compared to baseline but remained higher than the control. CLINICAL SIGNIFICANCE: DMSO pretreatment may be a useful strategy to improve the bond interface over time. Its incorporation seems to favor the non-solvated systems regarding DC while it seems to show long-term benefits for bond strength using 1 % DMSO for MP and SU systems.

Sodium trimetaphosphate combined to calcium as a strategy to improve dentin-bonding interface / Trimetafosfato de sódio associado ao cálcio como uma estratégia para melhorar a interface adesiva da dentina

Objective: The aim of this study was to evaluate the effect of STMP as biomimetic analog of dentin matrix on the dentin bond strength submitted to artificial cariogenic challenge over time. Material and Methods: The total number of teeth used in the experiment was 60 teeth, which were divided into 6 groups (n = 10). Of these total amount, 10 teeth were not submitted to the artificial cariogenic challenge (ACC), serving as control group (Sound Dentin - SD) while the other 50 were submitted to an ACC (7d/37ºC), being treated with treatment solutions according to each group: SD- deionized water/sound dentin, CD- deionized water/ artificial caries dentin, GIII- STMP, GIV- STMP + Ca(OH)2, GV- STMP + NaF, and GVI- NaF. After treatments (24h), the specimens were restored (Adper Single Bond Universal + Filtek Z250), to obtain resin­dentin sticks with a cross sectional area of 0.8mm2, approximately. Two-third of these sticks were stored in artificial saliva (37°C) for analyzes after 6 and 12 months. The 1/3 remains were subjected to µTBS test (baseline). Data were analyzed by two-way ANOVA and Tukey tests (p<0.05). Results: In general, the highest µTBS values were obtained in sound condition (SD), while the artificial caries condition (CD) determined minimum values. Groups treated with NaF (with or without STMP- GV and GVI) were not able to improve adhesion over time. Only the use of STMP + Ca(OH)2(GIV) improved the µTBS compared to the others caries-challenged dentin after 1 year. The adhesive failure pattern was predominant in all time. Conclusion: The use of the STMP associated with Ca(OH)2 seems to be a viable therapeutic strategy conciliating the biomimetizing capacity to the adhesive process satisfactorily even its performance is not superior to initial condition (AU)

Objetivo: O objetivo deste estudo foi avaliar o efeito do STMP como análogo biomimético da matriz dentinária na resistência de união à dentina submetida a desafio cariogênico artificial ao longo do tempo. Material e Métodos:foram utilizados um total de 60 dentes neste experimento, os quais foram divididos em 6 grupos (n = 10). Desse total, 10 dentes não foram submetidos ao desafio cariogênico artificial (DCA), servindo como grupo controle (Dentina Hígida - DH) enquanto os outros 50 foram submetidos ao DCA (7d / 37ºC), sendo tratados com soluções de tratamento específicas para cada grupo: DH- água deionizada / dentina hígida, DC- água deionizada / dentina submetida ao DCA, GIII- STMP, GIV- STMP + Ca(OH)2, GV- STMP + NaF e GVI- NaF. Após os tratamentos (24h), os corpos-de-prova foram restaurados (Adper Single Bond Universal + Filtek Z250), para obtenção de palitos de resina-dentina com área transversal de aproximadamente 0,8mm2. Dois terços desses palitos foram armazenados em saliva artificial (37°C) para análises após 6 e 12 meses. Os outros 1/3 foram submetidos ao teste µTBS (baseline). Os dados foram analisados por ANOVA a dois fatores e testes de Tukey (p <0,05). Resultados:Em geral, os maiores valores de µTBS foram obtidos em condição hígidas (DH), enquanto a condição subtmetidas ao DCA determinou os menores valores. Os grupos tratados com NaF (com ou sem STMP associado -GV e GVI) não foram capazes de melhorar a resistência de união, ao longo do tempo. Somente o uso de STMP + Ca (OH)2(GIV) melhorou o µTBS em comparação com as outras condições desafiadas por cárie após 1 ano. O padrão de falha adesiva foi predominante em todos os tempos. Conclusão: O uso do STMP associado ao Ca (OH)2 parece ser uma estratégia terapêutica viável conciliando a capacidade biomimetizante ao processo adesivo de forma satisfatória mesmo que seu desempenho não seja superior à condição inicial.(AU)

Giomer technology for preventive and restorative clinical management of erosive tooth wear: a case report / Tecnologia Giomer para manejo clínico preventivo e restaurador de desgaste dentário erosive: relato de caso

Increasing prevalence of erosive tooth wear (ETW) is notable mainly due to current knowledge and its early diagnosis. Once teeth are functionally and/or esthetically affected, dental restorations may become necessary. Materials capable of interacting with the eroded dental tissue allied to their resistance to subsequent continuous erosive challenges are desirable. Giomer technology based on S-PRG (surface pre-reactive glass) filler has been launching to provide benefits for the dental treatment due to its innovative multi-ionic release system, which involves fluoride. This case report describes the employment of preventive and restorative materials based on this technology for a patient under frequent erosive challenges and complaining about dental sensitivity. Patient reported immediate reduction on this sensitivity and the restorations has been followed up for 2 years, presenting satisfactory performance. S-PRG-based systems seem to be promissory for preventive and therapeutic management of ETW used simultaneously with the patient compliance. (AU)

O aumento da prevalência do desgaste dentário erosivo (DDE) é notável especialmente devido ao conhecimento atual e seu diagnóstico precoce. Uma vez que os dentes são afetados funcional e/ou esteticamente, restaurações dentárias se tornam necessárias. Materiais focados na habilidade de interagir com o tecido dentário erodido associados com sua resistência aos desafios erosivos contínuos subsequentes são desejáveis. A tecnologia Giomer baseada em partículas S-PRG (superfície de vidro pré-reativo) foi lançada no mercado para oferecer benefícios para o tratamento odontológico devido ao seu sistema inovador de liberação multi-iônica, que envolve o flúor. Esse caso clínico descreve o uso de materiais preventivo e restaurador baseados nessa tecnologia em um paciente em desafio erosivo e com queixa de sensibilidade. O paciente relatou redução imediata da sensibilidade e as restaurações foram acompanhadas por 2 anos apresentando desempenho satisfatório. Sistemas baseados em S-PRG se mostram promissores para manejo preventivo e terapêutico do DDE empregados simultaneamente à colaboração do paciente.(AU)

Performance of MDP-based system in eroded and carious dentin associated with proteolytic inhibitors: 18-Month exploratory study.

The aim of this study was to explore the impact of the interaction between an MDP-based universal adhesive system in etch-and-rinse mode and two proteolytic inhibitors on the longevity of restorations bonded to artificially-affected-dentin substrates. 90 sound human third molars were randomly distributed into three groups according to the substrate: N-no challenges-control (stored in artificial saliva), ACD-artificial caries dentin (6 h DE + 18 h-RE/5 days + 48 h RE) and ERO-artificial erosion dentin (3 × 5 min/5 days with orange juice). They were further redistributed according to dentin pretreatment: W- water (control), CHX-2% digluconate chlorhexidine and E64- 5 µM E64-Trans-Epoxysuccinyl-L-Leucylamido-(4-guanidino) butane, which resulted in the following 9 groups (n = 10): N-W, N-CHX, N-E64, ACD-W, ACD-CHX, ACD-E64, ERO-W, ERO-CHX and ERO-E64. All specimens were restored with Adper Single Bond Universal (Etch-and-rinse mode)/Filtek Z250. Sticks (0.64 mm2) were obtained and subjected to microtensile test (µTBS) in a universal testing machine at 0.5 mm/min for 7-days, 6 and 18-month analyses. Failure modes were classified using optical microscopy (40X). Data were statistically analyzed by three-way ANOVA and Tukey tests (p < 0.05). All individual factors (p < 0.0001) and interaction between factors were statistically significant (substrate X pretreatment (p = 0.00093); substrate X time (p = 0.01035) and pretreatment X time (p = 0.0035). Caries-affected substrate was the most compromised one, disregarding the pretreatment. CHX was mostly affected compared with E64 up to 18 months, possibly due to its calcium-dependent mechanism.

Profile of a 10-MDP-based universal adhesive system associated with chlorhexidine: Dentin bond strength and in situ zymography performance.

The incorporation of functional monomers and proteolytic inhibitors into adhesive systems have shown to be promising strategies to improve the longevity of adhesive restorations. The aim of this study was to evaluate the long-term bonding performance and anti-gelatinolytic effect of a 10-MDP-based universal adhesive system applied in combination with 2% chlorhexidine digluconate (CHX). For that, this study assessed the resin-dentin bond strength and the in situ gelatinolytic activity profile at the adhesive interface at initial and after 6 month of storage. One hundred and two sound human third molars were prepared and randomly divided into 3 groups according to the adhesive strategy: SB (two-step etch-and-rinse adhesive, Adper Single Bond 2, 10-MDP-free control group); SU-ER (Adper Single Bond Universal, 10-MDP containing universal adhesive applied on etch-and-rinse mode); and SU-SE (SU applied on self-etching mode). The groups were subdivided into two according to the dentin pretreatment: W - water or CHX- 2% chlorhexidine digluconate aqueous solution (SB-W; SB-CHX; SU-ER-W; SU-ER-CHX; SU-SE-W; SU-SE-CHX) and subsequently restored according to the manufacturer's instructions. Bond strength (n = 12) was assessed by a microtensile test (µTBS) (500N/0.5 mm/min) after 24h or after 6 months of storage. In situ zymography was performed to evaluate anti-gelatinolytic activity (n = 5). Resin-dentin samples were incubated with fluorescein-conjugated gelatin for 24 h at 37 °C and analyzed by confocal laser scanning microscopy. Fluorescence indicating gelatinolytic activity at hybrid layer zone and adjacencies was quantified using Image J. Data was analyzed by three-way ANOVA and Tukey post-hoc tests (p < 0.05). Results: SU-SE showed the highest bond strength values, while similar results were observed for SU-ER and SB. No statistical significant differences were observed between pretreatment (CHX vs. W) or storage time (initial vs. 6 months of aging). For in situ zymography, fluorescence was detected in all groups and CHX pre-treatment was able to inhibit the gelatinolytic activity in all conditions. The 10-MDP-based universal adhesive system in self-etching mode was the strategy that showed the best bonding performance irrespective of its combination with chlorhexidine. Pre-treatment with CHX did not impair the bond strength when used in combination with 10-MDP and it may promote collagen stability overtime.

Effect of ethanol-dissolved rhodamine B marker on mechanical properties of non-simplified adhesives.

OBJECTIVES: Rhodamine B (RB) is commonly used to evaluate dental polymers, including dental bonding systems (DBS). For reliability assessments, its effect should not only allow visualization of the dentin-polymer interface but also must not interfere with the bonding of the DBS to dentin as measured by the microtensile bond strength and hardness tests. MATERIAL AND METHODS: Flat human dentin surfaces were prepared and randomly distributed (n = 10) into six groups: Adper Scotchbond Multi-Purpose (MP) or Clearfil SE Bond (SE) in concentrations of none/control, 0.02 or 0.1 mg/mL. These combinations were prepared through ethanol dissolution to improve their penetration into the dentin. All specimens were fabricated with Filtek Z250 (n = 10) and prepared for a microtensile bond test (µTBS) (0.5 mm/min) after 7 days and 6 months. The failure modes were determined using a stereomicroscope (×40). For the hardness test, flat human dentin blocks were prepared and treated as previously described (n = 6). The specimens were stored at 37 °C/48 h and were tested (Knoop indenter - 25 gF/10 s). Data were analyzed with two-way ANOVA and Tukey tests for multiple comparisons (α = 0.05). The effect of time was evaluated using the Student t-test. RESULTS: For 7-day µTBS, both the DBS and RB concentrations were significant factors (p < 0.01). After 6 months, only the RB concentration was significantly different. Adhesive failures were prevalent for all groups. Regarding hardness, the DBS differed only with the use of 0.10 mg/mL of RB. CONCLUSIONS: Ethanol-dissolved rhodamine B in concentrations of 0.02 and 0.10 mg/mL in non-simplified adhesives can affect the physical-mechanical properties of functional monomer-based systems rather more than those of BisGMA systems.

Sodium Trimetaphosphate as a Novel Strategy for Matrix Metalloproteinase Inhibition and Dentin Remineralization.

The effect of sodium trimetaphosphate (STMP) as an antiproteolytic and remineralizing agent on demineralized dentin was evaluated in vitro. The inhibitory potential of STMP at 0.5, 1.5, 3.5, and 5% against recombinant matrix metalloproteinases (MMPs) MMPs-2 and -9 was assessed by zymography. To investigate its remineralization potential, 40 bovine root specimens were obtained and subjected to a demineralization protocol to produce caries-like dentin lesions. After that, dentin surfaces were divided into 3 areas: (1) mineralized (no treatment); (2) demineralized; and (3) demineralized/treated with STMP and submitted to a pH-cycling associated or not with STMP (1.5, 3.5, or 5% STMP, 10 min of treatment). After that, superficial hardness (SH) and cross-sectional hardness (CSH) were determined. Polarized light microscopy (PLM) was used to qualitatively evaluate mineralization within the caries-like lesions. The zymographic analysis showed that STMP solution is a potent inhibitor of the gelatinolytic activity of MMPs-2 and -9 depending on the dose, since the lowest concentration (0.5%) partially inhibited the enzyme activity, while the higher concentrations completely inhibited enzyme activity. Regarding remineralization effect, only 1.5% STMP solution enhanced both the SH and CSH. PLM showed that the area treated with 1.5% STMP presented similar birefringence as mineralized sound dentin. In conclusion, 1.5% STMP solution is effective as an antiproteolytic agent against MMPs and promotes dentin remineralization.

How proteolytic inhibitors interact with dentin on glass-fiber post luting over 6 months.

OBJECTIVES: Enzyme inhibitors minimize the degradation of unprotected collagen of dentin promoted by matrix metalloproteinases (MMPs) and cysteine cathepsins (CCs). As the evidence of their effect on the root canal is limited, this study aimed to evaluate the role of EDTA, chlorhexidine and E-64 as antiproteolytic agents on the bond strength (BS) of glass-fiber posts in root canals. MATERIALS AND METHODS: Ninety-six bovine roots were distributed in groups for each time point (n = 8). Adper Scotchbond Multipurpose (MP)/ RelyX ARC system was used to lute the post according to the treatment: negative control (NC)- water, EDTA- 17% ethylenediaminetetraacetic acid, CHX- 2% digluconate chlorhexidine, E-64-5- 5µM E-64, E-64-10- 10µM E-64 and positive control (PC)- MP associated with activator/ catalyst. Then, slices were subjected to push-out test (0.5mm/min) after 24h/6 mons. Data were analyzed by three-way ANOVA/Tukey tests. Failure modes were analyzed (40×). RESULTS: The factors treatment, time, root canal third and the interaction between treatment and time were statistically significant. At 24h, no negative interactions were observed among the root dentin, bonding system and post. At 6 mons, CHX improved the BS for middle and apical root thirds. CONCLUSIONS: CHX was able to promote beneficial BS after 6 mons, which was not noted for any other tested enzyme inhibitors.

Use of sodium trimetaphosphate in the inhibition of dentin matrix metalloproteinases and as a remineralizing agent.

OBJECTIVES: Because of its ability to act as an antiproteolytic agent, the effect of sodium trimetaphosphate (STMP) against specific enzymes extracted from sound dentin and its performance under acidic challenge on demineralized dentin were investigated. METHODS: The antiproteolytic potential of STMP (0.5%, 1.0%, and 1.5%) was assessed in triplicate by zymography. For the evaluation of remineralization activity, 50 bovine-root dentin specimens were selected and randomly divided into 5 groups (n=10). Three areas were determined for each specimen: 1) control (no treatment); 2) demineralized (artificial caries-like challenge); 3) treated (demineralized and subjected to pH-cycling for 7days, and treated for 10min with 1.5% STMP, 1.5% STMP+calcium hydroxide (Ca[OH]2), 1.5% STMP+sodium fluoride (NaF), NaF, or deionized H2O). The dentin specimens were analyzed for superficial hardness (SH) and cross-sectional hardness (CSH) at different depths (10, 30, 50, 70, 90, 110, and 220µm) using a Knoop penetrator (10g/10s). Statistical analyses were performed with analysis of variance (ANOVA) and Tukey tests (p<0.05). RESULTS: The zymographic analysis showed that 1.5% STMP promoted complete inhibition of gelatinolytic activity. Therefore, 1.5% STMP was investigated in association with supplemented calcium or fluoride; a combination of 1.5% STMP and Ca(OH)2 significantly increased the mechanical properties of the treated dentin. CONCLUSION: 1.5% STMP serves as an antiproteolytic agent against matrix metalloproteinases extracted from human dentin. Furthermore, when supplemented with Ca(OH)2, 1.5% STMP may potentially induce remineralization. CLINICAL SIGNIFICANCE: STMP can be introduced as a novel strategy that combines enzymatic inhibition and remineralizing potential, which can serve to strengthen dentin and improve stability. STMP may have potential in the treatment of demineralized dentin lesions, especially when supplemented with calcium.

Influence of Erosive and Abrasive Cycling on Bonding of Different Adhesive Systems to Enamel: An In situ Study.

This study evaluated the impact of orange juice on the bond strength (BS) of dentin bonding systems (DBSs) to enamel surface after simulation with an in situ/ ex vivo erosive cycling. One hundred and ninety two bovine enamel fragments (4x4x2mm) were obtained and randomized regarding superficial microhardness and distributed to palatal devices for 8 volunteers, in three phases (one for each DBS), containing 8 blocks, which were, allocated in 4 pairs. Daily, these pairs were subjected extraorally to the following conditions: CONT- neither erosive nor abrasive challenge; ERO- erosive challenge only; ABR- abrasive challenge only and ERO + ABR- with erosive and abrasive challenges. Erosive cycles (immersion in orange juice, 3 times/day/5 min/5 days) or/and abrasive challenges (electric toothbrush, 3 times/day/1 min/5 days) were performed. After these cycles, all specimens were restored with the adhesive systems Adper Scotchbond Multi Purpose (MP), Adper Single Bond 2 (SB) or Clearfil SE Bond (SE), and the composite resin Filtek Z250. After 7 days, sticks (area ≅1 mm2) were obtained and subjected to the microtensile bond strength test (µTBS) at 0.5 mm/min. Data was statistically analyzed by ANOVA and Tukey tests (a=0.05). Failure modes were determined using a digital microscope (40´). DBS was the only statistical significant factor. SE was the unique DBS not affected in any challenge, whereas MP and SB performed according to the scenario. The adhesive and mixed failures were predominant in all groups. Overall performance suggested that BS to enamel after erosive /abrasive challenged by orange juice was not affected and it was material-dependent.

Influence of Erosive and Abrasive Cycling on Bonding of Different Adhesive Systems to Enamel: An In situ Study

Abstract This study evaluated the impact of orange juice on the bond strength (BS) of dentin bonding systems (DBSs) to enamel surface after simulation with an in situ/ ex vivo erosive cycling. One hundred and ninety two bovine enamel fragments (4x4x2mm) were obtained and randomized regarding superficial microhardness and distributed to palatal devices for 8 volunteers, in three phases (one for each DBS), containing 8 blocks, which were, allocated in 4 pairs. Daily, these pairs were subjected extraorally to the following conditions: CONT- neither erosive nor abrasive challenge; ERO- erosive challenge only; ABR- abrasive challenge only and ERO + ABR- with erosive and abrasive challenges. Erosive cycles (immersion in orange juice, 3 times/day/5 min/5 days) or/and abrasive challenges (electric toothbrush, 3 times/day/1 min/5 days) were performed. After these cycles, all specimens were restored with the adhesive systems Adper Scotchbond Multi Purpose (MP), Adper Single Bond 2 (SB) or Clearfil SE Bond (SE), and the composite resin Filtek Z250. After 7 days, sticks (area ≅1 mm2) were obtained and subjected to the microtensile bond strength test (μTBS) at 0.5 mm/min. Data was statistically analyzed by ANOVA and Tukey tests (a=0.05). Failure modes were determined using a digital microscope (40´). DBS was the only statistical significant factor. SE was the unique DBS not affected in any challenge, whereas MP and SB performed according to the scenario. The adhesive and mixed failures were predominant in all groups. Overall performance suggested that BS to enamel after erosive /abrasive challenged by orange juice was not affected and it was material-dependent.

Resumo Este estudo avaliou o impacto de suco de laranja na resistência de união (RU) de sistemas adesivos dentinários (SAD) à superfície do esmalte após a simulação com uma ciclagem erosiva in situ/ex vivo. Cento e noventa e dois fragmentos de esmalte bovino (4x4x2mm) foram obtidos e randomizados considerando a microdureza superficial, e distribuídos em dispositivos palatinos para 8 voluntários, em três fases (uma para cada SAD), contendo 8 blocos, os quais foram alocados em 4 pares. Diariamente, esses pares eram submetidos às seguintes condições extraoralmente: CONT- sem desafio erosivo ou abrasivo; ERO- desafio erosivo somente; ABR- desafio abrasivo somente; e ERO+ABR- com desafio erosivo e abrasivo. A ciclagem erosiva (imersão em suco de laranja, 3 vezes/dia/5 min/5 dias) e/ou ciclagem abrasiva (escova dentária elétrica, 3 vezes/dia/1 min/5 dias) foram feitas. Após estas ciclagens, todos os espécimes foram restaurados com os sistemas adesivos Adper Scotchbond Multi Purpose (MP), Adper Single Bond 2 (SB) ou Clearfil SE Bond (SE), e com a resina composta Filtek Z250. Após 7 dias, palitos (área ≈1 mm) eram obtidos e submetidos ao teste de resistência de união por microtração (μTBS) a 0,5 mm/min. Os dados foram estatisticamente analisados por ANOVA e teste de Tukey (a=0,05). Os modos de fratura foram determinados utilizando um microscópio digital (40×). SAD foi o único fator estatisticamente significante. SE foi o único SAD não afetado por qualquer desafio, enquanto o MP e o SB apresentaram um desempenho de acordo com o cenário. As fraturas do tipo mista e adesiva foram predominantes em todos os grupos. O desempenho geral sugeriu que RU ao esmalte após desafio erosivo/abrasivo por suco de laranja não foi afetada e foi material-dependente.

Effect of simulated intraoral erosion and/or abrasion effects on etch-and-rinse bonding to enamel.

PURPOSE: To assess the influence of simulated oral erosive/abrasive challenges on the bond strength of an etch-and-rinse two-step bonding system to enamel using an in situ/ex vivo protocol. METHODS: Bovine enamel blocks were prepared and randomly assigned to four groups: CONT - control (no challenge), ABR - 3x/day-1 minute toothbrushing; ERO - 3x/day - 5 minutes extraoral immersion into regular Coca Cola; and ERO+ABR - erosive protocol followed by a 1-minute toothbrushing. Eight blocks were placed into an acrylic palatal appliance for each volunteer (n = 13), who wore the appliance for 5 days. Two blocks were subjected to each of the four challenges. Subsequently, all the blocks were washed with tap water and Adper Single Bond 2/Filtek Z350 were placed. After 24 hours, 1 mm2 beams were obtained from each block to be tested with the microtensile bond strength test (50 N load at 0.5 mm/minute). The data were statistically analyzed by one-way RM-ANOVA and Tukey's tests (alpha = 0.05). RESULTS: No difference was detected among the ABR, ERO, and CONT groups (P > 0.05). ERO+ABR group yielded lower bond strengths than either the ABR and ERO groups (P < 0.0113).