Improving the Osteogenicity of PCL Fiber Substrates by Surface-Immobilization of Bone Morphogenic Protein-2.

Polycaprolactone (PCL) fiber scaffolds are attractive, albeit inert, substrates for ligament regeneration, that may be improved by incorporating trophic factors to guide tissue remodeling in vivo. In particular, immobilization of bone morphogenic protein-2 (BMP-2) to the scaffold surface may facilitate rapid and robust integration of the scaffold with adjacent bone tissues. As a first step toward testing this, model PCL surfaces were modified by the addition of heparin (Hep) and BMP-2 to facilitate osteoblastic differentiation. Specifically, Hep was combined with PCL at 0, 0.5, and 1 wt% (denoted as PCL, PCL-0.5Hep, and PCL-1Hep), cast into films, and then BMP-2 was immobilized to surfaces by either adsorption and covalent conjugation. Here, BMP-2 concentration increased systematically with incorporation of Hep, and higher concentrations were achieved by covalent conjugation. Next, blends were electrospun to form thin meshes with fiber diameters of 0.92, 0.62, and 0.54 µm for PCL, PCL-0.5Hep, and PCL-1Hep, respectively. Mesenchymal stem cells (MSCs) had no difficulty attaching to and proliferating on all meshes. Lastly, PCL-1Hep meshes were prepared with adsorbed or covalently conjugated BMP-2 and cultured with MSCs in the absence of osteogenic factors. Under these conditions, alkaline phosphatase activity and deposition of bone sialoprotein, osteopontin, and calcium minerals-markers of osteoblastic differentiation-were significantly higher on surfaces with immobilized BMP-2. Together, these data indicate that covalent immobilization of trophic factors confers bioactivity to scaffolds, which may be applied in a spatially controlled manner for ligament regeneration and bone integration.

Cell layer-electrospun mesh composites for coronary artery bypass grafts.

This work investigates the potential of cell layer-electrospun mesh constructs as coronary artery bypass grafts. These cell-mesh constructs were generated by first culturing a confluent layer of 10T½ smooth muscle progenitor cells on a high strength electrospun mesh with uniaxially aligned fibers. Cell-laden mesh sheets were then wrapped around a cylindrical mandrel such that the mesh fibers were aligned circumferentially. The resulting multi-layered constructs were then cultured for 4 wks in media supplemented with TGF-ß1 and ascorbic acid to support 10T½ differentiation toward a smooth muscle cell-like fate as well as to support elastin and collagen production. The underlying hypothesis of this work was that extracellular matrix (ECM) deposited by the cell layers would act as an adhesive agent between the individual mesh layers, providing strength to the construct as well as a source for structural elasticity at low strains. In addition, the structural anisotropy of the mesh would inherently guide desired circumferential cell and ECM alignment. Results demonstrate that the cell-mesh constructs exhibited a J-shaped circumferential stress-strain response similar to that of native coronary artery, while also displaying acceptable tensile strength. Furthermore, associated 10T½ cells and deposited collagen fibers showed a high degree of circumferential alignment. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2200-2209, 2016.

Fiber/collagen composites for ligament tissue engineering: influence of elastic moduli of sparse aligned fibers on mesenchymal stem cells.

Electrospun microfibers are attractive for the engineering of oriented tissues because they present instructive topographic and mechanical cues to cells. However, high-density microfiber networks are too cell-impermeable for most tissue applications. Alternatively, the distribution of sparse microfibers within a three-dimensional hydrogel could present instructive cues to guide cell organization while not inhibiting cell behavior. In this study, thin (∼5 fibers thick) layers of aligned microfibers (0.7 µm) were embedded within collagen hydrogels containing mesenchymal stem cells (MSCs), cultured for up to 14 days, and assayed for expression of ligament markers and imaged for cell organization. These microfibers were generated through the electrospinning of polycaprolactone (PCL), poly(ester-urethane) (PEUR), or a 75/25 PEUR/PCL blend to produce microfiber networks with elastic moduli of 31, 15, and 5.6 MPa, respectively. MSCs in composites containing 5.6 MPa fibers exhibited increased expression of the ligament marker scleraxis and the contractile phenotype marker α-smooth muscle actin versus the stiffer fiber composites. Additionally, cells within the 5.6 MPa microfiber composites were more oriented compared to cells within the 15 and 31 MPa microfiber composites. Together, these data indicate that the mechanical properties of microfiber/collagen composites can be tuned for the engineering of ligament and other target tissues. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 1894-1901, 2016.

Static and cyclic mechanical loading of mesenchymal stem cells on elastomeric, electrospun polyurethane meshes.

Biomaterial substrates composed of semi-aligned electrospun fibers are attractive supports for the regeneration of connective tissues because the fibers are durable under cyclic tensile loads and can guide cell adhesion, orientation, and gene expression. Previous studies on supported electrospun substrates have shown that both fiber diameter and mechanical deformation can independently influence cell morphology and gene expression. However, no studies have examined the effect of mechanical deformation and fiber diameter on unsupported meshes. Semi-aligned large (1.75 µm) and small (0.60 µm) diameter fiber meshes were prepared from degradable elastomeric poly(esterurethane urea) (PEUUR) meshes and characterized by tensile testing and scanning electron microscopy (SEM). Next, unsupported meshes were aligned between custom grips (with the stretch axis oriented parallel to axis of fiber alignment), seeded with C3H10T1/2 cells, and subjected to a static load (50 mN, adjusted daily), a cyclic load (4% strain at 0.25 Hz for 30 min, followed by a static tensile loading of 50 mN, daily), or no load. After 3 days of mechanical stimulation, confocal imaging was used to characterize cell shape, while measurements of deoxyribonucleic acid (DNA) content and messenger ribonucleic acid (mRNA) expression were used to characterize cell retention on unsupported meshes and expression of the connective tissue phenotype. Mechanical testing confirmed that these materials deform elastically to at least 10%. Cells adhered to unsupported meshes under all conditions and aligned with the direction of fiber orientation. Application of static and cyclic loads increased cell alignment. Cell density and mRNA expression of connective tissue proteins were not statistically different between experimental groups. However, on large diameter fiber meshes, static loading slightly elevated tenomodulin expression relative to the no load group, and tenascin-C and tenomodulin expression relative to the cyclic load group. These results demonstrate the feasibility of maintaining cell adhesion and alignment on semi-aligned fibrous elastomeric substrates under different mechanical conditions. The study confirms that cell morphology is sensitive to the mechanical environment and suggests that expression of select connective tissue genes may be enhanced on large diameter fiber meshes under static tensile loads.

Electrospun meshes possessing region-wise differences in fiber orientation, diameter, chemistry and mechanical properties for engineering bone-ligament-bone tissues.

Although bone-patellar tendon-bone (B-PT-B) autografts are the gold standard for repair of anterior cruciate ligament ruptures, they suffer from drawbacks such as donor site morbidity and limited supply. Engineered tissues modeled after B-PT-B autografts are promising alternatives because they have the potential to regenerate connective tissue and facilitate osseointegration. Towards the long-term goal of regenerating ligaments and their bony insertions, the objective of this study was to construct 2D meshes and 3D cylindrical composite scaffolds - possessing simultaneous region-wise differences in fiber orientation, diameter, chemistry and mechanical properties - by electrospinning two different polymers from off-set spinnerets. Using a dual drum collector, 2D meshes consisting of an aligned polycaprolactone (PCL) fiber region, randomly oriented poly(lactide-co-glycolide) (PLGA) fiber region and a transition region (comprised of both PCL and PLGA fibers) were prepared, and region-wise differences were confirmed by microscopy and tensile testing. Bone marrow stromal cells (BMSCs) cultured on these meshes exhibited random orientations and low aspect ratios on the random PLGA regions, and high aspect ratios and alignment on the aligned PCL regions. Next, meshes containing an aligned PCL region flanked by two transition regions and two randomly oriented PLGA regions were prepared and processed into 3D cylindrical composite scaffolds using an interpenetrating photo-crosslinkable polyethylene glycol diacrylate hydrogel to recapitulate the shape of B-PT-B autografts. Tensile testing indicated that cylindrical composites were mechanically robust, and eventually failed due to stress concentration in the aligned PCL region. In summary, this study demonstrates a process to fabricate electrospun meshes possessing region-wise differences in properties that can elicit region-dependent cell responses, and be readily processed into scaffolds with the shape of B-PT-B autografts.

Electrospun fibre diameter, not alignment, affects mesenchymal stem cell differentiation into the tendon/ligament lineage.

Efforts to develop engineered tendons and ligaments have focused on the use of a biomaterial scaffold and a stem cell source. However, the ideal scaffold microenvironment to promote stem cell differentiation and development of organized extracellular matrix is unknown. Through electrospinning, fibre scaffolds can be designed with tailorable architectures to mimic the intended tissue. In this study, the effects of fibre diameter and orientation were examined by electrospinning thin mats, consisting of small (< 1 µm), medium (1-2 µm) or large (> 2 µm) diameter fibres with either random or aligned fibre orientation. C3H10T1/2 model stem cells were cultured on the six different electrospun mats, as well as smooth spin-coated films, and the morphology, growth and expression of tendon/ligament genes were evaluated. The results demonstrated that fibre diameter affects cellular behaviour more significantly than fibre alignment. Initially, cell density was greater on the small fibre diameter mats, but similar cell densities were found on all mats after an additional week in culture. After 2 weeks, gene expression of collagen 1α1 and decorin was increased on all mats compared to films. Expression of the tendon/ligament transcription factor scleraxis was suppressed on all electrospun mats relative to spin-coated films, but expression on the large-diameter fibre mats was consistently greater than on the medium-diameter fibre mats. These results suggest that larger-diameter fibres (e.g. > 2 µm) may be more suitable for in vitro development of a tendon/ligament tissue.

Cellularized cylindrical fiber/hydrogel composites for ligament tissue engineering.

Electrospun meshes suffer from poor cell infiltration and limited thickness, which restrict their use to thin tissue applications. Herein, we demonstrate two complementary processes to overcome these limitations and achieve elastomeric composites that may be suitable for ligament repair. First, C3H10T1/2 mesenchymal stem cells were incorporated into electrospun meshes using a hybrid electrospinning/electrospraying process. Second, electrospun meshes were rolled and formed into composites with an interpenetrating polyethylene glycol (PEG) hydrogel network. Stiffer composites were formed from poly(lactic-co-glycolic acid) (PLGA) meshes, while softer and more elastic composites were formed from poly(ester-urethane urea) (PEUUR) meshes. As-spun PLGA and PEUUR rolled meshes had tensile moduli of 19.2 ± 1.9 and 0.86 ± 0.34 MPa, respectively, which changed to 11.6 ± 4.8 and 1.05 ± 0.39 MPa with the incorporation of a PEG hydrogel phase. In addition, cyclic tensile testing indicated that PEUUR-based composites deformed elastically to at least 10%. Finally, C3H10T1/2 cells incorporated into electrospun meshes survived the addition of the PEG phase and remained viable for up to 5 days. These results indicate that the fabricated cellularized composites are support cyclic mechanical conditioning, and have potential application in ligament repair.

Calcium phosphate ceramics in bone tissue engineering: a review of properties and their influence on cell behavior.

Calcium phosphate ceramics (CPCs) have been widely used as biomaterials for the regeneration of bone tissue because of their ability to induce osteoblastic differentiation in progenitor cells. Despite the progress made towards fabricating CPCs possessing a range of surface features and chemistries, the influence of material properties in orchestrating cellular events such as adhesion and differentiation is still poorly understood. Specifically, questions such as why certain CPCs may be more osteoinductive than others, and how material properties contribute to osteoinductivity/osteoconductivity remain unanswered. Therefore, this review article systematically discusses the effects of the physical (e.g. surface roughness) and chemical properties (e.g. solubility) of CPCs on protein adsorption, cell adhesion and osteoblastic differentiation in vitro. The review also provides a summary of possible signaling pathways involved in osteoblastic differentiation in the presence of CPCs. In summary, these insights on the contribution of material properties towards osteoinductivity and the role of signaling molecules involved in osteoblastic differentiation can potentially aid the design of CPC-based biomaterials that support bone regeneration without the need for additional biochemical supplements.

Degradable segmented polyurethane elastomers for bone tissue engineering: effect of polycaprolactone content.

Segmented polyurethanes (PURs), consisting of degradable poly(a-hydroxy ester) soft segments and aminoacid-derived chain extenders, are biocompatible elastomers with tunable mechanical and degradative properties suitable for a variety of tissue-engineering applications. In this study, a family of linear PURs synthesized from poly(ϵ-caprolactone) (PCL) diol, 1,4-diisocyanobutane and tyramine with theoretical PCL contents of 65-80 wt% were processed into porous foam scaffolds and evaluated for their ability to support osteoblastic differentiation in vitro. Differential scanning calorimetry and mechanical testing of the foams indicated increasing polymer crystallinity and compressive modulus with increasing PCL content. Next, bone marrow stromal cells (BMSCs) were seeded into PUR scaffolds, as well as poly(lactic-co-glycolic acid) (PLGA) scaffolds, and maintained under osteogenic conditions for 14 and 21 days. Analysis of cell number indicated a systematic decrease in cell density with increasing PUR stiffness at both 14 and 21 days in culture. However, at these same time points the relative mRNA expression for the bone-specific proteins osteocalcin and the growth factors bone morphogenetic protein-2 and vascular endothelial growth factor gene expression were similar among the PURs. Finally, prostaglandin E2 production, alkaline phosphatase activity and osteopontin mRNA expression were highly elevated on the most-crystalline PUR scaffold as compared to the PLGA and PUR scaffolds. These results suggest that both the modulus and crystallinity of the PUR scaffolds influence cell proliferation and the expression of osteoblastic proteins.

Response of bone marrow stromal cells to graded co-electrospun scaffolds and its implications for engineering the ligament-bone interface.

Biomaterial scaffolds with gradients in architecture, mechanical and chemical properties have the potential to improve the osseointegration of ligament grafts by recapitulating phenotypic gradients that exist at the natural ligament-bone (L-B) interface. Towards the larger goal of regenerating the L-B interface, this in vitro study was performed to investigate the potential of two scaffolds with mineral gradients in promoting a spatial gradient of osteoblastic differentiation. Specifically, the first graded scaffold was fabricated by co-electrospinning two polymer solutions (one doped with nano-hydroxyapatite particles) from offset spinnerets, while the second was created by immersing the first scaffold in a 5 × simulated body fluid. Rat bone marrow stromal cells, cultured in the presence of osteogenic supplements, were found to be metabolically active on all regions of both scaffolds after 1 and 7 days of culture. Gene expression of bone morphogenic protein-2 and osteopontin was elevated on mineral-containing regions as compared to regions without mineral, while the expression of alkaline phosphatase mRNA revealed the opposite trend. Finally, the presence of osteopontin and bone sialoprotein confirmed osteoblastic phenotypic maturation by day 28. This study indicates that co-electrospun scaffolds with gradients in mineral content can guide the formation of phenotypic gradients and may thus promote the regeneration of the L-B interface.

Fabrication and characterization of poly(lactic-co-glycolic acid) microsphere/amorphous calcium phosphate scaffolds.

Although hydroxyapatite (HAP) and ß-tricalcium phosphate have been used extensively as osteoconductive minerals in biomaterial scaffolds for bone regeneration, they lack the capacity to stimulate osteoblastic differentiation of progenitor cells. In contrast, amorphous calcium phosphates (ACPs), which convert to HAP under aqueous conditions, have the potential to facilitate osteoblastic differentiation through the transient local release of calcium and phosphate ions. Therefore, in this study ACPs were synthesized using zinc and zirconia divalent cations as stabilizers (denoted ZnACP and ZrACP, respectively) and compared to HAP. Analysis of ion release into serum-containing cell culture medium revealed transiently elevated levels of calcium and phosphorous, consistent with the enhanced solubility of ZrACP and ZnACP relative to HAP. In addition, X-ray diffraction analysis revealed partial conversion of ZrACP to HAP but no conversion of ZnACP after 96 h. Next, scaffolds were fabricated by sintering mixtures of 300-500 µm poly(D,L-lactic-co-glycolic acid) (PLGA) microspheres and 0.5 wt% calcium phosphate mineral (HAP, ZrACP or ZnACP) at 70 °C for 24 h. Scanning electron microscopy revealed a porous microsphere matrix with calcium phosphate particulates clinging to the microsphere surfaces both prior to and after 14 days in culture medium. Finally, the incorporation of calcium phosphate resulted in a lower compressive modulus in the range 127 to 74-89 MPa. Taken together, these results indicate that ZrACP, ZnACP and HAP minerals exhibit very different properties, and therefore may elicit different osteoblastic responses in vitro.

Nerve growth factor-immobilized electrically conducting fibrous scaffolds for potential use in neural engineering applications.

Engineered scaffolds simultaneously exhibiting multiple cues are highly desirable for neural tissue regeneration. To this end, we developed a neural tissue engineering scaffold that displays submicrometer-scale features, electrical conductivity, and neurotrophic activity. Specifically, electrospun poly(lactic acid-co-glycolic acid) (PLGA) nanofibers were layered with a nanometer thick coating of electrically conducting polypyrrole (PPy) presenting carboxylic groups. Then, nerve growth factor (NGF) was chemically immobilized onto the surface of the fibers. These NGF-immobilized PPy-coated PLGA (NGF-PPyPLGA) fibers supported PC12 neurite formation ( 28.0±3.0% of the cells) and neurite outgrowth (14.2 µm median length), which were comparable to that observed with NGF (50 ng/mL) in culture medium ( 29.0±1.3%, 14.4 µm). Electrical stimulation of PC12 cells on NGF-immobilized PPyPLGA fiber scaffolds was found to further improve neurite development and neurite length by 18% and 17%, respectively, compared to unstimulated cells on the NGF-immobilized fibers. Hence, submicrometer-scale fibrous scaffolds that incorporate neurotrophic and electroconducting activities may serve as promising neural tissue engineering scaffolds such as nerve guidance conduits.

In vitro evaluation of osteoblastic differentiation on amorphous calcium phosphate-decorated poly(lactic-co-glycolic acid) scaffolds.

Calcium phosphate-decorated polyester matrices are promising scaffolds for bone tissue engineering that combine the tunable degradation of synthetic polymers and the osteoconductivity of calcium phosphate minerals. In this study, scaffolds decorated with stabilized amorphous calcium phosphate (ACP) minerals-which exhibit sustained dissolution and release of calcium and phosphate ions-were tested for their ability to support osteoblast proliferation and stimulate differentiation. The two ACPs tested were zirconia-hybridized ACP (ZrACP), which releases ions over a few days and converts in aqueous solution to hydroxyapatite (HAP), and zinc-hybridized ACP (ZnACP), which has a longer period of sustained ion release. MC3T3-E1 pre-osteoblasts were cultured in these scaffolds for up to 21 days, and cell number, alkaline phosphatase (ALP) activity and expression of osteogenic and bone-specific proteins were measured. Cell number, prostaglandin E(2) (PGE(2) ) synthesis and osteopontin (OPN) mRNA expression were elevated on calcium phosphate-decorated scaffolds relative to PLGA controls, while mRNA expression of osteocalcin (OCN), bone sialoprotein and bone morphogenetic protein (BMP)-4 were suppressed. Although MC3T3-E1 responses to the two ACPs were not statistically different, ZrACP-which converts more quickly to HAP-gave rise to slightly higher levels of mRNA expression for BMP-4, osterix, vascular endothelial growth factor (VEGF)-A, OCN and OPN, but slightly lower levels of PGE(2) synthesis, ALP activity and cell number. These results indicate that sintered PLGA microsphere scaffolds decorated with 0.5 wt% ZnACP or ZrACP support cell attachment and elicit a series of biological responses, but these responses do not appear to accelerate osteoblast differentiation.

Effect of pulse frequency on the osteogenic differentiation of mesenchymal stem cells in a pulsatile perfusion bioreactor.

Perfusion bioreactors are a promising in vitro strategy to engineer bone tissue because they supply needed oxygen and nutrients and apply an osteoinductive mechanical stimulus to osteoblasts within large porous three-dimensional scaffolds. Model two-dimensional studies have shown that dynamic flow conditions (e.g., pulsatile oscillatory waveforms) elicit an enhanced mechanotransductive response and elevated expression of osteoblastic proteins relative to steady flow. However, dynamic perfusion of three-dimensional scaffolds has been primarily examined in short term cultures to probe for early markers of mechanotransduction. Therefore, the objective of this study was to investigate the effect of extended dynamic perfusion culture on osteoblastic differentiation of primary mesenchymal stem cells (MSCs). To accomplish this, rat bone marrow-derived MSCs were seeded into porous foam scaffolds and cultured for 15 days in osteogenic medium under pulsatile regimens of 0.083, 0.050, and 0.017 Hz. Concurrently, MSCs seeded in scaffolds were also maintained under static conditions or cultured under steady perfusion. Analysis of the cells after 15 days of culture indicated that alkaline phosphatase (ALP) activity, mRNA expression of osteopontin (OPN), and accumulation of OPN and prostaglandin E(2) were enhanced for all four perfusion conditions relative to static culture. ALP activity, OPN and OC mRNA, and OPN protein accumulation were slightly higher for the intermediate frequency (0.05 Hz) as compared with the other flow conditions, but the differences were not statistically significant. Nevertheless, these results demonstrate that dynamic perfusion of MSCs may be a useful strategy for stimulating osteoblastic differentiation in vitro.

Fabrication of a model continuously graded co-electrospun mesh for regeneration of the ligament-bone interface.

Current scaffolds for the regeneration of anterior cruciate ligament injuries are unable to capture intricate mechanical and chemical gradients present in the natural ligament-bone interface. As a result, stress concentrations can develop at the scaffold-bone interface, leading to poor osseointegration. Hence, scaffolds that possess appropriate mechano-chemical gradients would help establish normal loading properties at the interface, while promoting scaffold integration with bone. With the long-term goal of investigating regeneration of the ligament-bone interface, this feasibility study aimed to fabricate a continuously graded mesh. Specifically, graded meshes were fabricated by co-electrospinning nanohydroxyapatite/polycaprolactone (nHAP-PCL) and poly(ester urethane) urea elastomer solutions from offset spinnerets. Next, mineral crystallites were selectively deposited on the nHAP-PCL fibers by treatment with a 5× simulated body fluid (5× SBF). X-ray diffraction and energy-dispersive spectroscopy indicated calcium-deficient hydroxyapatite-like mineral crystallites with an average Ca/P ratio of 1.48. Tensile testing demonstrated the presence of a mechanical gradient, which became more pronounced upon treatment with 5× SBF. Finally, biocompatibility of the graded meshes was verified using an MC3T3-E1 osteoprogenitor cell line. The study demonstrates that graded meshes, for potential application in interfacial tissue engineering, can be fabricated by co-electrospinning.

Hydrogel-electrospun mesh composites for coronary artery bypass grafts.

The aim of the present study was to investigate the potential of hydrogel-electrospun mesh hybrid scaffolds as coronary artery bypass grafts. The circumferential mechanical properties of blood vessels modulate a broad range of phenomena, including vessel stress and mass transport, which, in turn, have a critical impact on cardiovascular function. Thus, coronary artery bypass grafts should mimic key features of the nonlinear stress-strain behavior characteristic of coronary arteries. In native arteries, this J-shaped circumferential stress-strain curve arises primarily from initial load transfer to low stiffness elastic fibers followed by progressive recruitment and tensing of higher stiffness arterial collagen fibers. This nonlinear mechanical response is difficult to achieve with a single-component scaffold while simultaneously meeting the suture retention strength and tensile strength requirements of an implantable graft. For instance, although electrospun scaffolds have a number of advantages for arterial tissue engineering, including relatively high tensile strengths, tubular mesh constructs formed by conventional electrospinning methods do not generally display biphasic stress-strain curves. In the present work, we demonstrate that a multicomponent scaffold comprised of polyurethane electrospun mesh layers (intended to mimic the role of arterial collagen fibers) bonded together by a fibrin hydrogel matrix (designed to mimic the role of arterial elastic fibers) results in a composite construct which retains the high tensile strength and suture retention strength of electrospun mesh but which displays a J-shaped mechanical response similar to that of native coronary artery. Moreover, we show that these hybrid constructs support cell infiltration and extracellular matrix accumulation following 12-day exposure to continuous cyclic distension.

Enhanced polarization of embryonic hippocampal neurons on micron scale electrospun fibers.

Electrospun fibers have been fabricated for wide use as artificial tissue engineering scaffolds. In particular, fibers smaller than a cell body have been extensively employed to mimic natural extracellular matrix (ECM) and to explore specific responses by various cell types. We investigated the effects of various poly(lactic acid-co-glycolic acid) (PLGA) fiber features on embryonic hippocampal neurons in the early developmental stages in terms of initial axon formation (i.e., polarization) and axon orientation. We produced PLGA fibers that have average diameters ranging from 0.44 microm to 2.2 microm and different degrees of fiber alignment (16-58 degrees in angular standard deviation). After 22 h in culture, embryonic hippocampal neurons grown on PLGA fibers exhibited more axon formation with a 30-50% increase over those on spin-coated smooth PLGA films. This improvement was independent of fiber diameter and alignment; however, slightly more polarization was observed on the smaller fibers and the more aligned fibers. In addition, average axon length of the polarized embryonic hippocampal neurons was not significantly different among the PLGA fibers when compared with cells grown on spin-coated PLGA films. These findings suggest that fibers of subcellular diameters stimulate initial axon establishment and guide the direction of axonal extension; however, these fibers do not appear to affect the overall axon length. This information will be valuable in understanding the roles of subcellular features on neuron development and for the design of biomaterials for neural tissue interfacing.

Polypyrrole-coated electrospun PLGA nanofibers for neural tissue applications.

Electrospinning is a promising approach to create nanofiber structures that are capable of supporting adhesion and guiding extension of neurons for nerve regeneration. Concurrently, electrical stimulation of neurons in the absence of topographical features also has been shown to guide axonal extension. Therefore, the goal of this study was to form electrically conductive nanofiber structures and to examine the combined effect of nanofiber structures and electrical stimulation. Conductive meshes were produced by growing polypyrrole (PPy) on random and aligned electrospun poly(lactic-co-glycolic acid) (PLGA) nanofibers, as confirmed by scanning electron micrographs and X-ray photon spectroscopy. PPy-PLGA electrospun meshes supported the growth and differentiation of rat pheochromocytoma 12 (PC12) cells and hippocampal neurons comparable to non-coated PLGA control meshes, suggesting that PPy-PLGA may be suitable as conductive nanofibers for neuronal tissue scaffolds. Electrical stimulation studies showed that PC12 cells, stimulated with a potential of 10 mV/cm on PPy-PLGA scaffolds, exhibited 40-50% longer neurites and 40-90% more neurite formation compared to unstimulated cells on the same scaffolds. In addition, stimulation of the cells on aligned PPy-PLGA fibers resulted in longer neurites and more neurite-bearing cells than stimulation on random PPy-PLGA fibers, suggesting a combined effect of electrical stimulation and topographical guidance and the potential use of these scaffolds for neural tissue applications.

Effect of fiber diameter and alignment of electrospun polyurethane meshes on mesenchymal progenitor cells.

Effective strategies to guide cell alignment and the deposition of an oriented extracellular matrix are critical for the development of anisotropic engineered tissues suitable for the repair of ligament defects. Electrospinning is a promising means to create meshes that can align adherent cells, but the effect of fiber mesh architecture on differentiation has not been examined closely. Therefore, the goal of this study was to determine the effect of fiber diameter and the degree of fiber alignment on mesenchymal progenitor cell morphology, proliferation, and ligament gene expression. Specifically, a poly(ester urethane)urea elastomer was electrospun onto rigid supports under conditions designed to independently vary the mean fiber diameter (from 0.28 to 2.3 microm) and the degree of fiber alignment. Bone marrow stromal cells--seeded onto supported meshes--adhered to and proliferated on all surfaces. Cells assumed a more spindle-shaped morphology with increasing fiber diameter and degree of fiber alignment, and oriented parallel to fibers on aligned meshes. Expression of the ligament markers collagen 1alpha1, decorin, and tenomodulin appeared to be sensitive to fiber diameter and greatest on the smallest fibers. Concurrently, expression of the transcription factor scleraxis appeared to decrease with increasing fiber alignment. These results suggest that the formation of a ligament-like tissue on electrospun scaffolds is enhanced when the scaffolds consist of aligned submicron fibers.