Using Metal-Organic Framework HKUST-1 for the Preparation of High-Conductive Hybrid Membranes Based on Multiblock Copolymers for Fuel Cells.

Novel proton-conducting hybrid membranes consisting of sulfonated multiblock copolymer of polysulfone and polyphenylsulfone (SPES) reinforced with a HKUST-1 metal-organic framework (MOF) (5, 10, and 20 wt. %) were prepared and characterized for fuel cell applications. The presence of the MOF in the copolymer was confirmed by means of FE-SEM and EDS. The hybrid membranes show a lower contact angle value than the pure SPES, in agreement with the water uptake (WU%), i.e., by adding 5 wt. % of the MOF, this parameter increases by 20% and 40% at 30 °C and 60 °C, respectively. Additionally, the presence of the MOF increases the ion exchange capacity (IEC) from 1.62 to 1.93 mequivH+ g−1. Thermogravimetric analysis reveals that the hybrid membranes demonstrate high thermal stability in the fuel cell operation temperature range (<100 °C). The addition of the MOF maintains the mechanical stability of the membranes (TS > 85 MPa in the Na+ form). Proton conductivity was analyzed using EIS, achieving the highest value with a 5 wt. % load of the HKUST-1. This value is lower than that observed for the HKUST-1/Nafion system. However, polarization and power density curves show a remarkably better performance of the hybrid membranes in comparison to both the pure SPES and the pure Nafion membranes.

Loading of the Model Amino Acid Leucine in UiO-66 and UiO-66-NH2: Optimization of Metal-Organic Framework Carriers and Evaluation of Host-Guest Interactions.

Two metal-organic frameworks (MOFs), UiO-66 and UiO-66-NH2, were considered as containers for bioactive chemicals. We provide a synthesis technique, which allowed the production of these materials suitable for biomedical applications. Both MOFs were characterized as single-phase porous materials composed of nanoparticles (30-65 nm) with a ζ-potential of more than 40 mV in water suspension. D,L-Leucine was applied as a model molecule, which allowed us to trace the mechanism of the loading process. We showed that after synthesis, amino groups of UiO-66-NH2 are coordinated with solvent residuals. It results in a similar route of leucine loading in UiO-66 and UiO-66-NH2 samples. Using joint data of thermogravimetric analysis and calorimetry, infrared spectroscopy, and nitrogen adsorption, we revealed that methyl groups of leucine molecules are responsible for bonding of an MOF matrix. We proposed the formation of bonds between CH3 groups and benzene rings of linkers via CH-π interaction. We also assessed the toxicity of the synthesized MOFs toward HeLa cells at 50 µg/mL after 24 h incubation and revealed no negative effects on the viability of the cells, prompting further biomedical research in the areas of small-molecule delivery and cell signaling and metabolism modulation.

ᶫ-Leucine Loading and Release in MIL-100 Nanoparticles.

Synthesis of the MIL-100 metal-organic framework particles was carried out by hydrothermal (HT) and microwave (MW)-assisted methods. Transmission electron microscopy showed formation of microparticles in the course of hydrothermal synthesis and nanoparticles for microwave-assisted synthesis. Powder X-ray diffraction confirmed formation of larger crystallites for hydrothermal synthesis. Particle aggregation in aqueous solution was observed by dynamic light scattering. However, the stability of both samples could be improved in acetic acid solution. Nitrogen sorption isotherms showed high porosity of the particles. ᶫ-leucine molecule was used as a model molecule for loading in the porous micro- and nanoparticles. Loading was estimated by FTIR spectroscopy and thermogravimetric analysis. UV-VIS spectroscopy quantified ᶫ-leucine release from the particles in aqueous solution. Cytotoxicity studies using the HeLa cell model showed that the original particles were somewhat toxic, but ᶫ-leucine loading ameliorated the toxic effects, likely due to signaling properties of the amino acid.